Advances in fabrication of ceramic corundum abrasives based on sol–gel process

Corundum abrasives with good chemical stability can be fabricated into various free abrasives and bonded abrasive tools that are widely used in the precision machining of various parts. However, these abrasives cannot satisfy the machining requirements of difficult-to-machine materials with high hardness, high strength, and strong wearing resistance. Although superhard abrasives can machine the above-mentioned materials, their dressing and manufacturing costs are high. By contrast, ceramic corundum abrasives fabricated by sol–gel method is a cost-effective product between conventional and superhard abrasives. Ceramic corundum abrasives exhibit self-sharpening and high toughness. In this review, the optimization methods of ceramic corundum abrasive properties are introduced from three aspects: precursor synthesis, particle shaping, and sintering. Firstly, the functional mechanism of seeds and additives on the microstructural and mechanical properties of abrasives is analyzed. Specifically, seeds can reduce the phase transition temperature and improve fracture toughness. The grain size and uniformly dense structure can be controlled by applying an appropriate amount of multicomponent additives. Then, the urgent need of engineering application and machinability of special shape ceramic corundum abrasives is reviewed, and three methods of abrasive shaping are summarized. The micromold replication technique is highly advanced and can be used to prepare functional abrasives. Additionally, the influence of a new sintering method, namely, two-step sintering technique, on the microstructural and mechanical performance of ceramic corundum abrasives is summarized. Finally, the challenge and developmental trend of the optimization of ceramic corundum abrasives are prospected.     

合金元素及第二相对钨的影响

综述了活化烧结元素,合金化元素,杂质元素及化合物对钨合金组织和性能的影响,并对新型钨基合金及其复合材料的研究、开发提出了一些看法。     

复杂陶瓷件烧结过程温度场数值模拟及仿真

随着陶瓷应用领域的不断扩展,对其品质要求也越来越高.而传统的设计工艺与制造过程是相分离的,到最终生产工艺的定型需要大量的反复修改.为解决传统陶瓷设计工艺只能依靠经验的现状,节约成本,缩短生产周期,故开发了复杂陶瓷零构件烧结过程计算机仿真软件.首先借助传热学原理来建立温度场模型,其次借助有限差分法处理温度场模型,编写出此仿真模拟软件的核心计算代码,从而实现了复杂陶瓷零件和组合构件烧结过程中温度场的模拟仿真.      

亚微米晶NiAl-Al2O3复合材料的制备及其烧结-锻造短流程成形

以Ni粉和Al粉为原料,通过机械合金化和真空热压烧结制备了高致密的NiAl-5％Al2O3(体积分数,下同)复合材料,并利用烧结-锻造技术制成了该材料的前缘模拟件.机械球磨后,粉末颗粒充分细化,Ni和Al发生原位反应,并最终生成NiAl-5％Al2O3复合材料粉末.经1300℃真空热压烧结,获得致密的NiAl-Al2O...     

聚苯乙烯粉末选择性激光烧结成型机理的研究

分析了聚苯乙烯粉末材料选择性激光烧结成型机理,并通过填充改性方法提高其成型性能.结果表明,添加无机填料可提高聚苯乙烯粉末材料烧结性能,而且,多种填料同时添加,效果更明显.     

覆膜陶瓷粉末的选择性激光烧结工艺研究及参数优化

研究了选择性激光烧结成形制造过程中激光功率密度、扫描速度、预热温度和激光束扫描间距对烧结成形件致密度的影响,通过正交试验及方差分析,判定了各工艺参数的显著性及其重要性顺序,并给出覆膜陶瓷粉末烧结的最佳工艺参数。     

太空原位制造和修复技术研究现状分析

概述了太空原位制造和修复技术（In—situ Fabrication and Repair,ISFR）的概念和特点,并结合该技术的发展背景,介绍了国内外以选择性激光烧结和电子束熔融技术为代表的太空原位制造、空间钎焊修复、太空基地建筑构建等方向发展现状及趋势。结合我国空间技术事业发展,提出充分借鉴国外相关技术成果,围绕主要应用材料,重点开展空间环境适应性和应用验证研究,并探索利用模拟月壤开展太空原位制造技术研究的设想与建议。     

石墨含量对PEEK基复合涂层性能的影响

利用石墨和聚四氟乙烯(PTFE)对聚醚醚酮(PEEK)进行混杂改性,控制PTFE和PEEK的质量比不变,通过冷压烧结的方法在不锈钢表面制备不同石墨质量分数的PEEK基复合涂层,研究石墨含量对涂层力学和摩擦性能的影响。结果表明:随着石墨质量分数的增多,PEEK基复合涂层的结晶度逐渐下降,涂层的硬度先增高后降低,摩擦因数不断降低,磨损率先降低后上升。在石墨质量分数为4%时,硬度最高21.78HV,摩擦因数为0.0461,磨损率最低为2.06×10~(-6)mm~3/(N·m),这与之前的研究相比,涂层的耐磨性得到大幅提高。但是过高的石墨质量分数会使分子链柔顺性下降、链段运动降低,涂层的耐磨性大大降低。     

等温锻造对Ti-17粉末合金显微组织的影响

采用烧结 等温锻造的方法制备Ti-17粉末合金,对粉末合金制备过程中各工序的密度、显微组织变化规律等进行了试验研究.试验结果表明:经相同条件烧结后,-140目粉末烧结棒材和-80/ 140目粉末烧结棒材分别达到理论密度的98.06%和93.55%,在-80/ 140目粉末烧结棒材显微组织中观察到有大量的残留空隙存在.采用高低温等温锻造工艺能够有效去除粉末合金烧结后残留的空隙,提高合金的密度,使合金的显微组织得到显著细化和均匀化.烧结 等温锻造是制备优质粉末钛合金的有效方法.     

金属零件的一种快速成型制造方法

金属零件的快速制造是快速成型技术的最终目标之一,也是当今快速成型领域的一大研究热点。本文在介绍快速成型技术的一个重要分支－选区激光烧结的基础上,提出了一种基于小功率激光快速成型系统的金属零件成型工艺。这种方法首先烧结金属与有机粘结剂的混合粉末,生成“绿件”,而后除粘、熔渗金属,最终得到致密的金属件。最后,文中给出了加工实例,并对这种工艺的影响因素进行了详细的分析与讨论。