Coupling behavior between adhesive and abrasive wear mechanism of aero-hydraulic spool valves

Leakage due to wear is one of the main failure modes of aero-hydraulic spool valves. This paper established a practical coupling wear model for aero-hydraulic spool valves based on dynamic system modelling theory. Firstly, the experiment for wear mechanism verification proved that adhesive wear and abrasive wear did coexist during the working process of spool valves. Sec-ondly coupling behavior of each wear mechanism was characterized by analyzing actual time-variation of model parameters during wear evolution process. Meanwhile, Archard model and three-body abrasive wear model were utilized for adhesive wear and abrasive wear, respectively. Furthermore, their coupling wear model was established by calculating the actual wear volume. Finally, from the result of formal test, all the required parameters for our model were obtained. The relative error between model prediction and data of pre-test was also presented to verify the accuracy of model, which demonstrated that our model was useful for providing accurate prediction of spool valve’s wear life.     

航天器复合材料胶接连接工艺分析

文章叙述了航天器复合材料胶接工艺应具备的条件,航天器产品常用胶粘剂及其特性,研制航天器复合材料耐久型胶接结构基本要素及复合材料胶接连接工艺特性和品质控制等内容。     

国产中温固化热破胶膜性能

考察了一种适用于卫星太阳翼基板的国产中温固化胶膜的胶接性能和热破工艺性,并分别采用国产和进口胶膜,利用胶膜热破施胶方法制备了碳纤维网格面板/铝蜂窝芯夹层结构,对其弯曲性能进行评价。结果表明,国产胶膜的室温拉伸剪切强度（铝基材）为34.9 MPa,150 ℃时拉伸剪切强度降为10.2 MPa,-150 ℃时拉伸剪切强度降为30.4 MPa。碳纤维复合材料作为胶接基材时,室温拉伸剪切强度为17.5 MPa,破坏模式为基材分层破坏和胶黏剂内聚破坏的混合破坏模式。国产胶膜具有良好的热破工艺特性,在合适的工艺条件下,破孔率优于99.9%,90°板-芯剥离强度为15.4 N/cm;采用国产胶膜制备的蜂窝夹层结构的弯曲性能与采用进口Redux312UL的接近,弯曲刚度为1.94×10⁸ N·mm²,弯曲强度为35.7 MPa。     

一种飞机结构修理胶粘剂性能分析

针对飞机结构修理过程中常用胶粘剂的固化温度高、固化时间长、固化热应力大的问题,以环氧树脂为基本配料,通过添加丁腈橡胶增强胶粘剂的韧性,添加固化剂和硅烷偶联剂缩短固化时间.剪切试验表明,该胶粘剂在80C下经90min固化后剪切强度可达到35MPa,可满足飞机结构损伤平时修理和应急修理的要求.     

红外无损检测技术粘接结构产品应用

介绍了红外无损检测技术的检测原理和对粘接结构产品的试验应用。试验结果表明,红外无损检测技术可以有效的对玻璃钢泡沫夹层、软木粘接、碳纤维蒙皮蜂窝夹层等粘接结构进行产品质量检测,具备广阔的应用前景。     

卫星胶粘剂出气性质测试和预处理结果分析

根据航天工业总公司标准ＱＪ１５５８—８８，对资源一号卫星用１３种胶粘剂材料出气污染性质进行了标准筛选测试和不同预处理条件下的标准筛选测试。测试在中国微可凝挥发物标准测试设备Ｍｉｃｒｏ—ＶＣＭ上完成。引用的标准和设备与目前国际认定标准ＡＳＴＭ—Ｅ５９５—９０完全一致，所测数据具有国际可比性。测试结果分析表明：真空烘烤预处理可明显降低材料总质量损失（ＴＭＬ），但不能明显更改材料水汽回吸性（ＷＶＲ）。     

基于数字图像相关方法的粘接界面细观破坏分析

对粘接界面在拉伸过程的变形破坏过程进行了观察,对获得的图像采用数字图像相关方法进行处理,获得了界面的位移场,进而分析其变形演化过程与细观破坏机理。结果表明:数字图像相关方法可以有效地分析粘接界面中细观破坏过程,界面的细观破坏经历损伤的累积及局部化过程,最终沿某一局部化带发生宏观破坏。     

自动铺放工艺的复合材料预浸带的适宜性评价方法

依据自动铺带头的结构从离型纸与预浸带的作用、预浸带间的粘附性、预浸带对模具的粘附性这3个影响自动铺放成功的方面简介了预浸带的自动铺放适宜性的评价方法。首先,通过离型纸剥离力的测量和比较可以选择出适合自动铺放的离型纸。其次,通过楔子剥离测试预浸带间的平均剥离力,为选择出一定温度下适宜自动铺放的预浸带提供了参考。最后,通过预浸带与垂直金属板间的粘性测量,为选择适宜在金属模具表面自动铺放的预浸料提供指导。     

热真空环境对常用胶接材料性能的影响

空间的热真空环境是造成光电子器件胶接材料性能退化和放气污染的重要因素.为此,考察了几类典型胶接材料的热真空老化和热真空挥发特性,分析了热真空老化后的力学性能变化及真空挥发产物的主要来源,并对热真空挥发预处理方法进行了验证.结果表明软质的硅橡胶与硬质的环氧树脂胶和丙烯酸树脂胶相比有着更大的质量损失,且含有端羟基的缩聚型硅橡胶和环氧树脂胶真空老化后的模量变化较大.通过真空预处理可以作为降低固化胶真空挥发产物来源的一种有效手段.可为宇航用光电子器件胶接材料的设计选型提供参考依据.     

纳米粒子对星用胶粘剂空间环境性能影响的试验研究

对中国卫星上大量应用的几种胶粘剂进行了地球同步轨道环境模拟试验,同时试验了添加纳米SiO2粉体后的影响。研究表明,纳米材料的加入对胶粘剂空间排气性降低、抑制电子辐照、冷热交变循环损伤等有明显作用。研究结果为中国长寿命卫星胶接结构、材料的寿命可靠性提供了相关依据,展现了纳米材料空间应用的前景。