Brazing diamond grits onto AA7075 aluminium alloy substrate with Ag–Cu–Ti filler alloy by laser heating

The brazing of diamond is a promising way to fabricate grinding wheels for efficient machining and precision grinding. This work investigated the feasibility of bonding diamond grits onto Aluminium Alloy 7075 (AA7075) substrate with a Ag–Cu–Ti filler alloy via laser fusion brazing. The interfacial microstructures and the strength of the brazed diamond joints were studied. The cross-section of the brazed diamond joint consists of a molten filler alloy layer, a molten pool, a heat effect zone, a columnar crystal zone and an equiaxed crystal zone. Within the interface of the filler alloy/substrate metal, microstructures observed possibly were Ag(s.s), Al(s.s), TixAl, Al2Cu and Mg intermetallic compounds. A layer of TiC with a thickness of about 30–50 nm was found at the bonding interface of the diamond/filler alloy. The averaged peak shear force of the brazed joints was found to be approximately 39.8 N. The abrasion grinding test indicated that the diamond/AA7075 brazed joint was adequate for grinding. However, the pulled-off of grit was found to be the primary failure of this type of brazed joint. This work broadened the brazing diamond technique and the range of applications of brazed diamond wheels for efficient grinding.     

高强铝合金复合脉冲VPTIG焊缝组织和性能

采用超快速变换复合超音频脉冲方波变极性TIG电弧焊接工艺进行2219-T87高强铝合金焊接,研究分析了焊缝显微组织和接头拉伸性能变化.结果表明,2219-T87铝合金复合超音频脉冲电流变极性焊接接头的组织和性能均发生显著变化,焊缝区显微组织明显细化,由粗大柱状晶向细小等轴晶转变,接头抗拉强度和断后伸长率显著提高.接头断口由脆性断裂主要特征转变为"韧性+脆性"的混合型断裂模式.在一定范围内,脉冲电流频率越高,脉冲占空比越小,作用效果越明显.复合超音频脉冲电流频率为40 kHz,脉冲电流占空比为20%时,接头抗拉强度和断后伸长率分别达到母材金属的70%和58%.     

硼酸酯键合剂在丁羟四组元推进剂中作用机理研究

采用反相气相色谱仪测试了BA-5键合剂,RDX,AP和HTPB-TDI胶片的表面酸碱性参数,并估算出各组分之间的界面相互作用焓。结果表明ΔHBA-RDX和ΔHBA-AP均显著大于ΔHBA-HTPB,证实键合剂BA-5与RDX,AP作用力远大于与粘合剂作用力,能在混合过程中优先迁移吸附在RDX,AP颗粒表面,并产生强烈吸附。采用电子能谱仪定性表征了RDX,AP从HTPB中吸附BA-5的情况。结果表明:随着电子束加速电压降低,测试厚度变小,AP样品中硼原子含量增加,证实BA-5是吸附在AP的表面。结合组分基团活性分析,阐述了BA-5键合剂的作用机理。     

Effect of Rhenium Addition on Isothermal Oxidation Behavior of Tribaloy T-800 Alloy

The effects of 4 wt% rhenium (Re) addition on isothermal oxidation behavior of Tribaloy T-800 alloy have been studied at 800 °C and 1 000 °C in air. At 800 °C, T-800 shows nonuniform oxidation between dendritic and eutectic areas. Re addition clearly promotes the nonuniform oxidation, leading to considerably higher mass gains than that of T-800 at this temperature. At 1 000 °C exposure, the thickness of scale on T-800 increases significantly, accompanied by severe scale spallation during cooling to room temperature. On the contrary, T-800Re shows a marked decrease of oxide growth rate compared to the linear one of T-800 at 1 000 °C. The scale adhesion is also improved with Re addition at this higher temperature. Therefore, the role of Re depends on the exposure temperature. Re addition gives high oxidation rate at 800 °C, however, the excellent oxidation resistance is obtained by the addition of Re at a higher temperature of 1 000 °C.     

真空与磁场热处理改善FeCo合金的软磁性能

针对发电机中转子用FeCo合金(国产牌号1J22)进行了组织结构与磁性能的研究.通过对该合金进行真空处理以及磁场热处理,研究了组织结构对软磁性能的影响规律;研究了附加磁场强度以及热处理温度对磁场处理效果的影响,并结合该合金的磁致伸缩伸缩系数的变化规律,分析了磁场热处理效果的微观机制.当合金组织为轧制态时,磁场热处理效果不明显;在合金的再结晶温度以上进行磁场热处理时,获得了显著的磁场热处理效果,矫顽力下降至72A/m(0~9Oe)以下.     

内氧化制备A1_2O_3/Cu复合材料载流条件下表面磨损形貌和摩擦学性能研究(英文)

Two Al2O3/Cu composites containing 0.24 wt.% Al2O3 and 0.60 wt.% Al2O3 separately are prepared by internal oxidation. Effects of sliding speed and pressure on the frictional characteristics of the composites and copper against brass are investigated and compared. The changes in morphology of the sliding surface and subsurface are examined with scanning electron microscope （SEM） and energy dispersive X-ray spectrum （EDS）. The results show that the wear resistance of the Al2O3/Cu composites is superior to that of copper under the same conditions, Under a given electrical current, the wear rate of Al2O3/Cu composites decreases as the Al2O3-content increases, However, the wear rates of the Al2O3/Cu composites and copper increase as the sliding speed and pressure increase under dry sliding condition. The main wear mechanisms for Al2O3/Cu composites are of abrasion and adhesion; for copper, it is adhesion, although wear by oxidation and electrical erosion can also be observed as the speed and pressure rise.     

铝铜点焊的研究

提出了铝铜过渡接头的点焊新方法,用交流焊机点焊铝铜,解决了Al2O3氧化膜层的破碎问题。从而可利用热活化、压力、电磁搅拌力,使铝铜固溶,扩散和铝液面移动,完成铝铜点焊,获得比铝强度高的焊接接头,为铝代铜的运用提供了一种特殊的途径。     

火箭发动机燃烧室用高强高导Cu-0．8Cr-0．2Zr合金的组织与性能

采用硬度、拉伸力学性能及导电率测试研究了Cu-0.8Cr-0.2Zr合金的力学性能和导电性能,采用金相显微镜(OM)和透射电子显微镜(TEM)观察了不同处理态合金的显微组织。研究结果表明:时效热处理过程中,合金发生回复和再结晶,同时过饱和固溶体分解析出新相,析出的纳米弥散强化相,能显著提高合金的强度,同时保持良好的导电性。Cu-0.8Cr-0.2Zr合金的最佳热处理工艺为:热轧后980℃/1h固溶处理,经70%冷变形,然后再经过450℃/4h时效处理后,硬度、抗拉强度和屈服强度分别为153HB5、29MPa和489Mpa,导电率达到85.1%IACS。研究的加工工艺实现了高强高导,获得了强度和导电率的最佳匹配。     

置氢对TC21合金粉末物理性能和压制性能的影响

采用扫描电镜观察、粉末镶嵌试样、XRD和模压成形等方法,研究了置氢(H,wt%)对TC21合金粉末颗粒形貌、表面状态、显微组织、相组成、显微硬度和压制性能等的影响.结果表明:置氢TC21粉末颗粒形貌为不规则状,粉末主要由亮相α相及暗相β相组成,颗粒显微组织呈片状、α/β集束状和网篮状.随置氢量的增加,置氢TC21粉末显微硬度呈降低趋势;α相逐渐减少,β相逐渐增多,并且有少量的α"相生成;粉末的压缩性能呈先变差后变好的不明显变化趋势,成形性能先变差又逐渐变好,置氢量0.10 wt%,0.39 wt%TC21粉末压制性能较好,置氢量0.22 wt%的TC21粉末的压制性能最差.     

铸造钛铝合金组织与力学性能