Mechanical Properties and Microstructure of In Situ TiB_2-7055 Composites

In order to fabricate a kind of high strength particulate reinforced aluminum-matrix composites, the high strength aluminum alloy 7055 was selected as a matrix. Composites reinforced with varying amounts of TiB2 particles were synthesized using the in situ method, and their mechanical properties and microstructure were analyzed. It is found that the in situ TiB2 particles sized from 50 to 400 nm uniformly disperse in the matrix. With the weight fraction of TiB2 particles increasing, the elastic modulus as well as the yield strength and the ultimate tensile strength increase, while the ductility decrease. The improvement of strength could be attributed to good bonding between TiB2 and the matrix, and also the TiB2 particles act as a barrier to dislocation.     

Al-TiO2-C系原位合成铝基复合材料高温拉伸性能及断裂机理

讨论了Al-TiO2-C反应系原位反应合成铝基复合材料的常温和高温拉伸性能及其断裂机理.当C/TiO2摩尔比为0时,增强相由α-Al2O3和Al3Ti组成,随C/TiO2摩尔比的增加,Al3Ti逐渐减少,在C/TiO2摩尔比为1时,Al3Ti基本消失.室温抗拉强度和延伸率随C/TiO2摩尔比的增加而同步提高,分别由250.4 MPa和4.0%上升到350.8 MPa和6.0%.SEM观察发现有的Al3Ti自身解理开裂,并在四周形成较大韧窝,拉伸时裂纹核可在Al3Ti棒中和基体中α-Al2O3的聚集处形成,并分别在棒的解理面和基体中扩展引起断裂.高温时,热错配应力促使裂纹核先于基体在Al3Ti棒与基体的界面萌生扩展,Al3Ti从基体中脱离,断口出现洞坑,C/TiO2摩尔比为1的复合材料在727K时,拉伸强度降为93.3MPa,延伸率升为11.0%.     

Al_2O_3/TiAl 复合材料的原位合成、结构与性能研究(英文)

以 Ti, Al, TiO2和 Nb2O5混合粉为原料,采用热压反应合成技术制备了 Al2O3/TiAl 复合材料。对复合材料的微观组织与力学性能进行了研究。结果表明:产物由γ-TiAl, α2-Ti3Al, Al2O3和 NbAl3相组成。原位反应形成的细小 Al2O3粒子主要分布在基体晶界处。随着 Nb2O5含量的增加,晶粒明显细化,Al2O3粒子呈弥散分布在基体中。最终形成了由γ和γ α2构成的特殊组织。随着 Nb2O5含量的增大,复合材料的硬度逐渐增大,抗弯强度和断裂韧性在 Nb2O5含量为 6 wt%时达到最大,分别为 398.5 MPa 和 6.99 MPa·m1/2。     

多重纳米结构轻质高强铝基复合材料的制备和组织性能

为了研究多重纳米结构对块体材料强化和变形能力的影响机制,采用粉末冶金法制备了多重纳米结构的B4C颗粒增强铝基复合材料,并对复合材料的强化和形变破坏机制进行了定量和定性的讨论。由100%球磨复合粉末制备的块体复合材料的室温压缩强度为670MPa;当加入10vol%气雾化态的Al2024粉末后,复合材料的室温压缩强度升高到1.115GPa;之后随着气雾化态Al2024粉末含量的增加,复合材料的强度逐渐下降,但是没有产生明显的塑性变形;当气雾化态Al2024粉末的含量增加到50vol%时,复合材料的压缩强度下降到580MPa,断裂前变形率达到了10%。扫描电镜(SEM)和透射电镜(TEM)的分析结果显示,亚微米级的B4C颗粒、位错以及纳米晶基体分别通过Orowan强化、位错强化和细晶强化机制对复合材料进行强化;粗晶Al2024区域与复合结构区域的比例显著影响复合材料的形变及破坏机制。     

超细晶Laves相NbCr2颗粒增强Nb基复合材料的制备及其组织性能研究

采用机械合金化 热压工艺制备了Laves相NbCr2增强的Nb基复合材料。研究了Nb-22.5Cr配比成分的Nb,Cr元素粉经MA30h后在1250℃分别热压10min,20min和30min所获得的Nb/NbCr2复合材料的组织和性能。结果表明:三种热压时间均可制备出组织均匀,致密度高的Nb/NbCr2复合材料,体积分数约为30%的近等轴状的Laves相NbCr2颗粒弥散分布于Nb固溶体基体中。热压20min的试样具有最佳的组织和性能,其Laves相NbCr2的晶粒尺寸达到亚微米级,致密度达到99.2%,维氏硬度为9.41GPa,屈服强度为2950 MPa,抗压强度为3345 MPa,塑性应变达到了7.01%,充分实现了Laves相NbCr2颗粒强化和细晶强韧化的效果。     

Microstructure and Mechanical Properties of In-situ Synthesized Al2O3/TiAl Composites

Al2O3 particle-reinforced TiAl composites are successfully reaction-synthesized from the powder mixture of Ti, Al, TiO2, and Nb2O5, using the hot pressing reaction synthesis technique. The microstructure and mechanical properties of the as-sintered products are investigated. It is found that in the as-sintered products consisting of γ-TiAl, α2-Ti3Al, Al2O3, and NbAl3 phases, the fine Al2O3 particles tend to disperse on the grain boundaries. With the Nb2O5 content increasing, the grains are remarkably refined and the Al2O3 particles are dispersing more uniformly in the TiAl matrix, forming a partial lamellar structure containing α and lamellar phases. The hardness of the in-situ composites increases gradually, and the bending strength and the fracture toughness of the as-sintered products reach the maximum value of 398.5 MPa and 6.99 MPa·m^1/2, respectively, as the Nb2O5 content increases to 6 wt%.     

粉末粒度对快速凝固／粉末冶金Al-Fe-Mo-Si／Zn-Al复合材料组织与性能的影响

研究不同粉末粒度Al-9.0?-1.8%Mo-1.7%Si/5%(Zn-30%Al)金属/金属复合材料的组织、拉伸性能和阻尼性能.快速凝固粉末由气体雾化制备,选取平均粒度d50分别为27.3,36.2,41.6μm粉末装入包套,经除气,再热挤压制成棒材.结果表明,粉末粒径越粗,强化相越粗大,呈团聚体存在,且有偏聚现象,材料的强度明显下降,室温下粉末较细材料的阻尼性能较好,高于100℃时粉末粒度较粗材料的阻尼性能好.     

热压工艺对SiO2f／SiO2复合材料结构与力学性能的影响

采用真空热压烧结工艺制备了SiO2短纤维补强增韧的SiO2玻璃陶瓷基复合材料，研究了烧结温度和保温时间对其显微结构和力学性能的影响规律，结果表明，SiO2f/SiO2复合材料的强度和韧性较石英玻璃有明显改善；延长热压保温时间、提高烧结温度、虽有利于材料致密化，但析晶量增加和纤维退化更严重，复合材料的强度和断裂韧性随之下降。     

激光熔化沉积TA15+Ti_2AlNb合金的组织与力学性能

将TA15和Ti_2AlNb合金粉末以不同比例预混,采用激光熔化沉积工艺,制备出40%TA15+60%Ti_2AlNb,50%TA15+50%Ti_2AlNb,60%TA15+40%Ti_2AlNb(质量分数)3种比例的合金薄壁,分析了薄壁的成分、组织及力学性能。结果表明:3种沉积薄壁的成分分布均匀,合金由α相、α2相及β/B2相组成,针状α相和α2相呈网篮状分布在初生β/B2晶粒内部;3种合金的抗拉强度分别为1108 MPa,1071 MPa,1105 MPa,断裂伸长率分别为3.0%,2.2%,3.8%;拉伸断口可见沿α2相撕裂产生的撕裂棱,断裂方式均为准解理断裂。     

Microstructure, Mechanical Properties and Oxidation Resistance of Nb-22Ti-14Si-2Hf-2Al-xCr Alloys

Nb-22Ti-14Si-2Hf-2Al-xCr (x=2, 6, 10, 14, 17 at%) alloys are prepared by arc-melting under argon atmosphere. Microstructural characteristics, mechanical properties and oxidation resistance of the arc-melted alloys are investigated. At 2 at% Cr content, the microstructure is composed of Nbss, Nb3Si and a small quantity of Nb5Si3, when the Cr contents increase, Nb3Si disappears. For the high Cr content (x ≥ 10 at%) alloys, besides the Nbss and Nb5Si3, Cr2Nb is also detected. With the increase of Cr content, the volume fractions of Cr2Nb and Nb5Si3 increase, while that of Nbss increases firstly and then begins to degrade when the Cr content is higher than 6 at%. For the alloy with 2 at% Cr, the room temperature fracture toughness is about 14.5 MPa·m1/2, but badly decreases to about 8.5 MPa·m1/2, when the Cr contents increase. Vickers hardness of Nbss tends to increase linearly from about 400 to 500, while that of silicides is not sensitive to Cr contents, about 950. The appearance of Cr2Nb phase significantly improves the high temperature oxidation resistance of the alloys with high Cr contents. The isothermal oxidation tests show that the oxidation kinetics of the alloys with various Cr contents follows parabolic oxidation kinetics.     

Ni3Al基IC6返回料合金的显微组织与力学性能

利用带能谱的扫描电镜（SEM／EDS）和透射电镜（TEM）等分析手段研究了返回料添加比例对Ni3Al基合金IC6成分，显微组织及力学性能的影响。结果表明，返回料的加入对合金中主量元素的成分没有明显影响，但C，N含量随返回料加入比例增加而升高；除了在枝晶间析出了一些M6C碳化物颗粒外，IC6返回料合金的显微组织与新料合金没有明显差别；返回料的加入对IC6合金的室温拉伸性能几乎没有影响，高温持久性能略有下降，冷热疲劳性能明显恶化。建议在实际生产中返回料添加比例不超过50％。     

EB-PVD工艺制备Ti/Ti-Al超薄多层复合材料的微观结构与性能研究

利用大功率电子束物理气相沉积(EB-PVD)技术制备了Ti和Ti-48at%Al交替蒸发沉积形成的金属/金属间化合物型多层材料薄箔.研究了靶基距、微观结构参数及试样在制备材料的选取位置对其性能的影响,考察了Ti/Ti-Al微叠层材料在不同温度下的拉伸性能,结果表明材料的室温脆性得到了明显改善,高温下由于金属间化合物层的反常强化作用,使材料在500～800 ℃之间的性能较为理想.     

晶粒尺寸对钛合金TIG焊接接头组织及力学性能的影响

进行了2μm及8μm,19μm三种晶粒尺寸的细晶粒TC4钛合金常规TIG焊试验,分析了母材晶粒尺寸对钛合金焊接接头组织转变规律及力学性能的影响。结果表明,细晶粒TC4钛合金焊缝中心和热影响区组织相似,为α马氏体组织。相同焊接规范下,随着晶粒尺寸的减小,焊缝中心和热影响区组织由编织(网篮)状α组织向片状组织过渡;随着晶粒尺寸的减小,热影响区晶粒长大越来越明显,热影响区细晶区(FHAZ)明显变窄,热影响区粗晶区(CHAZ)明显变宽,焊缝—热影响区—母材的晶粒梯度增大,焊接接头三区域晶粒过渡越来越差;随着晶粒尺寸的减小,焊接接头拉伸强度和伸长率均有不同程度的提高。常温拉伸断口呈准解理断裂特征,随着母材晶粒度的增大,焊接接头解理断裂特征越明显。     

热等静压温度对K447A高温合金显微组织及性能的影响

研究了热等静压温度对K447A合金显微组织及性能的影响。测试了合金的持久性能和室温拉伸性能。利用金相显微镜(OM)和扫描电镜(SUM)观察了合金显微组织。结果表明,1185～1210℃/180MPa/4h(+1185℃/2h,AC+1100℃/4h,AC+870℃/20h,AC)下,随热等静压温度的提高,合金中显微疏松逐步闭合,碳化物逐步细化和球化;γ-γ’共晶相尺寸和数量逐步减小,共晶特征趋于不明显;晶界呈不连续颗粒状;存在大、小两种尺寸的γ’相。经1185～1210℃HIP处理的合金980℃/200MPa持久性能大幅提高;经1195℃HIP的合金760℃/724MPa持久性能达到最高。经1210℃HIP处理的合金980℃/200MPa持久性能达到最高。180MPa/4h条件下,K447A合金合适的热等静压温度为1185～1210℃。     

激光熔覆制备TC4基复合药型罩材料的力学性能

为了提高TC4药型罩的侵彻性能,将激光熔覆制备工艺用于TC4复合药型罩材料的制备。选用TA15+30%(质量分数,下同)TiC粉、TA15+20%Cr_3C_2粉和TA15+15%B_4C粉作为TC4基体的熔覆材料。采用XRD、扫描电镜和显微硬度测试、准静态压缩实验、SHPB动态压缩实验以及3点弯曲实验方法,研究熔覆层与基体界面处微观形貌、熔覆层硬度变化情况以及3种复合材料的力学性能。结果表明:TC4基体与3种材料都能形成完全冶金结合,TC4-(TA15+TiC),TC4-(TA15+Cr_3C_2)和TC4-(TA15+B_4C)材料的强度均高于TC4基体材料,塑性略差;TC4-(TA15+TiC),TC4-(TA15+Cr_3C_2)材料的抗弯强度分别为168 MPa,101 MPa,均高于TC4基体材料的45 MPa。     

熔体处理时间对铸态镍基高温合金K465组织和力学性能的影响

用金相显微镜和扫描电镜研究了镍基高温合金K465在1530-1540℃下进行1-10min熔体处理后碳化物尺寸、分布以及枝晶杆区γ'相尺寸、形态立方化效果的变化,并研究了其对合金室温拉伸性能和高温持久性能的影响。结果表明,熔体处理5-7min能减小碳化物和枝晶杆区γ'相尺寸,改善碳化物分布和γ'相立方化程度,而使合金得到良好的室温塑性和高温持久性能。     

TC4＋TC17线性摩擦焊接头的微观组织与力学性能

进行了TC4+TC17异种钛合金试件的线性摩擦焊实验,利用光学显微镜、扫描电镜及透射电镜分析了焊接接头的微观组织,并进行了焊后接头的力学性能测试.着重分析了焊接接头的焊缝、近缝区及变形区的组织特点及相变规律,并结合线性摩擦焊的工艺特点,初步分析了形变组织的形成机理.实验结果表明,利用合理的焊接工艺参数,用线性摩擦焊方法可获得可靠的Tc4+TC1钛合金焊接接头,接头的拉伸性能优于TC4母材.TC4与TC17接头的焊缝区为等轴细品组织,两侧近缝区、变形区的组织形貌差异较大.     

AA 7055铝合金板材的微观组织与力学性能

研究AA 7055-T7751板材不同厚度层的力学性能,并采用电子背散射衍射(EBSD)、透射电子显微镜(TEM)、小角度X射线散射(SAXS)等分析技术研究板材不同厚度层的微观组织。结果表明:从板材表层到厚度中心,再结晶程度从69%下降到19.1%,亚晶粒尺寸从10μm减小到2μm;板材厚度中心主要为轧制型织构,远离中心层其含量逐渐减少,板材表层主要为剪切型织构;板材主要强化相为盘状η'相,其盘面半径为3.7 nm,厚度为1~3 nm,与基体的共格应变约为0.0133;板材不同厚度层沿轧制方向的拉伸屈服强度近似呈线性变化:σ_y=-38.7S+604.8(0≤S≤1)。     

TC21细晶钛合金TIG焊接接头组织及力学性能研究

开展了不同晶粒尺寸的细晶粒TC21钛合金的TIG焊接实验,研究了母材及接头组织和力学性能。结果表明：细晶粒TC21钛合金TIG焊接接头抗拉强度达到母材的95％左右,焊接性较好;但是焊接接头脆化严重,伸长率和断面收缩率均较低。焊缝中心和热影响区组织相似,为α’马氏体组织。相同焊接规范下,21μm的细晶TC21合金焊缝及热影响区为片状或长粒状α’组织;而7μm的细晶TC21合金接头中α’丛的尺寸较小且相互交错,形成针状或短粒状α’组织。硬度测试表明：靠近母材的热影响区细晶区存在一个软化区,该区域硬度最低,而焊缝中心与热影响区粗晶区分界处（细晶过渡区（FTZ））也存在硬度的下降,不过此区域下降幅度不大。常温拉伸断口呈准解理断裂特征,随着母材晶粒度的增大,焊接接头解理特征越明显。     

富镧混合稀土对Mg-10Li-4Al合金组织和力学性能的影响

研究了不同添加量的富镧混合稀土对Mg-10Li-4Al合金显微组织的影响,分析了稀土化合物在合金中的作用,测量了铸态合金室温力学性能.研究表明,富镧混合稀土加入后,细化了晶粒,合金中生成短棒状稀土化合物Al3La,抑制了合金中MgLiAl2相和Mg17Al12相的生成,提高了合金的力学性能;当Al3La数量增多时,合金强度缓慢提高,延伸率下降.