碳纳米管在金属材料保护中的应用

碳纳米管（简称CNTs）是一类新型碳材料，具有中空无缝管状纳米结构。自Iijima1991年发现CNTs以来，其制备、表征和应用引起人们的极大兴趣。随着CNTs制备工艺获得突破，其潜在的应用前景日益受到关注，CNTs应用研究已经取得长足进展，其范围涉及到纳米电子器件、场发射材料、模板材料、复合材料、储氢材料和传感器组件等领域。CNTs具有优良的力学性能和独特的电学性能等，是复合材料的理想增强相，在CNTs复合材料领域的研究已经取得了一定的成果。     

Preparation and Mechanical Properties of Glass Coats with High Temperature Radar Absorber

BaO-La2O3-B2O3 （BLB） glass, suitable to be used as a sealing between metals, was chosen to be the binder in preparing glass coats on the Ti-alloy substrate. The SiCN nano-powder was introduced as the filler for the absorbing coat because it is considered to be a good high temperature absorber. The effect of the coating temperature and coating time on the tensile strength of the glass coat was investigated and the proper coating parameters to get good mechanical properties were determined. In addition, the effects of the SiCN content on the tensile strength of the absorbing coat were also discussed. Results show that it is possible to prepare the glass coat using the BLB glass as a binder. That the coat formed at 730℃ for 30 min has the best tensile strength witnesses 730 ℃, 30 min to be the proper parameter to prepare the glass coat. The BLB glass coat without SiCN powder possesses good tensile strength and the introduction of the SiCN absorber into the glass coat will lower the tensile strength. As the SiCN content increases, the tensile strength of the absorbing coat decreases, which could be attributed to the aggregation of SiCN in the coats.     

First-principle Calculations of V/Fe Doped Anatase TiO2

The electronic structures of the titanium dioxide（TiO2） doped with V and Fe were analyzed by using first-principle calculations based on the density functional theory（DFT） with the full potential linearized augmented plane wave method （FP-LAPW）. The fully optimized structure and the relaxation introduced by impurity were obtained by minimizing the total energy and atomic forces. The unit cell of the V-doped anatase TiO2 is smaller than that of the non-doped one, but for the Fe-doped one, the case is just the opposite. It is found that the apical Ti-O and impurity-O bond lengths of the V/Fe-doped anatase TiO2 are greater than those of the non-doped structure, but smaller for the equatorial bond length. Through the band structures and the density of states, the V-doped TiO2 is shown to be a kind of half-metal, while the Fe-doped TiO2 a kind of metal. The magnetic moments of the V/Fe-doped system are mainly generated by the dopants. The results may be helpful for us to understand the experimental outcome of this system.     

纳米Fe2O3的制备及其对AP热分解的催化作用

采用溶胶-凝胶法、水热法及强迫水解法,制备了球形、立方形、纺缍形及针形四种不同形貌的纳米Fe2O3粒子.通过透射电子显微镜(TEM)、X衍射(XRD)、比表面积(BET)对纳米粒子的粒径、形貌、结构、比表面积进行了表征,用差示扫描量热仪(DSC)研究了Fe2O3对高氯酸铵(AP)热分解的催化性能.结果表明纳米Fe2O3对AP的高温热分解催化作用较微米的效果好.不同形貌的纳米Fe2O3粒子有着各自不同的比表面积,比表面积较大的纳米纺缍形和针形Fe2O3较比表面积较小的纳米立方形和球形的催化效果好.比表面积最大的纳米针形Fe2O3使AP的高温热分解峰温度降低了67.3℃,表观分解放热提高了785J·g-1,表现出较好的催化性能.     

聚丙烯/纳米SiO2复合材料的结晶行为研究

纳米SiO2经过超声波分散后,用硅烷偶联剂和分散剂A组成的复合偶联剂体系进行表面处理,通过熔融共混法与聚丙烯混合制得聚丙烯/纳米SiO2复合材料.通过DSC分析,研究纳米SiO2对聚丙烯结晶行为的影响.研究发现,纳米SiO2在聚丙烯中起到异相成核的作用,使聚丙烯的结晶温度提高,结晶速率增大,微晶尺寸分布减小.非等温结晶动力学研究表明,不同降温速率下的成核机理基本不变.降温速率越快,单位结晶时间达到的相对结晶度越高.     

纳米CaCO3／PPS复合材料微观结构及性能研究

纳米碳酸钙(CaCO3)与聚苯硫醚(PPS)通过熔融共混挤出制得复合材料,通过透射电镜对纳米碳酸钙的形态及粒径分布进行观察,并用原子力显微镜、力学测试等方法对复合材料微观结构和力学性能进行表征.结果表明,纳米碳酸钙的平均粒径约56nm,从复合材料表面形貌可见纳米碳酸钙分散在树脂基体里,少量粒子变形;复合材料的韧性得到明显提高,在添加量为5wt%时,冲击强度达到74.13kJ/m2,抗拉强度则在10wt%时达到最大,83.73MPa.     

纳米陶瓷复合材料研究进展

介绍了纳米陶瓷复合材料的研究进展，包括纳米陶瓷复合材料的制备工艺、材料性能、纳米补强增韧机理以及纳米与传统补强增韧方法并用技术。     

纳米二氧化硅目标杂化聚酰亚胺复合材料膜的制备与性能表征

原位聚合制备了纳米二氧化硅(SiO2)目标杂化聚酰亚胺(PI)复合材料膜。实验表明,采用溶胶 凝胶法原位聚合制备的纳米SiO2 PI杂化膜在SiO2含量达到20wt%时,仍然是透明的,而且根据电镜观察,SiO2粒子在PI基体中均匀分散。随着SiO2含量的增加,杂化PI复合材料膜的耐热性、动态力学性能、拉伸性能均有不同程度的提高,且吸湿性降低。分析表明,SiO2前驱体在反应初期即被"固定"在聚酰胺酸大分子链的羧基(-COOH)上,然后在酰亚胺化过程中原位生成纳米SiO2粒子,SiO2粒子表面上的大量高活性硅羟基(-Si-OH)与PI大分子链上的羰基(>C=O)形成氢键而实现目标杂化。     

纳米技术在纤维增强树脂基复合材料中的应用

纳米技术是以扫描探针显微镜为技术手段，在纳米尺度(0．1-100nm)上研究，利用原子、分子结构的特性及其相互作用原理，并按人类需要在纳米尺度上直接操纵物质表面的分子、原子甚至电子来制造特定产品或创造纳米级加工工艺的一门新兴交叉技术。     

材料表面薄膜硬度的测试计算

给出了基于纳米硬度试验的表层薄膜的硬度测算方法。首先研究如何利用有限元计算弥补纳米硬度测量在压痕深度小于百纳米时的精度缺陷，进而探讨薄膜一基体材料系统的硬度随压痕深度变化的规律，最后导出了根据实验曲线预测表层薄膜材料的硬度的公式，并进行了实验验证。