防护涂层对Ni3Al基合金IC6AE微观组织和抗腐蚀性能的影响

采用料浆法和粉末包埋渗法在Ni3Al基等轴晶合金IC6AE上分别制备了Al-Si和NiCr-CrAl涂层,并对Al-Si和NiCr-CrAl涂层及不加涂层的IC6AE合金三种试样进行900℃/20h,40h,60h,80h,100h的涂盐(5wt%NaCl 95wt%Na2SO4)抗腐蚀性能试验.试验结果表明,与Al-Si涂层试样和无涂层IC6AE合金试样相比,NiCr-CrAl涂层试样表现出最好的抗热腐蚀性能;与无涂层的IC6AE合金试样相比,Al-Si涂层试样的抗腐蚀性没有明显的改善.微观结构分析表明,无涂层的IC6AE合金在900℃时经过几个小时后就遭到了严重的腐蚀破坏.涂盐腐蚀100h后,表面生成了一层主要由Mo,Ni的氧化物组成的多孔无保护性的疏松层.对于Al-Si涂层的试样,900℃/100h腐蚀后试样表面生成了大量Mo,Ni的氧化物,此外还有少量Al2O3及NiAl3相,这些相对样品有一定的保护作用.涂覆NiCr-CrAl涂层的样品经900℃/100h腐蚀后,试样表面主要生成了连续致密的Al2O3及NiAl2O4层,并有少量的Mo,Ni的氧化物,因此对合金有着较好的保护作用,抗腐蚀性能得到了显著改善.     

直升机桨叶刚柔耦合特性及计算方法分析

为了研究桨叶刚柔耦合特性,采用中等变形梁模型处理桨叶弹性变形,分别采用小转角和有限转角两种方法处理桨叶绕铰的刚性运动。以桨叶扬起下坠碰撞问题为研究对象。计算分析表明:(1)弹性桨叶存在较明显的刚性运动和弹性变形耦合;(2)挥舞角较小时,两种处理方法计算结果一致,均与试验数据吻合较好;(3)挥舞角较大时,刚柔耦合增强,两种处理方法的计算值差别较为明显;(4)桨叶弯曲刚度对桨叶刚柔耦合特性有较明显影响,刚度越小,耦合越强;(5)桨叶如果比较柔软,小转角处理方法计算值相对有限转角处理方法,相位滞后、幅值增加均较为明显,计算桨叶动响应时需引起注意。      

跷跷板旋翼舰面瞬态气弹响应分析及抑制方法

为了研究跷跷板旋翼在舰面起动和停转过程中的瞬态气弹响应问题,本文在中等变形梁的基础上,引入跷跷板旋翼整体挥舞有限转角广义坐标,采用非线性准定常气动模型,根据Hamilton原理建立了基于广义力的跷跷板旋翼动力学方程,舰面流场采用试验测试数据。通过与国外试验数据及计算值的对比验证了本文计算模型的正确性。计算表明,舰面跷跷板旋翼存在桨叶过大挥舞与机体相碰的问题。对于可能防止相碰的机械措施和操纵方式进行了分析。      

冷却剂不同流动方式对膨胀循环推力室再生冷却换热的影响

为了解液体火箭发动机膨胀循环推力室再生冷却换热特性,对某一参考发动机推力室和另外两种面积比的膨胀循环推力室建立三维计算模型,采用数值模拟的方法,考察冷却剂的温升、冷却通道压降以及推力室内壁面温度和热流密度的分布情况.重点比较了不同燃烧室圆柱段长度、冷却剂不同流动方式以及不同面积比对以上结果的影响.计算过程中采用二阶迎风格式离散控制方程.计算结果表明:采用逆流冷却时,通过加长推力室圆柱段长度使推力室受热面积增加70%后,冷却剂温升提高了一倍左右;对膨胀循环推力室进行再生冷却时,采用顺流冷却要比逆流冷却的冷却通道压降低,但同时冷却剂温升也较低,并且对喉部壁面的冷却效果较差.     

ASL3000集成电路测试系统的检定方法

介绍了ASL3000集成电路测试系统的检定方法.通过分析该测试设备的特性,对线性信号、数字信号、混合信号、射频信号、基带信号模块的检定,采用自带通用仪表和检定程序实现;对于自带仪表的检定,则通过定期送检,溯源到国家标准.     

Thermal Fatigue Behavior of Ni_3Al Based Superalloy IC6E

The thermal fatigue behavior of Ni3Al based superalloy IC6E during the cycles between 900 ℃/1 000 ℃ and the room tempera-ture was investigated. The experimental results indicate that the primary and secondary thermal fatigue cracks initiate inside or round the borides and then spread away along grain boundaries and/or in interdendritic areas. The fracture of borides and their separation from the matrix at interfaces are mainly responsible for the crack initiation and its spreading. At temperatures higher than 1 000 ℃, the grain boundary oxidation combined with cyclic stresses accelerates the crack growth.     

Combustion Synthesis of h-BN-SiC Ceramic Composites

The feasibility was demonstrated to fabricate h-BN-SiC ceramics through combustion synthesis of the mixture of boron carbide and silicon powders under 100 MPa nitrogen pressure. The mass fraction of BN and SiC in the combustion products were found to be 72 % and 28 % respectively. The thermodynamics of the synthesis reaction and the adiabatic combustion temperature were calculated on the theoretical ground. The bending strengths of the ceramics were measured to be 65.2 MPa at room temperature and 55 MPa at 1350 ℃. The phase composition and microstructure of the combustion products were identified by X-ray diffraction (XRD) and scanning electron microscopy (SEM).     

联合应用现代优化方法与S2流面计算进行多级涡轮的气动设计

本文联合应用S2流面正问题计算和多级局部优化设计对某三级涡轮进行多级气动优化设计。优化联合采用人工神经网络和遗传算法,流场计算采用全三维粘性流N-S方程求解,计算网格采用H-O-H型网格,即入口段、出口段采用H型网格,叶片区域采用O型网格。通过优化,总效率提高1.1%,总体性能提高,达到设计要求。     

基于模式匹配的中文问答系统

网络信息的迅速增长,传统搜索引擎的不足,促使了人们对问答系统的研究。首先介绍了一些问答系统相关知识;然后重点介绍了我们设计开发的基于模式匹配技术的中文问答系统;最后使用该系统进行实验,并给出实验结果与分析。实验结果表明,基于模式匹配的中文问答系统是有效的。     

基于组件开发的并行过程模型研究

基于组件开发(CBD)是当前软件开发技术的趋势,但目前还缺乏合适的过程模型,从而制约了其优点的发挥.本文定义了一个并行过程模型来描述CBD过程内在的并行性.该模型具有两个并行维:组件维将CBD过程分解为系统开发、已有组件基础上的开发和新组件的开发;过程维将CBD过程分解为需求、设计、实现、测试和维护等子过程.凭借对并行性的分解,可以更清晰地描述CBD的并行过程并能更容易地管理该过程的复杂性.这种CBD二维并行过程模型可以作为诸如统一过程模型等其它模型的内核,因此给出了一个可能的三维并行模型作为范例,该模型还有一个迭代维.最后,通过一个集成平台软件开发的例子,详细阐述了这种并行模型的应用.