Chaboche随动硬化模型参数确定及棘轮效应

采用遗传算法确定不同Chaboche随动硬化模型的参数,得到的3种模型中,四分量模型对棘轮的预测与试验结果符合最好.增大应力幅值或应力平均值,都会使应变峰值增大,应变累积速度加快;利用确定的四分量模型研究加载顺序对棘轮的影响.结果表明,平均应力加载顺序对棘轮预测有较大影响,加载顺序高-低的累积应变低于加载顺序低-高的累积应变,而且先加载的平均应力越大,后加载的载荷产生的累积应变越小;而应力幅值加载顺序对应变累积几乎没有影响.     

统一硬化模型在复杂加载条件下的应用

超固结土模型是能够描述土的剪缩、剪胀、硬化、软化和应力路径依赖性等特性的简单、实用的模型,与剑桥模型相比,仅增加了一个材料参数(Hvorslev面斜率).采用基于SMP(Specialy Mobilized Plane)强度准则的变换应力方法对模型实现了三维化.在模型中应用加卸载准则来反映复杂加载条件下土体的应力应变特性,模拟了随着循环次数的增加,土体会逐渐变硬,剪切模量逐渐增大、孔隙比减小、超固结程度不断增大等趋势.由循环加载以及真三轴试验数据和预测结果的基本吻合表明了模型能够合理地反映复杂加载条件下土的变形特性.      

低掺量石墨水泥基材料的压敏特性

通过减水剂将少量石墨加入水泥基材料中制成石墨水泥基材料试样,采用交流分压电路测量其电阻率,研究其在一次性加载破坏试验中的压敏特性.试验结果表明,低掺量石墨粉作为导电组份加入水泥基材料后会导致其强度降低,但可以使水泥基材料具有一定程度的压敏特性.随着石墨掺量的增加,各组试样电阻率的离散性变小,材料的压敏特性提高,在加载过程电阻率的波动变小.在本试验的测量方法下得到的石墨水泥基材料的压敏特性曲线与混凝土材料的应力应变曲线有相关性,试样的电阻率随着应力的增大而产生变化的过程大体可分为3个阶段,即波动阶段、稳定下降阶段和急剧下降阶段,分别对应混凝土材料应力应变关系的弹性变化、非弹性变化和应变迅速增大阶段.      

高强度铝合金7804-T6板材温拉伸本构方程

通过在293~573K的温度范围内和应变速率为0.0006~0.06s^-1下对高强度铝合金7B04-T6薄板进行温拉伸试验,研究了高强度铝合金温拉伸性能,以及该合金在升温条件下流变应力与变形温度、应变速率之间的关系,可以得出结论:合金的流动应力随温度的升高而降低,随应变速率的升高而升高;延伸率随变形温度的升高而增大,随应变速率的增大而减小,并基于Fields and Backofen方程建立了该型铝合金在温拉伸时应力-应变模型.     

钢管和铜管之塑性应力应变关系实验

对钢管和铜管进行了加载方式不同的各项复合应力实验。实验表明,在简单加载情况下?米捷司塑性条件和依留辛塑性应力应变关系理论很能符合实验结果;在主轴固定的复杂加载情况下,上述理论也大致与实验符合;但在主轴回转较大的情况下,则相差较大。 由于采用了自制的电阻丝片测量变形,使变形的测量范围相当大,故使实验结果能相当明确地说明问题。 在完成本实验的过程中,高镇同同志给予了很多有益的建议,胡文贞等同志协助作了许多实际工作,特此说明。 作为对自制电阻丝片测量塑性变形之应用,并验证和推广现有之塑性理论,我们进行了铜管和钢管之复合应力实验工作。     

砂土硬化特征的描述及其试验验证

采用不同路径下砂土的三轴拉伸和三轴压缩试验结果,分别选用塑性体积应变、塑性剪应变、清华模型硬化参数、塑性功和统一硬化参数H作为硬化参数,在以上硬化参数和应力比空间里探讨了砂土的硬化规律和应力路径相关性.基于修正剑桥模型的屈服函数,采用塑性体积应变、塑性功和H作为硬化参数,推导了分别对应的本构模型.通过饱和塔克拉玛干沙漠砂的三轴试验结果,表明了H在描述砂土应力应变特性上的适用性.      

窄板拉弯成形的数值分析与回弹计算

在考虑加载历史的情况下,为采用数值方法研究窄板拉弯成形,将变形区划分成若干个单元,按塑性变形体积不变条件,确定单元应变.利用增量理论,由差分方程算出应力分布,并分析了加载历史对其影响.依据卸载变形的分析计算,推导出回弹后中性层弯曲半径及弯曲角变化量的计算公式.计算结果表明,先弯曲再拉伸时应力分布规律更利于减小回弹.     

压延过程的应力应变分析

本文利用最大剪应力理论的塑性条件,考虑材料的硬化(应变刚),对筒形件第一次压延的变形区的应力应变分量作了分析。并且在这个基础上,将问题加以简化。这些分析结果表明,一般用的肖夫曼推荐的计算公式是近似的,本文提供了比较精确的结果。这些结果并经实验验证。本文同时对变形区材料的厚度变化及其外沿厚度估计作了研究。     

比例加载下应力幅比对2A12-T4疲劳寿命的影响

采用2A12-T4铝合金漏斗形试件,针对不同拉扭应力幅比,进行了比例加载下多轴高周疲劳寿命试验,研究了不同应力幅比对多轴高周疲劳寿命的影响.针对试验结果,采用3种常用的多轴高周疲劳寿命预测模型,包括等效应力准则、应力不变量准则、临界面准则进行了预测.结果表明:在相同的Von-Mises等效应力下,随着扭转应力幅与拉压应力幅比值的增大,疲劳寿命逐渐升高.等效应力准则的预测结果或过于危险,或过于安全;应力不变量准则的预测结果认为应力幅比的变化对疲劳失效没有影响,与试验结果不符;临界面准则的预测结果优于其他准则.     

Experimental investigation on deformation behavior of TJ-1 lunar soil simulant subjected to principal stress rotation

The knowledge of mechanical properties of lunar soil is of fundamental importance for the coming exploration of the Moon. This paper aims to investigate the fundamental deformation behavior of lunar soil and the effects of the intermediate principal stress coefficient, deviatoric stress ratio, and mean stress during the principal stress rotation. First, an improved technique was proposed to generate homogeneous samples based on the Multi-layer Undercompaction Method. Second, three series of tests on TJ-1 lunar soil simulant under the principal stress rotation were performed with a hollow cylinder apparatus at Tongji University, China. In each series of tests, only one value of the three variables mentioned above was changed while the others were kept constant. The test results demonstrate that the rotation of principal stress can result in significant plastic deformation, volumetric strain, and non-coaxiality (non-coincidence of the increment direction of principal plastic strain with the principal stress direction) of TJ-1 lunar soil simulant. In addition, it is found that the intermediate principal stress coefficient, deviatoric stress ratio, and mean stress have different influences on the four strain components, i.e. _εz,_εr,_εθ${\epsilon }_z\text{,}{\epsilon }_{\text{r}}\text{,}{\epsilon }_{\theta }$ and _γzθ${\gamma }_{z\theta }$, volumetric strain, and non-coaxiality during the principal stress rotation. The influence of deviatoric stress ratio is relatively stronger than the others. Therefore, the influence of principal stress rotation on the deformation behavior of lunar soil should be taken into account carefully in the design and construction of facilities on the lunar surface in the future.     

可重复使用火箭发动机再生冷却槽失效分析

完成了可重复使用液体火箭发动机推力室再生冷却槽热力循环载荷下的蠕变非弹性热结构分析,对比研究了各向同性硬化和随动硬化定律对冷却槽结构分析的影响,并在多循环结构场基础上分析了冷却槽"狗窝"失效过程.结果表明可以通过选取热传导率差别小的内外壁材料、优化几何结构改善温度场及结构场;各向同性和随动硬化结构曲线变化趋势相似,但塑性应变有较大差别,残余应变相差约0.06%;多循环加载中每个循环的结构曲线形状相似并不断右移,硬化效应明显,低周疲劳损伤和蠕变损伤分别取决于循环载荷下的应变和应力值.     

临近空间风切变特性及其对飞行器的影响

基于MERRA再分析资料的风场数据,根据数理统计理论,对酒泉（39.1°N,98.5°E）上空临近空间的20~78 km的大气风场进行了风切变特征分析,并分析了临近空间风切变对飞行器的影响。研究表明,临近空间最多风向在1月和10月为西风,7月为东风,4月在50 km以下为西风,以上为东风;99%概率最大风速在1月最大;最大风引起的风切变存在一定的高度范围。根据最大风和最小风给出了综合矢量风。此外发现临近空间风切变对飞行器产生的风攻角显著,对马赫数为3、5和8的飞行器产生风攻角在69 km最大,分别为8.5°、5.1°和3.2°。      

基于褶皱的平流层浮空器升空结构形变模拟

平流层浮空器囊体材料具有非线性、黏弹性、各向异性和不能抗压等特点,起皱现象是在升空膨胀过程中必然会出现的形变状态,褶皱的扩展会影响整个囊体结构的受力状态,改变囊体变形和应力分布.同时,褶皱的存在还会影响囊体结构的动力学行为和空间环境下的热力学分布.通过主应力-主应变相结合准则对褶皱区域进行判别,采用修正褶皱单元的本构矩阵方程的方法对褶皱区域进行处理,地面充氦气试验证明了新方法的模拟结果更加接近测试值.从而为平流层浮空器设计提供了一种有效的分析方法.     

开孔泡沫塑料的应力松弛问题

开孔泡沫塑料具有良好的能量吸收和缓冲性能, 在工程中得到了广泛的应用, 对其粘弹性行为进行研究具有重要的意义.基于Lederman模型,应用三参数标准线性固体模型考虑基体的粘弹性性能,对开孔泡沫塑料的应力松弛行为进行了研究,并讨论了所加应变载荷、结构参数和泊松比对应力松弛曲线的影响.结果表明:应力松弛曲线对泊松比是不敏感的,并且,应变载荷的增加和相对密度的提高会使应力松弛变得更加明显,但应力响应的初始值和终值的比却不随应变载荷的提高而变化.     

Udimet 720 Li 高温变形特性的粘塑性本构建模研究

采用Chaboche统一粘塑性本构方程,对Udimet 720 Li在700℃时的单调拉伸、循环加载及蠕变特性等复杂的高温变形现象进行了建模研究.探讨了Chaboche本构理论对这些变形现象进行建模的形式,并特别针对快速各向同性软化和非对称循环加载时的平均应力松弛现象,对Chaboche本构理论进行了修正和变化.将经过修正的Chaboche本构理论,与Levenberg-Marquadt非线性优化算法相结合,编制了材料参数优化程序,得到了材料参数值.研究表明,经过修正的Chaboche本构模型可较好地建模镍基高温合金Udimet 720 Li在高温下的各种变形行为.