温度对溶剂热改性C/C复合材料显微结构和氧化性能的影响

以硼酸三正丁酯、乙酸、B2O3粉体为原料,无水乙醇为溶剂,采用一种新颖的溶胶/凝胶结合溶剂热法对C/C复合材料基体进行了抗氧化改性.采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、能量色散谱仪(EDS)及X射线光电子能谱(XPS)对改性后试样进行了表征.重点研究了溶剂热反应温度对改性后试样的物相组成、微观结构和氧化性能的影响.结果表明:经过溶剂热改性处理后,C/C复合材料表面缺陷被玻璃相B2O3组成的涂层所覆盖,材料内部一部分孔隙也被B2O3相填充,且随着溶剂热温度的上升,试样表面的微裂纹逐渐消失,B2O3涂层的致密度上升;C/C基体的抗氧化性能随着溶剂热改性温度(范围353～433 K)的升高而提高;经433 K溶剂热改性后的C/C复合材料在873 K的空气中氧化16 h后的质量损失仅为4.09％.     

镁合金等离子体氧化时火花变化规律的研究

研究Magoxid工艺中镁合金等离子体氧化的过程,此过程分为三个阶段:普通阳极氧化、微弧氧化以及弧光氧化.随着氧化的进行,施加的电压不断升高,火花由微弧向弧光过渡.而微弧和弧光开始均主要集中于样品的边缘,然后均匀分布于整个样品表面.与微弧氧化阶段相比,弧光氧化阶段火花的数量明显减少,尺寸增大,并且持续的时间延长.与火花变化过程相对应,氧化膜表面孔数量减少,直径逐渐增大.氧化时间超过10min后,氧化膜表面呈现不明显的多孔结构.     

Preparation of SiCp/Al2O3-Al Composites by Directed Metal Oxidation

SiCp/Al2O3-Al composites were synthesized by means of direct metal oxidation method. The composition and microstructures of the composites were investigated using X-ray diffraction （XRD）, scanning electron microscopy （SEM） and metallurgical microscope. The effects of technical parameters on the properties of the product were analyzed. The results indicate that the composite possesses a dense microstructure, composed of three interpenetrated phases. Of them, SiO2 layer prohibits the powdering of the composites; Mg promotes the wetting and infiltration of the system and Si restricts the interfacial reaction while improving the wetting ability between reinforcement and matrix.     

高速电弧喷涂FeCAl涂层组织结构及抗高温氧化性能研究

用高速电弧喷涂技术(HVAS)制备FeCrAl涂层,测试涂层在800℃的氧化性能,研究涂层在喷涂态和氧化后的组织结构.结果表明,由于冷却速率极快,FeCrAl涂层中形成比较多的Fe-Cr非晶态相,还有少量的Cr1.3Fe0.7O3和体心立方晶格的Fe-Cr固溶体,喷涂过程中Al的氧化比较严重.FeCrAl涂层的抗高温氧化性明显高于12Cr1MoV钢,接近于T91钢,涂层具有优异的抗氧化性一方面是由于层片间形成保护性的Cr氧化膜,阻止进一步氧化,也与含有较多抗氧化性好的非晶态相有关.高温氧化后,涂层中部分非晶态相晶化,转变为Fe-Cr晶体相.     

Ti40阻燃钛合金的基础研究

阻燃钛合金具有重要的应用前景,Ti40合金是我国研制的新型阻燃钛合金.重点综述Ti40合金的基础理论研究结果,如变形机理、氧化机理、阻燃机理等.     

电解催化氧化法处理L一乳酸精制残留液的初步研究

电解催化氧化法能很好地降解高浓度有机废水中的有机污染物，是一种高级氧化技术。针对L-乳酸精制残留液CODcr值约高达140000mg/L的特点，本文对电解催化氧化处理L-乳酸精制残留液进行了初步研究。结果表明，在直流电解电流密度为280A／m^2时，电解12小时，并消解5天，CODcr的去除率为98．57％，脱色率为52．77％。     

光催化氧化技术在环境保护中的应用

光催化氧化技术在环境污染防治领域的应用研究已显现出良好的应用前景，尤其是利用太阳为驱动力的光催化降解技术具有充分利用清洁的可再生能源的特点，可用于空气中有害物质、废水中有机污染物、重金属污染物的降解以及微污染饮用水的深度处理。文中还对目前存在的一些问题以及要解决的关键技术进行了简要分析。     

Electrochemical Behavior of Oxide Films of Stainless Steel in 40 kHz Sonicated Sulphate Electrolytes

This paper describes effects of 40 kHz ultrasound on the oxide films of stainless steel in sulphate electrolytes so as to determine the transmitted power and to characterize mass transfer and peak current density on the electrode surface. Emphasis was mainly laid on electrochemical oxidations and peeling mechanism of oxide films in sonicated sulphate solutions (0.5 and 1.0 mol/L). Polarization voltammetry, current response traces and SEM analysis were carried out in order to provide full information as to oxide films surface. Results shows that the rate of electrochemical oxidation, the shape of polarization curves and the surface micrographs in sonicated sul- phate electrolytes are different from those obtained without introduction of ultrasound. It is concluded that ultrasound can change the electro-chemical behavior of oxide films by its cavitaion effects, which would produce transient mechanical impulsive force and enhance electrochemical reactions.     

高温氧化及颗粒冲蚀对C/C-SiC复合材料使用性能的影响

采用3K斜纹碳布和12K无纬布铺层的针刺预制体,经化学气相渗透法（CVI）及先驱体浸渍裂解法（PIP）最终成型C/C-SiC复合材料,采用长时间氧乙炔烧蚀实验及高速颗粒冲蚀实验进行复合材料长时间抗氧化及抗冲刷性能测试,研究影响其抗烧蚀（冲蚀）行为的主要因素。结果表明：经过600 s氧乙炔烧蚀后,C/C-SiC复合材料发生一定程度的烧蚀,采用无纬布预制体较采用斜纹碳布预制体成型的C/C-SiC复合材料的线烧蚀率、质量烧蚀率、烧蚀深度低;两种材料颗粒冲蚀实验结果一致,试样冲刷面呈现明显的机械冲刷的特征,在短短的10 s内,冲刷坑深度能达到7.21～7.25 mm,材料失效严重;而没有颗粒气流冲刷实验时,材料冲蚀程度显著下降。C/C-SiC复合材料在实际使用过程中一般受到气流压力、粒子冲击及高温氧化的综合作用,粒子冲击引起的机械剥蚀比长时间高温氧化产生的热化学烧蚀对C/C-SiC复合材料的失效影响更大,直接影响材料的使用性能。     

工艺参数对2A12铝合金微弧氧化陶瓷层生长的影响

研究了正／负向电流密度、频率和正／负向占空比对铝合金微弧氧化陶瓷层生长的影响,采用扫描电子显微镜（SEM）和X射线衍射仪（XRD）,分析了不同氧化时间陶瓷层表面和截面形貌、成分和相组成,讨论了陶瓷层的生长过程。研究表明,正／负向电流密度相同时,随电流密度的增加膜层厚度增大;而当正向电流密度相同时,负向电流密度增加有利于膜层的生长;成膜速率随脉冲频率和负向占空比增加,均呈现先增大后减小的趋势;陶瓷层总厚度随氧化时间接近于线性增长,致密层占总膜层的比例先快速增加,其后略微下降。SEM结果显示,随氧化时间延长,样品表面膜厚度趋于均匀,界面处氧化膜变得比较平坦。陶瓷层主要由α—Al2O3和γ-Al2O3相组成,随氧化时间的延长,γ-Al2O3相在陶瓷层中的相对含量逐渐减少。而α-Al2O3相的含量逐渐提高。