Al2O3/hBN自润滑复合材料的制备及显微结构分析

以Al2O3为陶瓷基体,hBN为固润滑组元添加剂,在N2保护下烧成,制得了Al2O3/hBN自润滑复合陶瓷,通过SEM、EDS、XRD等分析探讨了固润滑组元的引入量、添加助熔剂及常压和热压两种烧成条件下材料显微结构的变化。结果表明,hBN引入量为10%时已有足够的量均匀分散在基体中;相同烧成温度下,热压过程中施加的压力可以破坏hBN的卡片房式结构,伴随液相的出现有利于hBN的定向排列,获得了结构致密的自润滑复合陶瓷材料。     

质子辐照Kapton/Al的蒙特卡罗模拟

采用蒙特卡罗方法(MC方法),模拟了质子辐照时质子的能量损失、射程、射程偏离及其产生的空位缺陷和电离能损分布。模拟结果表明:入射能量在10~300keV区间,Kapton/Al对入射质子的阻止本领主要取决于电子阻止本领,在80keV出现峰值,可作为地面模拟试验能量选取的参考;质子在Kapton/Al中的射程分布可近似看作高斯分布,质子射程及其偏离随能量增加而增加;位移缺陷和电离作用是两个相对的过程,低能时主要表现为位移缺陷,高能时表现为电离作用。     

无压浸渗制备Si3N4／Al复合材料的界面反应研究

研究Si3N4多孔预制体的表面氧化程度对无压浸渗制备Si3N4/Al复合材料界面反应以及复合材料性能的影响是复合材料优化设计的基础.不同氧化程度的Si3N4多孔预制体在相同的浸渗工艺下无压浸渗制得Si3N4/Al复合材料,利用EDS,XRD和洛氏硬度计分别测定陶瓷多孔预制体的成份,复合材料的相组成和硬度.结果表明:Si3N4/Al复合材料组成相包括Al,Si3N4,AlN以及少量的Si,Mg2Si,MgO,MgAl2O4;随着氧化程度增加,复合材料内AlN相减少,MgO含量增加,并逐渐出现MgAl2O4相;复合材料的硬度随预制体的氧化程度增加而线性下降;预制体的氧化造成Si3N4和Al之间的反应减弱是硬度下降的重要原因.     

防护涂层对Ni3Al基合金IC6AE微观组织和抗腐蚀性能的影响

采用料浆法和粉末包埋渗法在Ni3Al基等轴晶合金IC6AE上分别制备了Al-Si和NiCr-CrAl涂层,并对Al-Si和NiCr-CrAl涂层及不加涂层的IC6AE合金三种试样进行900℃/20h,40h,60h,80h,100h的涂盐(5wt%NaCl 95wt%Na2SO4)抗腐蚀性能试验.试验结果表明,与Al-Si涂层试样和无涂层IC6AE合金试样相比,NiCr-CrAl涂层试样表现出最好的抗热腐蚀性能;与无涂层的IC6AE合金试样相比,Al-Si涂层试样的抗腐蚀性没有明显的改善.微观结构分析表明,无涂层的IC6AE合金在900℃时经过几个小时后就遭到了严重的腐蚀破坏.涂盐腐蚀100h后,表面生成了一层主要由Mo,Ni的氧化物组成的多孔无保护性的疏松层.对于Al-Si涂层的试样,900℃/100h腐蚀后试样表面生成了大量Mo,Ni的氧化物,此外还有少量Al2O3及NiAl3相,这些相对样品有一定的保护作用.涂覆NiCr-CrAl涂层的样品经900℃/100h腐蚀后,试样表面主要生成了连续致密的Al2O3及NiAl2O4层,并有少量的Mo,Ni的氧化物,因此对合金有着较好的保护作用,抗腐蚀性能得到了显著改善.     

Al2O3(YAG)/LaPO4层状陶瓷复合材料研究

选择Al2O3(YAG)作为基体片层材料,LaPO4作为界面层材料,采用凝胶注模成型技术制备出基体层材料的坯片,然后在基体层坯片上采用浸渍或喷涂工艺附着界面层材料,最后将坯片叠置于模具中热压烧结.制备的陶瓷复合材料微观结构均匀,基体片层厚度为110-150μm,界面层厚度为10～30μm,实测层厚比为11.重点研究工艺参数及界面层成分对层状陶瓷复合材料室温性能的影响.结果表明,氧化物基层状陶瓷复合材料的抗弯强度比基体材料略有下降,但室温断裂韧性达到了13.52MPa·m1/2,是基体材料断裂韧性的3倍.对比氧化物基层状陶瓷复合材料与基体材料在断裂过程中裂纹扩展路径的差异.     

应变速率和温度对NiAl-30Cr-4Mo 共晶合金拉伸性能的影响

研究了温度和应变速率对NiAl-30Cr-4Mo共晶合金的拉伸性能的影响.研究结果表明在同一应变速率(1.67×10-4/s)下,随着温度的升高,材料的塑性增加;在韧脆转变温度(BDTT)923 K以上,随着应变速率的降低,合金的拉伸断口韧窝密集程度增大,合金塑性断裂的趋势越明显,且屈服强度随应变速率的降低而下降.     

Thermal Fatigue Behavior of Ni_3Al Based Superalloy IC6E

The thermal fatigue behavior of Ni3Al based superalloy IC6E during the cycles between 900 ℃/1 000 ℃ and the room tempera-ture was investigated. The experimental results indicate that the primary and secondary thermal fatigue cracks initiate inside or round the borides and then spread away along grain boundaries and/or in interdendritic areas. The fracture of borides and their separation from the matrix at interfaces are mainly responsible for the crack initiation and its spreading. At temperatures higher than 1 000 ℃, the grain boundary oxidation combined with cyclic stresses accelerates the crack growth.     

DC Characteristics of Gamma-ray Irradiated SiGe HBT in Comparison with Si BJT

The changes of DC characteristics of SiGe HBT after being submitted to γ-ray irradiation of 700 krad, 7 000 krad and 10 000 krad were compared to those of Si BJT. Generally speaking, Ib and Ib–Ib0 increase with the doses increasing. For SiGe HBT, with the doses increasing, Ic and Ic–Ic0 as well as the related changes of the current gain (β) will decrease at higher Vbe, while for Si BJT, with the doses increasing, after irradiation, Ib and Ic–Ic0 increase; β and its related changes also decrease with their differences, however, tending to be very small at high doses of 7 000 krad and 10 000 krad. Moreover, given the same doses, the decreases of β are much larger than SiGe HBT, which shows that SiGe HBT’s anti-radiation performance proves to be better than Si BJT. Still, in SiGe HBT, some strange phe-nomena were observed: Ic–Ic0 will increase after the radiation of 7 000 krad in less than 0.65 V and as will β in less than 0.75 V. The mechanism of radiation-induced change in DC characteristics was also discussed.     

钛/铝异质金属搅拌摩擦焊技术研究进展

钛合金和铝合金均具有质轻、比强度高和抗腐蚀性能好等优点,已广泛应用于航空航天、军事工业和公共交通等领域,钛/铝异种金属复合结构的连接逐渐成为研究热点。然而,由于物理和化学性能差异明显,钛/铝焊接难度大,存在成形困难、接头性能较差等问题。搅拌摩擦焊作为一种固相焊接方法,对克服异种材料性能差异带来的焊接困难具有极大的优势。本文综述了钛/铝异质金属搅拌摩擦焊的研究现状,主要涉及焊缝成形、焊接参数、力学特征、冶金结合和连接机制等,以及衍生的搅拌摩擦焊新技术,为钛/铝异质金属结构的轻量化设计提供新思路,并对其未来发展进行了展望。     

扰流环对粉末发动机燃烧流动影响的数值模拟

为了提高粉末火箭发动机的燃烧效率,通过数值模拟方法研究了扰流环的有无、通径及位置对燃烧室燃烧流动特性的影响。结果表明:扰流环会增强Al颗粒和气相的掺混和换热程度,促进Al颗粒蒸发和燃烧,从而提高粉末火箭发动机的燃烧效率。当扰流环通径比在0.538~0.846范围内时,扰流环的通径越小,燃烧效率越高;当扰流环头部距离比在0.3~0.8范围内时,扰流环位置离头部越近,燃烧效率越高。设计扰流环时,应在距离燃烧室头部30%~40%的位置布置小通径的扰流环。