聚对苯撑苯并双噁唑(PBO)纤维制备及性能研究

采用4,6-二氨基间苯二酚(DAR)与对苯二甲酸(TPA)缩聚的方法制备PBO聚合物溶液,在180~200℃使聚合物形成液晶态,利用干喷湿纺制法制备纤维。采用DSC、Raman及XRD等方法对纤维进行表征。制备的纤维与商品纤维相比,具有相同的结构和热性能,但表面形貌和强度有差异;两种纤维具有6个相同的主要Raman光谱带,但制备纤维的峰面积较小。制备的PBO纤维热降解温度达650℃,热牵伸处理可使纤维的模量提高至240~300 GPa。     

PBO/SWNT复合纤维的合成与性能

利用原位聚合法成功制备了聚对苯撑苯并双噁唑(PBO)/单壁碳纳米管(SWNT)复合物,并用干喷湿纺法对聚合物进行了纺制.SWNT采用强氧化性酸处理,形成羧基化的单壁碳纳米管(SWNT-COOH).用拉曼光谱(Raman)、X射线光电子能谱(XPS)、强度测定、热重分析等分别对SWNT、PBO/SWNT复合纤维进行了表征.研究表明,碳纳米管经过酸处理后,表面含有较多的羟基和羧基官能团.PBO/SWNT复合纤维保持了PBO纤维的优异耐高温性能,纤维拉伸强度与同条件下PBO纤维相比提高了50%.     

热老化对APMOC和PBO拉伸性能的影响

为研究热对阿莫斯（APMOC）和聚对亚苯基苯并双唑（PBO）力学行为的影响,用高温干燥箱在温度100,120,150℃下分别对两者进行热老化实验,并对老化试样进行单丝拉伸测试和拉伸断口的电镜扫描观察（SEM）。实验结果表明：PBO具有较APMOC更优的热稳定性,在实验温度范围内,PBO的性能基本不变;AP-MOC在温度100,120℃处理时性能有所增强;老化对两种纤维模量的影响均很小,而断裂伸长率均有所下降;SEM发现纤维失效形式由原纤化向脆性断裂转变,与其他芳纶老化情形一致。     

PBO/环氧树脂界面的分子建模与力学性能预测

PBO纤维具有十分优异的力学性能和耐高温性能,但由于其分子结构复杂、纤维表面光滑且呈化学惰性,PBO纤维与环氧树脂基体的界面性能与其他纤维相比具有许多差异,且相关实验研究难度较大。采用分子动力学方法,通过动态模拟环氧树脂基体在PBO纤维表面的固化过程,建立了PBO纤维与不同交联度的PBO/环氧树脂界面分子模型。根据体系的相对原子浓度图,确定了界面的存在及其厚度,并通过虚拟单轴拉伸研究了不同交联度下PBO/环氧树脂界面的力学性能。结果表明,不同交联密度下界面厚度基本一致,均在5~6,小于炭纤维等其他增强体复合材料的界面厚度;力学性能随着交联密度的增加而增强,与其他纤维定性类似,但交联度对界面力学性能影响较小,纤维与界面之间的分子作用力对界面力学性能影响较大,使界面力学性能显著增强。     

纺丝工艺参数对初生PBO纤维性能的影响

采用干喷-湿法液晶纺丝技术制得初生PBO纤维,对纺丝原液浓度、纺丝温度、纺丝压力、拉伸比等几个主要工艺参数的选择进行了讨论,分析了这些工艺参数对初生PBO纤维性能的影响。研究结果表明,随着聚合物浓度的升高,PBO的分子量增大,制得纤维的拉伸强度增大;最佳纺丝温度为160~180℃;纺丝压力提高,有利于纺丝;拉伸比增大,有利于提高纤维的性能。     

原位聚合法制备多壁碳纳米管-聚对苯撑苯并双噁唑纳米复合材料

采用强氧化性酸处理多壁碳纳米管(MWNTs),形成官能化的多壁碳纳米管(FMWNTs),用傅立叶红外光谱(FT-IR)、光电子能谱(XPS)对处理前后MWNTs的表面官能团进行了分析,并利用原位聚合法成功制备了FMWNTS-PBO纳米复合材料。结果表明,碳纳米管经过酸处理后,表面含有较多羰基和羟基的极性官能团,FMWNTs-PBO纤维的钩接强度比同条件下PBO纤维的钩接强度高出30%。文中给出了FMWNTs和PBO低聚物的聚合机理。     

热处理对PBO纤维分子链结构和性能的影响

利用红外光谱分析(FTIR)、示差扫描量热法(DSC)和磷含量分析方法研究了热处理对PBO纤维结构和性能的影响。结果表明,热处理使PBO纤维分子链中聚合后期少量的未关环反应趋向完全,使得PBO分子的共轭链长增加,弱键消失,提高了PBO纤维的力学性能;提高了分子链与链之间排列的有序性,使链与链之间堆砌更加紧密,使得热处理后的纤维较难溶于MSA中;热处理使PBO纤维表面化学组成发生变化,并使其表面粗糙化,能改善其表面润湿性能;热处理对纤维强度影响甚微,提高热处理温度、延长热处理时间和增大热处理张力,能提高PBO纤维的模量。     

有机纤维束纱弹性模量测试分析

介绍了一种超声波测试技术,能快速简便地对有机纤维进行动态弹性模量测试,给出了动态和静态弹性模量的计算式,并测试了F-12芳纶、国产芳纶Ⅲ和PBO纤维的动态弹性模量,且采用GJB 348—87复丝拉伸实验对上述几种纤维的静态杨氏模量进行测试对比。实验结果表明,超声波测试F-12芳纶纤维、芳纶Ⅲ纤维和PBO纤维的动态弹性模量平均值分别比采用GJB 348—87测得的静态模量稍高;与GJB 348—87复丝拉伸实验相比,此方法具有测试装置简单、取样容易等特点,可作为一种常用的测试方法。     

几种高性能纤维的表面性能及其对界面粘接的影响

分别使用扫描电镜和X射线光电子能谱仪，对T-800炭纤雏、F-12有机纤维及新型超高强度PBO纤雏(聚对苯撑苯并双嗯唑)进行了物理与化学表征和分析，用SEM观察得出这三种纤雏表面物理形态差别清晰可见，T-800纤雏表面沟槽深且直径小，PBO纤雏表面极光滑且直径中等，F-12纤维直径最大且表面有微小沟槽。XPS定量分析表明，这三种纤维表面活性也不一样，T-800纤维表面活性较多，PBO纤维表面活性最差。纤维表面状态的差异体现在它们与树脂复合后的材料界面粘接性能上，T-800纤维的界面剪切强度(IFSS)高，F-12纤雏次之，PBO纤雏最差。     

湿热老化对PBO纤维/环氧树脂单向复合材料弯曲性能的影响

研究了在湿热老化过程中,PBO纤维/环氧树脂单向复合材料弯曲性能的变化规律,发现PBO纤维/环氧树脂复合材料具有不同于一般的纤维增强树脂复合材料的湿热老化特点。研究发现PBO纤维/环氧树脂单向复合材料在湿热老化过程中,相比温度而言,湿度对复合材料弯曲性能的影响更为显著,复合材料在老化过程中吸水率增加的同时,弯曲性能相应降低。其主要原因在于PBO纤维的表面为化学惰性,表面形貌光滑,与环氧树脂浸润性不好,界面粘接力主要是较弱的范德华力。在湿热老化过程中,水分的吸收和渗透造成PBO纤维与环氧树脂基体之间的界面的破坏,构成了该类复合材料独特的湿热老化特性。     

Availability of O(2) and H(2)O(2) on pre-photosynthetic Earth

Old arguments that free O(2) must have been available at Earth's surface prior to the origin of photosynthesis have been revived by a new study that shows that aerobic respiration can occur at dissolved oxygen concentrations much lower than had previously been thought, perhaps as low as 0.05?nM, which corresponds to a partial pressure for O(2) of about 4?×?10(-8) bar. We used numerical models to study whether such O(2) concentrations might have been provided by atmospheric photochemistry. Results show that disproportionation of H(2)O(2) near the surface might have yielded enough O(2) to satisfy this constraint. Alternatively, poleward transport of O(2) from the equatorial stratosphere into the polar night region, followed by downward transport in the polar vortex, may have brought O(2) directly to the surface. Thus, our calculations indicate that this "early respiration" hypothesis might be physically reasonable.     

聚四氢呋喃-聚丁二烯-聚四氢呋喃三嵌段共聚物的合成与力学性能

以端羟基聚丁二烯(HTPB)为引发剂,三氟化硼乙醚络合物为催化剂,环氧丙烷为促开环剂,通过四氢呋喃的阳离子开环聚合反应,制备出聚四氢呋喃-聚丁二烯-聚四氢呋喃三嵌段共聚物(PTHF-PB-PTHF)。采用红外光谱、核磁共振氢谱及碳谱、凝胶渗透色谱-激光光散射联用技术,对目标化合物的结构进行了表征。采用相对分子质量为8 066 g/mol的PTHF-PB-PTHF与甲苯二异氰酸酯反应制备了交联弹性体,应力-应变试验显示,在相同交联密度下,PTHF-PB-PTHF交联弹性体的拉伸强度及断裂伸长率较纯HTPB交联弹性体分别提高了16%及19%。动态热机械性能分析表明,PTHF-PBPTHF交联弹性体具有优异的粘弹性能,其玻璃化转变温度为-55.99℃,低于HTPB交联弹性体。     

Transmitting (and listening) may be good (or bad)

Both listening and transmitting may, on an existential level, be either dangerous or beneficial. So we should ignore our irrational fears and listen in the hope of detecting ETI and transmit on the basis of promoting SETI activity.     

苯并二嗯唑类（PBZs）聚合物溶液在极稀浓度区的异常行为研究

运用Ubbelohde式粘度计测定PBO／MSA和PBOT／MSA溶液的粘度，采用稀释外推法对溶液浓度和粘度的关系进行了分析。结果发现，当溶液浓度极低时，出现溶液粘度随浓度降低而增大的反常行为。通过实验研究，排除了粘度计和临界接触浓度的影响导致PBZs聚合物的极稀浓度区异常行为的可能性；同时通过加入不同浓度外加盐的方法，证明了可用半刚性聚电解质模型合理解释PBZs聚合物溶液极稀浓度区的异常行为。为了避免极稀溶液区出现反常现象，保证PBZs聚合物特性粘数测量的准确性，应尽量保证溶液的ηr=1．2～2．0。     

苯并二噁唑类(PBZs)聚合物溶液在极稀浓度区的异常行为研究

运用Ubbelohde式粘度计测定PBO/MSA和PBOT/MSA溶液的粘度,采用稀释外推法对溶液浓度和粘度的关系进行了分析。结果发现,当溶液浓度极低时,出现溶液粘度随浓度降低而增大的反常行为。通过实验研究,排除了粘度计和临界接触浓度的影响导致PBZs聚合物的极稀浓度区异常行为的可能性;同时通过加入不同浓度外加盐的方法,证明了可用半刚性聚电解质模型合理解释PBZs聚合物溶液极稀浓度区的异常行为。为了避免极稀溶液区出现反常现象,保证PBZs聚合物特性粘数测量的准确性,应尽量保证溶液的ηr=1.2~2.0。     

常用词"栉"、"梳"之演变研究

"栉"是先秦时期表示"梳头用具"义的常用词."梳"在口语中出现不晚于东汉末.在魏晋时期,"梳"和"栉"之间在文学语言中呈现同义竞争状态.南北朝时期,"梳"取代"栉"成为"梳头用具"义的常用语.隋唐时期,这种优势得到进一步强化.     

稳态加速度模拟试验设备——离心机的设计(1)

文章分3篇10章详细介绍了在非标准设备制造加工中稳态加速度模拟试验设备--离心机的设计.上篇对稳态加速度环境及其效应、相关试验方法和国家标准作了阐述;中篇(上)系统介绍了国内外离心机发展的历史,提供了较为全面具体的离心机结构概况,并对它们逐一进行小结与点评;中篇(下)对离心机进行基本理论分析,研究总体设计和部件设计问题,提出离心机设计原则及其计算方法;下篇通过一个国家"七五"科技攻关项目的实践作为实例,提供读者作设计参考.在文章中,作者对多年来积累的技术资料和实践心得进行了系统的整理和归纳,梳理出一条在离心机研制中科学的设计思路和实用的工作程序.该文章对相关领域的研究人员和技术人员会有很大启发和帮助,同时对其他同类设备的设计也有触类旁通的作用.文章主要探讨的对象是中型、大型、特大型航空航天离心机,土工离心机和载人离心机.     

通信同步的干扰（Ⅰ）

主要讨论了无线电通信中的同步问题,其目的是为了进一步分析破坏通信同步的可行性及方法。