激光重熔等离子喷涂纳米氧化锆热障涂层组织与性能

采用等离子喷涂纳米氧化锆(ZrO_2-8%Y_2O_3)团聚粉末制备了纳米氧化锆热障涂层,利用连续CO_2激光对其进行重熔处理.以常规热障涂层作为比较对象,研究了纳米氧化锆热障涂层和激光重熔涂层的组织结构、硬度、抗热冲击性能.结果表明:纳米氧化锆热障涂层组织结构为独特的纳米-微米复合结构,主要有柱状晶和未熔融或部分熔融纳米颗粒组成;激光重熔热障涂层的组织结构为表面等轴晶+断面柱状晶.硬度试验和抗热冲击性能试验综合比较结果显示:相对于常规氧化锆热障涂层,纳米氧化锆热障涂层和激光重熔热障涂层拥有更好的性能.因此将纳米技术和激光重熔表面处理技术与等离子喷涂技术结合起来制备热障涂层是提高热障涂层性能的非常有前景的工艺方法.     

热处理对大气等离子喷涂纳米结构YSZ热障涂层晶粒长大的影响

采用大气等离子喷涂制备了纳米结构氧化钇稳定的氧化锆热障涂层。运用SEM ,TEM和XRD等方法研究了涂层和原料粉末的微观结构和相组成。结果表明 ,喷涂过程中平均晶粒大小由4 0nm变为 6 7nm ,涂层主要由亚稳四方相组成。涂层热处理结果显示 ,90 0℃以下晶粒长大速度缓慢 ,然而 1 0 0 0℃以上晶粒长大速度迅速增加 ,而且出现较多的单斜相     

Effect of Thermal Treatment on the Grain Growth of Nanostructured YSZ Thermal Barrier Coating Prepared by Air Plasma Spraying

采用大气等离子喷涂制备了纳米结构氧化钇稳定的氧化锆热障涂层。运用SEM，TEM和XRD等方法研究了涂层和原料粉末的微观结构和相组成。结果表明，喷涂过程中平均晶粒大小由40nm变为67nm，涂层主要由亚稳四方相组成。涂层热处理结果显示，900℃以下晶粒长大速度缓慢，然而1000℃以上晶粒长大速度迅速增加，而且出现较多的单斜相。     

等离子喷涂纳米结构8%Y2O3-ZrO2热障涂层研究

研究了纳米结构8%Y2O3-ZrO2(YSZ)热障涂层(TBCs)的等离子喷涂工艺及其组织性能.使用大颗粒纳米结构8%Y2O3-ZrO2粉末,在一定的等离子热喷涂条件下制备出纳米结构TBCs,然后分别进行1 000℃、1 100℃和1 200℃至室温(约20℃自来水)的热震试验,通过光学金相、扫描电镜、透射电镜等分析手段,对涂层进行了形貌、微观结构分析.结果表明,同传统的微米粉体制备的传统TBCs比较,纳米结构TBCs热震寿命更高.     

等离子喷涂纳米陶瓷热障涂层组织与性能

采用纳米陶瓷粒子团聚体粉末等离子喷涂制备纳米陶瓷热障涂层,研究了纳米陶瓷热障涂层的组织和性能.试验表明,采用纳米结构的陶瓷涂层有利于增加热障涂层的高温使用寿命.     

航空发动机隔热屏等离子喷涂氧化锆热障涂层工艺研究

介绍了在某新型发动机加力燃烧室隔热屏上等离子喷涂氧化锆热障涂层工艺，重点介绍了涂层抗热震性能、抗高温氧化性能及隔热效果。     

长寿命热障涂层的剥落机理及抗剥落结构设计

涂覆于高温合金热端部件表面的热障涂层,具有隔热防护作用,属新一代燃气轮机的关键核心技术。等离子喷涂制备的热障涂层隔热性能好,但长时间高温服役后存在开裂剥落问题,引发基体烧蚀、造成巨大经济损失。因此,发展长寿命热障涂层是该技术领域的重大难题。本文从等离子喷涂热障涂层的独特层状结构特征入手,阐述涂层在高温服役中结构和性能的演变规律,揭示涂层剥落失效机理,总结长寿命热障涂层设计方法。研究表明,等离子喷涂热障涂层呈现以连通2D孔隙为主的层状多孔结构,具有优异的隔热功能和协调应变能力。然而,涂层在高温服役中发生烧结,2D孔隙大量消失,涂层显著刚化,使热障涂层开裂驱动力急剧增加,引发微观裂纹扩展并贯通形成大尺度裂纹,导致涂层最终剥落失效。据此,分别从降低开裂驱动力和增加开裂阻力两方面着手,总结抗开裂新结构涂层设计方法,为研发长寿命热障涂层指明了发展方向。在未来研究中,如何保证涂层高隔热和长寿命并同时兼顾经济性,是发展新一代高性能热障涂层的重点方向。     

纳米结构热障涂层的制备与性能研究

为充分发掘氧化锆(YSZ:ZrO2-6wt%Y2O3)基热障涂层的潜力,利用纳米级的YSZ粉末作为陶瓷涂层原材料,分别对采用等离子喷涂(APS)和电子束物理气相沉积(EB-PVD)沉积具有纳米结构陶瓷涂层的工艺过程进行全面研究.对比性试验结果表明,涂层中引入纳米结构使热障涂层具有更高的隔热效果,更高的硬度以及更高的抗剥落能力.并对纳米结构陶瓷涂层微观结构的高温稳定性进行研究分析.     

CeO_2含量对Nd_2Ce_xO_(3+2x)热障涂层性能的影响

采用高温固相法合成了Nd2CexO3+2x(x=2.0,2.25,2.5,2.75,3.0)复合氧化物,在高温合金基体上采用等离子喷涂制备了该材料热障涂层.XRD分析结果表明Nd2CexO3+2x粉末和涂层均为立方萤石晶体结构.考察了CeO2含量对Nd2CexO3+2x的力学性能(弹性模量、维氏硬度和断裂韧性)和等离子喷涂涂层在1250℃抗热震性能的影响.随着CeO2含量增加,材料的弹性模量降低,维氏硬度和断裂韧性提高.通过提高初始粉末中CeO2的含量,获得了组成接近化学计量比Nd2Ce2O7的涂层,涂层的抗热震性能增强,热循环次数达到1000次以上.Nd2CexO3+2x涂层的失效原因主要是:与金属基体之间热膨胀系数不匹配、粘结层氧化和涂层烧结.     

基于热喷涂技术制备的热障涂层

着眼于热喷涂技术在热障涂层制备方面的研究现状,在分析热障涂层失效原因的基础上,介绍了等离子喷涂技术及冷喷涂技术和在热障涂层结合层和陶瓷层制备方面的研究进展。     

Effect of Sintering on Thermal Conductivity and Thermal Barrier Effects of Thermal Barrier Coatings

Thermal barrier coatings (TBCs) are mostly applied to hot components of advanced turbine engines to insulate the components from hot gas. The effect of sintering on thermal conductivity and thermal barrier effects of conventional plasma sprayed and nanostructured yttria stabilized zirconia (YSZ) thermal barrier coatings (TBCs) are investigated. Remarkable increase in thermal conductivity occurs to both typical coatings after heat treatment. The change of porosity is just the opposite. The grain size of the nanostructured zirconia coating increases more drastically with annealing time compared to that of the conventional plasma sprayed coating, which indicates that coating sintering makes more contributions to the thermal conductivity of the nanostructured coating than that of the conventional coating. Thermal barrier effect tests using temperature difference technique are performed on both coatings. The thermal barrier effects decrease with the increase of thermal conductivity after heat treatment and the decline seems more drastic in low thermal conductivity range. The decline in thermal barrier effects is about 80 °C for nanostructured coating after 100 h heat treatment, while the conventional coating reduces by less than 60 °C compared to the as-sprayed coating.     

Effects of Shot Peening Process on Thermal Cycling Lifetime of TBCs Prepared by EB-PVD

Conventional two-layered thermal barrier coatings (TBCs) are prepared by electron beam physical vapor deposition (EB-PVD) with ZrO2-8 wt% Y2O3 (8YSZ) as top coat and CoCrAlY as bond coat on disk-shaped Ni based super-alloy. In this paper, three kinds of shot peening process with different lengths of operating time were adopted for bond coating. As a result, changes took place in its sur- face roughness and the surface micro-hardness. A thermal cycling test at 1 273 K×55 min and another at room temperature for 5 min were performed to study the effects of shot peening process on the thermal cycling lifetime of TBCs. It is found that a moderate shot peening process will be able to prolong the life time. The oxidation dynamic of the as-processed TBCs basically accords with the para- bolic rule, and the oxidation test also attests to the spallation between YSZ and thermal growth oxide (TGO) responsible mainly for the failure of TBCs.     

电子束物理气相沉积La2Zr2O7热障涂层研究

为克服传统热障涂层材料YSZ耐温性能和隔热性能的不足,以ZrO2和La2O3为原料,采用无压烧结法合成了烧绿石结构化合物La2Zr2O7,用电子束物理气相沉积(EB-PVD)法在高温合金基体上制备了La2Zr2O7涂层,分析了涂层的成分,并对其显微结构、热物理性能与传统YSZ热障涂层进行了对比研究.结果表明,La2Zr2O7涂层成分处于P结构范围内,呈典型的柱状晶结构,柱状晶头部呈明显的金字塔形状.与传统YSZ柱状晶相比,La2Zr2O7涂层的柱状晶紊乱度更大,尺寸更加细小,并且柱状晶上的树枝状亚晶更多.在25～1200℃范围内,La2Zr2O7涂层的热导率最大为0.985W/(m·K),最小为0.796 W/(m·K),大大低于同条件下的YSZ涂层.低本征热导率、小柱状晶直径、大紊乱度、密度轻及高孔隙率是造成La2.Zr2O7涂层低热导率的主要因素.     

热障涂层残余应力的拉曼光谱测量及数值分析

 为了研究航空发动机热障涂层(TBCs)制备过程中残余应力的分布问题,采用大气等离子喷涂技术(APS)在镍基高温合金GH99上制备了热障涂层(CoCrAlY粘结层和ZrO₂陶瓷面层),对热障涂层进行了100~3 500 cm^-1激光拉曼光谱扫描,并采用有限元方法计算了与之对应的热障涂层有限元模型应力分布.分析了涂层系统内部轴向残余应力的分布情况并对比分析了激光拉曼光谱频移及有限元计算结果.激光拉曼分析结果表明:轴向陶瓷层内部呈现压应力,在陶瓷层/粘结层界面处应力达到最大值14.8 MPa,粘结层内呈现拉应力;数值分析应力变化趋势与激光拉曼测试分析结果相吻合.     

热障涂层的制备及热震性能

采用电火花沉积+微弧氧化的方法在GH4169合金表面制备ZrO_2/NiCrAlY涂层,制备过程为:采用电火花沉积技术在GH4169基体表面先沉积厚度为250μm的NiCrAlY涂层,再沉积厚度为150μm的Zr涂层,最后通过微弧氧化的方法将Zr涂层氧化成ZrO_2涂层,从而得到ZrO_2/NiCrAlY涂层。采用Qauta 200F型场发射扫描电镜观察涂层的显微组织和形貌,研究ZrO_2/NiCrAlY涂层在不同温度下的热震性能,结果表明:当热震温度分别为750℃,850℃,950℃时,热震失效次数分别为51次、32次和19次,涂层的热震性能良好。     

航空发动机热障涂层材料体系的研究

介绍了热障涂层的结构、陶瓷表层材料和中间粘结层的材料发展趋势。热障涂层的结构已由经典的双层结构向成分、结构连续变化的梯度结构发展,涂层的寿命有明显的提高。制备方法中电子束物理气相沉积技术具有明显优势。热障涂层表层材料的最佳成分是(质量百分数6%～8%)Y2O3部分稳定的ZrO2陶瓷材料。粘结层体系发展的一个重要趋势是能同时保证力学性能和抗氧化性能的低Al含量NiCoCrAlY。     

Influence of Gd2O3 and Yb2O3 Co-doping on Phase Stability,Thermo-physical Properties and Sintering of 8YSZ

The role of multicomponent rare earth oxides in phase stability, thermophysical properties and sintering for ZrO2-based thermal barrier coatings (TBCs) materials is investigated. 8YSZ codoped with 3 mol% Gd2O3 and 3 mol% Yb2O3 (GYb-YSZ) powders are synthesized by solid state reaction for 24 h at various temperatures. As temperature increases, stabilizers are dissolved into zirconia matrix gradually. Synthesized at 1 500 °C, GYb-YSZ is basically composed of cubic phase. GYb-YSZ exhibits excellent phase stability and sinters lower than 8YSZ by nearly three times. The thermal conductivity of GYb-YSZ is much lower than that of 8YSZ, and the thermal expansion coefficient of GYb-YSZ is comparable to that of 8YSZ. The influence of Gd2O3 and Yb2O3 co-doping on phase stability, thermal conductivity and sintering of 8YSZ is discussed.     

电子束物理气相沉积YSZ热障涂层热循环性能

考察了YSZ热障涂层的抗热循环性能;分别利用SEM、XRD分析了热循环前后涂层的显微结构和相组成。经分析可知,YSZ热障涂层具有典型的柱状晶结构,沉积态时YSZ涂层为t/t′相,经过600次热循环后,YSZ涂层未发现脱落。     

ZrO2基热障涂层陶瓷材料研究进展

由于ZrO2基陶瓷材料在热障涂层上的广泛应用,本文综述了氧化物(一元、二元、多元)稳定ZrO2、MZrO3化合物及Ln2Zr2O7化合物的研究情况。结果指出氧化物稳定ZrO2在热障涂层上的应用空间已十分有限,随着航空发动机技术的发展,化学式为A32 B24 O7焦绿石结构的陶瓷材料有望替代YSZ,根据声子导热理论和晶体化学原理,用稀土元素离子对A32 B24 O7型陶瓷材料进行掺杂进一步降低其热导率,将为热障涂层技术应用开辟广阔的空间。该机理对MZrO3同样适用。