Ti2AlNb基合金的ISM熔炼研究

讨论了Ti2AlNb基合金的熔炼特点,概括介绍了真空水冷铜坩埚感应凝壳熔炼的设备结构原理和工艺技术,结合Ti2AlNb基合金的熔炼实践,研究了合金元素的加入形式、熔炼室真空度对合金铸锭的均匀性以及合金中Al挥发烧损的影响规律。结果表明:采用水冷铜坩埚真空感应凝壳熔炼Ti2AlNb基合金,合金铸锭成分均匀性很好,随着熔炼工艺的不同,Al挥发烧损在5％～10％（质量分数）之间。     

TiAl合金不同钛铝比层片组织的稳定性

对钛铝比为１．１７４、１．１０５和１．０４１的（ＴｉＡｌ）－２．５Ｖ－１Ｃｒ（ａｔ％）合金层片组织在１３２３Ｋ热暴露中的组织变化进行了观察和分析。发现钛铝比对ＴｉＡｌ合金层片组织的稳定性和失稳分解机理有重要影响，钦铝比适当大于１：１（如１．１０５）的合金可以得到稳定性更好的层片组织。     

新型阻燃Ti40合金TIG焊焊接性能研究

研究新型阻燃钛合金Ti40合金的TIG(tungest inert gas)焊焊接性能,采用金相、SEM等方法分析Ti40合金焊缝及热影响区的组织变化.结果表明,Ti40合金钨极氩弧焊焊缝室温、高温拉伸性能良好,冲击性能较低.焊接之后的热处理制度对组织有一定的改善.经500℃×100h热暴露后,晶界粗化,为连续α相.     

Ti-24A1-17 Nb合金的激光焊接

研究了Ti-24Al-17Nb合金的激光焊接及其接头的力学性能.研究结果表明,连续激光氦气双面保护可以获得保护效果可靠、无缺陷、成型良好的焊接接头.焊接热输入增大不利于接头的纵向弯曲塑性,而接头的横向拉伸强度与母材基本相同,塑性可以接近母材的塑性,达到14%～17%.     

Microstructure,porosity and mechanical properties of selective laser melted AlSi10Mg

Finite element modeling (FEM), microscopy, X-ray computed tomography (CT) and mechanical property tests were used to study the microstructure, porosity and mechanical properties of an AlSi10Mg alloy produced by selective laser melting (SLM). The simulation of the melt pool and thermal history under different energy densities produced an optimized result with an energy density of 44.5 J·mm⁻³. The high cooling rate during the SLM process significantly refined the previous α-Al dendrites. The growth direction of the network-like Al-Si eutectic structure at different orientations confirmed the anisotropic nature of the microstructure. Furthermore, the microhardness, tensile testing and fracture analysis results proved that there were no obvious distinctions in the strength between the transverse and longitudinal directions, and that the ductility was anisotropic, possibly due to the shape and distribution of the pores. The pores measured by X-ray CT at different energy densities confirmed that the sphericity of the pores was inversely related to pores volumes. With optimized processing conditions, the porosity of the selective laser melted sample decreased leading to the improved fabricated fuel system component via SLM.     

10cm氙离子推力器变推力特性研究

非重力阻尼的连续、快速、高精度补偿是实现重力梯度测量卫星精细重力场测量的关键技术之一,直接影响到整星工程任务的成败。针对重力梯度测量卫星在轨飞行期间对电推进系统宽范围连续变推力能力的应用需求,分析了10cm氙离子推力器推力调节响应特性。在此基础上,通过对阳极电流、励磁电流和阳极流率等推力高敏感响应参量的组合调节,开展了推力调节试验研究,验证了10cm氙离子推力器宽范围连续变推力调节能力,获得了1～20mN范围内的推力调节性能及其变化规律。试验结果表明：在采用地面供电、供气设备条件下,10cm氙离子推力器能够在100～597W的功率范围内实现0.98～20.29mN的推力宽范围调节,比冲175～3500s,推力分辨率优于50μN。研究为建立10cm氙离子电推进系统的推力控制数学模型及调节控制算法奠定基础。     

Corrosion mechanism investigation of TiN/Ti coating and TC4 alloy for aircraft compressor application

It is imperative to develop multifunctional erosion and corrosion resistant coatings for compressor blades of aircraft engines in harsh environment. PVD (Physical Vapor Deposition) technology has the advances in processing erosion-resistant coatings; however, the performance of PVD coatings to combat corrosion depends on various coating defects. Determining and comparing the corrosion performances of PVD TiN/Ti coating and uncoated TC4 alloy was the main objective of present work. The 960 h salt spray corrosion and 116 h hot corrosion tests were conducted to simulate the grounding and working environments of the aircraft compressors. The corrosion mechanisms due to the coating defects such as pinhole, columnar boundary and large grain were analyzed based on the OM, Confocal microscope, electrochemical measurements, SEM, XRD and EDS results. Owing to the disordered state associated with the columnar boundary and the coating defect, nitrogen could be easily replaced by oxygen in the hot corrosion process, these structures were channels for fast diffusion of oxygen. Moreover, the Gibbs energy changes of Ti oxidation and TiN oxidation were thermodynamically calculated according to the working condition of aircraft compressors, and considerable research effort was focused on mapping out the phase diagram of Ti, TiN and high pressure gases. The findings of this research can provide insights into developing multifunctional coatings for future aircraft engines.     

TC4钛合金激光焊缝超塑性行为研究

研究了TC4钛合金板激光焊缝的超塑性变形行为、组织演变,以及激光焊接板的横向超塑性变形特征.引进等轴化系数表征超塑性变形过程中焊缝组织等轴化进程,并对激光焊接/超塑成型技术基础问题提出了进一步展望.     

阻燃钛合金Ti40的热物理性能及力学性能

作为一种功能性钛合金,Ti40阻燃钛合金的热物理性能数据首次被报道。采用真空自耗电弧熔炼技术制备的Ti40合金铸锭成分均匀,利用热挤压开坯+包套保护锻造方法制备的板坯组织均匀。性能测试结果表明:Ti40合金的室温抗拉强度为950 MPa级,且在500℃下具有良好的热暴露性能、高温蠕变性能和高温持久性能。在室温到600℃范围内,合金的杨氏模量和剪切模量随着温度的升高呈线性下降,泊松比随着温度升高而缓慢增加;线性热膨胀曲线随着温度升高呈抛物线增加,平均线膨胀系数随着温度的升高呈线性增加。     

热处理对激光增材制造Ti2AlNb基合金组织及性能的影响

利用激光增材制造技术制备出Ti-22Al-25Nb合金薄壁试样,分析了沉积态和热处理态试样的宏观形貌、相组成和显微组织,以及不同制度热处理态试样的组织和室温拉伸性能.结果表明,沉积态试样相组成沿沉积高度方向呈现由B2+O+α2→B2+O→B2的变化趋势;热处理态试样的微观组织和相组成均匀,由B2、O、α23相组成;经930℃保温2h空冷的固溶处理和800℃保温24h空冷的时效处理后,合金室温拉伸性能好,抗拉强度为1017MPa,断后伸长率为6.0％.