C/ C-PAA 与C/ C-FA 弯曲性能对比

通过PIP工艺制备了C/C-PAA、C/C-FA复合材料,对PAA、FA裂解碳的XRD、浸渍效果以及C/C-PAA和C/C-FA的弯曲强度进行了分析.结果表明:PAA裂解碳的炭质量、浸渍效果较好,C/C-PAA弯曲强度比C/C-FA弯曲强度高34.9％,弯曲模量对比不明显.     

电-热耦合对航空复合材料拉伸及疲劳性能的影响

为研究碳纤维增强树脂基复合材料(CFRP)层合板的导电性能和电-热耦合效应及其对拉伸和疲劳性能的影响,主要针对2种不同铺层的试件(单向层合板(UD)[0]8和准各向异性层合板(QI)[45/90/-45/0]s)进行导电及电-热耦合实验和通电状态下的拉伸及疲劳实验。在电-热耦合实验中分别对试件通以1~8A的直流电和交流电,测量其温度场的分布及最高温度,以确定温度对电阻的影响。依据实验现象建立了简化后的电-热耦合分析模型,并与实验结果进行对比,发现两者吻合很好。简化后的电-热耦合模型能够很好地预测试件在达到稳态平衡时的最高温度值。在通电情况下对不同初始状态时的QI试件进行拉伸和疲劳实验,通过实验发现,在疲劳加载过程中无论是通以直流电、交流电或者是改变电流强度和电流频率,对试件的疲劳寿命影响不大,没有发现明显差异,但在实验过程中试件表面的温度会随着电流强度的增加而升高。同时,在监测试件沿着纤维方向的电阻变化时发现,在一定的疲劳载荷下,随着循环次数的增加,试件的电阻会不断增加,这表明试件内部出现了损伤,累积后直至试件断裂。依据实验现象分别建立了电阻模型-1和电阻模型-2,分析计算后发现模型-1能够较好地模拟试件变形的线性阶段(εxx≤0.4%),而模型-2能较好地模拟非线性阶段直至试件断裂(εxx0.4%)。     

人体代谢耗氧模拟方法研究

利用沸石分子筛对氧气和氮气选择性吸附的特性,提出了分子筛吸附-解吸模拟密封舱内人体消耗氧气的方法,研制了能够模拟5人耗氧量的试验装置,并对装置的富氧气体氧浓度、密封舱内气体成分吸附情况、耗氧模拟精度及补氮气功能等进行了测试和分析,经环控生保系统集成性能试验的使用考核,装置出口富氧气体氧浓度可达93%以上,耗氧模拟精度优于5%,基本不消耗密封舱内的其它气体成分,能够较好地模拟人体对氧气的消耗。结果表明:分子筛耗氧模拟方法精度高,对密封舱内气体成分影响小,装置工作稳定性好,适用于长期载人航天任务中密封舱环境参数控制能力的研究。     

纤维增强复合材料涡轮轴结构疲劳寿命预测

研究了连续纤维增强复合材料低压涡轮轴结构在给定低循环载荷作用下的疲劳寿命估算方法.考虑连续纤维增强复合材料结构特性,研究了基于局部应力应变法的低周疲劳寿命预测方法,并对预测方法的有效性进行了验证.基于此方法,计算了某型航空发动机低压涡轮轴的最大应力、应变和疲劳寿命.结果表明:在0°~90°范围内,45°铺层角度的复合材料层疲劳寿命值最大;当金属厚度不变,外层金属和首层复合材料层的疲劳寿命随复合材料厚度增加而增大;当轴结构壁厚保持6mm不变,减小复合材料层的厚度,同时相应增大最内层或最外层金属包套的厚度,其结构疲劳寿命都随着复材层的厚度减小而减小;外层金属包套的寿命则远大于首层复合材料的疲劳寿命.      

陶瓷基复合材料疲劳寿命预测方法

为了建立CMC疲劳寿命预测方法,推广CMC在航空发动机中的应用,根据BHE剪滞模型理论,分析了随着疲劳峰值应力的大小不同,CMC可能出现的4种疲劳迟滞行为,推导了每种迟滞行为下的循环应力-应变公式,模拟了给定应力条件下的疲劳迟滞回线,通过与试验数据对比,证明了迟滞回线模拟的准确性,进一步分析了界面剪应力随疲劳循环数的退化关系。结合界面剪应力退化模型与纤维强度退化模型,设计了纤维应力计算和疲劳寿命计算流程。针对2维编织CMC,根据单胞有限元计算结果提取了纤维束应力,并对CMC进行了疲劳寿命计算,推导了CMC疲劳寿命S-N曲线,其结果与试验数据基本吻合。针对2维编织CMC的疲劳寿命预测方法,可用于编织结构的CMC涡轮导叶疲劳寿命分析。     

热处理对9 Cr13 Mo3 Co3 Nb2 V组织与硬度的影响

采用金相分析、硬度测试等技术手段,研究热处理对马氏体不锈钢9Cr13Mo3Co3Nb2V组织和硬度的影响。结果表明：9Cr13Mo3Co3Nb2V经淬火、冰冷处理及多次回火后,残余奥氏体充分转变为回火马氏体,并产生较强的二次硬化效果,进而获得稳定的组织和高的硬度;在350℃以上回火时,由于组织中二次碳化物的析出,开始出现二次硬化倾向,至480~520℃时,回火硬度达到了最大值。     

Ti2AlNb合金双层辉光等离子表面渗钼的扩散行为研究

Ti2AlNb合金(O相)具有高的比强度、断裂韧性以及优良的抗蠕变性能,因而在航空制造中成为一种颇具吸引力的高温结构材料.但是,较差的耐磨性是其主要的缺陷并限制其实际应用.为解决这一问题,对Ti2AlNb合金进行双层辉光等离子表面渗Mo.探讨主要工艺参数对Mo的扩散行为的影响.采用扫描电镜(SEM)、X射线衍射(XRD)和辉光放电光谱仪(GDS)分析表面合金化层的成分分布和微观结构.测定从表面到中心的显微硬度变化曲线.结果表明温度与时间均对扩散过程具有显著的影响.最后通过回归分析计算出在优化的工艺温度980℃下的扩散系数.     

Preparation and Microstructure of Cu/Ti_3SiC_2 Nanocomposite

Mixed micron-sized Cu/Ti3SiC2 (vol5%) powder was mechanically milled using agate balls and zirconia balls separately. Then followed an examination of it with the FEI-SEM. The experimental results show that, distributed homogenously in Cu matrix, the Ti3SiC2 particles have a size of about 30-50 nm after milled with agate balls for 8 h, while it remains approximately unchanged after milled with zirconia balls. The microstructure of the mixture at different ball-milling stages was also studied. Bulks of Cu/Ti3SiC2 nano-composite were fabricated by hot pressing nano-sized Cu/Ti3SiC2 powder at the temperature of 1 073 K under 100 MPa. Then came an investigation of the effects of the particle size and agglomerate state of Ti3SiC2 as well as the microstructure of Cu/Ti3SiC2 nano-composite. It was found that the nano-sized Ti3SiC2 particles distribute evenly in copper.     

Electrolytic Passivation of Nitinol Shape Memory Alloy in Different Electrolytes

The corrosion behavior of the nitinol alloy was studied in various corrosion media of different Cl^- ion concentrations. The results demonstrate that the Cl^- ion concentration has significant influences on the corrosion behavior of the nitinol alloy. In order to enhance the corrosion resistance, protective films were generated on the surface of the nitinol alloy by means of the electrochemical passivation method, for which five different electrolytic solutions were investigated. The surface analysis indicates full growth of all samples passivated in the different electrolytic solutions with layers, however, showing different morphological features. Without any defects like micro-cracks and pores, the surface of the samples passivated in the molybdate solution turns out smoother and denser than those passivated in other solutions. It is shown that the electro-chemical passivation will reduce Ni content but increase Ti content in the surface, reaching the Mole ratio of Ti：Ni = 9.01：1 on the outermost surface. Potentiodynamic polarization test demonstrates that the samples electrochemically passivated in the molybdate solution present a significant increase in breakdown potential due to titanium enrichment on the outermost surface.     

航空发动机燃烧室火焰筒掺混区特性的研究

采用FLUENT6.2软件对某型航空发动机燃烧室火焰筒掺混区的典型工作状态进行了三维两相湍流燃烧温度场、速度场及油滴轨迹的数值计算。通过对计算结果的分析,得出掺混区的特性:掺混区的冷、热区决定出口温场的冷、热区;掺混区燃烧效率对燃烧室效率有一定的影响;高负荷状态的速度场均很相似;随着负荷的增加,油滴轨迹呈减小趋势,模拟计算结果与试验结果及燃烧室工作特点基本一致。