为了研究C/SiC复合材料紧固件的拉-拉疲劳行为,在疲劳应力比为0. 1、加载频率为10 Hz的条件下对不同应力水平的疲劳寿命进行统计。采用断口分析和金相分析方法对C/SiC复合材料螺钉疲劳破坏的细观机制进行了研究。结果表明:C/SiC复合材料螺钉拉-拉疲劳包含拉断疲劳及拉脱疲劳两种失效形式;基于双参数幂指数形式的寿命模型,两种失效形式的疲劳寿命经验公式相似;C/SiC复合材料螺钉的疲劳极限约为拉伸强度的65%～70%,若最大疲劳应力大于0. 7σmax,其材料损伤随循环次数增多而明显增大。     

2.5维机织复合材料疲劳寿命预测方法

针对疲劳载荷作用下的2.5维机织复合材料,建立了疲劳寿命预测方法.该方法主要包括单胞模型、疲劳失效判定准则和材料性能退化方法3部分.选取单胞模型为研究对象,利用三维有限元技术进行应力分析;引入改进的三维Hashin疲劳失效准则和Mises准则作为纤维束和树脂基体的疲劳失效判据;采用刚度性能突降准则描述疲劳失效后的材料性能,采用考虑纤维体积分数影响的剩余刚度和剩余强度退化模型描述失效前材料的性能.通过疲劳寿命预测值与试验值的对比,验证了疲劳寿命预测方法的有效性.研究表明:经向拉-拉疲劳寿命随经纱纤维体积分数增大而增加,纬向拉-拉疲劳寿命受纬纱纤维体积分数影响较小.      

镍基粉末冶金高温合金的压缩疲劳性能研究

对镍基粉末冶金高温合金的压缩强度和压缩疲劳性能进行了试验,结合拉-拉应变疲劳试验数据,证明粉末冶金高温合金具有良好的耐压能力,抗压强度极限比抗拉强度极限高出约50%。不同载荷形式的疲劳试验结果发现,粉末冶金高温合金试样的压-压疲劳性能十分优良,不易产生压缩疲劳破坏。对试样的破坏断口进行了扫描电镜分析,初步分析了材料在不同疲劳载荷作用下的细观破坏机理。      

"湿热"老化对复合材料胶补金属结构 力学特性的影响

通过玻璃纤维复合材料补片对含穿透双边裂纹的铝合金板进行单面胶接修补,测试修补试件"湿热"(加温浸泡)老化实验前后力学性能,并与未修补试件进行对比,分析老化前后修补结构的破坏模式、失效机理,评估"湿热"老化对修补结构疲劳裂纹扩展寿命和承载能力的影响。结果表明:"湿热"老化降低了复合材料补片削弱疲劳裂纹之间干涉效果的能力,老化试件从裂纹的扩展长度小于未老化试件的;距离补片越近,沿金属板厚度方向疲劳裂纹扩展速率越慢,老化后复合材料补片减缓沿金属板厚度方向疲劳裂纹扩展速率的作用下降;老化严重削弱了修补结构承载能力恢复率和疲劳裂纹扩展寿命,老化试件的承载能力恢复率下降为未老化试件的45%,疲劳裂纹扩展安全寿命下降为未老化试件的63.7%;老化降低了胶层与金属之间的粘合力,造成了复合材料补片的提前脱落,胶层的破坏模式由内聚破坏转变为界面破坏。     

针刺C/C复合材料高温力学性能

文摘采用材料超高温力学性能设备及高温应变测试系统,对针刺C/C复合材料拉伸、压缩性能进行了研究。结果表明:针刺C/C复合材料具有明显的拉、压双模量特性,拉、压模量均随着温度的升高而线性下降,且拉伸模量下降更快;针刺C/C复合材料拉伸、压缩强度均随温度升高而先升高后降低,1 600℃时拉伸强度达到最大值,1 200℃时压缩强度达到最大值;其拉伸破坏为脆性断裂,断口呈现45°豁口;其压缩破坏为典型剪应力引起的压缩失效,破坏面倾角为40°~50°。     

复合材料层压板疲劳特性的试验研究

1.引言 最初人们认为复合材料对疲劳载荷不敏感,因为它们在拉一拉载荷下对应干10~7次循环的疲劳强度与静强度十分接近,显示了极其优越的抗疲劳性能。但进一步的研究却发现,与一般的金属材料不同,复合材料对以压为主的疲劳载荷比较敏感,在这些载荷下的寿命明显地低于拉-拉疲劳载荷下的寿命。因此,复合材料的疲劳问题重新受到了注意,而且对它的研究也主要集中在压缩载荷的范围内。尽管已投入了大量的人力,但由于复合材料     

含孔复合材料层板疲劳损伤扩展的实验研究

 本文对一种多向对称铺层的T300/914C碳-环氧复合材料含孔层合板,在拉-压疲劳加载下的损伤扩展进行了实验研究。通过研究层板刚度的变化、试样破坏前的应力-应变特性和损伤的分布,分析了试样破坏机理,阐明了损伤扩展的特征,并对一些实验条件下的分层增长给出了经验的表征。     

低速冲击后复合材料蜂窝夹芯板的疲劳特性

对含低速冲击损伤的蜂窝夹芯板试样进行了拉－拉、压－压和拉－压等３种疲劳试验,以及疲劳后的静载拉伸、压缩破坏试验。用Ｘ光技术、热揭层技术和外观检测等对疲劳损伤的扩展和疲劳后静载的破坏进行了研究,分析了疲劳损伤对蜂窝夹芯板性能的影响。结果表明,低速冲击后蜂窝夹芯板单向疲劳性能良好,而双向疲劳性能可能较差。     

拉伸载荷下GFRP疲劳韧性-寿命模型

<正>由于玻璃纤维增强复合材料(Glass fiber-reinforced plastics,GFRP)在受拉伸循环载荷作用下的疲劳寿命机理不同于金属材料。金属材料主要是由一条控制整个材料疲劳性能的主裂纹扩展而导致材料破坏,而复合材料疲劳破坏机理则比较复杂,即在疲劳加载过程中产生基体裂纹、界面脱胶、分层和纤维断裂以及由它们相互作用而产生的诸多破坏形式。所以寻找一个合适的有较明确物理意义的损伤参量来估算复合材料疲劳寿命是迫切的,也是很有必要的。     

单面螺纹抽钉干涉配合复合材料连接结构的疲劳性能研究

通过疲劳试验研究了单面螺纹抽钉干涉配合复合材料连接结构的疲劳性能,分别考虑了紧固件类型、干涉配合量、搭接板材料及铺层次序等影响因素。采用了拉压疲劳试验,拉压比R=-1,循环应力水平则根据静载极限挤压强度值选定。根据疲劳试验循环应力和疲劳寿命曲线(S-N曲线),得到了不同影响因素对疲劳寿命的影响规律。结果表明,选择适当的干涉配合量、紧固件类型及搭接板均能提高结构的疲劳寿命,4种不同主板铺层次序均对结构疲劳寿命影响不大。     

复合材料桨叶结构损伤演化模型

与金属材料桨叶相比,复合材料桨叶因具有更加优良的抗疲劳性能而被广泛应用到直升机旋翼上。但由于复合材料破坏机理复杂,疲劳性能分散,影响因素众多,导致复合材料桨叶疲劳现象尚处于研究探索之中,在复合材料的微观失效机制与宏观结构的力学性能之间仍然缺少一座桥。鉴于此,文章利用典型复合材料试样的拉伸疲劳实验数据,建立了基体裂纹、纤维断裂和界面脱胶等损伤变量累积模型,从断裂能的角度出发构建了基体裂纹密度、纤维断裂面积与复合材料属性之间的函数关系,分析了基体裂纹密度、纤维断裂面积等损伤变量对复合材料工程性能参数的影响。利用复合材料宏观力学理论,研究了各物理损伤变量对桨叶刚度特性的影响,采用连续损伤变量的状态方程建立了复合材料桨叶的损伤演化模型,这种以有理多项式为状态转移函数微分模型能很好地体现复合材料桨叶在疲劳初期和疲劳末期刚度快速损伤的现象。     

碳纤维/双马复合材料层板疲劳损伤累积和寿命估算

给出了T300/QY8911材料单向板和多向层合板在不同应力水平下的拉-拉疲劳试验结果,提出了以疲劳应变累积为基础的损伤累积模型和相应的寿命估算方程。对于以纤维断裂和基体拉伸开裂损伤累积为控制因素的层板,理论结果与试验值十分吻合。     

复合材料单搭胶接接头静力与疲劳裂纹扩展研究

胶层裂纹是复合材料胶接接头的常见损伤形式之一,严重影响复合材料结构的完整性。以胶接结构中常见的复合材料单搭胶接接头为研究对象,建立其三维数值模型,采用双线性内聚力本构关系表征静态裂纹扩展,并将静态模型扩展至疲劳裂纹扩展模型;结合静力与疲劳试验,对单搭胶接接头的应力应变分布规律、裂纹扩展与破坏机理展开研究。结果表明：单搭胶接接头在静力和疲劳载荷下,由于偏心拉伸应变呈非线性变化,搭接区域两端由于应力集中首先出现裂纹,由两端向中央区域扩展并迅速贯穿整个搭接区域,静力失效模式为内聚破坏,疲劳断面为界面脱胶。     

Bolt insertion damage and mechanical behaviors investigation of CFRP/CFRP interference fit bolted joints

Interference fit has advantages in improving fatigue behaviors of composite bolted joints; however, interference fit bolt insertion tends to cause damages in laminates weakening joint mechanical properties. Therefore, an experimental study was conducted to investigate bolt insertion damages of Carbon Fiber Reinforced Polymer (CFRP)/CFRP interference fit bolted joints. Mechanical behaviors of joints were also evaluated experimentally under both quasi-static loads and cyclic loads. Scanning Electron Microscope (SEM) and high-resolution X-ray micro-CT scan were used to examine micro damages in laminates. Damage and failure behaviors of joints were characterized. The results demonstrated that the hole entrance in upper laminate and the laminate boundary near the hole wall were the most critical regions for damages during bolt insertions. However, the influence of those damages on quasi-static failure loads and fatigue failure modes of joints was minimal. Delamination and matrix cracking occurred first in laminates following fiber and matrix fracture in quasi-static tensile tests. Interference fit could improve the fatigue resistance of the laminate hole; however, the bolt seemed to suffer a more critical local fatigue loading condition. This paper can contribute to composite structure designs, especially in understanding damage and failure behaviors of composite bolted joints.     

Multiaxial fatigue life prediction of composite laminates

A study of composite laminates under tension–torsion biaxial loading is presented. The focus is placed on fatigue lives of composite laminates under different tension–torsion biaxial fatigue loading paths. A macro-meso model used to predict multiaxial fatigue life of composite laminates is also presented in this paper. Firstly, a macro-scale 3D RVE corresponding to composite laminates is established to determine strain components in the material principal direction of each layer for each biaxial stress ratio. Secondly, a meso-scale 3D RVE corresponding to each layer with fibers distributed randomly is established, with progressive damage prediction method, biaxial strength of composite laminates can be predicted, and the final failure layer can be confirmed. Thirdly, select any one of fatigue loading path at which the final failure of composite laminates is fiber failure (matrix failure) to establish the reference curve for fiber (matrix). Finally, with reference curve, fatigue life of composite laminates under any biaxial loading path can be predicted. And numerical results show good agreements with experimental data.     

碳纤维复合材料短梁剪切疲劳特性

研究了碳纤维增强双马来酰亚胺复合材料的层间剪切静态与疲劳加载性质,分析了不同基体、不同铺层界面对层剪性质的影响。给出了层剪疲劳加载的S-N曲线;讨论了层间剪切损伤和增强机理,观察了微观特征。与碳/环氧复合材料相比,双马来酰亚胺基体复合材料在碳纤维和基体之间粘接良好,从而改进了纤维抗疲劳裂纹扩展的能力。     

铺放参数对复合材料厚度方向力学行为影响

为了探究铺放工艺参数的变化对复合材料厚度方向力学行为的影响,通过面外拉伸实验分析了铺放压力与铺放温度对复合材料厚度方向面外拉伸强度与拉伸模量的影响,并对不同铺放工艺的试件失效模式进行了分析。试验结果表明,增大铺放压力会减小层间富树脂区厚度,使复合材料面外拉伸强度不断增大,当铺放压力为0.225 MPa时取得实验组最大值,与铺放压力0.075 MPa相较强度提升约13.1%,失效模式由纤维断裂与纤维层剥离的组合转变为纤维断裂;铺放压力的进一步增大会挤压层间树脂,改变树脂富集形态,使面外拉伸强度下降,剥离失效模式再度出现。实验用复合材料的适宜铺放温度为30℃,过高的铺放温度会导致孔隙率的上升,使复合材料的面外拉伸强度严重下降,裂纹扩展失去规律性;与铺放温度25℃相比,铺放温度为45℃时复合材料面外拉伸强度下降达19.2%,失效模式由纤维断裂与纤维层剥离的组合失效转化为单一的纤维层剥离失效。     

某型直升机尾桨断裂故障分析

明确某型直升机尾桨断裂故障原因，对于该型机的使用、维护有现实意义，对于新机型的安全性提升有借鉴意义。首先通过故障树分析法对某型直升机尾桨叶断裂故障进行分析，得到底事件分析结果；然后开展宏、微观断口分析；最后对柔性梁断口损伤演化开展仿真分析。结果表明：桨叶断裂性质为低应力高周双向弯曲疲劳断裂，当柔性梁纤维压缩方向强度性能值小于700 MPa 时，断口的形式与故障尾桨柔性梁断口类型相似；大载荷状态尾桨会产生较大的振动，振动的增加加剧了尾桨的载荷，导致尾桨柔性梁根部载荷增加，超出柔性梁设计承载能力，桨叶柔性梁根部疲劳断裂。     

直升机主桨毂复合材料星形件疲劳研究

直11型机主桨毂星形件是典型的复合材料层合板结构,在复杂的疲劳载荷环境下,有可能出现几种不同形式破坏模式,如:分层破坏和纤维断裂,忽略任何一种可能出现的破坏模式都将可能给飞行带来安全隐患。理想的试验是有限的试验件能得到所有的破坏模式的结果。本文较完整地总结和介绍了直11型机和“海豚”的复合材料星形件疲劳试验及试验结果,较详细地分析了各种破坏模式的形成机理和挥摆载荷比对破坏模式出现率的影响,认为疲劳试验载荷的挥摆载荷比不应仅仅根据实际飞行时载荷状况,主要应根据星形件结构性能来确定。     

General aspects on structural integrity

This paper seeks to mark the fruitful collaborative research between scholars in the University of Southampton and Beihang University for last 25 years on structural integrity. Their efforts addressed some important issues in structural integrity such as fatigue and fracture behavior,fatigue load spectra, fatigue and fracture lifetimes, reliability-based service period, adhesively bonded composite patch repairs, Plain Woven Fabric(PWF) composites and composite artefacts.New advances in engineering approaches, experimental methods, numerical algorithms and understanding of failure mechanisms relating to structural integrity are highlighted. Probable limits(or drawbacks) are also discussed. This review provides an insight into the general aspects on structural integrity and constitutes a basis for pointers to the further works on structural integrity.