国产T700级碳纤维增强双马树脂基复合材料的力学性能

采用扫描电子显微镜(SEM)、反气相色谱(IGC)和X射线光电子能谱仪(XPS)对国产T700级碳纤维和东丽T700S碳纤维的表面形貌、表面能和表面化学特性进行表征,测试两种碳纤维增强双马树脂基复合材料的力学性能,考察国产碳纤维复合材料的界面黏结性能、韧性和湿热性能。结果表明:碳纤维表面特性(表面形貌、表面能和表面化学组成等)对复合材料界面黏结性能具有显著影响;国产T700级碳纤维/QY9611复合材料在室温下的界面黏结性能优于T700S/QY9611复合材料;国产T700级碳纤维/QY9611复合材料的韧性优异,冲击后压缩强度达到了国外先进复合材料IM7/5250-4的水平;经湿热处理后的层间剪切强度仍与T700S/QY9611复合材料相当,说明国产T700级碳纤维/QY9611复合材料具备良好的湿热性能。     

不同纤维预制体结构对SiC_f/PyC/SiBCN复合材料力学性能的影响

使用不同织造方式(二维机织,法向增强2.5维机织和三维五向编织)制备了3种SiC纤维预制体,采用树脂转移模塑(RTM)和聚合物浸渍裂解(PIP)工艺制备了SiC_f/PyC/SiBCN复合材料。观察复合材料的显微组织,测试弯曲强度、拉伸强度、压缩强度等力学性能,探究不同预制体结构对复合材料力学性能的影响行为。结果表明:同一预制体结构在不同方向的纤维分布不同导致材料力学性能的各向异性;不同预制体结构对材料力学性能有着显著的影响。     

飞秒激光能量密度对镍基合金重铸层和加工效率的影响

以航空发动机叶片制孔为导向,结合飞秒激光对单晶镍基高温合金材料的非热熔性损伤阈值(Φth1)和热熔性损伤阈值(Φth2)特征,研究了飞秒激光能量密度(0Φ44.2J/cm2)对制孔重铸层和加工效率的影响规律。研究结果表明:在Φth1ΦΦth2时,镍基合金经飞秒激光加工后加工侧壁没有出现明显的重铸物;在ΦΦth2时,加工侧壁开始出现重铸物,并随着能量密度的增加,重铸层厚度增大。在试验结果的基础上,建立了飞秒激光单脉冲加工深度与能量密度的定量关系。能量密度越高,飞秒激光单脉冲加工深度越大,加工效率越高。     

扩散连接界面缺陷对Ti-6Al-4V合金力学性能的影响

研究了φ4mm与φ2mm的扩散连接界面缺陷对Ti-6Al-4V合金力学性能的影响。当拉伸载荷方向与缺陷平面平行时,材料的强度与塑性与无缺陷材料相当,这是由于此类缺陷对样品受力截面的面积几乎没有影响。含有φ4mm缺陷试样的拉压疲劳寿命展现出很大的分散性,界面缺陷并未成为裂纹萌生的唯一位置。从表面起裂的样品均处于高寿命区域,而绝大部分从缺陷处起裂的样品均落于低寿命区域。有限元分析表明,当缺陷位于中心位置时其引起的应力集中较小,应力分布梯度较小;缺陷位于边缘位置时,应力集中效应增大。     

基于绳系并联机器人支撑系统的SDM动导数试验可行性研究

详细给出了在低速风洞中,采用绳系并联机器人(WDPR)支撑模型,用强迫振荡法进行标准动态模型(SDM)动导数试验可行性的研究。试验中将杆式六分量应变天平内置入模型中以测量模型的气动力和气动力矩,建立了适用于绳系并联机器人支撑系统的模型运动控制子系统和数据采集子系统。采用绳拉力作为参考信号,对气动力矩信号与位姿信号进行数据的同步处理,解决了绳系并联机器人支撑系统应用于动导数试验时所测力矩信号与位姿信号之间的相位差确定问题,给出了WDPR支撑下模型动导数的计算方法。整个试验样机置于某开口式低速直流风洞中进行了俯仰、带偏航角的俯仰以及升沉的动导数试验,通过测量和计算得到各动导数。试验结果与参考文献相比较具有合理的一致性。研究结果表明,采用绳系并联机器人支撑模型进行动导数试验是可行的,至少对于SDM是这样的结果;使用一套绳系并联机器人支撑系统,可以完成多套硬式支撑系统才能完成的动导数试验,从而提高试验效率,降低试验成本。     

动态保障结构下多级多层备件配置优化建模

针对作战编队执行长时间、远距离任务期间,编队后方保障站点变更的情况,结合部队维修保障的特点,基于可修复备件多级管理(METRIC)理论,通过计算编队剩余备件分布规律,建立了动态保障体系结构下基于时变可用度的三级两层备件保障模型。以备件储存空间为约束,可用度为目标,建立了分阶段边际优化模型。列举实例,采用分阶段边际算法对备件方案进行优化,对比分析了动态保障结构下和固定保障结构下装备可用度随时间的变化,并采用蒙特卡罗仿真方法对案例进行实验验证。案例结果表明:采取多个后方站点的保障方式能有效提高装备可用度;案例仿真实验结果与解析结果误差在4%以内。模型可为保障决策者制定备件方案提供辅助决策工具。     

An experimental system for release simulation of internal stores in a supersonic wind tunnel

Aerodynamic parameters obtained from separation experiments of internal stores in a wind tunnel are significant in aircraft designs. Accurate wind tunnel tests can help to improve the release stability of the stores and in-flight safety of the aircrafts in supersonic environments.A simulative system for free drop experiments of internal stores based on a practical project is provided in this paper. The system contains a store release mechanism, a control system and an attitude measurement system. The release mechanism adopts a six-bar linkage driven by a cylinder, which ensures the release stability. The structure and initial aerodynamic parameters of the stores are also designed and adjusted. A high speed vision measurement system for high speed rolling targets is utilized to measure the pose parameters of the internal store models and an optimizing method for the coordinates of markers is presented based on a priori model. The experimental results show excellent repeatability of the system, and indicate that the position measurement precision is less than0.13 mm, and the attitude measurement precision for pitch and yaw angles is less than 0.126°, satisfying the requirements of practical wind tunnel tests. A separation experiment for the internal stores is also conducted in the FL-3 wind tunnel of China Aerodynamics Research Institute.     

基于Ansys的永磁同步电机转子振动分析

振动是电机的重要指标,对电机转子进行振动分析为其结构改进和性能优化提供理论依据。运用Ansys有限元分析软件对永磁同步电机转子进行模态分析,得到该电机转子振动系统的低阶固有频率和模态振型,分析了电机振动特性。 通过电机转子模态试验,求得电机低阶固有频率,对比仿真与试验结果,验证有限元分析结果的可靠性。由结果分析可知,研究对象在额定转速下未产生共振,验证了其结构设计的合理性。研究内容对永磁同步电机的设计和优化有一定的指导意义。     

基于混合控制集预测控制的永磁同步电机电流脉动抑制方法

模型预测控制(MPC)技术近年来在高动态性能电机驱动系统中应用广泛。为了克服传统MPC技术中有限控制集(FCS)造成的稳态电流脉动问题,提出了一种基于混合控制集(MCS)预测控制的永磁同步电机(PMSM)电流脉动抑制方法。分析建立PMSM预测控制系统离散数学模型,并分析电压矢量精度与电流脉动之间的关联性;在此基础上,MCSMPC将电压源型逆变器有限的有效电压矢量数,扩展为多个以占空比形式存在的虚拟电压矢量,并基于上述虚拟电压矢量完成MPC优化问题在线求解;此外,考虑到MCSMPC系统的参数敏感性问题,对MCSMPC系统反馈噪声问题进行分析讨论。最后,搭建双15 kW PMSM对拖样机测试平台进行试验分析,分析内容包括MCS方法动态跟踪特性、电流脉动稳态效果。试验结果表明所提出的MCSMPC方法在保留了传统预测控制技术高动态响应的基础上,可有效降低PMSM稳态电流脉动幅度和运行噪声。     

镍基高温合金DZ125激光再铸层化学研磨的实验研究

研究了镍基高温合金DZ125激光再铸层组织特征、电化学腐蚀行为,并分析了再铸层化学研磨的优化条件,测试了研磨后基体的热疲劳性能。研究发现,DZ125合金激光再铸层主要为枝晶结构,且强化相γ′相析出较少,激光再铸层的耐腐蚀性能明显弱于DZ125合金基体。化学研磨溶液保温在60℃以上、浓度在90%以上时,再铸层的化学研磨高效可靠,研磨后基体表面光滑,无明显腐蚀发生,且基体的热疲劳性能得到明显改善。