1.
2.
GH4169合金疲劳裂纹扩展性能的试验研究 总被引:1,自引:0,他引:1
本研究中对GH4169高温合金的疲劳裂纹扩展性能进行了试验研究。主要进行了400℃~600℃范围内的疲劳裂纹扩展试验.其中对GH4169环形锻件进行了室温下的疲劳裂纹扩展试验。结果表明,在400℃-600℃范围内,温度对GH4169高温合金疲劳裂纹扩展性能的影响很小,随温度上升,裂纹扩展速率稍有加快;优质成分对GH4169高温合金的疲劳裂纹扩展性能几乎没有影响,在相同温度下,YZGH4169与GH4169的疲劳裂纹扩展速率几乎一样;材料品种对YSGH4169高温合金的疲劳裂纹扩展性能有一定影响,YSGH4169锻件比棒材的疲劳裂纹扩展性能要好一些。 相似文献
3.
通过添加稀土元素Ce对0.2mm厚的GH4169高温合金进行微激光对接焊接,利用光学显微镜、扫描电镜、电子精密拉伸仪测试等分析方法,对比研究稀土元素对焊缝表面成形、接头显微组织及力学性能的影响。结果表明:在添加稀土元素的条件下焊接时,对焊接工艺参数进行正交试验优化,得出焊接最优工艺参数为脉冲功率17%、脉冲频率4.0Hz、脉冲宽度3.1 ms,此时焊接接头断裂在母材。焊接过程中,液态金属流动使稀土在熔池中均匀混合,获得了组织均匀的焊缝。稀土元素能够改变焊缝温度梯度,形成“梯形”状焊缝;同时,稀土元素能够降低接头的显微硬度,增强接头的韧性和塑性。 相似文献
4.
《航空材料学报》2015,(5)
对GH536合金焊接接头的硬度进行测试和分析,对母材及焊接接头进行室温和500℃拉伸试验,并分析了断裂特征,分析了母材和焊接接头不同区域的断裂韧度。结果表明:热影响区硬度未见明显变化,与母材一致;从熔合线到焊缝中心,由于枝晶变细,显微硬度逐渐升高。焊接接头整体室温拉伸强度、屈服强度和断后伸长率分别为810MPa,392MPa和30%,达到了母材的99.6%,99.7%和93.8%;在500℃时,接头整体抗拉强度、屈服强度和断后伸长率分别为678MPa,300MPa和26%,达到了母材的98.1%,96.8%和78.8%;GH536合金焊接接头具有良好的力学性能。在熔合区组织不均匀性最为严重,熔合区是GH536合金焊接接头的薄弱环节。在室温和500℃,母材及焊接接头的断裂方式均为塑性断裂。 相似文献
5.
6.
对GH2132材料对接焊接头进行了两种不同温度(360℃和410℃)下的静载拉伸试验和疲劳试验。静载拉伸试验结果表明.应变速率对GH2132对接焊接头的断裂载荷影响不大。由疲劳试验结果得到了两种温度下的S-N曲线,利用该曲线和有限元分析预测了某GH2132材料对接焊构件焊接接头处的疲劳寿命,结果表明所得寿命满足此构件的设计要求。 相似文献
7.
为了发展航空用先进的柔性密封技术,采用电子束焊接对GH4169+Haynes214刷丝进行了刷式密封结构的研制,研究了不同的焊接工艺对焊缝成形规律的影响,焊接接头的组织特征、显微硬度及密封性能。结果表明,采用电子束焊接技术能够获得成形良好、无裂纹和气孔的焊接接头。焊缝组织为横向短枝晶、长主轴的树枝状晶,主要是由γ相、γ’相及γ’’相(Ni3Nb)构成,在横向枝晶间形成共晶组织(γ+Laves)。熔合线区的碳化物在热循环下发生了长大,在晶界上团聚。焊接接头的显微硬度呈近似对称分布,焊缝区域的平均硬度约435HV,小于GH4169母材(约540HV),由于焊缝区域主要为Haynes214,其Ni和Al的含量高,在焊缝凝固时Haynes214与GH4169的合金元素发生了混合,凝固后的焊缝组织差异引起显微硬度变化。刷式密封结构常温(20℃)和高温(403℃)的泄漏率均小于20 g/s。常温(20℃)下泄漏系数稳定在0.006附近,小于预期泄漏系数0.007,当加温到403℃条件时,随着压力升高泄漏系数逐渐升高,最终稳定在0.004左右,表明刷式密封结构具有优越的密封性能,可在航空航天发动机上... 相似文献
8.
对GH2132材料对接焊接头进行了两种不同温度(360℃和410℃)下的静载拉伸试验和疲劳试验。静载拉伸试验结果表明,应变速率对GH2132对接焊接头的断裂载荷影响不大。由疲劳试验结果得到了两种温度下的S—N曲线,利用该曲线和有限元分析预测了某GH2132材料对接焊构件焊接接头处的疲劳寿命,结果表明所得寿命满足此构件的设计要求。 相似文献
9.
进行了固溶强化型镍基高温合金GH3044线性摩擦焊接试验,光镜与扫描电镜组织观察、EDS成分分析及拉伸测试表明,接头中焊缝与热力影响区晶粒明显细化,碳化物分布发生改变使焊缝与热力影响区均可见明显流线,但未对接头拉伸强度造成影响,接头拉伸强度与母材相当。EBSD分析表明,接头主要发生了不连续动态再结晶,并伴随部分连续动态再结晶及静态再结晶,使焊缝与热力影响区中小角度晶界比例大幅增高,孪晶界大幅减少。热力影响区中小角度晶界比例更高,是因为该区形成较强织构而焊缝区再结晶更为充分。 相似文献
10.
采用氩弧焊焊接工艺对GH4169合金导管进行焊接,并对接头的宏观形貌进行观察,接头质量进行X光检测。焊接前在导管焊接处20mm范围内进行打磨,并对接头端头进行刮削处理。采用优化的定位焊工艺参数及优化的焊接工艺参数进行焊接,焊接后GH4169导管接头焊接质量良好,无焊接缺陷。 相似文献
11.
针对某燃气涡轮发动机发生的GH4169合金螺栓断裂故障,通过对故障螺栓进行断口宏微观观察、化学成分分析、硬度检测和金相组织分析,以及对未发生断裂失效的螺栓和螺母进行检查与分析,确定了该燃气涡轮发动机螺栓断裂性质为镉脆断裂;与螺母表面的镀镉层紧密接触、受到拉应力的作用以及工作温度较高,是导致螺栓发生镉脆断裂的主要原因。为此,提出了在涡轮后机匣连接部位选用GH4169合金螺母,并在发动机热端零部件连接件中避免使用镀镉层进行表面防护等建议,可供排除类似故障时借鉴。 相似文献
12.
13.
14.
15.
GH4169 alloy is one of the most commonly used materials in aero engine turbine blades, but its machinability is poor because of its excellent strength at high temperatures. Electrochemical machining (ECM) has become a common method for machining this alloy and other difficult-to-machine materials. Electrochemical grinding (ECG) is a hybrid process combining ECM and conventional grinding. In this paper, investigations conducted on inner-jet ECG of GH4169 alloy are described. Two types of inner-jet ECG grinding wheels were used to machine a flat bottom surface. The machining process was simulated using COMSOL software, and machining gaps under different machining parameters were obtained. In addition, maximum feed rates and maximum material removal rates under different machining parameters were studied experimentally. The maximum sizes and the uniformity of the distributions of the gaps machined by the two grinding wheels were compared. The effects of different applied voltages on the machining results were also investigated. 相似文献
16.
基于高应变率下GH4169高温合金的本构关系是采用有限元法对GH4169高温合金进行切削加工数值分析研究的基础。本文针对GH4169高温合金,通过试验对其在温度为室温至1 000 ℃、应变率为2 000~10 000 s-1的范围内的本构关系进行了研究。研究发现高应变率下GH4169高温合金的流动应力与塑性应变关系接近线性关系,同时温度影响着高应变率下应变率对本构关系的影响程度及方式。根据GH4169合金流动应力曲线的特点,对Johnson-Cook本构模型进行修正。基于试验结果,通过数据拟合确定了对应高应变率GH4169高温合金的材料常数,建立了描述GH4169高温合金高应变率下的本构模型,为切削加工有限元数值分析提供了理论基础,并为相关类似研究提供了思路。 相似文献
17.
针对典型盘用镍基高温合金GH4169,采用Bai-Wierzbizki(B-W)塑性理论对其塑性变形行为进行建模和应用评估。B-W塑性理论假设金属材料塑性变形仍服从von Mises屈服准则,但屈服函数考虑了静水压力和LODE角(偏应力第3不变量)对塑性行为的影响。采用Abaqus/Explicit商业有限元软件编制了该塑性模型的用户材料子程序,设计开展了GH4169合金的光滑、缺口圆棒和缺口平板拉伸试验,基于有限元分析和优化方法确定了B-W模型相关材料参数,对GH4169合金光滑和缺口拉伸响应曲线进行有限元预测,并与试验结果进行对比分析。结果表明:B-W模型预测的GH4169合金缺口圆棒和平板拉伸响应曲线与试验结果非常吻合,而基于传统von Mises塑性模型预测的GH4169合金缺口拉伸响应曲线均明显高于试验曲线。 相似文献
18.
对GH4169合金进行了固溶温度为1 233,1 253,1 273,1 293 K,保温时间为30~60 min的固溶处理试验,得到了GH4169合金中δ相形貌由针状向短棒状和颗粒状转变,数量逐渐减少直至消失的演变规律。将固溶处理后的GH4169合金通过热模拟压缩实验,研究变形工艺参数和固溶处理对GH4169合金高温变形行为的影响。热模拟压缩实验时选取的变形温度为1 123~1 288 K,应变速率为0.1~10.0 s-1,变形程度为60%。结果表明:流动应力随变形温度的降低和应变速率的提高而迅速增大,δ相不仅使流动应力降低,而且对动态再结晶过程产生强烈的促进作用;利用多元回归分析方法建立的流动应力模型的计算值与实验值的误差小于10%,较好地描述了固溶处理GH4169合金在高温变形过程中的塑性流动行为。 相似文献
19.
现代航空发动机轮盘工况复杂,常常在榫槽、通气孔、螺栓孔等几何不连续处遭受破坏。这些几何不连续性特征可以视为广义的缺口,为了分析缺口附近几何特征尺寸对航空发动机轮盘复杂结构件抗拉强度的影响规律,基于典型盘用合金GH4169设计了双边缺口平板试样、双边不等缺口平板试样、不等厚双边缺口平板试样以及不等厚双边不等缺口平板试样进行试验研究。试验结果表明:缺口平板试样的应力集中系数与缺口抗拉强度存在一定的相关性,缺口抗拉强度无量纲化常数与应力集中系数的试验数据点存在一定的分布规律,二者的拟合曲线能很好地描述试验结果分布规律。包括GH4169、GH738和TC11合金等常用航空塑性金属材料在内的缺口平板试验数据点落在拟合曲线±10%以内的分散带内。 相似文献
20.
为了使总应变寿命方程能够在较大寿命范围内具有理想的预测精度且其参数物理意义明确,基于总应变寿命方程中疲劳强度系数与疲劳延性系数的物理意义,建立了总应变寿命方程参数与单调拉伸强度极限和断面收缩率之间的关系,并结合TC4,GH4169及GH901合金的单调拉伸及疲劳试验数据,对其各自的总应变寿命方程参数进行了拟合,进而开展了疲劳寿命预测.结果表明:采用该方法确定的总应变寿命方程参数具有明确的物理意义,且对TC4,GH4169及GH901合金的疲劳寿命预测结果较为理想,其分散带基本在2倍以内. 相似文献