针对三维C/C和钨渗铜两种不同材质,开展了发动机喉栓的静态烧蚀及动态烧蚀研究,揭示了静态和互变条件下喉栓发动机的烧蚀规律.试验结果表明,高压静态条件与互变过程相比,喉栓烧蚀率有明显差别,高压静态比互变过程烧蚀更严重,互变过程引起的热环境变化没有造成烧蚀异常增大.因此,在工程中可采用高压静态烧蚀试验来考核喉栓材料,简化试验系统;在文中试验条件下,钨渗铜喉栓最大径向烧蚀率为0.085 mm/s,三维编织C/C材料最大径向烧蚀率为0.545 mm/s,钨渗铜比C/C材料更适用于喉栓;发动机非轴对称结构、粒子冲刷和沉积现象对烧蚀影响较大,采用同轴结构可改善流动的对称性,有利于进一步研究其他因素对烧蚀的影响.     

C/C喉衬烧蚀性能的实验研究

开展不同推进剂和压强对喉衬烧蚀的影响研究,对认识喉衬烧蚀机理和指导设计很有意义.采用小型烧蚀实验发动机,开展了不同压强下无铝双基推进剂和含铝17%的复合推进刺工况下C/C喉衬烧蚀的实验研究,分析了粒子沉积、燃气组分和燃烧室压强等时烧蚀性能的影响.结果表明,随着工作压强的升高,喉衬烧蚀率明显增大,主要机制是热流密度增加和气流剥蚀加剧,粒子沉积减弱;相同压强条件下,含铝复合推进剂工况下C/C喉衬的烧蚀率远小于无铝双基推进剂工况,主要原因是氧化铝沉积严重.对喉村烧蚀起到了一定保护作用.     

环氧基纳米复合材料抗真空紫外辐照性能研究

文章模拟真空紫外辐照条件,研究波长5~200 nm的真空紫外线(VUV)对环氧树脂648以及环氧基纳米复合材料的辐照损伤效应.质量损失、扫描电子显微镜、质谱仪和X射线光电子谱仪分析结果表明:纳米TiO2起到明显抗真空紫外辐照的作用.辐照后,与环氧树脂相比,环氧基纳米复合材料的质量损失大幅度降低,弯曲强度变化较小,出气量和出气成分减少,表面没有新的C峰出现,表面O 1s峰的主要成分没有发生变化.     

航空轴承表面合成DLC薄膜的结构特征和滚动-接触疲劳物理模型

利用等离子体浸没离子注入与沉积（PIIID）复合强化技术,在AISI440C航空轴承钢表面合成了类金刚石碳（DLC）薄膜。Raman光谱分析揭示出所制备的DLC膜层主要是由金刚石键（sp³）和石墨键（sp²）组成的混合无定形碳膜,且sp³键含量大于10%。原子力显微镜（AFM）形貌表明,DLC膜层表面光滑,结构致密均匀,与基体结合良好。被处理薄膜试样在90%置信区间下的疲劳寿命L₁₀,L₅₀,特征疲劳寿命L_a和平均寿命较基体分别延长了10.1,4.2,3.5和3.6倍。ANSYS模拟结果显示,最大剪切应力出现在膜基结合处并且靠近膜层内部,最大值达到2 150 MPa。结合ANSYS模拟结果和扫描电镜（SEM）观察形貌分析发现,膜层内部存在的微观缺陷是滚动接触疲劳裂纹产生的诱因,循环载荷所形成的最大剪切应力和润滑油中污染颗粒的共同作用是疲劳磨坑最终形成的外在动力。建立了循环载荷条件下PIIID DLC/AISI440C轴承接触疲劳破坏的5阶段物理模型。     

基于阻抗内环的新型力外环控制策略

对于空间装配等与环境进行交互的任务,迫切要求空间机器人具有力控制的能力。利用机器人的关节力矩传感器,提出了一种新型的基于阻抗内环的力外环控制策略。在该方法中,内环采用阻抗控制代替传统的位置控制。阻抗控制内环使机器人具有一定的柔顺性,力外环通过期望力与实际力的误差对内环的参考轨迹进行修正,实现了机器人的力跟踪控制。另外,为了验证利用关节力矩传感器间接测量末端接触力的效果,机器人末端安装了一个高精度的JR3腕力传感器用来直接测量实际接触力。在基于位置内环和阻抗内环的力外环控制方式下,进行了机器人接触刚度变化较大环境（海绵、泡沫和铁块）的力跟踪实验。实验表明,当环境刚度变化较大时,相对于传统的力外环方法,本文提出的方法能够实现稳定的力跟踪性能。尤其对于铁块这种刚度很大的环境,该方法的有效性更加明显。     

电化学合成法修饰高模碳纤维表面

采用电化学合成法,分别以对氨基苯甲酸/双酚A(PABA/BPA)、对氨基苯甲酸/聚乙二醇600(PABA/PEG600)为反应体系,修饰高模碳纤维(HMCF)表面;研究了这两种体系下的连续电化学合成工艺,以及反应电位对HMCF性能的影响.通过SEM照片可见,HMCF经PABA/BPA体系修饰后表面存在化合物涂层;由红外光谱分析证实,表面化合物的红外谱图中存在明显的酯基峰.层间剪切强度(ILSS)结果表明,经PABA/BPA体系修饰过的HMCF复合材料的ILSS可达到73.1 MPa,表明PABA/BPA体系对HMCF具有较好的修饰效果.     

The declined phosphorylation of Heat shock protein 27 in rat cardiac muscle after hindlimb unloading

Hindlimb unloading can induce the cardiac atrophy and diminished cardiac function, however, the mechanisms responsible for which remain elusive. The chronic volume unloading of heart, which decreases the local mechanical stress, may lead to cardiac atrophy after hindlimb unloading. Many studies showed that integrin signaling, p38 MAPK, Heat shock protein 27 and cytoskeleton involved in the hypertrophic growth induced by mechanical stress. However, the mechanisms responsible for cardiac atrophy after hindlimb unloading are still unclear. In this study, we used the tail-suspended, hindlimb unloading rat model to simulate the effects of microgravity. Western blot analysis was used to detect the protein expression of Heat shock protein 27, focal adhesion kinase, p38 MAPK and their phosphorylation levels in rat cardiac muscle after 14d hindlimb unloading. The results showed that the phosphorylation levels of both Heat shock protein 27 and p38 MAPK were decreased significantly in rat cardiac muscle after hindlimb unloading. However, the phosphorylation level of focal adhesion kinase was not decreased significantly. The results suggested that Heat shock protein 27, the downstream of p38 MAPK, might play a critical role in the cardiac atrophy in response to simulated microgravity induced by hindlimb unloading.     

半球形伞流固耦合工程算法

降落伞流固耦合模拟非常难以实现,而一些工程设计任务要求迅速高效地完成.为了适应该要求,针对稳定下降阶段的半球形伞,提出了一种流固耦合工程算法.以轴对称伞形为伞衣初始形状,通过流场模拟得到结构模拟所需的伞衣压力系数分布,通过结构模拟得到新的伞衣外形,如此循环,直到伞衣中幅线和伞绳外形趋于稳定为止.结果表明,伞衣外形能迅速收敛,该方法能满足工程设计要求.     

CABAC算术编码器硬件优化实现

为了解决上下文自适应二进制算术编码器(CABAC,Context-based Adaptive Binary Arithmetic Coder)硬件实现吞吐率难以提高的问题,提出了基于数据流动态特性的电路优化方法.通过建立算法的数据流模型,提取出限制硬件实现性能的数据流反馈环路.针对上下文环路,采用3条迭代周期不同的子环路更新具有不同依赖周期的上下文变量,提高了时钟频率和吞吐率;对于字节打包环路,通过提取一类可简化电路结构的数据元素,并为之构建快速旁路,增加了环路的处理速度.基于上述方法并辅以基本的电路优化手段,设计实现在现场可编程门阵列(FPGA,Field-Programmable Gate Array)平台上频率可达309MHz,并且每个时钟周期处理一个编码符号.     

同轴突扩燃烧室低频不稳定燃烧数值模拟

采用大涡模拟耦合预混燃烧方法,建立了液体冲压发动机不稳定燃烧计算模型。对模型发动机进行了不稳定燃烧数值研究,计算得到的发动机内压强振荡和火焰传播过程与文献中的实验数据吻合较好。结果分析表明,突扩构形发动机内大尺度的旋涡结构支配了燃烧室中的火焰传播过程,旋涡运动耦合非稳态的燃烧热释放是激发燃烧室低频压强振荡的重要原因。