定应变贮存条件下HTPB推进剂填料/黏合剂界面性能

为研究定应变贮存条件下HTPB推进剂的主要失效原因,基于单轴拉伸实验,得到HTPB推进剂的宏观力学性能。基于扫描电镜观察和测试探测液在填料AP,黏合剂基体上的接触角方法,表征了微观界面性能。实验结果显示,随老化时间的延长,最大延伸率显著降低,填料与黏合剂基体黏结变差,黏附功Wa减小,界面张力γsl增大。HTPB推进剂填料与黏合剂基体的界面黏结情况可由填料与黏合剂基体的黏附功、界面张力来表征。定应变作用下推进剂老化后黏附功的值远低于无应变热老化的值,界面张力的值远高于无应变热老化的值,定应变的存在严重影响了推进剂填料/基体界面的黏结。宏观-微观性能的相关性研究表明,最大延伸率和黏附功存在线性相关关系,最大延伸率的降低主要由界面黏结的劣化引起的。     

硼纤维/环氧复合材料界面剪切强度的测试与研究

设计了一种单纤维拔出试样制备方法,分析了单根硼纤维拔出特性;同时采用该方法分别测试了四种硼纤维/环氧复合材料界面剪切强度。固化剂采用异佛尔酮二胺(IPDA)的硼纤维/环氧复合材料界面剪切强度比采用二乙烯三胺(DETA)的提高了44.7%;采用液体丁腈橡胶(LNBR)改性环氧树脂的硼纤维/环氧复合材料界面剪切强度提高了97.7%~135%。     

Zn-Al-Si钎料钎焊铜/铝接头显微组织及性能研究

采用Zn-14.1Al-0.9Si和Zn-21.5Al-1.5Si两种钎料钎焊获得铜/铝接头,研究了Cu/Zn-Al-Si/Al接头Cu母材/钎缝界面结构、钎缝中心区显微组织、接头抗剪切性能和断口形貌.研究发现,Cu/Zn-14.1Al-0.9Si/Al接头和Cu/Zn-21.5Al-1.5Si/Al接头界面结构均为Cu/扩散层/Al4.2Cu3.2Zn0.7,其中Al4.2Cu3.2Zn0.7化合物层厚度分别为1～2 μm和3～4μm.2种铜/铝接头钎缝中心区均由α-Al固溶体,η-Zn固溶体,Zn-Al共晶和Si单质组成,未发现脆性CuAl2化合物.由于具有较薄的界面化合物层,在剪切力作用下,Cu/Zn-14.1Al-0.9Si/Al接头断裂一部分起源于Al4.2Cu3.2Zn0.7化合物层,另部分起源于界面扩散层,而Cu/Zn-21.5Al-1.5Si/Al接头断裂均起源于较厚的Al4.2Cu3.2Zn0.7化合物层.因此,Cu/Zn-14.1Al-0.9Si/Al接头的抗剪切强度高于Cu/Zn-21.5Al-1.5Si/Al接头,分别为60.1MPa和55.6MPa.     

复合固体推进剂细观损伤扫描电镜实验及数值模拟

对复合固体推进剂进行单向拉伸载荷条件下的原位扫描电镜观察实验,分析其受载条件下的细观损伤发生及扩展特性。基于原位电镜图片,运用数字图像处理技术提取推进剂细观形貌,建立了推进剂椭圆形颗粒填充模型,对受载条件下颗粒与基体之间的脱粘行为进行数值模拟。研究表明,数值分析结果能反映推进剂受载条件下的细观损伤发生及扩展特性。     

高性能铝基复合材料的颗粒分布及界面结合

采用常规粉末冶金和高能球磨粉末冶金法制备了B4Cp/Al复合材料，研究了B4C颗粒分布与界面结合特点、形成机制以及对材料性能的影响。结果表明，17％（体积分数）B4Cp/6061Al复合材料的屈服和抗拉强度分别为415MPa和470MPa，比常规粉末冶金复合材料分别提高了69％和70％。微观分析表明，高能球磨粉末冶金复合材料中B4C颗粒均匀分布、颗粒与基体之间存在近百纳米厚度的界面层，界面层由呈带状且有序分布的微细铝晶粒和弥散分布的纳米颗粒组成。高能球磨过程中，铝粉末在钢球表面形成冷焊层，B4C不断被挤入而均匀化是实现颗粒均匀分布的主要机制；球磨过程中铝粉末表面氧化层破碎暴露出新鲜铝表面且与镶嵌与铝粉末中的B4C颗粒形成界面结合是获得良好界面结合复合材料的重要条件     

碳纤维表面特征对碳/环氧复合材料界面性能影响研究

为了研究碳纤维表面特征与碳/环氧复合材料界面剪切强度的定量关系。采用扫描电子显微镜、比表面积分析仪、X射线光电子能谱仪对T800级碳纤维表面形貌、比表面积和表面化学特征进行了测试表征,并使用微珠脱粘法测试了复合材料的界面剪切强度（IFSS）。基于碳纤维比表面积测试结果,引入真实界面面积的概念,重点分析了界面面积和化学特征对IFSS的影响机理和规律。结果表明,不同表面状态的T800级碳纤维比表面积存在明显差异,两种除浆方法处理的碳纤维比表面积相差25.4%。消除界面面积影响的真实界面剪切强度（IFSS’）与碳纤维表面氧碳比呈现出较好的线性相关性,R2达到了0.94。反映出提高碳纤维比表面积和表面氧碳比是改善复合材料界面性能的有效手段。同时,也为定量研究碳纤维表面物理和化学特征对复合材料界面性能的影响提供了一种新的分析思路。     

Brazing diamond grits onto AA7075 aluminium alloy substrate with Ag–Cu–Ti filler alloy by laser heating

The brazing of diamond is a promising way to fabricate grinding wheels for efficient machining and precision grinding. This work investigated the feasibility of bonding diamond grits onto Aluminium Alloy 7075 (AA7075) substrate with a Ag–Cu–Ti filler alloy via laser fusion brazing. The interfacial microstructures and the strength of the brazed diamond joints were studied. The cross-section of the brazed diamond joint consists of a molten filler alloy layer, a molten pool, a heat effect zone, a columnar crystal zone and an equiaxed crystal zone. Within the interface of the filler alloy/substrate metal, microstructures observed possibly were Ag(s.s), Al(s.s), TixAl, Al2Cu and Mg intermetallic compounds. A layer of TiC with a thickness of about 30–50 nm was found at the bonding interface of the diamond/filler alloy. The averaged peak shear force of the brazed joints was found to be approximately 39.8 N. The abrasion grinding test indicated that the diamond/AA7075 brazed joint was adequate for grinding. However, the pulled-off of grit was found to be the primary failure of this type of brazed joint. This work broadened the brazing diamond technique and the range of applications of brazed diamond wheels for efficient grinding.     

低温推进剂热分层研究

通过详细分析热分层产生的机理,阐述了低温流体热分层所引起的流体温度分布、气液界面现象以及箱体压力增加过程。对有关流体热分层的试验研究以及数值模拟的文献进行了整理;对不同低温流体工质、箱体初始设置参数及尺寸参数、箱体形状、壁面曲率大小、壁面是否加肋片以及箱体晃动旋转等对热分层的影响进行了分类总结;对不同热分层数学物理模型进行了系统对比。介绍了不同重力水平下,流体流动状态与热分层的关系。归纳了有关热分层现象的一些重要结论,阐明了我国在该领域开展研究的必要性。最后指出低温流体热分层对推进剂箱体优化设计及安全运行的重要意义。     

碳纤维增强镁基复合材料的界面反应和拉伸性能研究

采用气压浸渗法, 制备了碳纤维增强镁基复合材料. 实验中分别选用了c.p.Mg, AZ31 和AZ91 三种基体材料进行研究. 分别采用了扫描电子显微镜(SEM) 和透射电子显微镜(TEM) 分析了复合材料的拉伸断口和界面微区. 结果发现, 随着基体中Al 含量的增加, 界面处的化学反应逐渐加剧, 界面处不同程度的化学反应导致了不同的界面结合状态和界面结构.采用纯镁基体时, 界面呈现弱结合; 采用AZ31 和AZ91 为基体材料时,界面处出现针状反应产物, 且界面结合都较强.      

基于表面粘结损伤的复合固体推进剂细观损伤数值模拟

为更准确地模拟固体推进剂的细观损伤,研究复合固体推进剂的非线性力学性能,采用分子动力学方法对高填充比复合固体推进剂细观模型进行建模,验证了Surface-based cohesive方法的可行性,并替代经典粘结单元模拟了复合固体推进剂细观颗粒与基体之间界面损伤的产生和聚合.通过对比固体推进剂细观模型的计算结果,研究了复合固体推进剂颗粒粒径、位置的随机分布对固体推进剂细观损伤及宏观力学性能的影响.结果表明,采用Surface-based cohesive方法对固体推进剂细观模型较易进行有限元前处理,易收敛,计算结果比较合理.