一种弹性低密度耐高温隔热涂层

针对固体火箭发动机实际使用的热环境要求,研制了一种弹性低密度耐高温隔热涂层,通过石英 灯辐射和电弧风洞试验对其进行了防热性能考核。该涂层密度为0. 62 g/ cm3,伸长率为25%,热导率为0． 18 W/ (m·K);在401℃时DSC 失重率仅为6. 6%;验证考核表明,采用1. 0 mm 涂层时,壳体与涂层界面温度最高 为77. 3℃,壳体背温度最高为44. 5℃。     

二维C/C复合材料高温力学、热物理性能研究

研究了二维C/C(2D -C/C)复合材料在高温下层剪强度、弯曲强度和模量、热导率和线膨胀系数的变化规律。结果表明 ,所制得的 2D -C/C复合材料的层剪强度随温度的升高变化不大、弯曲强度随测试温度的升高而增加 ;2 0 0 0℃的层剪强度、弯曲强度分别达到 1 4 .8MPa和 2 2 7.4MPa ,较室温分别提高了9.6 %和 6 0 %。弯曲模量在 1 0 0 0℃时增加到 39.4GPa ,在 2 0 0 0℃则下降 ,低于室温数值。 2D -C/C复合材料的热导率、线膨胀系数在z向和x -y向都具有明显的各向异性。未石墨化 2D -C/C复合材料 2 0 0℃的z向热导率是 4 .4 1W / (m·K) ,且随温度的升高而增加 ;而石墨化 2D -C/C复合材料 2 0 0℃的z向、x -y向热导率分别是 1 8.0 2W / (m·K)和 73.2 9W / (m·K) ,随温度的升高而下降。 2D -C/C复合材料在z向的线膨胀系数较大 ,80 0℃以内在 8× 1 0 - 6 /K～ 1 0× 1 0 - 6 /K之间 ;而在x -y向线膨胀系数在 80 0℃以内都很小 ,基本上接近于零     

一种耐高焓低热流环境隔热材料

采用模压工艺将耐高温阻燃硅橡胶和隔热填料RMX 压制成胶结片材,其密度为0. 56 g/ cm3,比 热容为1. 371 J/ (g·K),热导率为80 mW/ (m·K),拉伸强度为1. 87 MPa,断裂伸长率为25%。在高焓低热流 风洞考核环境下,厚度为1 mm 隔热材料试件界面平均温度为70. 7℃,试片表观完整、无龟裂。     

C/ C 复合材料SiC/ SiO2 涂层的制备及其抗氧化性能

为提高C/C复合材料的抗氧化性能,采用包埋法和低压化学气相法制备了SiC/SiO2涂层.借助XRD、SEM和EDS等测试手段分析了复合涂层的微观结构,并研究了其在l273、1773 K静态空气中的抗氧化性能.结果表明,包埋法制备的SiC涂层具有一定的浓度梯度.低压化学气相法制备的非晶Si02外涂层则有效地封堵了SiC内涂层的的裂纹和孔洞,并解决了SiC涂层在中温区(1073～1473 K)无法形成完整SiO2膜的问题.在l 273、1 773 K静态空气中经10h氧化后,涂层试样的质量损失率分别仅有4.97和0.36 mg/cm2,表现出良好的抗氧化性能.     

双陶瓷层热障涂层3.5％Y2O3-La2(Zr0.7Ce0.3)2O7/YSZ研究

采用EB-PVD沉积了3.5％Y2O3-La2(Zr0.7Ce0.3)2O7(3.5Y-LZ7C3)/YSZ双陶瓷热障涂层,分析了涂层的成分、相结构、组织形貌和热循环氧化性能.研究表明:La2(Zr0.7Ce0.3)2O7(LZ7C3)材料中掺杂Y2O3能有效地降低涂层中La2O3/ZrO2/CeO2的成分偏差;双陶瓷涂层在1050℃下氧化增重动力学为M=0.1219t1/3,相比抛物线型YSZ涂层的氧化增重曲线,较大减缓了氧化速度;沉积态双陶瓷涂层表面结构(即3.5Y-LZ7C3涂层结构)为烧绿石结构,经过热循环后逐渐分解,出现了萤石结构以及La2O3的衍射峰;在1050℃双陶瓷层热循环氧化寿命达768h.     

温度对溶剂热改性C/C复合材料显微结构和氧化性能的影响

以硼酸三正丁酯、乙酸、B2O3粉体为原料,无水乙醇为溶剂,采用一种新颖的溶胶/凝胶结合溶剂热法对C/C复合材料基体进行了抗氧化改性.采用X射线衍射仪(XRD)、扫描电子显微镜(SEM)、能量色散谱仪(EDS)及X射线光电子能谱(XPS)对改性后试样进行了表征.重点研究了溶剂热反应温度对改性后试样的物相组成、微观结构和氧化性能的影响.结果表明:经过溶剂热改性处理后,C/C复合材料表面缺陷被玻璃相B2O3组成的涂层所覆盖,材料内部一部分孔隙也被B2O3相填充,且随着溶剂热温度的上升,试样表面的微裂纹逐渐消失,B2O3涂层的致密度上升;C/C基体的抗氧化性能随着溶剂热改性温度(范围353～433 K)的升高而提高;经433 K溶剂热改性后的C/C复合材料在873 K的空气中氧化16 h后的质量损失仅为4.09％.     

Si-Zr-B涂层结构稳定性及对DD3单晶高温合金深过冷的非催化形核惰性

以 Si O2 玻璃粉、分析纯 Zr O2 粉为粉料,分析纯 C2 H5OH,Zr OCl2 · 8H2 O,去离子 H2 O与分析纯Si(OC2 H5) 4按 4∶ 0.1 1∶ 3∶ 1的摩尔比配制的前驱液经 3 5℃,1 80 min水解 -聚合反应后形成的 Si O2 -Zr O2溶胶为粘结剂,H3 BO3 为软化剂,用熔模制壳技术在壳型内壁制备了 Si-Zr-B基底涂层。利用溶胶 -凝胶原理,以 Si O2 -Zr O2 溶胶中加入 H3 BO3 形成的 Si O2 -Zr O2 -B2 O3 溶胶为原料,经浸涂 -分级热处理和 80 0℃玻璃化热处理后,在基底涂层表面制备了适宜厚度的同成分玻璃薄膜涂层。将涂层在 1 5 0 0℃保温 3 0 min后,XRD结果表明,涂层的析晶量仅为 1 %～ 3 %,具有很高的高温结构稳定性。过冷实验表明,DD3单晶高温合金可在该 Si-Zr-B涂层壳型内获得最大 1 4 0 K过冷度,完全可以实现深过冷快速凝固,证明 Si-Zr-B涂层具有良好的非催化形核惰性。     

激光重熔WC复合陶瓷涂层组织及耐腐蚀性能

在45号钢表面,制备了WC/Co-NiCrAl等离子喷涂涂层(TC-1)和WC/Co-NiCrAl/laser-remelting激光直接重熔等离子喷涂陶瓷涂层(TC-2)。以纳米SiC粉末为填料,对等离子喷涂层TC-1进行了填料下的激光重熔,制备了纳米SiC改性的WC/Co-NiCrAl/nano-SiC复合陶瓷涂层(TC-3)。采用X射线衍射、扫描电镜对三种涂层微观组织进行了分析,同时对陶瓷涂层的耐腐蚀性能进行了研究。结果表明,TC-1涂层由WC,W2C,W6C2.54,W,Co,CoO组成;TC-2重熔涂层由WC,W2C,CoO及W组成;纳米改性后的重熔涂层TC-3由SiC,Si2W,WC,W及CoO组成。在激光作用下,原等离子喷涂层WC/Co的片层状组织得以消除。与TC-1涂层相比,TC-2及TC-3陶瓷涂层致密化程度明显提高,涂层耐腐蚀性能也得到了明显的改善。     

电弧离子镀Al扩散障结构及抗高温氧化性能研究

采用电弧离子镀技术(AIP)在HY3(NiCrAlYSi)涂层与镍基高温合金(K5合金)之间沉积一层Al薄膜经过马弗炉870℃加热1h形成Al2O3作为扩散障层,研究了Al2O3对HY3(NiCrAlYSi)涂层与基体的元素互扩散的阻碍作用和对涂层氧化动力曲线的影响。对于添加扩散障层前后的试样,进行循环抗氧化试验来评价其抗高温氧化性能,并用扫描电镜(SEM)分析氧化前后试样微观形貌和成分,用X-射线衍射仪分析涂层的相结构。试验结果表明:Al2O3有效阻止基体与涂层之间的元素互扩散,提高了HY3(NiCrAlYSi)涂层和K5合金的抗高温氧化性能。     

HGB 含量对SiO2 / PF 复合材料性能的影响

采用模压成型复合材料层压板工艺,制备了HGB 质量分数分别为0、3%、5%、10%的SiO2 / PF 复 合材料,研究了HGB 含量对其密度、热物理、烧蚀及力学性能的影响规律。结果表明,HGB 加入可降低SiO2 / PF 密度,提高耐热、耐烧蚀及其力学性能。当HGB 含量为5wt% 时,体系密度为1. 634 g/ cm3;23℃ 时cp 从 1． 062 提高到1. 137 J/ ( g·K),950℃ 时,质量保留率为82. 08%;线烧蚀率和质量烧蚀率分别为91 μm/ s 和 66． 9 μg/ s,降低了35. 9% 和20. 1%;拉伸、弯曲和剪切强度分别提高了12. 86%、21. 50%和7. 80%。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。     

Research on Auto-detection for Remainder Particles of Aerospace Relay Based on Wavelet Analysis

Aerospace relay is one kind of electronic components which is used widely in national defense system and aerospace system. The existence of remainder particles induces the reliability declining, which has become a severe problem in the development of aerospace relay. Traditional particle impact noise detection (PIND) method for remainder detection is ineffective for small particles, due to its low precision and involvement of subjective factors. An auto-detection method for PIND output signals is proposed in this paper, which is based on direct wavelet de-noising (DWD), cross-correlation analysis (CCA) and homo-filtering (HF), the method enhances the affectiv-ity of PIND test about the small particles. In the end, some practical PIND output signals are analysed, and the validity of this new method is proved.