C/C-B-SiC复合材料的烧蚀性能研究

采用聚合物浸渗裂解法制备了C/C-B-S iC复合材料,用H2-O2焰法对其烧蚀性能进行了研究,并推测了C/C-B-S iC复合材料的烧蚀机理。结果表明,C/C-B-S iC复合材料的烧蚀率随材料密度ρ的增加呈下降趋势,ρ=1.50 g/cm3的C/C-B-S iC复合材料的线烧蚀率相当于ρ=1.86 g/cm3的C/C复合材料的61%,烧蚀时间为60 s时的质量烧蚀率相当于ρ=1.77 g/cm3的C/C复合材料。C/C-B-S iC复合材料在H2-O2焰条件下的烧蚀机制是热化学烧蚀(氧化和升华)和机械冲刷的综合作用。     

C/SiC复合材料热辐射性能研究

利用稳态量热计法和傅里叶红外光谱仪分别测定了C/SiC复合材料在90℃时的半球向总发射率和室温法向光谱反射率.研究了纤维预制体编织方式、涂层厚度及表面形貌对C/SiC复合材料热辐射性能的影响.结果表明,3D C/SiC复合材料的热辐射性能优于2D C/SiC.2D C/SiC的总发射率为0.78,3D C/SiC达到0.82;SiC涂层厚度对C/SiC复合材料的热辐射性能影响很大,随着SiC涂层厚度的增加,C/SiC总发射率先降低后上升,最高值可达0.85;表面抛光后C/SiC复合材料热辐射性能有所下降,2D和3D C/SiC总发射率分别为0.74和0.75.     

固体冲压发动机燃气阀用C/SiC复合材料研究

采用“化学气相渗透法 先驱体浸渍裂解法”(CVI PIP)混合工艺制备了固体冲压发动机燃气阀用3D C/S iC复合材料,并对复合材料的显微结构和力学性能进行了研究。复合材料的密度为2.1 g/cm3,复合材料的室温剪切强度和轴向弯曲强度分别为55 MPa和643 MPa。在断裂过程中,复合材料表现出明显非灾难性的韧性断裂行为,试样断裂面存在大量的拔出纤维。复合材料具有优异的绝热性能,Z向热导率为14.5 W/(m.K),X-Y面内热导率为5.0 W/(m.K)。研制的3D C/S iC复合材料燃气阀成功通过冷气轴向抗冲击试验和发动机高温搭载试验考核。     

氧化硼含量对C/C复合材料SiC涂层结构和抗氧化性能的影响

为了改善涂层和C/C复合材料之间热膨胀系数不匹配的问题,提高涂层在高温下保护C/C复合材料的能力,以氧化硼为添加剂制备了具有楔状结构的C/C复合材料SiC抗氧化涂层,研究了摩尔百分含量分别为0%、2%、5%和10%的氧化硼对SiC涂层组织、结构和抗氧化性能的影响.SEM、XRD及抗氧化实验的测试结果表明,随着氧化硼含量的增加,SiC涂层的厚度和致密度依次增加;涂层中的氧化硼可促使涂层物料充分渗入C/C复合材料基体内;1 500 ℃空气介质氧化试验结果显示,涂层中氧化硼含量为2%的C/C复合材料在氧化5 h后增重0.32%,具有较好的抗氧化性能.     

热解炭涂层对C/C-SiC复合材料性能的影响

采用反应熔渗法(RMI)将不同密度的C/C坯体制备成C/C-SiC复合材料,利用化学气相沉积法(CVD)在C/C-SiC复合材料表面进行炭沉积形成热解炭涂层,选用HS-19A型肖氏硬度计测试其硬度,利用MM1000-II型摩擦磨损实验机测试摩擦性能,研究热解炭涂层对C/C-SiC复合材料孔隙率、硬度及摩擦性能的影响。结果表明:热解炭涂层可以有效地降低孔隙率,提高硬度,减小摩擦系数。     

热处理温度对针刺C/C复合材料热力学性能的影响(英文)

对炭布叠层针刺C/C复合材料分别进行了不同温度的高温热处理,研究了热处理温度对C/C复合材料热学、力学和抗热震等性能的影响。结果表明,经过高温热处理,针刺C/C复合材料的导热率升高,线膨胀系数降低,材料的抗热震因子从未处理的42 kW/m提高到70 kW/m以上,表明热处理后材料具有更佳的热稳定性,但材料的弯曲强度随热处理的升高从126 MPa降到70 MPa,且经过2 000℃及更高温度处理后弯曲强度降低幅度较大。     

C/C复合材料SiC/mullite-Si-Al_2O_3复合涂层微观结构及防氧化性能研究

采用原位生成法在C/C复合材料SiC内涂层表面制备了mullite(莫来石)-Si-Al2 O3抗氧化涂层.采用XRD、SEM分析了涂层的物相组成和微观结构,并测试了SiC/mullite-Si-Al2 O3复合涂层的抗氧化性能.结果表明,外涂层主要由mullite、Si和Al2O3三相组成;涂层致密无裂纹;SiC/mullite-Si-Al2 O3复合涂层在1500℃静态空气中等温氧化75 h后,试样失重仅为4.6%,防氧化性能明显优于单一的SiC内涂层.     

低成本制造C/SiC复合材料的热物理性能研究

采用先驱体浸渍裂解工艺制备了三维针刺C/SiC复合材料,系统地研究了其热物理性能.结果表明:该低成本制造工艺制备的C/SiC复合材料热膨胀系数随温度升高总体上呈增大趋势,但随着温度的升高,热膨胀系数增大程度逐渐减弱,并且z向的热膨胀系数要高于x-y方向,而CVD-SiC涂层的存在会降低其热膨胀性能;C/SiC复合材料比热容、导热率也随着温度的升高呈现逐渐增大的趋势,但增加速率逐渐减小.CVD-SiC涂层的存在会提高C/SiC复合材料的导热性能,有利于C/SiC复合材料产品与外界环境的热能交换,但会使材料的比热容降低.     

界面改性对混杂基C/SiC复合材料性能的影响

通过界面设计与实验研究,对C/SiC材料进行C/SiC/C多层涂层界面处理,实现了保护纤维和提高复合材料韧性及调节机械性能的多重目的.同时还研究了界面涂层前后纤维表面处理对复合材料性能的影响,结果表明,对增强体进行界面涂层处理和"酸处理",适当强化弱界面,起到了提高复合材料高温强度保留率和增韧的目的,酸处理+CVD-C/SiC/C界面涂层的C/SiC 复合材料的高温强度保留率达到90%;进行了C/SiC/C界面涂层的C/SiC 复合材料的断裂韧性高达20.72 MPa·m1/2,较未进行界面涂层的C/SiC 复合材料的断裂韧性提高了31.8%.     

航天用碳纳米管增强铝合金复合材料的力学与阻尼性能

碳纳米管(CNT)作为增强体的铝基复合材料(CNT/Al)具有轻质、高强、高模量、易加工的性能优势,用作轻量化材料在航天航空领域具有巨大的应用前景。为了获得兼顾其力学性能和阻尼性能的轻量化结构材料,采用叠片粉末冶金与合金化方法制备了质量分数为1.5% CNT/2A12复合材料,并研究了不同时效条件下的力学性能与阻尼性能。在130 ℃时效6~14 h时,复合材料具有最佳的拉伸强度与延伸率,抗拉强度最高可达595 MPa(时效12 h),延伸率最高可达14.0%(时效8 h)。复合材料的阻尼在0~180 ℃时变化不大,其在0.005左右,180~300 ℃时明显提高,300 ℃时可达0.05,阻尼性能受时效时间影响不大。复合材料的储存模量随测试温度升高而下降,在180~300 ℃时随振动频率升高而升高。时效条件为130 ℃-8 h时,质量分数1.5% CNT/2A12复合材料性能兼具良好的力学性能与阻尼性能。     

从汉译英的赘冗和疏漏问题看汉英语法特征之差异——汉语语法的柔性之于英语语法的刚性

本文从汉译英的翻译实践出发，从英语译文的错误以及汉英译文对比中，去发现并分析汉语和英语语法特征的差异。论述了英语语法的刚性、显性和汉语语法的柔性、隐性，并从语言对思维的影响的角度，探讨了汉语语言文化的深邃独特和英语语言的缜密精确。     

Antenna for precise orbit determination

The ESA SWARM mission will consist of three satellites that will measure the Earth magnetic field. The system calls for metre accuracy knowledge of the measurement locations. To achieve this a GPS receiver is used. At least four GPS signals are tracked to determine the code and carrier ranges, from which the position can be derived. The accuracy improves when using more GPS satellites and by averaging over many measurements. The latter is achieved in ground processing with a model-based orbit prediction, resulting in cm accuracy. The main error contributions in the processing are often measurement errors due to satellite multi-path effects. The multipath effects are characterized by measuring the antenna on a 1.5 m mock-up, representing the 9 m long satellite. In order to verify that the mock-up is representative, extensive electromagnetic simulations were made. The simulations included the antenna and the complete satellite and were then reduced to the antenna and a section of the satellite. The actual design of the antenna was performed with several levels of software. First, a fast bodies-of-revolution simulation found a geometry with the right coverage. Then, a finite element method simulation allowed us to match the antenna at two frequencies simultaneously.     

浅谈档案室的管理

如何加强档案规范化管理,充分发挥档案在实际工作中的作用,本文从档案的收集、整理、保管、利用和人员的素质五个方面来进行阐述。从而提高人们对档案室管理工作的认识,以确保档案室管理工作的进一步提高。     

一种多标校源的高轨伴星时差频差定位算法

针对高轨伴星时差频差无源定位系统中卫星位置、速度、时差和频差等参数的测量系统误差严重影响定位精度的问题,提出了一种基于四个或四个以上已知位置的地面标校源的高斯-牛顿定位算法。该算法首先利用差分法消除星间时差、频差测量的系统误差,再利用标校源的时差频差测量方程组估计出主星和伴星的相对位置和相对速度误差,最后结合时差、频差、地球球面以确定非合作辐射源位置。理论和数字仿真均表明在时差和频差测量的随机误差较小时,本文算法的均方根误差（MSE）接近克拉美-罗下限(CRLB)。
     

Numerical Simulation of Impact Loading on Solid Propellant Within an Orthotropic Shell

The strain–stress state of the solid propellant rocket engines (SPREs) is simulated under impact. The effect of orientation of elastic and strength properties of orthotropic organoplastic shell material on the strain–stress state of the solid propellant is investigated. Normal and oblique impact of single steel cylinder projectiles, both simultaneous and at different times of multiple, converging steel spheric particles with SPRE are investigated in this study. The investigation is conducted numerically. The numerical modeling was carried out in a three-dimensional formulation by the method of finite elements for the continuous approach of the mechanics of a deformable solid. The destruction of the anisotropic material is described by the tensor-polynomial criterion of the fourth degree, which takes into account the influence of hydrostatic pressure.     

HMX含量对HTPB复合固体推进剂微波衰减的影响

研究了HMX含量对HTPB复合固体推进剂微波衰减的影响。实验结果表明:含HMX的HTPB复合固体推进剂的微波衰减随HMX含量的增加而增加,HMX含量由5%增加到50%时,HTPB复合固体推进剂的微波衰减增加了约1倍。     

测控技术标准体系浅析

在新版《军用标准体系表》中,测控技术标准作为24项共用技术之一被单独列项,为测控技术标准体系建设提供了良好机遇。在扼要介绍新版《测控技术标准体系》的基础上,对新版《测控技术标准体系》的构建思路、技术特点进行了简要分析。     

高超声速跳跃-滑翔弹道方案设计及优化

针时常规弹道导弹突防能力差、成本高的缺点,提出了一种高超声速跣跃-滑翔弹道方案.以某弹道导弹为例,通过采用高升阻比外形和末级发动机多次点火技术,将其再入弹道设计成大气层边缘的跳跃-滑翔弹道,并以航程为目标对弹道进行了优化.结果表明,跳跃-滑翔弹道能大幅增加导弹航程,同时还具有较强的突防能力,而且当跳跃幅度较大时,还可减轻气动加热;优化后导弹的航程进一步增加,跳跃幅度减小,热流峰值减小,加热时间和总气动加热量增加.     

涨落、协同、竞争及启示

运动的破缺产生差异，导致涨落，造成对系统原有方向、轨道的偏离，致使事物发展与进化，由此带来一系列富有生机和活力的启示。作为系统内在机制的协同与竞争，也深深地楔人了我们的生活。     

碳化硅纤维增强铝复合材料疲劳性能及疲劳破坏机理研究

介绍了SiC/Al复合材料单向板和正交板试样的拉—拉疲劳特性和疲劳破坏机理研究结果。研究结果表明,SiC/Al板试样拉—拉循环5×10~4次后,其剩余静拉伸强度系数超过0.87,随着循环应力水平的提高,材料的剩余静拉伸强度几乎没有变化,但声发射信号的起始峰值向应变增大方向移动;疲劳将导致复合材料表面产生温升,通过测量材料表面温度的变化,可以提前预告SiC/Al复合材料的疲劳破坏。