The changes of DC characteristics of SiGe HBT after being submitted to γ-ray irradiation of 700 krad, 7 000 krad and 10 000 krad were compared to those of Si BJT. Generally speaking, Ib and Ib–Ib0 increase with the doses increasing. For SiGe HBT, with the doses increasing, Ic and Ic–Ic0 as well as the related changes of the current gain (β) will decrease at higher Vbe, while for Si BJT, with the doses increasing, after irradiation, Ib and Ic–Ic0 increase; β and its related changes also decrease with their differences, however, tending to be very small at high doses of 7 000 krad and 10 000 krad. Moreover, given the same doses, the decreases of β are much larger than SiGe HBT, which shows that SiGe HBT’s anti-radiation performance proves to be better than Si BJT. Still, in SiGe HBT, some strange phe-nomena were observed: Ic–Ic0 will increase after the radiation of 7 000 krad in less than 0.65 V and as will β in less than 0.75 V. The mechanism of radiation-induced change in DC characteristics was also discussed.     

塞式喷管底部特性研究

基于实验数据和数值模拟结果,研究了外界反压和底部二次流对塞式喷管底部的影响。实验表明,底部压强分布相对较均匀,底部在不同外界反压下具有不同的气动状态。如果主流在底部受压缩,底部有气动开放的趋势;如果主流在底部受膨胀,底部有气动闭合的趋势;如果底部同时存在压缩和膨胀,其状态与受到压缩和膨胀的相对强弱有关。二次流的注入使底部开闭过渡点的压比值升高,底部闭合后的压强值增大,有利于防止底部开闭过渡时推力出现较大幅度降低。二次流流量达到主流的2.0％后,加大底部二次流流量不再影响底部压强,过多地注入反而会降低塞式喷管的总体效率,1.5％~2.0％主流流量的二次流注入是比较好的选择。     

航空常用铝合金动态拉伸力学性能探究

利用分离式Hopkinson拉杆设备对五种航空常用铝合金2A12-CZ,2A12-M,2024-T351,7050-T74,7050-T7451进行了室温动态拉伸力学性能探究,并利用电子万能试验机对这五种材料进行了准静态拉伸力学性能测试,得到了五种铝合金在不同应变率下的拉伸真实应力应变曲线。试验结果显示:7050系列铝合金有较高的屈服强度,2A12M抗拉强度则最低。五种航空铝合金都表现出不同程度的正的应变率敏感效应,其中2A12-CZ敏感性最强,7050T7451敏感性最弱。五种铝合金动态拉伸失效应变明显大于准静态拉伸失效应变。2A12M与2024T351有较高的动态拉伸失效应变。在试验结果的基础上,选择Johnson-Cook本构模型,Cowper-Symonds本构模型来拟合这五种材料的动态本构,模型预测与试验结果吻合较好。     

大尺寸薄壁钛合金筒体结构的离心精密铸造

采用离心精密铸造方法,初步研究了铸造大尺寸薄壁钛合金筒体(直径660 mm,高750 mm,壁厚4 mm)的可行性。结果表明:离心转速较小时,Ti-6Al-4V筒体无法完整充型,而较大的转速可实现完整充型。对于完整充型的筒体,其内部疏松缺陷数量随转速提高而减少。对于给定转速和具有均匀温度场的型壳,筒体中疏松缺陷数量随熔液路径增长而增加。采用Y2O3面层型壳可获得无α壳层的表面质量良好的精密铸件,其内部疏松可通过热等静压消除。铸件的晶粒度随铸件截面厚度变化改变较大,需通过微合金化和后续热处理等措施加以调整。     

基于细观位错机理的单晶合金高温力学性能模拟

利用基于细观位错运动的蠕变筏化模型对镍基单晶合金CMSX-4在1223K下的拉伸、蠕变、循环、蠕变疲劳交互及各向异性进行模拟,结果表明:拉伸过程中应变率较高时应力略微下降的现象;蠕变条件下应力越大则蠕变第1阶段越明显,而蠕变稳定阶段越短的趋势;蠕变疲劳交互作用下的应力松弛和应变增大;以及单晶3个典型晶体取向的循环应变硬化特征。通过与试验结果对比,验证了此模型在较高温度下对单晶合金性能的综合模拟能力。     

浇注温度对1种新型铸造镍基高温合金组织和拉伸性能的影响

为分析浇注温度与合金的组织结构和力学性能之间的变化关系,通过改变浇注温度获得不同枝晶组织试样,采用金相显微镜和扫描电镜来观察和分析合金的组织结构,结合拉伸性能测试研究了合金的组织结构对拉伸性能的影响。结果表明：降低浇注温度使γ＇相和碳化物得到细化;降低浇注温度提高了合金的拉伸强度,并改善了塑性。     

淬火／回火热处理对TiAl基合金晶粒细化的影响

研究了淬火/回火热处理中淬火温度和回火时间对Ti-48Al-2Cr-0.5Mo合金晶粒细化的影响。研究表明:一定的淬火/回火热处理能将大小约为1000μm的铸态组织细化成为18～30μm的均匀双态组织;TiAl基合金的细化效果严重依赖淬火阶段的加热温度,温度升高,得到的块状组织较细,羽毛状组织体积分数减少,在两相区回火时,高温淬火组织的回火组织较细,而时间的延长,晶粒长大,但不明显。     

环保型镁合金阳极氧化工艺研究

利用正交实验方法对AZ91D压铸镁合金环保型阳极氧化成膜工艺进行了研究.结果表明环保型阳极氧化成膜工艺能在镁合金上形成银灰色的氧化膜层,所得膜层的综合耐蚀性能优于传统含铬工艺DOW17所成的膜;阳极化膜层的主要成分是MgO和Mg3B2O6;膜层具为多孔结构,孔径较均匀;膜层的成分和结构是影响膜层耐蚀性能的主要因素.     

飞机电源系统故障诊断专家系统的分析和设计

应用人工智能理论对某型飞机电源系统进行故障诊断分析。本文给出励磁电流过大故障树模型,建立电源系统知识库和推理机,完成飞机电源系统故障诊断专家系统的设计,进行故障诊断,得出异常或故障信息,为整个飞机非航电系统采用专家系统进行故障诊断提供经验。     

基于人工神经网络的预腐蚀铝合金疲劳性能预测

 通过对BP神经网络算法分析和收敛性改进,从获得的预腐蚀和疲劳试验数据中通过训练建立了LY1 2CZ铝合金腐蚀性能和疲劳特性与预腐蚀温度和时间的映射模型,从而可预测铝合金在一定预腐蚀环境谱下的最大腐蚀深度和疲劳特性。神经网络算法采用 BP算法 ,网络结构采用2-4-2形式。结果表明 ,神经网络用于预腐蚀铝合金的腐蚀状况和疲劳性能预测是可行的