复合材料雷击防护电热耦合模型

为了研究复合材料雷击防护(lightning strike protection,LSP)系统在雷电流作用下的损伤规律,基于雷击过程中的能量守恒关系,建立复合材料层合板雷击防护的电-热耦合数学模型。在此基础上,在ABAQUS中建立铝涂层防护的碳纤维增强复合材料(carbon fiber reinforced polymer,CFRP)层合板雷击烧蚀损伤有限元模型,并对雷击烧蚀损伤进行分析,和实验结果对比验证仿真的有效性,得出复合材料层合板在不同峰值雷电流、不同组合波形和不同铝涂层厚度雷电流作用下的烧蚀损伤规律。结果表明:铝涂层厚度相同时,峰值电流从50kA 增大到100kA时,复合材料层合板损伤面积约增大 1.5 倍;10/350波形50 kA峰值雷电流作用下,基准件的损伤面积约为0.05 mm厚度铝涂层防护系统下复合材料损伤面积的4倍。     

复合材料层合板雷击烧蚀损伤模拟

 为解决复合材料层合板的雷击烧蚀问题,通过复合材料层合板雷电流烧蚀的热-电-结构耦合分析,建立复合材料层合板烧蚀的三维有限元模型。利用删除单元法模拟复合材料层合板在不同脉冲波形雷电流作用下的冲击响应,进行复合材料层合板雷击损伤机理和损伤模式分析,得出了复合材料层合板在不同脉冲波形和峰值雷电流作用下的瞬态热传递和热烧蚀规律。分析了不同雷电流参数对烧蚀结果的影响。结果表明峰值电流、放电量和比能对复合材料层合板的烧蚀尺寸和内部损伤产生很大的影响。     

碳纤维复合材料雷电防护特性仿真及试验研究

为了研究不同防护方式下的碳纤维增强型复合材料(CFRP)层合板雷电损伤特性,针对无防护、喷铝涂层防护以及铜网防护的三种CFRP层合板注入D+B+C*雷电流组合波形,通过观察损伤区域、C扫描探测并结合电热耦合与电流密度分布仿真,研究不同防护方式下CFRP损伤特性.研究表明,CFRP损伤类型有树脂烧蚀、纤维断裂、分层等损伤...     

基于热力耦合层合板雷击损伤特性分析

为研究复合材料层合板在雷电流作用下的烧蚀损伤力学特性,建立复合材料雷击热力耦合有限元分析模型,与文献实验结果对比验证模型的有效性。根据Hashin三维失效准则编写用户材料子程序,分别得出层合板雷击烧蚀区域周围出现的力学损伤、各层力学损伤分布以及首层在不同方向上的应力分布,分析得出层合板的烧蚀损伤随雷电流持续时间的变化规律。结果表明:由于存在较高的温度梯度,导致层合板出现较大的热膨胀应力,进而导致层合板内部产生各种力学损伤,即基体开裂、分层及纤维断裂;雷击电流施加时间、峰值电流与温度场均对层合板烧蚀面积产生较大的影响。     

CFRP层合板雷击烧蚀损伤模拟的电流加载方式分析

通过改进加载方式减小数值模拟与试验结果误差对于提高仿真准确性具有一定意义。本文探究复合材料层合板在不同形式雷击电流下的烧蚀损伤特性，改进Braginskii 电弧半径扩展公式，建立适用于雷击过程的电弧扩展半径数值模型；基于ABAQUS 建立CFRP 层合板有限元模型，分析不同电流加载方式下的烧蚀损伤情况。结果表明：建立的有限元模型能够模拟CFRP 层合板雷击烧蚀损伤；扩展移动加载造成的损伤面积、损伤深度和损伤体积与试验结果对比误差均约为7%，较其他加载方式仿真结果与试验结果对比具有良好的一致性，模拟复合材料雷击烧蚀损伤时应同时考虑电流扩展和移动的影响。     

含紧固件层合板雷击烧蚀损伤分析

为了研究含紧固件复合材料层合板在雷击电流作用下的烧蚀损伤规律,基于热电耦合建立含紧固件层合板的雷击有限元分析模型,并对雷击烧蚀损伤结果进行分析,与参考结果对比验证模型的合理性,并分析得到含紧固件层合板在不同峰值电流、紧固件尺寸、层合板宽度比条件下的烧蚀损伤结果,总结不同因素影响下烧蚀损伤面积的变化规律。结果表明:雷击峰值电流、紧固件的尺寸、层合板的宽度对含紧固件层合板烧蚀损伤面积具有极大的影响,相同的雷击电流波形,峰值150 kA雷击电流导致的烧蚀损伤面积是峰值50 kA的15.39倍;紧固件越小,烧蚀损伤面积越大,分层损伤面积越大,其中,当紧固件直径减小至1/2时,烧蚀损伤面积最大可增加4.97倍,分层损伤面积最大可增加1.91倍;层合板损伤面积随宽度的增加先增大后减小,最后趋于平稳,其中最大损伤面积与最小损伤面积的比值可达1.81倍,且比值随着紧固件直径的增加而增大。     

含铜网复合材料雷电流直接效应实验研究

为了研究铜网防护层对复合材料的雷击防护效果,采用两种不同雷电流波形,对不同尺寸含铜网(0.25 mm厚)与无铜网防护复合材料试件进行模拟雷电流冲击实验,通过目视损伤观察、光学显微镜放大、超声损伤扫描,对比分析复合材料的雷击损伤程度及特征。结果表明:雷电流波形1,峰值电流分别为50 k A和80 k A时,Type1(150 mm×100 mm)型试件无铜网防护下复合材料的雷击损伤面积和深度分别为1785 mm~2,0.63 mm和3041 mm~2,0.96 mm,而含铜网防护试件基本无损伤;雷电流波形2,峰值电流为40 k A时,Type 2(250 mm×45 mm)型试件无铜网防护下的雷击损伤面积和深度分别为2156.75 mm~2,0.36 mm,而含铜网防护试件损伤面积小于100 mm~2,里层还未损伤;0.25 mm铜网能够承受的最大雷电流强度存在一个门槛值,该门槛值可用作用积分来表示,雷击防护效果与试件尺寸无关,仅与作用积分有关,其对应作用积分门槛值约为85218 A~2·s。     

复合材料电导率对雷击烧蚀损伤程度的影响

根据雷击过程中能量转换关系,建立基于热-电耦合的复合材料雷击烧蚀损伤分析模型,该模型考虑了复合材料电导率随热解度的变化。通过该模型,对比复合材料三个方向电导率多个数量级变化后的雷击烧蚀损伤。结果表明:在相同雷电流参数下,复合材料沿不同方向的电导率变化对雷击烧蚀损伤影响程度不同;沿纤维方向电导率提升,表观损伤面积和损伤深度均下降;垂直于纤维方向电导率提升,表观损伤面积增加,损伤深度下降;沿厚度方向电导率提升,表观损伤面积下降,损伤深度增加;三个方向任一电导率提升,复合材料总体的损伤体积均下降,当各方向上的电导率分别提高1、2、3个数量级,损伤体积影响程度最大的是沿纤维方向变化,分别降低47.83%、75.08%和97.82%,沿厚度方向变化影响程度次之,分别降低36.25%、53.44%、65.54%,垂直于纤维方向影响程度最小,分别降低8.72%、12.58%和24.76%;提高复合材料电导率,能够对雷击防护起到明显作用,对于防雷击效果的全面评估需要二维损伤和三维损伤相结合。     

飞机复合材料表面导电层的雷击仿真研究

复合材料在飞机上的应用越来越广泛,与金属相比复合材料导电性较差,因此处于雷击区域的复合材料部件表面要设计导电防护层以承受雷击时的瞬间放电,避免复合材料部件的烧蚀损伤。本研究利用数值仿真的方法建立了数学模型,计算了复合材料表面导电层通过雷击电流脉冲后的电场和温度场分布,并对该导电层的雷击防护能力及可靠性进行了评价。模拟结果表明,厚度为0.20 mm的铝导电层最适宜做飞机表面的雷击防护层。     

碳纤维复合材料雷击损伤的瞬态红外热成像检测

通过雷电模拟,对复合材料层合板试样进行雷击损伤试验。基于热扩散原理,针对不同的雷击试验件,采用波形为长脉冲形式的瞬态热激励方式对雷击损伤进行红外热成像检测,并对不同时刻的检测结果进行分析、比较,对缺陷轮廓进行界定,对结果进行定量测量。检测结果表明,无论是否对碳纤维复合材料表面进行防护,瞬态红外热成像方法均能够有效检测出雷击后的内部分层损伤,可对损伤的严重程度进行有效区分,能够对缺陷尺寸、面积进行准确测量。     

Carbon nanotube protected composite laminate subjected to lightning strike: Interlaminar film distribution investigation

A kind of interlaminar film with carbon nanotubes inserted into polyether ketone with cardo was used for lightning strike protection of composite laminates. The distribution of the interlaminar film was investigated by experimental and numerical methods. Artificial lightning strike tests were conducted for 12-film carbon nanotube and traditional surface silver coating protected specimens. Then corresponding finite element models (FEMs) were established to analyze the lightning strike effect and validated by the experimental results. Based on the FEMs, the number, distribution and thickness of interlaminar film were investigated in order to obtain equivalent protection effect with the traditional surface silver coating. The results show that only the first two layers were damaged for the surface silver coating protected specimen, while 5 layers were ablated for the 12-film protected specimen. Lightning strike damage area of the laminate protected with 5-film carbon nanotube is almost the same as that of the laminate protected with 12-film carbon nanotube. Compared with traditional surface silver coating protection, one film protection with thickness of 360 μm can make the laminate to obtain equivalent damage depth, 54.8% smaller damage area and 58% less additional weight. And reparability of the laminate is better than that of the laminate protected with 5 interlaminar films.     

民用飞机短舱复合材料结构雷电直接效应试验验证方法及漆层厚度影响研究

随着飞机设计的发展,复合材料广泛应用于民用飞机短舱结构。由于碳纤维复合材料结构的导电性以及抗雷电损伤能力比铝合金结构差,复合材料短舱结构雷电防护能力已成为影响飞机飞行安全的一项关键问题。依据相关适航条款和相应的国际标准,阐述了民用飞机短舱复合材料雷电防护试验验证方法,并依据验证方法对漆层厚度的损伤影响进行了试验研究。短舱常规蒙皮构型的复合材料试验件,在不同漆层厚度下的雷电防护试验结果表明,漆层较薄时,漆层对短舱复合材料的雷电直接效应防护能力无明显的影响;当漆层厚度达到一定厚度时,较厚的漆层将显著降低短舱复合材料的雷电直接效应防护能力,最严重时将造成复合材料蒙皮的击穿,损伤蒙皮内部系统设备,从而危害飞行安全。试验结果与理论的机理分析具有良好的一致性,对民用飞机短舱复合材料结构的雷电防护设计提供了指导方向和参考意义。     

飞机复合材料雷击防护层设计与应用

结合复合材料自身的弱导电性特点,通过在其表面增加导电功能层的方式解决复合材料的防雷击问题.设计了复合材料表面火焰喷涂铝涂层、粘接铝箔网及粘接铝箔三种雷击防护层形式,并对三种防护层的制备工艺特点、导电性及适用性进行了研究和分析.结果表明:以上三种雷击防护层显著地提高了复合材料的导电性并具有很好的适用性.     

Thermal damage analysis of aircraft composite laminate suffered from lightning swept stroke and arc propagation

Lightning strike is a complicated process involving multi-field coupling. In order to investigate the thermal damage mechanism of carbon fiber reinforced composites subject to lightning swept stroke, a complete numerical method is presented. Numerical model of lightning discharge is established based on Magneto Hydro Dynamics (MHD) and calculated by FLUENT secondary development technology. Considering aerodynamic flow effect, channel formation and evolution process during lightning discharge is analyzed for lightning current waveform A. Thermal-electric Coupling model is presented according to Radial Basis Function (RBF) interpolation theory, which is implemented by compiling program to make lightning current and heat energy inject into composite laminate. Consequently, damage mechanism of composite laminate under lightning swept stroke is studied based on the coupled numerical model and element deletion method. Ablation damage morphology of composite laminate is analyzed to understand plasma expansion and reattachment in arc root. The results show that aerodynamic flow makes the lightning channel move fast and composite laminate is deteriorated due to thermal damage.     

飞机雷电防护

雷电是一种危险现象,但是到目前为止还没有一种技术能够防止飞机遭受雷击。本文分析了雷电造成的危害,并论述了飞机结构设计应该为雷电流提供低阻抗的通路。对于对雷击放电敏感的部位和部件,必须根据其自身的重要性采取适当的雷电防护措施,以尽可能减少雷电对飞机的损害。最后介绍了为确保雷电防护措施的可靠性而进行的验证试验方法。