多处损伤平板的剩余强度研究

进行了多处损伤平板的剩余强度试验,用净截面屈服准则、塑性区连通准则和修正的断裂韧性准则分别计算了MSD平板的剩余强度,并把预测结果与试验进行了对比。结果表明对不同的主裂纹长度和不同的韧带长度,净截面屈服准则预测结果的误差较大,而且偏危险;塑性区连通准则对较长的韧带预测结果的误差较小,而修正的断裂韧性准则对较短的韧带预测的误差较小。研究了不同的主裂纹长度对平板剩余强度的影响,主裂纹长度的增加使平板的剩余强度减小。     

含多处损伤未加筋铝合金壁板的剩余强度

 进行了含多处损伤（MSD）的未加筋LY12CZ铝合金壁板的剩余强度试验。用0.12的钼丝切割预制裂纹,在垂直于裂纹面的方向施加单调增加的拉伸载荷,直至壁板破坏。得到了含不同裂纹几何的未加筋壁板的剩余强度。试验结果表明随着主裂纹长度增加,未加筋壁板的剩余强度减小;对相同的主裂纹长度,主裂纹和相邻的MSD裂纹之间的距离b减小,平板的剩余强度也减小。用5种失效准则分别计算了每个壁板的剩余强度。与试验结果的比较表明,净截面屈服准则和表观断裂韧性准则的误差较大,塑性区连通准则预测的平均误差为22.17%,改进的表观断裂韧性准则的平均误差为16.98%,而改进的塑性区连通准则预测的平均误差为8.27%,改进的塑性区连通准则大大提高了预测结果的精度。     

含MSD铝合金平板的剩余强度试验研究

针对飞机结构中日趋显著的多部位损伤(MSD)问题,进行含多部位损伤铝合金平板结构剩余强度的试验研究.试验中使用三种不同的试验件,将其在相同应力水平下预制出一定长度的多条裂纹后拉断,记录断裂时的载荷.试验结果与常用的五种评估含多裂纹结构失效准则进行计算分析和对比,了解各个准则的准确程度.最后的对比表明,五种估算剩余强度的方法中,净截面失效和裂纹尖端张开位移法误差较大,断裂力学估算方法对于有显著主裂纹的情况更适用,塑性区连通和平均应力准则预测的偏差较小.     

改进的确定多处损伤平板剩余强度的连通模型

为了评估多处损伤（MSD）对未加筋平板剩余强度的影响,进行了多处损伤平板的剩余强度试验研究。用钼丝切割预制疲劳裂纹,每个试验件承受拉伸载荷直到破坏,记录破坏载荷,得到不同裂纹几何平板的剩余强度。试验结果表明主裂纹长度增加使平板的剩余强度减小;对相同的主裂纹长度,主裂纹与相邻MSD裂纹之间的韧带（b）减小,试验件剩余强度也减小。以试验数据为基础,提出了一种改进的塑性区连通模型。用塑性区连通准则和改进的塑性区连通模型分别计算了多处损伤平板的剩余强度,结果表明对不同的主裂纹长度和不同的韧带长度,塑性区连通准则预测的平均误差为23．39％;而改进的塑性区连通准则的平均误差为7．57％,大大提高了预测结果的精度。还研究了主裂纹长度和b对剩余强度的影响。     

含多处损伤结构的剩余强度研究

系统地回顾了含多处损伤MSD结构的损伤连通准则,指出采用Dugdale的片状塑性区尺寸的Swift韧带屈服准则对一般工程材料最为合适.对具有潜在危险性的典型的广泛MSD结构作了剩余强度分析,分析结果表明:广泛MSD大大地降低了结构的剩余强度.     

含分层损伤的复合材料层压板轴压剩余强度分析

基于渐进损伤分析方法对含正方形分层损伤的复合材料层压板开展了剩余强度仿真分析。不同损伤尺寸大小的仿真结果表明,层压板的轴压剩余强度和失效机理与分层损伤尺度密切相关,分层损伤尺寸较小时,层压板剩余强度对损伤尺寸不敏感,降低幅度较小;损伤尺寸大于某一临界值后,层压板剩余强度较完好结构件大幅度下降,并趋于稳定;中小尺寸分层损伤层压板在屈曲后,其失效模式为结构件中部横向整体直接压溃;大尺寸分层损伤层压板出现子层屈曲诱发的界面损伤并扩展,在复合材料薄板中部压溃前达到最大剩余强度。该仿真结果对复合材料损伤容限设计、修理具有指导意义。     

铝合金结构腐蚀疲劳裂纹扩展与剩余强度研究

 在3.5%NaCl腐蚀溶液环境下对含中心孔LY12 CZ铝合金紧固件的疲劳裂纹扩展进行了试验研究,得到3种不同频率下紧固件的腐蚀疲劳裂纹扩展曲线。试验结果说明,随着频率的增加,腐蚀疲劳裂纹扩展速率逐渐降低,腐蚀溶液中疲劳裂纹扩展速率比在空气中大。以试验数据为基础,结合裂纹扩展分析软件AFGROW,提出一种可以用数值方法模拟腐蚀疲劳裂纹扩展的方法,模拟结果和试验结果符合较好。对紧固孔试验件利用2种失效模式进行了剩余强度分析,得到腐蚀环境下紧固孔结构的剩余强度曲线。     

加筋板广布疲劳损伤模式及剩余强度分析

给出了两种加筋板广布疲劳损伤模式和两种加筋板广布疲劳损伤剩余强度判据，并用这两种判据对3种形式损伤的加筋板剩余强度进行了预测，预测结果和试验结果符合得很好。     

含损伤复合材料层合板剩余压缩强度研究进展

综述了含损伤复合材料层合板剩余压缩强度的研究进展,重点介绍受低速冲击后复合材料层合板的剩余压缩强度问题,主要包括:(1)层合板压缩失效的损伤特征及损伤状态表征;(2)层合板压缩试验研究;(3)损伤模型分析及失效分析;(4)研究展望.     

Residual Strength of Stiffened LY12CZ Aluminum Alloy Panels with Widespread Fatigue Damage

Experimental and analytical investigations on the residual strength of the stiffened LY12CZ aluminum alloy panels with widespread fatigue damage （WFD） are conducted. Nine stiffened LY12CZ aluminum alloy panels with three different types of damage are tested for residual strength. Each specimen is pre-cracked at rivet holes by saw cuts and subjected to a monotonically increasing tensile load until failure is occurred and the failure load is recorded. The stress intensity factors at the tips of the lead crack and the adjacent WFD cracks of the stiffened aluminum alloy panels are calculated by compounding approach and finite element method （FEM） respectively. The residual strength of the stiffened panels with WFD is evaluated by the engineering method with plastic zone linkup criterion and the FEM with apparent fracture toughness criterion respectively. The predicted residual strength agrees well with the experiment results. It indicates that in engineering practice these methods can be used for residual strength evaluation with the acceptable accuracy. It can be seen from this research that WFD can significantly reduce the residual strength and the critical crack length of the stiffened panels with WFD. The effect of WFD crack length on residual strength is also studied.     

广布损伤的试验研究与有限元分析

 通过对无钉载3排平行孔平板和无钉载3排交错孔平板从无裂纹开始的疲劳试验,发现应力大小对是否出现广布损伤(MSD)有重要影响,首裂孔和断裂排位不总是一一对应。在试验中观察到了MSD的竞争现象,证实了群发小裂纹也是MSD中一种重要的破坏形式。采用FRANC2D/L建立了对生裂纹、非对生裂纹和单裂纹3种开裂模式的有限元模型。计算结果表明:短裂纹扩展过程中,裂纹间干涉效应不明显,3种模式的应力强度因子增长趋势相近;而对于长裂纹,试验和有限元计算都证明了裂纹间的干涉显著地加快了裂纹的扩展。     

含冲击损伤复合材料加筋层板压缩剩余强度

将复合材料加筋层板受低速冲击后的损伤区域描述为一个椭圆形弹性核,材料在核区的弹性模量下降由冲击表面的凹坑深度确定。利用含任意椭圆核各向异性板杂交应力有限元来模拟含损伤区域,杆单元来模拟筋条,钉单元模拟铆钉（胶层）和常规8节点等参单元模拟其余无损区域,建立起含低速冲击损伤复合材料加筋层板的力学响应分析方法。利用基于特征曲线概念的点应力判据、最大正应力判据和最大剪应力判据分别预测蒙皮的破坏、筋条的破坏和铆钉（胶层）的破坏,从而预测加筋层板在压缩载荷下的剩余强度,获得了与试验相吻合的结果。最后讨论了损伤尺寸、损伤形态、铺层比例等参数对加筋层板剩余强度的影响。     

铝合金腐蚀损伤演化数学模型

 对LY12 CZ铝合金试验件进行了腐蚀实验,着重考虑了腐蚀时间和腐蚀温度这两个参数。从电化学微观角度考察了腐蚀损伤的发展,利用蒙特卡罗方法对腐蚀损伤演化的概率模型进行模拟计算,并讨论了不同预腐蚀温度和时间对腐蚀损伤的影响,建立了腐蚀损伤度演化全过程的数学模型。此损伤演化数学模型的模拟结果与实验结果符合较好,可以用此模型来预测不同腐蚀环境下的腐蚀损伤情况。     

高强铝合金疲劳特性研究

研究了室温大气环境下不同应力比R和不同应力集中系数Kt条件下2E12高强铝合金的高周疲劳性能,并利用扫描电镜及透射电镜对合金疲劳断口附近的微观组织及疲劳断口进行了分析.研究结果表明,在同一应力水平下,2E12高强铝合金的疲劳寿命随着应力比R的增大而提高;Kt=1时合金的疲劳寿命远远大于Kt=3时合金的疲劳寿命,表明此合金具有明显的缺口效应.疲劳断口由疲劳源区、裂纹扩展区及瞬断区组成.第二相对疲劳裂纹的萌生起着重要的作用,并且初步讨论了有关的疲劳断裂机理.