浆料浸渍工艺制备高性能Al2O3/Al2O3陶瓷基复合材料

为了利于大型构件的制备,采用浆料浸渍工艺,以Nextel 720连续氧化铝纤维增韧,通过一次烧结过程制备了Al₂O₃/Al₂O₃陶瓷基复合材料。测试了复合材料的物理及力学性能,并采用光学显微镜、SEM对试样的微观形貌进行了表征。结果表明：复合材料的体积密度为2.64 g/cm³,显气孔率为26%,材料基体呈现典型的多孔结构特征;室温及1 200 ℃,复合材料厚度方向的热导率分别为3.49及2.04 W/（m·K）;200～1 200 ℃,复合材料面内方向的热膨胀系数为（4.7～7.1）×10^-6/K;复合材料室温、1 100及1 200 ℃拉伸强度分别为202.4、222.4及228.4 MPa,试样断面纤维拔出明显;室温弯曲强度为200.5 MPa,试样发生韧性断裂;层剪强度为21.0 MPa。制备的材料主要性能与美国ATK-COI陶瓷公司的同类型材料相当,部分力学性能更优异。     

3种铝合金材料动态性能及其温度相关性对比研究

 对3种铝合金2024-T351、7050-T7451和LY12-CZ进行了温度在77～573 K的静、动态压缩（应变率10^-3～6 000/s）和拉伸（应变率10^-3～3 000/s）试验,分别得到了3种铝合金材料的应力 应变关系和失效应变。对比研究结果表明,随温度升高3种材料的塑性流动应力降低,应变率敏感性增加。最后基于Johnson-Cook模型,拟合了用以预测铝合金材料塑性流动应力的模型参数,其预测结果与试验结果吻合较好。     

陶瓷隔热瓦的缺陷修补

分别采用了MgO、YSZ和Al₂O₃三种陶瓷粉体和一种含隔热瓦本体成分的粉料对陶瓷隔热瓦缺陷进行修补。研究了修补前后材料的微观形貌、力学及隔热性能。结果表明：采用含隔热瓦本体组成的粉料对陶瓷隔热瓦进行修补,修补部位与本体部位相容性好,且微观形貌相似,仍保持纤维搭接的多孔空间网络结构;修补后试样密度0.24 g/cm³、室温热导率0.044 W/（m·K）、压缩强度0.58 MPa;1 200℃、30 min热处理后,修补部位与本体部位结合性好,未出现裂纹、凹陷等缺陷,是有效的缺陷修补方法。     

熔融渗硅工艺制备的SiCf/SiC复合材料微观结构与性能

SiC纤维增强SiC陶瓷基复合材料（SiC_f/SiC复合材料）在航空发动机热端部件方面具有重要应用。本文以第二代碳化硅纤维为增强材料,采用熔融渗硅工艺制备出SiC_f/SiC复合材料,测试复合材料的基本物理性能及常规力学性能,并利用Micro-CT、SEM对试样的微观结构和断面进行了表征分析。结果显示：SiC_f/SiC复合材料的体积密度为2.78 g/cm³,开气孔率小于2.0%,基体较为致密,1 200 ℃时热导率（厚度方向）为14.30 W/（m?K）,室温~1 200 ℃厚度方向和面内方向的线胀率分别为0.59%、0.56%,平均热胀系数分别为5.02×10^-6、4.73×10^-6/K;室温面内拉伸强度典型值为317 MPa,SEM显示试样断面具有明显的纤维拔出效应,弯曲强度和层间拉伸强度典型值分别达794和49 MPa。     

不同温度下IC10合金的本构关系

 利用材料试验机（MTS809）测得IC10合金在很宽的温度范围（25~800 ℃）和不同应变率（10^-5~10^-2s^-1）内的应力 应变曲线。试验结果表明：室温下IC10合金的流变行为对应变率不太敏感;相同应变率（10^-4s^-1）下,流变行为对温度较敏感;在不同应变率、25~800 ℃温度范围内,IC10合金的屈服应力变化很小。基于试验数据,修正并拟合了Johnson-Cook方程,并利用该方程对不同温度和不同应变率下IC10合金的流变应力进行预测。与试验数据对比表明,修正后的Johnson-Cook方程能较好地描述IC10合金在不同的温度和应变率条件下的流变行为。     

航天器用Parylene-C涂覆材料空间辐照适用性研究

派瑞林（Parylene）薄膜主要用于功率电刷的三防,确保电功率的稳定传输。本文对两种规格（17和27 μm）Parylene薄膜的厚度、热性能、绝缘性能、在铍青铜上的附着性能以及耐空间辐照性进行了研究。结果表明：通过真空气相沉积法制备的Parylene-C涂覆材料厚度误差可控在2 μm内;膜层在铍青铜上的附着力等级为1级,薄膜热分解温度为453 ℃,两种厚度薄膜击穿电压分别为3.65 kV（17 μm）和5.27 kV（27 μm）;经2.5×10¹⁵ p/cm²质子辐照后,膜层外观均完好,附着性能、热性能、绝缘性能仍满足工程使用需求;经2.5×10¹⁶ e/cm²电子辐照后,膜层出现严重开裂、起皮现象。对电子辐照前后膜层的热性能、红外结构等进行了进一步的研究,分析了电子辐照后膜层的失效机理并获得了Parylene-C涂覆材料膜层耐空间电子辐照上限为1×10¹⁴ e/cm²。     

真空100 keV质子辐照对石墨膜热性能的影响

研究了25 μm石墨膜在能量100 keV最大注量2.5×10¹⁵ p/cm²的真空质子辐照条件下的微观结构和热性能，采用拉曼光谱（Raman spectrum）、X射线衍射（XRD）、X射线光电子能谱（XPS）进行微观结构分析，采用激光闪射法（LFA）进行热性能分析。石墨膜晶面间距为0.335 83 nm，石墨化度为95.0%。结果发现，质子辐照会导致石墨膜表层产生缺陷，片层间距增大，石墨化度降低，氧含量升高；随着质子辐照注量的增加，Raman光谱中D和G峰的积分面积比表明缺陷密度不断增加。25 μm石墨膜经过能量为100 keV注量为2.5×10¹⁵ p/cm²质子辐照后，石墨膜热扩散系数无明显变化。     

工艺参数对轻质热防护组件胶接装配性能的影响

可重复使用运载器采用轻质热防护材料和应变隔离垫作为飞行器的热防护系统,轻质热防护组件通过硅橡胶胶黏剂粘接至碳纤维复合材料蒙皮表面。为提高可重复使用飞行器轻质热防护系统粘接质量,通过实验方法研究了加压压力、加压时间、表面处理方式等对轻质热防护组件与碳纤维复合材料的粘接强度的影响。结果表明：轻质热防护组件与碳纤维复合材料的粘接强度随加压压力的增大而增大,随加压时间的增长先迅速增大,当加压时间超过7 h时缓慢增大;打磨或涂处理剂表面处理方式均能提高粘接强度,同时施加两种处理方式时提高粘接强度大于52%。     

刚性隔热瓦组件拉伸强度有限元分析与验证

为研究侧面涂层和应变隔离垫厚度及两者刚度对刚性隔热瓦及组件力学性能的影响,构建一种对称结构的刚性隔热瓦分析模型,进行了拉伸试验和有限元分析。结果表明,在拉伸载荷作用下刚性隔热瓦的应力分布不均匀,具有明显应力集中现象,其拉伸强度水平与最大应力密切相关,随涂层厚度或刚度增加,刚性隔热瓦最大应力上升,拉伸强度降低;当刚性隔热瓦粘结应变隔离垫时,应变隔离垫厚度增加或刚度减小,刚性隔热瓦最大应力下降,拉伸强度增大;当刚性隔热瓦含涂层时,增加应变隔离垫可减缓涂层对刚性隔热瓦的影响;并对有限元分析结果进行了试验验证,计算结果与试验结果吻合良好,表明建立的刚性隔热瓦分析模型合理,揭示了涂层和应变隔离垫参数与刚性隔热瓦失效的关联关系。     

不同钝化工艺SiO2薄膜的辐射缺陷

为研究不同钝化工艺栅介质用SiO₂薄膜的高能电子辐射缺陷特征，采用能量为1 MeV的高能电子在辐照注量为1×10¹⁵ e/cm²、5×10¹⁵ e/cm²和1×10¹⁶e/cm²下对三种不同钝化工艺（I，700 nm SiN + 500 nm PSG;II，1.2 μm SiN;III，700 nm PSG + 500 nm SiN）的SiO₂薄膜进行了辐照试验。拉曼光谱和X射线光电子能谱结果表明I和III钝化工艺SiO₂薄膜形成了非晶硅及双氧根离子，傅立叶红外光谱结果表明I钝化工艺SiO₂薄膜形成缺陷结构未知的A₁、A₂、B₁及B₂缺陷；II钝化工艺SiO₂薄膜形成A₁、B₁、及 缺陷；III钝化工艺SiO₂薄膜形成A₁、及B₂缺陷。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。