高能球磨及热压合成Al_2O_3/Ti_3AlC_2复合材料显微机理分析

以Ti,Al和活性炭粉为主要原料,利用高能球磨及热压烧结工艺在1200℃合成Al2O3/Ti3AlC2复合材料,复合材料是在Ti3AlC2层状材料的制备过程中同时被合成。研究了在Ti-Al-C体系中,烧结温度对反应产物的影响,并重点分析了反应机理及材料微观结构对性能的影响。结果表明:通过高能球磨使的Ti3AlC2的烧结温度降低,在1200℃热压烧结时得到了物相比较均匀的、致密的Al2O3/Ti3AlC2复合材料;通过XRD,DSC和SEM测试,分析了Al2O3/Ti3AlC2复合材料的相组成及显微结构,发现Al2O3以颗粒形式均匀地分布在Ti3AlC2基体中,起到弥散增强的效果,并通过阻碍Ti3AlC2表面微裂纹的扩展使裂纹在断裂扩展过程中中断,起到微裂纹增韧效果,大大提高了复合材料的力学性能。     

NiCrAl/Ni3Al微叠层材料的断裂韧度测算

利用电子束物理气相沉积技术(EB-PVD)制备了NiCrAl/Ni3Al微叠层复合材料.建立了具有中心穿透裂纹有限宽NiCrAl叠层的Ⅰ型裂纹扩展模型,推导出它的断裂韧度表达式,并利用带预制裂纹的NiCrAl/Ni3Al叠层试样的四点弯曲断裂数据,估算出NiCrAl的断裂韧度,叠层后增强Ni3Al单体的断裂抗力.实验结果表明,制备态NiCrAl/Ni3Al微叠层复合材料试样的拉伸断口呈现出裂纹扩展和裂纹瞬断两个区域;随着温度的升高,塑性增加.     

Al_2O_3/TiAl 复合材料的原位合成、结构与性能研究(英文)

以 Ti, Al, TiO2和 Nb2O5混合粉为原料,采用热压反应合成技术制备了 Al2O3/TiAl 复合材料。对复合材料的微观组织与力学性能进行了研究。结果表明:产物由γ-TiAl, α2-Ti3Al, Al2O3和 NbAl3相组成。原位反应形成的细小 Al2O3粒子主要分布在基体晶界处。随着 Nb2O5含量的增加,晶粒明显细化,Al2O3粒子呈弥散分布在基体中。最终形成了由γ和γ α2构成的特殊组织。随着 Nb2O5含量的增大,复合材料的硬度逐渐增大,抗弯强度和断裂韧性在 Nb2O5含量为 6 wt%时达到最大,分别为 398.5 MPa 和 6.99 MPa·m1/2。     

碳化铬／Ni3Al复合材料的高温抗氧化性能

对比研究碳化铬/Ni3Al复合材料和传统高温耐磨材料Stellite 12合金在1000℃时的高温氧化行为.结果表明,Stellite 12合金表面形成以Cr2O3为主的氧化膜,并发生明显剥落;而碳化铬/Ni3Al复合材料表面形成以α-Al2O3为主的致密氧化膜,其空气中的氧化速率仅为Stellite 12合金的1/2,碳化铬具有良好的抗氧化稳定性并与Ni3Al基体有较好的氧化协同性.分析认为,碳化铬在堆焊过程中发生溶解导致部分Cr固溶于Ni3Al合金基体中,促进α-Al2O3的形成,从而改善复合材料的抗氧化性.而材料表面所形成的氧化膜类型是两种材料抗氧化性差异的主要原因.     

Al2O3(YAG)/LaPO4层状陶瓷复合材料研究

选择Al2O3(YAG)作为基体片层材料,LaPO4作为界面层材料,采用凝胶注模成型技术制备出基体层材料的坯片,然后在基体层坯片上采用浸渍或喷涂工艺附着界面层材料,最后将坯片叠置于模具中热压烧结.制备的陶瓷复合材料微观结构均匀,基体片层厚度为110-150μm,界面层厚度为10～30μm,实测层厚比为11.重点研究工艺参数及界面层成分对层状陶瓷复合材料室温性能的影响.结果表明,氧化物基层状陶瓷复合材料的抗弯强度比基体材料略有下降,但室温断裂韧性达到了13.52MPa·m1/2,是基体材料断裂韧性的3倍.对比氧化物基层状陶瓷复合材料与基体材料在断裂过程中裂纹扩展路径的差异.     

PIP工艺制备SiC晶须增强SiCf/SiC复合材料的性能

以不同界面层厚度的SiC纤维为增强相,采用先驱体浸渍裂解工艺(PIP)制备SiC_f(PyC)/SiC复合材料,并在复合材料基体中引入SiC晶须,对其性能进行研究。结果表明:热解碳(PyC)界面层厚度约为230 nm时,SiC纤维拔出明显,SiC_f/SiC复合材料拉伸强度、弯曲强度和断裂韧度分别达到192.3 MPa、446.9 MPa和11.4 MPa?m^1/2;在SiC_f/SiC复合材料基体中引入SiC晶须后,晶须的拔出、桥连及裂纹偏转等增韧机制增加了裂纹在基体中传递时的能量消耗,使复合材料的断裂韧度和弯曲强度分别提高了22.9%和9.1%。     

适合航空航天用SiCp/Al复合材料的性能

采用粉末冶金法制备了Φ300 mm的15%(体积分数)SiCp/A l复合材料坯锭,研究了热挤压、锻造后的材料力学性能以及断裂特点。结果表明,该材料的弹性模量在97 GPa、拉伸强度保持在550 MPa的水平下,延伸率仍高达7%左右,旋转弯曲疲劳强度在250~290 MPa范围内,断裂韧性为25 MPa.m1/2,冲击韧性为62.5 kJ/m2。与棒材挤压态相比,T4态复合材料拉伸强度和屈服强度分别提高66.7%和100%,但塑性保持在同一水平。断口观察表明,挤压态复合材料以基体韧性断裂为主要形式,而T4态复合材料除了基体韧性断裂外,还存在SiC颗粒断裂现象。挤压棒材锻造后有利于提高材料的横向强度。     

连续SiC纤维增强钛基复合材料高温变形研究

采用单轴拉伸的方法测试了Si C纤维增强钛基(Si Cf/Ti)复合材料横向高温变形的应力-应变关系,研究了温度、应变速率对应力-应变关系的影响规律,分析了复合材料的高温变形机制。研究表明,在应变速率为1.0×10-4~5.0×10-3s-1,温度为880~940℃条件下,延伸率为150%~200%。在高温变形过程中,复合材料主要的变形机制是纤维/基体界面剥离和基体的超塑性变形。     

纤维C涂层对SiC_f/Ti6Al4V界面及拉伸性能的影响

通过对SiC纤维增强Ti6Al4V复合材料的拉伸试件断口与界面观察,研究了SiC纤维C涂层对基体与纤维元素扩散、界面反应层厚度与成分、拉伸断口的影响。结果表明,与纤维无C涂层的SiCf/Ti6Al4V相比较,有纤维C涂层的SiCf/Ti6Al4V界面结合强度较弱、反应层厚度较厚,涂层能有效防止纤维性能在复合过程中下降,提高了复合材料拉伸强度。     

Ho_2O_3掺杂对原位合成HoAl-Al_2O_3/TiAl复合材料显微组织及性能的影响

采用固态置换反应原位合成工艺,利用Al—Ti—TiO2-Ho2O3体系的放热反应合成了HoAl-Al2O3／TiAl复合材料。利用XRD和SEM分析了Ho2O3掺：枭对原位合成HoAl,Al2O3颗粒强化钛铝基复合材料显微组织的影响,探讨了稀土氧化物（Ho2O3）的细化机制。测试了力学性能。结果表明：Al—Ti—TiO2-Ho2O3系原位合成的HoAl-Al2O3／TiAl复合材料由TiAl,Ti3Al,Al2O3以及HoAl相组成;HoAl金属间化合物弥散分布于基体晶粒和Al2O3颗粒交界处,限制颗粒长大,细化基体晶粒与Al2O3,颗粒,同时提高了HoAl,Al2O3颗粒在基体中的分散度;Ho2O3的引入改善了复合材料的力学性能。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。     

Research on Auto-detection for Remainder Particles of Aerospace Relay Based on Wavelet Analysis

Aerospace relay is one kind of electronic components which is used widely in national defense system and aerospace system. The existence of remainder particles induces the reliability declining, which has become a severe problem in the development of aerospace relay. Traditional particle impact noise detection (PIND) method for remainder detection is ineffective for small particles, due to its low precision and involvement of subjective factors. An auto-detection method for PIND output signals is proposed in this paper, which is based on direct wavelet de-noising (DWD), cross-correlation analysis (CCA) and homo-filtering (HF), the method enhances the affectiv-ity of PIND test about the small particles. In the end, some practical PIND output signals are analysed, and the validity of this new method is proved.