多处损伤平板的剩余强度研究

进行了多处损伤平板的剩余强度试验,用净截面屈服准则、塑性区连通准则和修正的断裂韧性准则分别计算了MSD平板的剩余强度,并把预测结果与试验进行了对比。结果表明对不同的主裂纹长度和不同的韧带长度,净截面屈服准则预测结果的误差较大,而且偏危险;塑性区连通准则对较长的韧带预测结果的误差较小,而修正的断裂韧性准则对较短的韧带预测的误差较小。研究了不同的主裂纹长度对平板剩余强度的影响,主裂纹长度的增加使平板的剩余强度减小。     

改进的确定多处损伤平板剩余强度的连通模型

为了评估多处损伤（MSD）对未加筋平板剩余强度的影响,进行了多处损伤平板的剩余强度试验研究。用钼丝切割预制疲劳裂纹,每个试验件承受拉伸载荷直到破坏,记录破坏载荷,得到不同裂纹几何平板的剩余强度。试验结果表明主裂纹长度增加使平板的剩余强度减小;对相同的主裂纹长度,主裂纹与相邻MSD裂纹之间的韧带（b）减小,试验件剩余强度也减小。以试验数据为基础,提出了一种改进的塑性区连通模型。用塑性区连通准则和改进的塑性区连通模型分别计算了多处损伤平板的剩余强度,结果表明对不同的主裂纹长度和不同的韧带长度,塑性区连通准则预测的平均误差为23．39％;而改进的塑性区连通准则的平均误差为7．57％,大大提高了预测结果的精度。还研究了主裂纹长度和b对剩余强度的影响。     

多位损伤铝合金平板剩余强度分析

针对飞机铝合金结构出现的多位损伤(MSD)问题,本文开展了含多位损伤铝合金平板试样的剩余强度试验研究.采用工程常用的8种不同剩余强度准则对MSD试样的剩余强度进行预测,并与试验结果进行对比,以评价各项预测准则的准确性.研究显示,对于本试验选用的材料和试样形式,Swift准则和平均应力准则相比其他准则取得了较好的预测效果...     

含多处损伤结构的剩余强度研究

系统地回顾了含多处损伤MSD结构的损伤连通准则,指出采用Dugdale的片状塑性区尺寸的Swift韧带屈服准则对一般工程材料最为合适.对具有潜在危险性的典型的广泛MSD结构作了剩余强度分析,分析结果表明:广泛MSD大大地降低了结构的剩余强度.     

多处损伤特性的研究

对老龄飞机结构中存在的多处损伤 ( MSD)进行了研究。从 MSD试件的裂纹扩展实验中得出 :MSD服从净截面屈服破坏准则 ;MSD使剩余强度明显降低,临界裂纹尺寸大大减小,裂纹扩展寿命显著缩短,从而使损伤容限能力减退,破损安全不复存在。试用组合法求解 MSD裂纹的应力强度因子,并将其用于 MSD裂纹的扩展分析,所得裂纹扩展寿命计算结果与实验符合良好     

含MSD铝合金平板的剩余强度试验研究

针对飞机结构中日趋显著的多部位损伤(MSD)问题,进行含多部位损伤铝合金平板结构剩余强度的试验研究.试验中使用三种不同的试验件,将其在相同应力水平下预制出一定长度的多条裂纹后拉断,记录断裂时的载荷.试验结果与常用的五种评估含多裂纹结构失效准则进行计算分析和对比,了解各个准则的准确程度.最后的对比表明,五种估算剩余强度的方法中,净截面失效和裂纹尖端张开位移法误差较大,断裂力学估算方法对于有显著主裂纹的情况更适用,塑性区连通和平均应力准则预测的偏差较小.     

含离散源损伤的复合材料壁板的剩余强度评估

为研究含离散源损伤的碳纤维增强树脂基复合材料曲面帽形加筋壁板在内压-轴压联合载荷下的剩余强度,对7长桁4框的复合材料曲面帽形加筋壁板进行了试验和分析。结果表明,与离散源损伤距离超过1个典型长桁间距壁板的蒙皮和长桁在轴压载荷作用下轴向应变分布较均匀;加载过程中,损伤区附近应力重新分配,降低了应力集中,离散源损伤可简化为圆孔;基于FD判据和经典层压板理论的计算方法能较准确的计算出含离散源损伤的曲面帽形加筋壁板在内压-轴压联合载荷下的剩余强度;并针对复合材料曲面帽形加筋壁板的结构特点、应变分布特征及破坏模式提出一种在内压-轴压联合载荷下轴向剩余强度的工程估算方法;计算结果均与试验结果吻合较好。     

含分层损伤碳纤维复合材料剩余强度等效评估原则

针对复合材料层合结构在制造及使用过程中形成的小范围分层损伤,对含不同形状、位置、大小的分层损伤层合板的压缩渐进失效过程进行模拟,研究了分层损伤特征参数对剩余强度的影响。根据分析结果有针对性地对预置分层试验件进行设计,与模拟结果相互修正,同时探讨了分层损伤特征参数对剩余强度的敏感性。结果表明:分层面积是影响结构剩余强度的最主要因素;对于损伤尺寸占比较小的分层缺陷,分层的形状、位置、方向及分层位置上下铺层角度对剩余强度影响不大。最后提出了含分层损伤层合板损伤等效评估原则。     

含多处损伤搭接结构应力强度因子有限元分析

 采用铆钉的两种表现形式（详细杆元和简化的弹簧元）的组合方式建立了含多处损伤(MSD)多铆钉搭接结构的有限元模型,通过分析得到了不同损伤模式下的应力强度因子(SIF)随裂纹扩展历程变化规律的曲线。结果表明,相对于单裂纹和无腐蚀情况,MSD和腐蚀损伤都会增加SIF值,当裂纹间距大于孔间距一半时,可不考虑裂纹间干涉效应;在给定的循环应力幅下,应力强度因子幅随干涉量的增加而降低,但干涉量大到一定值时,SIF对其不再敏感;铆钉材料对SIF的影响很小,而铆钉直径增大20%,SIF约增加6%。反平面翘曲对SIF有很大的影响,相对于无反平面翘曲,SIF下降一个数量级。     

Residual Strength of Stiffened LY12CZ Aluminum Alloy Panels with Widespread Fatigue Damage

Experimental and analytical investigations on the residual strength of the stiffened LY12CZ aluminum alloy panels with widespread fatigue damage （WFD） are conducted. Nine stiffened LY12CZ aluminum alloy panels with three different types of damage are tested for residual strength. Each specimen is pre-cracked at rivet holes by saw cuts and subjected to a monotonically increasing tensile load until failure is occurred and the failure load is recorded. The stress intensity factors at the tips of the lead crack and the adjacent WFD cracks of the stiffened aluminum alloy panels are calculated by compounding approach and finite element method （FEM） respectively. The residual strength of the stiffened panels with WFD is evaluated by the engineering method with plastic zone linkup criterion and the FEM with apparent fracture toughness criterion respectively. The predicted residual strength agrees well with the experiment results. It indicates that in engineering practice these methods can be used for residual strength evaluation with the acceptable accuracy. It can be seen from this research that WFD can significantly reduce the residual strength and the critical crack length of the stiffened panels with WFD. The effect of WFD crack length on residual strength is also studied.     

铝合金结构腐蚀疲劳裂纹扩展与剩余强度研究

 在3.5%NaCl腐蚀溶液环境下对含中心孔LY12 CZ铝合金紧固件的疲劳裂纹扩展进行了试验研究,得到3种不同频率下紧固件的腐蚀疲劳裂纹扩展曲线。试验结果说明,随着频率的增加,腐蚀疲劳裂纹扩展速率逐渐降低,腐蚀溶液中疲劳裂纹扩展速率比在空气中大。以试验数据为基础,结合裂纹扩展分析软件AFGROW,提出一种可以用数值方法模拟腐蚀疲劳裂纹扩展的方法,模拟结果和试验结果符合较好。对紧固孔试验件利用2种失效模式进行了剩余强度分析,得到腐蚀环境下紧固孔结构的剩余强度曲线。     

多裂纹结构中的多部位／多元件相互影响因子

多裂纹损伤严重影响飞机连接结构的损伤容限能力,针对多裂纹损伤结构引入了多部位相互影响因子（MSIF）和多元件相互影响因子（MEIF）的概念,以此来反映裂纹之间的相互影响,并给出了获得这两个影响因子的有限元计算过程。对典型的含多裂纹结构进行了模拟计算,获得了不同开裂状态下各裂纹尖端处的多部位相互影响因子和多元件相互影响因...     

广布损伤的试验研究与有限元分析

 通过对无钉载3排平行孔平板和无钉载3排交错孔平板从无裂纹开始的疲劳试验,发现应力大小对是否出现广布损伤(MSD)有重要影响,首裂孔和断裂排位不总是一一对应。在试验中观察到了MSD的竞争现象,证实了群发小裂纹也是MSD中一种重要的破坏形式。采用FRANC2D/L建立了对生裂纹、非对生裂纹和单裂纹3种开裂模式的有限元模型。计算结果表明:短裂纹扩展过程中,裂纹间干涉效应不明显,3种模式的应力强度因子增长趋势相近;而对于长裂纹,试验和有限元计算都证明了裂纹间的干涉显著地加快了裂纹的扩展。     

含分层损伤复合材料层合板压缩剩余强度计算

本文针对含分层损伤复合材料层合板,基于三维复合材料累积损伤分析方法,应用了非线性有限元技术,考虑了子层屈曲对层合板剩余强度的影响,提出了一种含初始分层损伤的复合材料层合板压缩剩余强度计算方法。在ANSYS软件平台上利用APDL语言编写相应的计算程序,对五块含不同初始分层损伤的复合材料层合板进行了压缩剩余强度计算和结果分析,计算结果与试验结果相比较,吻合良好。     

含分层损伤的复合材料层压板轴压剩余强度分析

基于渐进损伤分析方法对含正方形分层损伤的复合材料层压板开展了剩余强度仿真分析。不同损伤尺寸大小的仿真结果表明,层压板的轴压剩余强度和失效机理与分层损伤尺度密切相关,分层损伤尺寸较小时,层压板剩余强度对损伤尺寸不敏感,降低幅度较小;损伤尺寸大于某一临界值后,层压板剩余强度较完好结构件大幅度下降,并趋于稳定;中小尺寸分层损伤层压板在屈曲后,其失效模式为结构件中部横向整体直接压溃;大尺寸分层损伤层压板出现子层屈曲诱发的界面损伤并扩展,在复合材料薄板中部压溃前达到最大剩余强度。该仿真结果对复合材料损伤容限设计、修理具有指导意义。     

含冲击损伤复合材料加筋层板压缩剩余强度

将复合材料加筋层板受低速冲击后的损伤区域描述为一个椭圆形弹性核,材料在核区的弹性模量下降由冲击表面的凹坑深度确定。利用含任意椭圆核各向异性板杂交应力有限元来模拟含损伤区域,杆单元来模拟筋条,钉单元模拟铆钉（胶层）和常规8节点等参单元模拟其余无损区域,建立起含低速冲击损伤复合材料加筋层板的力学响应分析方法。利用基于特征曲线概念的点应力判据、最大正应力判据和最大剪应力判据分别预测蒙皮的破坏、筋条的破坏和铆钉（胶层）的破坏,从而预测加筋层板在压缩载荷下的剩余强度,获得了与试验相吻合的结果。最后讨论了损伤尺寸、损伤形态、铺层比例等参数对加筋层板剩余强度的影响。