稀土铝锂合金的直流冲击波点焊

本文对稀土铝锂合金焊试验结果进行了分析，并与ＬＹ１２铝锂合金点焊接头的组织性能相比较，发现稀土铝合金点焊接头的拉伸及剪切强度低于ＬＹ１２铝锂合金，但是延性比高于ＬＹ１２，且其熔核的金相组织与ＬＹ１２不同。     

转速对铝铜层状复合板搅拌摩擦焊接接头组织性能的影响

采用搅拌摩擦焊接(FSW)对铝铜层状复合板进行焊接,研究转速对焊接接头组织性能的影响。结果表明:FSW接头在焊缝区域内铝铜金属呈层状分布;随着搅拌头转速的增大,焊核区(NZ)中铝与铜晶粒尺寸增大;转速为1180 r/min时,铝层焊缝中心区域平均显微硬度为33.0 HV,超过母材显微硬度,抗拉强度为127.21 MPa;转速为750 r/min时,铜层焊缝中心区域平均显微硬度为99.7 HV,达到母材显微硬度的82.05%;孔洞缺陷是造成接头力学性能较低的主要原因。     

2195铝锂合金填充式摩擦点焊接头显微组织与力学性能

研究了2195铝锂合金填充式摩擦点焊不同焊接时间对接头力学性能的影响,对典型接头微观组织进行了分析和横截面显微硬度测试.实验结果表明,预热时间在0.2~1.4s时,焊点剪切拉伸抗力与十字拉伸抗力均先增大后减小;焊接时间在1.8~3.2s之间时,焊点剪切拉伸抗力与十字拉伸抗力均增大;摩擦点焊接头可分为焊核区、竖直面热机影响区、水平面热机影响区三个典型区域,其中竖直面热机影响区与焊核区的连接界面为接头的薄弱环节;焊核区发生了较大程度的软化.     

钢/铝异种金属点焊研究进展综述

钢/铝异种金属的复合结构具有轻量化兼具良好结构性能的优势，在航空、航天和汽车制造领域具有极大的应用前景。点焊是制造这种结构的重要技术手段。但是，钢/铝异种金属在焊接过程中会产生脆性金属间化合物，传统的电阻点焊连接钢/铝异种金属面临着巨大的挑战。对钢/铝异种金属的点焊技术的研究进展进行了广泛的调研，着重对电阻点焊技术、电阻铆焊技术、CMT点焊技术、超声波点焊技术和摩擦塞-铆复合点焊技术等技术的研究进展进行了系统比较与分析，并对钢/铝异种金属点焊技术发展趋势进行了展望。     

异种铝合金搅拌摩擦点焊工艺研究

研究了搅拌针长度对Al5754/Al6111搅拌摩擦点焊接头力学性能的影响。结果表明,在保持轴肩压入深度为500μm条件下,搅拌针长度从1.6 mm增加到2.0 mm的过程中,点焊接头的力学性能无明显变化;当搅拌针长度继续增加到2.2 mm时,点焊接头的力学性能迅速提高。通过分析提出高度锯齿状的HOOK形貌是点焊接头力学性能提高的主要原因。     

异种铝合金环形构件的搅拌摩擦焊接工艺

为实现异种铝合金环形构件的高精度装配与连接,文中设计一种卧式串联型轴向移动转径向伸缩的搅拌摩擦焊接工装。结果表明,采用此工装成功实现铝铜系/铝镁系异种铝合金环形构件的高精度装配与高质量焊接,接头内部质量达到了I级接头要求,接头的抗拉强度高于245 MPa,延伸率高于16%,且所有接头均断裂在铝镁系铝合金母材一侧,说明该接头的整体性能要优于铝镁系铝合金母材性能,解决了铝铜系/铝镁系异种铝合金熔焊易出现焊接裂纹的工程难题。     

铜与铜镶嵌非晶体焊料点焊的研究

研究了铜与铜镶嵌非晶体焊料ＱＪＹ－５Ａ、ＱＪＹ－５Ｂ点焊,以及调整点焊温度场来降低焊接区铜的熔点,提高焊接区电能利用率的措施;叙述了铜与铜镶嵌ＱＪＹ－５Ａ、ＱＪＹ－５Ｂ焊料点焊焊核形成过程及特点。     

基于超声波C 扫描的SUS304 不锈钢板点焊接头质量分析

利用超声波水浸聚焦入射法对1 mm厚的SUS304奥氏体不锈钢板点焊接头进行超声C扫描成像检测;研究了不同焊接工艺参数下获得点焊接头的超声波C扫描图像特征,据此分析了接头的焊核直径,并与焊核切口端面尺寸进行了比较;对点焊接头进行了拉伸—剪切试验,测试了接头的力学性能。结果表明:超声波水浸聚焦入射法能够观测出点焊焊核直径,并能有效地观测出焊核内部形貌特征。当焊接电流为定值(4k A),供给压力为0.15 MPa时,接头出现飞溅、焊穿等缺陷,并且在超声波C扫描图像中能够清晰地反映出来;当供给压力为0.45 MPa时,虽然点焊焊核直径增大,且未出现焊接缺陷,但是过大的供给压力导致接头厚度变小,影响了接头抗拉强度。当供给压力为定值(0.4 MPa),焊接电流为9 k A时,在C扫描图像上同样反映出飞溅、焊穿等典型的焊接缺陷,此时接头的失效载荷及能量吸收值急剧下降。     

铝合金回填式搅拌摩擦点焊工艺及组织特征分析

对2219+5A06铝合金进行了回填式搅拌摩擦点焊试验，研究了搅拌头旋转速度，下压-回抽速度和压入量等工艺参数对点焊接头力学性能的影响。对不同参数焊接的点焊接头进行了剪切拉伸抗力试验。结果表明：搅拌头旋转速度和下压-回抽速度对点焊接头的力学性能影响较大，而压入量对力学性能的影响较小。对点焊接头的微观组织分析表明，焊点接头可分为焊核区、竖直面热机影响区和水平面热机影响区三个部分。焊核区及水平面热机影响区为细小的等轴晶粒，水平面热机影响区形成与板材平行的结合面，竖直面热机影响区及焊点根部的hook缺陷是焊点力学性能的薄弱区域。     

SiCp/101铝基复合材料铜中间层TLP

通过颗粒增强铝基复合材料的铜中间层TLP扩散连接试验 ,对接头性能的影响因素进行了研究 ,并采用扫描电镜和电子探针等手段分析了接头连接机理、微观组织与接头性能的关系 ,从而确定了其试验条件和焊接规范。     

铝/铜异种金属搭接无倾角微搅拌摩擦焊接工艺特性

以0.5mm厚6061铝合金和2mm厚T2紫铜搭接接头为研究对象,开展了无倾角微搅拌摩擦焊接试验,通过对搅拌工具材料选择、焊缝成形、接头性能分析,研究了其焊接工艺特性。试验结果表明,相比热作模具钢,采用高速工具钢制成的搅拌工具有更长的使用寿命。对于铝/铜搭接接头,无倾角微搅拌摩擦焊接能获得成形良好的焊缝,并且其工艺窗口宽泛,接头的力学性能良好,其承载能力能够达到铝合金母材的95%以上,但是当焊接速度为200mm/min时,主轴转速一旦超过25000r/min,焊缝表面将会出现沟槽缺陷。     

推进剂贮箱用2A14铝合金接头应力腐蚀性能研究

为了研究推进剂贮箱用2A14铝合金接头介质相容性,分析了铝合金的应力腐蚀机理,以2A14-T6铝合金本体、搅拌摩擦焊(FSW)接头和变极性氩弧焊(VPTIG)接头为研究对象,通过慢应变速率拉伸法进行应力腐蚀试验研究。结果表明,2A14铝合金在3.5%NaCl溶液中存在应力腐蚀现象,FSW接头的抗腐蚀性能优于VPTIG接头。。     

超声冲击处理对2A12铝合金焊接接头疲劳性能的影响

采用超声冲击处理方法对2A12铝合金焊接接头进行全覆盖强化处理.通过弯曲疲劳对比试验,建立了未处理与超声冲击强化处理铝合金焊接接头试样的S-N曲线,分析了超声冲击处理对铝合金焊接接头疲劳性能的影响;通过接头组织、残余应力和断口形貌分析了超声冲击处理提高铝合金焊接接头抗疲劳断裂性能的微观机理.结果表明,超声冲击处理使2A...     

Microstructural formation and mechanical performance of friction stir double-riveting welded Al-Cu joints

A novel friction stir double-riveting welding (FSDRW) technology was proposed in order to realize the high-quality joining of upper aluminum (Al) and lower copper (Cu) plates, and this technology employed a Cu column as a rivet and a specially designed welding tool with a large concave-angle shoulder. The formations, interfacial characteristics, mechanical properties and fracture features of Al/Cu FSDRW joints under different rotational velocities and dwell times were investigated. The results showed that the well-formed FSDRW joint was successfully obtained. The cylindrical Cu column was transformed into a double riveting heads structure with a Cu anchor at the top and an Al anchor at the bottom, thereby providing an excellent mechanical interlocking. The defect-free Cu/Cu interface was formed at the lap interface due to the sufficient metallurgical bonding between the Cu column and the Cu plate, thereby effectively inhibiting the propagation of crack from the intermetallic compound layer at the lap interface between the Al and Cu plates. The tensile shear load of joint was increased first and then decreased when the rotational velocity and dwell time of welding tool increased, and the maximum value was 5.52 kN. The FSDRW joint presented a mixed mode of ductile and brittle fractures.     

2219薄板铝合金浮动式双轴肩搅拌摩擦焊接及组织性能分析

以运载火箭助推器贮箱广泛应用的4 mm厚2219薄板铝合金为焊接对象,研制了浮动式双轴肩搅拌头,分析了内部塑性金属流动模式及特点,并推测出需匹配较低焊接热输入才能获得优质焊缝。工艺探索及优化试验结果直接验证了焊缝内部塑性金属流动模式及推测。接头宏观组织形貌分析结果显示:不同焊接速度下的焊缝横截面宏观形貌都可以观察洋葱环特征,且随着焊接速度提高,洋葱环特征越发增多,并从靠近前进侧的焊核区逐渐向后退侧孕育发展,这也有效验证了薄板铝合金双轴肩搅拌头的设计思路。薄板铝合金双轴肩搅拌摩擦焊接头横截面显微硬度分布均呈"U"型,接头显微硬度最低点位于焊核区与后退侧热机影响区的交界处。接头力学性能测试结果显示:随着焊接速度逐渐升高,接头抗拉强度逐渐升高,且当焊接速度达到350 mm/min时,接头抗拉强度达到最高值。铝合金浮动式双轴肩搅拌摩擦焊接头延伸率整体较高,焊接速度对其影响不大。铝合金双轴肩搅拌摩擦焊接头正、背弯均可以达到180°无裂纹。基于立式纵缝搅拌摩擦焊系统成功实现了2 m长试片的浮动式双轴肩搅拌摩擦焊,累计焊接长度达到60 m,且双轴肩搅拌头完整,未发现裂纹、扭曲或其他损伤。     

机载电子电气设备缓蚀剂的评价

采用塔菲尔(Tafel)曲线法和电化学阻抗法(EIS)2种电化学方法评价了 4种不同型号的电子电气缓蚀剂在天然海水中对 T2铜合金、H62铜合金以及 2Al2-T4铝合金的缓蚀效果。对于 T2铜合金,缓蚀剂的缓蚀效率从高至低依次为 DZ-1、TFHS-20、DJB-823、WD-40;对于 H62铜合金,缓蚀效率从高至低依次为 DZ-1、DJB-823、WD-40、 TFHS-20;对于 2Al2-T4铝合金,缓蚀效率从高至低依次为 DZ-1、WD-40、DJB-823、TFHS-20。4种缓蚀剂中,DZ-1缓蚀剂 Tafel曲线法和 EIS法得到的缓蚀效率都高于 99.5%,所以,对于 T2铜合金、H62铜合金以及 2Al2-T4铝合金 3种金属材料来说,DZ-1是 4个型号的缓蚀剂中效果最优的。     

SPS温度对铜/镍粉/304不锈钢接头组织与剪切强度的影响

采用脉冲放电等离子烧结(SPS)制备了添加镍粉中间层的铜/304不锈钢接头,研究了焊接温度对接头组织及力学性能的影响。结果表明,以镍粉为中间层,可以实现铜与304不锈钢的扩散焊接。铜/镍界面处铜、镍互扩散形成铜/镍界面扩散层,镍/304不锈钢界面处镍、铁互扩散形成镍/铁界面扩散层,铜/镍扩散层厚度大于镍/铁扩散层厚度。在焊接压力为10 MPa、焊接温度为900℃时,铜/304不锈钢接头剪切强度最佳,为98 MPa。铜/304不锈钢接头断口形貌呈韧窝状,断裂均在镍中间层处,接头连接强度受制于镍中间层本身的强度。     

2219 铝合金VPTIG 焊接接头拉伸性能分析

2219 铝合金气孔敏感性较强,变极性TIG 焊接工艺可以有效减少和抑制气孔产生,是适合于
2219 铝合金的焊接工艺。本文介绍了2219T62 铝合金VPTIG 焊接接头的拉伸性能,进行了拉伸断口形貌分析
和微观组织分析。结果表明:2219T62 铝合金VPTIG 焊接接头强度系数可以达到65% 以上,焊接接头为混合
断裂方式,VPTIG 焊缝盖面层气孔相比打底层较多。     

7050铝合金搅拌摩擦焊接头组织特征研究

针对7050铝合金搅拌摩擦焊接头,给出各组织特征区的定义,并对各特征区的组织状态、晶粒大小、沉淀强化相分布等进行深入的分析。为同材质的铝合金搅拌摩擦焊接头的综合性能评估提供更好的依据。