热处理参数对GH2150A合金冲击韧性的影响

研究GH2150A合金经前期热处理与中间热处理后合金组织变化对室温冲击性能的影响。利用光学金相和扫描电镜对合金组织和冲击断口进行观察。结果表明,经过这种热处理可以显著提高合金的室温冲击韧性,比经标准热处理的Ak提高36%。主要原因是该处理改变合金中碳化物的析出数量、形态和分布,减小γ′相的尺寸,从而改变室温冲击的断裂机制。该处理可以使合金得到良好的综合性能。     

Multi-functional SiC/AI Composites for Aerospace Applications

Multi-functional Al-matrix composites with high volume fraction (55%-57%) of SiC particles are produced with the new pres-sureless infiltration fabrication technology, X-ray detection and microscopic observation display the composites which are macroscopi-tally homogeneous without porosity. The investigation further reveals that the SiC/Al composites possess low density (2.94 g/cm3), high elastic modulus (220 GPa), prominent thermal management function as a result of low coefficient of thermal expansion (8 × 10-6 K-1) and techniques, the multi-functional SiC/Al composites have managed to be made into near-net-shape parts. Many kinds of precision com-ponents of space-based optomechanical structures and airborne optoelectronic platform have been turned out. Of them, several typical products are being under test in practices.     

超声导波在大型薄铝板缺陷检测中的应用

 为了提高大型薄板超声检测的速度,研究了超声导波及其在大型薄铝板缺陷检测中的应用。推导了超声导波在大型薄铝板中传播的理论模型,分析了导波的波结构,设计并实践了导波检测薄铝板缺陷的方法。试验结果表明,若选取S0导波模式对1 mm薄铝板进行线扫描检测,在有缺陷的地方会出现明显的回波信号。根据缺陷回波与板端回波的传播时间差,可计算出缺陷的位置。缺陷越大,缺陷回波信号幅值越大。选择对缺陷灵敏度高的导波模式,导波法线扫描检测方式可以有效缩短检测时间,提高检测效率。     

INVESTIGATIONS ON LASER SHOCK-PROCESSING (LSP) TO IMPROVE FATIGUE LIFE OF SMALL HOLE IN AIRCRAFT STRUCTURES

SupportedbytheFoundationofAFFDThelasershock-processing(LSP)usesmechanics-effectproducedbyinteractionoflaserwithmattertoimprovesurfacepropertiesofmaterials.Thatistosay,anintensiveshort-pulselaserwithhigh-powerisusedtoshockthesurfaceofmetal,whichmakescoatingtovaporize,expand,ionize,andthentoformdetonationwavesthattravelintothemetals.Underthishighpressureoftheshockwavesitheplasticdeformationisproducedandastrengtheningsur-'facelayerisformed-Therefore,thefatigueresistanceisimproved.In199O,theF…     

Au基六元合金中的Ni固溶体研究

本文运用TEM.EDS等微观分析手段对Au基六元合金中的Ni固溶体进行了研究。结果表明,Ni固溶体为f,c,c结构(a_(Ni)=0.355nm).经调幅分解形成的置换式固溶体,成分为65at％Ni,10at％Au,18at％Fe,7at％cr,与基体有如下取向关系:(11-1)_(Ni)∥(11-1)_(Au),[011]_(Ni)∥[011]_(Au)。Ni固溶体在合金中起界面强化和弥散强化作用。     

粉末烧结Nd15Fe77B8永磁合金的矫顽力特征

通过测量粉末烧结Ｎｄ１５Ｆ３７７Ｂ８永磁合金的充磁和退磁曲线，结合金相组织及磁畴观察分析，证明该合金的矫顽力是由畴壁的钉扎来控制。     

稳定化对新型2324高纯铝合金组织性能的影响

研究了２３２４－Ｔ３９合金状态厚板未稳定化及经１２５℃／５０ｈ，１５０℃／５０ｈ稳定化处理后室温拉伸性能及其显微结构变化，探讨了热稳定化处理对合金性能的影响。结果表明，冷变形所造成的位错强化也是２３２４－Ｔ３９稳定化后拉伸性能优于２０２４－Ｔ３５１的主要原因。     

振动抛光钛合金叶片的试验研究

介绍了振动抛光装置的结构及工作机理,阐述了抛光钛合金叶片的工艺方法及试验结果,表明该法对加工具有复杂异型曲表面的零件效果较好。     

非晶态（Fe0.5Ni0.5）80—xCrxP14B6合金薄带的磁谱的研究

以阻抗电桥法对非晶态(Fe_(0.5)Ni_(0.5))_(80-z)Cr_zP_(14)B_6(x=0,1,2,3,4,6,10)合金薄带的淬态和等温退火后样品的磁谱进行了测量。结果表明:退火后相对起始磁导宰μ_(?)提高了3.6～6倍,截止频率f_c下降,磁损耗μ_2的磁谱出现了共振峰。同时,等温退火处理对各样品相对起始磁导率的影响比改变Cr元素含量x要大得多。     

非晶态Co_(90-x)T_xZr_(10)合金的热稳定性研究

非晶态合金材料有许多优异的特性,适合于制作多种敏感元件和传感器。近十年来,利用非晶态合金材料制作的各种敏感元件和传感器得到迅速发展,磁场敏感元件和磁强计是其中一个重要方面。由后过渡金属(Fe、Co、Ni)和前过渡金属(Zr、Nb、…)组成的非晶态合金是一类重要的软磁材料,但是目前国内外有关利用这类材料制作磁场敏