Effects of Shot Peening Process on Thermal Cycling Lifetime of TBCs Prepared by EB-PVD

Conventional two-layered thermal barrier coatings (TBCs) are prepared by electron beam physical vapor deposition (EB-PVD) with ZrO2-8 wt% Y2O3 (8YSZ) as top coat and CoCrAlY as bond coat on disk-shaped Ni based super-alloy. In this paper, three kinds of shot peening process with different lengths of operating time were adopted for bond coating. As a result, changes took place in its sur- face roughness and the surface micro-hardness. A thermal cycling test at 1 273 K×55 min and another at room temperature for 5 min were performed to study the effects of shot peening process on the thermal cycling lifetime of TBCs. It is found that a moderate shot peening process will be able to prolong the life time. The oxidation dynamic of the as-processed TBCs basically accords with the para- bolic rule, and the oxidation test also attests to the spallation between YSZ and thermal growth oxide (TGO) responsible mainly for the failure of TBCs.     

热障涂层氧化行为研究进展

综述了国内外粘接层氧化行为的研究进展,介绍了粘接层氧化动力学,热生长氧化物( TGO) 组

成、结构和形成规律,以及亚稳态Al2O3 向稳态Al2O3 的转变规律,分析了MCrAlY 粘接层及基体合金中的各种

元素对TGO 形貌和成分的影响,指出了深入研究粘接层氧化行为的方法以及热障涂层性能的改善措施。

     

电子束物理气相沉积LaZrCeO热障涂层微结构与热循环性能

热障涂层(thermal barrier coatings,TBCs)是一种由金属黏结层、热生长氧化物层和陶瓷面层组成的金属-陶瓷复合系统,在先进的航空发动机领域上引起了广泛的关注,但目前先进热障涂层的热循环寿命提升和失效行为研究仍然是一个难点。本研究采用电子束物理气相沉积技术(electron beam physical vapour deposition,EB-PVD)制备LaZrCeO/YSZ双陶瓷层热障涂层,研究热障涂层的相结构、显微组织和失效行为。结果表明:LaZrCeO/YSZ涂层为烧绿石与萤石结构组成的复合涂层材料,LaZrCeO/YSZ涂层的微观结构由羽毛状纳米结构和柱内孔隙组成;在1100℃热循环条件下,LaZrCeO/YSZ双陶瓷层热障涂层展现了良好的热循环寿命;热循环实验后,由于应力累积的作用裂纹在热生长氧化层(TGO)中萌生并扩展,包括水平裂纹和垂直裂纹两大类,进而引起整个涂层体系的不稳定,最终导致涂层失效。     

交流阻抗谱法在热障涂层失效研究中的应用

介绍了交流阻抗谱法作为无损检测方法在热障涂层失效分析中的应用。通过对热循环、静态氧化过程中热障涂层体系的阻抗谱分析,利用交流阻抗谱对热障涂层进行拟合,得到了服役过程中D_M以及TGO电阻R拟合的结果与氧化时间呈抛物线关系;并根据阻抗的变化确定了粘结层的氧化过程中氧化物成分从Al₂O₃变化到混合氧化物的过程;对陶瓷层电阻的拟合结果表明,陶瓷层在热循环250~350次之间的电阻变化与陶瓷层内微观结构以及应力的变化有关。     

大气等离子喷涂热障涂层高温氧化行为研究

采用等离子喷涂工艺在GH4099合金基体上制备了热障涂层,并进行了1050℃恒温氧化试验,综合利用X射线衍射仪、扫描电子显微镜、能谱分析仪等检测手段,分析了涂层的显微结构及高温氧化行为。结果表明：等离子喷涂（APS）热障涂层在高温氧化过程中,黏结层被氧化生成热生长氧化物（TGO）。但长时间氧化后,在与TGO毗邻的金属黏结层中产生了范围较窄但浓度变化较大的贫Al带,TGO层出现保护性Al2O3向非保护性混合氧化物转变的现象,导致致密Al2O3层的连续性被破坏,TGO厚度快速增加。     

等离子喷涂LaTi2Al9O19热障涂层的微观组织结构及热物理性能

 第一代热障涂层(TBCs)由氧化钇部分稳定的氧化锆(YSZ)陶瓷隔热层和金属粘结层组成,该涂层长期使用温度低于1 200℃。随着先进航空发动机向着高推重比发展,迫切要求发展新一代超高温、高隔热热障涂层材料。LaTi₂Al₉O₁₉(LTA)在1 500℃长期保持相稳定,是一种非常有前景的超高温热障涂层候选材料。本文采用大气等离子喷涂(APS)制备了LTA涂层,研究了喷涂工艺对涂层微观组织结构和热物理性能的影响。结果表明沉积态涂层中含少量的非晶态,在860℃和1 130℃出现晶化峰。等离子喷涂过程中La₂O₃挥发量较多,导致沉积态涂层中La元素与原始粉末相比含量偏低,而其他组分的化学成分随喷涂功率变化不大。LTA涂层的热扩散系数在1 400℃下为0.3~0.4 mm²·s^-1,热导率为1.1~1.6 W·m^-1·K^-1。1 050℃经过20小时热处理后,得到晶化的涂层在晶化温度范围内的热扩散系数和热导率值均增大。随着喷涂功率减小,涂层孔隙率增加,热导率减小。     

Hot Corrosion Behavior of Double-ceramic-layer LaTi2 Al9O19/YSZ Thermal Barrier Coatings

LaTi 2 Al 9 O 19 (LTA) exhibits promising potential as a new kind of thermal barrier coating (TBC) material, due to its excellent high-temperature capability and low thermal conductivity. In this paper, LTA/yttria stabilized zirconia (YSZ) TBCs are produced by atmospheric plasma spraying. Hot corrosion behavior and the related failure mechanism of the coating are investigated. Decomposition of LTA does not occur even after 1 458 hot corrosion cycles at 1 373 K, revealing good chemical stability in molten salt of Na 2 SO 4 and NaCl. However, the molten salt infiltrates to the bond coat, causing dissolving of the thermally grown oxide (TGO) in the molten salt and hot corrosion of the bond coat. As a result, cracking of the TBC occurs within the oxide layer. In conclusion, the ceramic materials LTA and YSZ reveal good chemical stability in molten salts of Na 2 SO 4 and NaCl, and the bond coat plays a significant role in providing protection for the component against hot corrosion in the LTA/YSZ TBCs. LTA exhibits very promising potential as a novel TBC material.     

表面处理对热障涂层界面微结构的影响

采用真空电弧离子镀技术在单晶高温合金DD32上制备HY5金属粘结层,通过振动光饰、吹砂2种不同的表面处理方法改变粘结层表面状态,再在粘结层表面利用电子束物理气相沉积技术制备陶瓷层。研究了不同处理方法对粘结层表面状态的影响;测试了不同表面处理方法下制备的热障涂层的高温氧化性能并对比分析了它们的变化规律。此外,探讨了不同表面处理方法对界面元素成分及失效特征的影响。研究结果表明,通过表面处理可以去除粘结层表面较大的凸起,提高表面平整度,提高热障涂层抗氧化性能。与粗糙界面相比,光滑界面形成的TGO层均匀致密,Al含量高。经长时间的高温氧化后,粗糙界面的TGO层出现明显皱曲现象,陶瓷层开裂剥落。     

涡轮叶片热障涂层在CMAS 环境下的失效分析

对于多台份某型发动机在试车后出现的带热障涂层涡轮叶片表面附着较多环境沉积物CMAS进而导致热障涂层脱落 失效的故障,通过宏观形貌观察、化学成分分析、微观结构分析等方法对CMAS分布规律、成分特征和失效模式进行了分析。结果 表明：CMAS沉积物在叶盆面较厚、叶背面较薄,靠近缘板处较厚、叶身中部位置较薄,进气边较厚、排气边较薄;厚度较薄处的附 着物颗粒细小、分布均匀,较厚处的附着物结构较疏松,大多呈块状不均匀分布;涡轮叶片热障涂层表面沉积物及气膜孔堵塞物的 成分以CMAS为主,同时还有中低温部件碰摩磨屑生成的Fe2O3、TiO2和NiO;由CMAS腐蚀引发的热障涂层失效模式主要有气膜孔 堵塞引发周围涂层烧结失效、涂层表面和内部应力失配、陶瓷层柱状晶被冲击撞断以及8YSZ热障涂层被溶解。     

电子束物理气相沉积YSZ热障涂层热循环性能

考察了YSZ热障涂层的抗热循环性能;分别利用SEM、XRD分析了热循环前后涂层的显微结构和相组成。经分析可知,YSZ热障涂层具有典型的柱状晶结构,沉积态时YSZ涂层为t/t′相,经过600次热循环后,YSZ涂层未发现脱落。     

等离子喷涂工艺参数对GdPO4热障涂层组织结构和结合强度的影响

随着航空发动机涡轮进口温度提升,目前最广泛使用的Y₂O₃部分稳定ZrO₂(YSZ)热障涂层(TBCs)已难以满足需求,亟须发展新一代超高温TBCs。GdPO₄是一种极具应用前景的TBCs材料。本工作采用等离子喷涂方法制备GdPO₄/YSZ双陶瓷层结构TBCs,研究喷涂工艺参数特别是喷涂功率对GdPO₄陶瓷涂层相组成、表面形貌、微观结构以及结合强度的影响。结果表明:等离子喷涂GdPO₄过程中会有元素P损耗,得到的涂层除了GdPO₄外,还有一些Gd₃PO₇相;随着喷涂功率降低,Gd₃PO₇相含量减少;GdPO₄陶瓷涂层的主体结构由充分熔融的喷涂粒子堆垛构成,其中镶嵌有未熔化粒子构成的微区;随着喷涂功率降低,未熔化微区增多,涂层厚度降低;GdPO₄/YSZ TBCs的结合强度随喷涂功率降低而减小,主要是由于未熔化微区增多降低了涂层的内聚力;因此,低喷涂功率不利于涂层的结合强度。     

Effect of Sintering on Thermal Conductivity and Thermal Barrier Effects of Thermal Barrier Coatings

Thermal barrier coatings (TBCs) are mostly applied to hot components of advanced turbine engines to insulate the components from hot gas. The effect of sintering on thermal conductivity and thermal barrier effects of conventional plasma sprayed and nanostructured yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) are investigated. Remarkable increase in thermal conductivity occurs to both typical coatings after heat treatment. The change of porosity is just the opposite. The grain size of the nanostructured zirconia coating increases more drastically with annealing time compared to that of the conventional plasma sprayed coating, which indicates that coating sintering makes more contributions to the thermal conductivity of the nanostructured coating than that of the conventional coating. Thermal barrier effect tests using temperature difference technique are performed on both coatings. The thermal barrier effects decrease with the increase of thermal conductivity after heat treatment and the decline seems more drastic in low thermal conductivity range. The decline in thermal barrier effects is about 80 °C for nanostructured coating after 100 h heat treatment, while the conventional coating reduces by less than 60 °C compared to the as-sprayed coating.     

微叠层结构EB-PVD热障涂层

采用EB-PVD非连续沉积工艺制备了微叠层结构热障涂层,对涂层结构和晶体形貌进行了SEM观察和分析,采用激光脉冲法测定了涂层的热扩散系数,并采用增重法研究了涂层的氧化动力学特征,分析了氧化后的元素扩散情况.结果表明,非连续EB-PVD沉积工艺制备的涂层具有明显的层状特征,常规EB-PVD热障涂层的柱状晶结构被周期性地打破;但在每一层中,柱状晶结构得以保留,且晶粒更加细化.微叠层热障涂层的热扩散系数比常规热障涂层降低20%～30%,涂层热扩散系数的降低主要与层间界面和晶粒的细化减小了声子的平均自由程有关.微叠层结构热障涂层的氧化增重速率明显低于常规试样,遵循典型的抛物线规律,垂直于元素扩散方向的层间界面和细晶更有效地降低或阻止了O、Al、Ni、Cr等元素的扩散,可能是氧化增重速率较低的主要原因.     

EB-PVD热障涂层对IC10合金力学性能的影响

采用电弧离子镀技术在IC20合金基体上制备NiCrAlYSi粘结层,利用电子束物理气相沉积（EB—PVD）技术在粘结层上制备YSZ陶瓷面层。研究了YSZ热障涂层对IC10合金拉伸、持久、疲劳性能的影响。结果表明：IC10合金沉积YSZ热障涂层后,980℃／200MPa高温持久寿命与IC10合金相当;900℃高温抗拉强度σb、屈服强度σ0.2、伸长率占和断面收缩率砂与基体相比,基本保持不变;室温抗拉强度σb。屈服强度σ0.2：与基体相比稍有下降;800℃／447MPa疲劳寿命与基体合金相当。因此,IC10合金沉积TBCs涂层后,对IC10合金力学性能无明显影响,不影响合金的实际使用。     

双层氧化物生长下热障涂层的界面失效与应力演化

在长时高温服役环境下,热障涂层（TBCs）会在内部的陶瓷层（TC）和粘结层（BC）之间生成由Al2O3层和混合性氧化物层（MO）组成的双层热生长氧化物（TGO）。其中,后期生成的MO 由于其疏松多孔、脆性大等特点,极易造成涂层内微裂纹的形成和扩展,导致涂层的过早剥落。因此,依据双层TGO 生长的扩散—氧化模型,在考虑材料非线性变形行为的基础上,运用生死单元法模拟TBCs 内双层TGO 异向生长下涂层界面的失效与应力演化过程。结果表明：MO 的生长会大幅度提升涂层界面的拉伸应力水平,易导致MO/TC 界面在高温阶段波峰区域和冷却阶段斜坡中心区域发生破坏及失效;MO/TC 界面的失效会引起BC 层波峰处更高的拉伸应力,促进冷却阶段Al2O3/BC 界面从波峰向波谷处的破坏;MO/TC 界面失效后,hAl2 O3 /hMO 的增加会加速Al2O3/BC 界面的破坏。     

电子束物理气相沉积La2Zr2O7热障涂层研究

为克服传统热障涂层材料YSZ耐温性能和隔热性能的不足,以ZrO2和La2O3为原料,采用无压烧结法合成了烧绿石结构化合物La2Zr2O7,用电子束物理气相沉积(EB-PVD)法在高温合金基体上制备了La2Zr2O7涂层,分析了涂层的成分,并对其显微结构、热物理性能与传统YSZ热障涂层进行了对比研究.结果表明,La2Zr2O7涂层成分处于P结构范围内,呈典型的柱状晶结构,柱状晶头部呈明显的金字塔形状.与传统YSZ柱状晶相比,La2Zr2O7涂层的柱状晶紊乱度更大,尺寸更加细小,并且柱状晶上的树枝状亚晶更多.在25～1200℃范围内,La2Zr2O7涂层的热导率最大为0.985W/(m·K),最小为0.796 W/(m·K),大大低于同条件下的YSZ涂层.低本征热导率、小柱状晶直径、大紊乱度、密度轻及高孔隙率是造成La2.Zr2O7涂层低热导率的主要因素.     

交流阻抗谱法评价热障涂层的热腐蚀行为(英文)

本文利用交流阻抗这种无损检测的方法研究了热障涂层在质量分数为25%NaCl+75%Na2SO4混合盐体系中的热腐蚀行为。实验结果显示,热腐蚀条件下,在陶瓷层和粘结层界面处形成TGO层为混合氧化物层,成分为Cr2O3、(Ni,Co)(Cr,Al)2O4和NiO,其厚度增长符合抛物线规律。热障涂层在110个循环腐蚀之前时,TGO层的电阻值随其厚度的增加而增加;110个循环后,虽然TGO层的厚度还是在增加,但由于TGO层孔隙的增多而导致其电阻值有所下降。陶瓷层的电阻值随着陶瓷层中裂纹的萌生和扩展而不断增大。等效电路中得到的参数可以用来表征热障涂层的失效行为。     

在高温蠕变环境中的热障涂层失效行为

对电子束物理气相沉积(EB-PVD)制备的由NiCoCrAlY粘结层和YSZ(YttriaStabilizedZirconia)陶瓷层组成的双层结构热障涂层,采用标准高温蠕变试验方法,研究了在高温、恒定外载荷作用下热障涂层中各层的形貌变化及裂纹的萌生、扩展,并探讨了涂层的失效过程和机理。垂直于试样轴向的断面观察表明,涂层在外力作用下氧化200h后层间裂纹非常明显,但几乎不发生在热氧化层(TGO)内,而是发生在陶瓷层与TGO层、TGO与粘结层之间,尤其发生在TGO与陶瓷柱状晶之间的等轴晶处。这种层间裂纹是在拉伸应力作用下,合金基体和粘结层发生径向收缩,而陶瓷层和TGO层的应变容限无法满足径向收缩而产生的。     

激光重熔改性热障涂层抗CMAS腐蚀特性

采用激光对大气等离子喷涂7YSZ热障涂层进行表面重熔处理,探讨基体预热和Al₂O₃溶胶涂敷对激光重熔层裂纹愈合的影响,研究处理后热障涂层的耐CMAS熔盐腐蚀性能。结果表明:涂层经过激光重熔和基体预热后的激光重熔处理后,与未经重熔处理涂层的CMAS腐蚀厚度基本相同;而采用表面Al₂O₃溶胶涂敷加激光重熔的热障涂层的CMAS腐蚀厚度明显减小,表明Al₂O₃溶胶涂敷加激光重熔工艺可以有效地减轻CMAS熔盐侵蚀,其机理是表面形成的Al₂O₃薄膜溶于CMAS后生成了难熔晶体钙长石,降低了熔盐的流动性和腐蚀性。     

电子束物理气相沉积热障涂层寿命预测模型

为了准确预测热障涂层（TBCs）的剥落寿命，把涂层使用过程中所存在的潜在危险减到最低，建立精确的热障涂层寿命预测模型具有十分重要意义。本文介绍了一种电子束物理气相沉积（EB-PVD）技术制备的热障涂层的寿命预测模型。该模型是通过对EB-PVD热障涂层陶瓷的物理和力学性能、结合强度的测定，热生长氧化层（TGO）生长动力学的研究以及热循环剥落寿命数据的定量研究而建立的一个TBCs系统的非线性寿命预测模型。从涂层实际寿命与模型预测寿命对比发现，该模型预测的涂层寿命与涂层的实际寿命相吻合。