C/ C-Cu 复合材料的烧蚀性能

以聚丙烯腈预氧化纤维针刺毡为预制体,经碳化后采用CVI和树脂浸渍(IR)工艺制备出不同密度的多孔C/C预制件,然后采用气体压力浸渗方法制备了C/C-Cu复合材料.采用氢氧(H2-O2)焰对C/C-Cu的烧蚀性能进行测试考核.结果表明:以密度为0.99 g/cm3的C/C预制件制备出的C/C-Cu复合材料的线烧蚀率和质量烧蚀率均小于密度为1.9 g/cm3的C/C复合材料,其烧蚀性能良好;在烧蚀过程中C/C-Cu的铜基体的熔化吸收了大量的热量,降低了材料的表面温度,提高了材料的抗烧蚀性能;烧蚀机制主要是热氧化烧蚀和机械冲刷的综合作用.     

C/C-Cu复合材料的烧蚀形貌和烧蚀机理

以PAN预氧化纤维整体毡为增强体,经碳化、等温CVI致密化后制备多孔的C/C复合材料预制体,利用气体压力浸渗法将Cu引入C/C预制体中制备C/C-Cu复合材料。采用氢氧(H2-O2)焰考核C/C-Cu复合材料的烧蚀性能,经扫描电镜和电子能谱对不同烧蚀区域的微观结构和成分进行分析,结果表明:预制体密度为0.96 g/cm3的C/C-Cu复合材料的线烧蚀率和质量烧蚀率分别为4.75μm/s、0.223 mg/s,烧蚀性能优良;其烧蚀表面具有不同的宏观形貌,在烧蚀中心区产生了明显的凹坑,主要烧蚀机制为C/C预制体的氧化和铜基体的机械冲刷;烧蚀过渡区聚集了大量的铜基体,其烧蚀机制为Cu的热氧化和机械冲刷;烧蚀边缘区材料表面变黑,主要因为C/C的氧化。为了提高C/C-Cu的烧蚀性能,需要发挥C/C预制体的"钉扎"作用,阻止Cu在高温下被气流冲刷而发生流动。     

C/C-SiC复合材料两种制备工艺及材料性能

以碳纤维整体毡为预制体,采用化学气相渗透法(CVI)制备出低密度碳/碳复合材料,再分别采用液相硅渗透工艺(LSI)制备出密度为2.1g/cm3的碳/碳-碳化硅复合材料(C/C-SiC),及先驱体转化工艺(PIP)制备出密度为1.9g/cm3的C/C-SiC.对2种工艺制备的C/C-SiC力学性能进行了比较,结果表明:PIP工艺制备的C/C-SiC弯曲强度为287MPa,明显高于LSI工艺制备的弯曲强度155MPa.     

2. 5D 衍生结构SiO2 f / SiO2 复合材料的经向力学性能

以几种不同的2.5D衍生结构织物为增强体,制备了法向增强、经向增强及经法向增强2.5D Si O2f/Si O2复合材料,比较了上述材料与现有2.5D Si O2f/Si O2复合材料的经向力学性能,并研究了经法向增强2.5D结构复合材料中增强纱比例、纤维体积分数与材料性能之间的关系,对织物结构进行了优化。结果表明,经法向增强2.5D Si O2f/Si O2复合材料的经向力学性能较现有2.5D复合材料有显著提高,该材料在较低密度下(1.6 g/cm3),经向拉伸强度与现有材料(1.65 g/cm3)持平,且经向压缩强度接近现有材料的4.3倍。     

浸渍工艺对先驱体转化制备Cf/SiC复合材料结构与性能的影响

以聚碳硅烷(PCS)/二乙烯基苯(DVB)为先驱体制备了3D-B Cf/SiC复合材料,研究了不同浸渍工艺对材料力学性能的影响.结果表明采用加热加压浸渍可以大大提高先驱体的浸渍效率,提高所制备材料的密度,从而明显提高Cf/SiC复合材料的力学性能.选用加热加压浸渍条件所制备的材料密度达到1.944g/cm3,室温弯曲强度达到662MPa,在1650℃(真空)和1800℃(真空)下测试,材料的弯曲强度分别为647MPa和609MPa.     

超高温陶瓷改性C/SiC复合材料的制备及其性能

以碳纤维为增强体,聚碳硅烷和聚烷基铪为前驱体,采用前驱体浸渍裂解(PIP)工艺制备C/Si C-HfC复合材料,将其与同种工艺所得C/SiC复合材料进行对比评价分析。发现C/SiC-HfC复合材料具有较低密度和较好的高温力学性能,且在1 650℃静态氧化实验中,含有HfC的基体对纤维具有更佳保护效果。C/SiC-HfC密度约为1.92 g/cm~3,常温弯曲强度为345 MPa,1 800℃高温无氧环境弯曲强度可达424 MPa。C/SiC-HfC复合材料表现出更加优异高温力学性能是由于HfC组分的添加抑制了SiC晶粒的生长,降低了基体内部较大裂纹产生的概率。在1 650℃空气环境下,含有HfC的基体对纤维具有更佳保护作用,主要是由于HfC组分的添加使材料表面的SiC及时氧化成SiO_2,SiO_2在纤维和基体表面形成包覆层,防止了材料内部的进一步氧化。     

以一种新型先驱体制备SiC/SiC复合材料高温弯曲性能研究

以新型先驱体LPVCS(含乙烯基液态聚碳硅烷)为原料,以经CVD裂解碳(PyC)界面改性的KD-1型SiC纤维作为增强相,采用先驱体浸渍裂解工艺(PIP)制备三维编织SiC/SiC复合材料,并对其室温及1300℃弯曲性能测试表征。试验结果表明,采用LPVCS为先驱体制备SiC/SiC复合材料,降低了材料制备周期,且9个周期后材料密度达到2.14g/cm3,开孔率为10.8%。在1300℃空气环境中,SiC/SiC复合材料弯曲强度达到470.2MPa,断裂韧性达到20.7MPa·m1/2。采用扫描电镜对SiC/SiC复合材料1300℃下断口形貌进行观察,SiC纤维存在一定拔出;断口表面存在较为严重的氧化现象,这是导致材料弯曲强度降低的主要原因。     

不同纤维预制体结构对SiC_f/PyC/SiBCN复合材料力学性能的影响

使用不同织造方式(二维机织,法向增强2.5维机织和三维五向编织)制备了3种SiC纤维预制体,采用树脂转移模塑(RTM)和聚合物浸渍裂解(PIP)工艺制备了SiC_f/PyC/SiBCN复合材料。观察复合材料的显微组织,测试弯曲强度、拉伸强度、压缩强度等力学性能,探究不同预制体结构对复合材料力学性能的影响行为。结果表明:同一预制体结构在不同方向的纤维分布不同导致材料力学性能的各向异性;不同预制体结构对材料力学性能有着显著的影响。     

SiC基体结构及其对C/SiC复合材料性能的影响研究北大核心CSCD

采用聚碳硅烷作为前驱体,在800、1000、1200℃下烧结得到SiC基体,研究了温度对SiC基体密度、结晶程度的影响。结果表明基体随着温度的提高,基体密度提高,结晶程度逐渐提高,Si含量比例升高。在800℃时,基体密度为2.30 g/cm^(3),所得基体结构接近无定型态,在1000和1200℃下的密度分别为2.50和2.56 g/cm^(3),晶粒尺寸分别为2.6和4.1 nm。再以聚碳硅烷为前驱体,以碳纤维织物为增强体,采用PIP工艺制备C/SiC复合材料,热解最高温度同样为800、1000、1200℃,得到三组C/SiC复合材料,对复合材料进行了力学性能测试和断口微观结构观察,分析了基体结构对复合材料力学性能的影响。研究结果表明,在一定范围内提高热解温度,有利于改善基体特性和提高复合材料的致密化效率,从而使复合材料的力学性能有所提升,特别是弯曲、层间剪切和压缩性能提高作用明显。     

预氧丝网胎体积分数对针刺C/ C 复合材料力学性能的影响

以预氧丝网胎体积分数为35%、40%和45%针刺织物为坯体,经数次沥青浸渍/炭化、高温石墨化处理后制备C/C复合材料,测定并分析这三种材料的拉伸、压缩、弯曲和剪切强度;采用扫描电子显微镜对其断口形貌进行观察,研究预氧丝网胎体积分数对C/C复合材料力学性能的影响。结果表明:材料的z向力学性能(除了压缩强度)随着预氧丝网胎体积分数的增加呈单调递增关系,材料的xy向力学性能受预氧丝网胎体积分数影响较小。扫描电镜观察显示:材料z向强度主要与针刺形成的轴向纤维束多少、分布等有关。     

Feasibility study of thermo-compensated resistance brazing welding of C/C composites and T2 copper with AgCuTi filler metal

The dissimilar materials joining of C/C composites to T2 copper were performed successfully by thermo-compensated Resistance Brazing Welding (RBW) with AgCuTi filler powder. The interfacial microstructure, phase composition, and shear strength of the resistance brazed joints were investigated by the relevant analysis method. Experiment results indicated that the order affecting the shear strength of the C/C-Cu joint was welding current, welding pressure, and welding time in turn. The shear strength of backward thermo-compensated RBW was higher than that of forward thermo-compensated RBW due to the Peltier effect. The maximum shear strength of the C/C-Cu joint was 11.56 MPa in the optimized welding parameter with welding current of 8.0 kA, welding time of 60 ms, and welding pressure of 0.10 MPa by backward thermo-compensated RBW. The interface structure at the resistance brazed joint with this welding parameter was C/C composites/TiC/Cu (s.s)/T2 copper. The TiC phase was verified at the interface of the brazed joint by Scanning Electron Microscope (SEM), Energy-Dispersive X-ray Spectrometer (EDS), and X-ray Diffraction (XRD). Considerable fractures occurred in the C/C composites and partial fracture occurred at the interfacial reaction layer.     

逾渗理论在先驱体浸渍裂解法制备CMC工艺中的应用

应用物理学的逾渗理论对PIP法制备Cf/SiC复合材料浸渍和裂解过程进行了模拟解释和分析，并在此基础上对工艺进行了优化，使Cf/SiC复合材料的密度由原来的1．75g/cm^3提高到2．03g/cm^3，强度由原来的300MPa提高到500MPa。     

准三维C/C复合材料的弯曲性能及其破坏机理

以碳纤维针刺毡为预制体,采用CVI法或结合液相法制备了热解碳、树脂碳和沥青碳基质的准三维C/C复合材料,并研究了这些材料的弯曲性能及其断裂机理.研究表明:对于热解碳基质,SL基质碳的弯曲强度明显高于RL和SL RL两种基质碳;弯曲强度随密度增高而增大;致密度越高,基体支撑越强,同时微裂纹和孔隙度越低,弯曲性能越好.     

三维碳/碳化硅复合材料的显微结构与力学性能

 利用三维碳纤维预制体，采用等温CVI法制备连续碳纤维增韧碳化硅陶瓷基复合材料。无热解碳界面层的复合材料，其力学性能随密度的增加而提高，但密度较高时却表现出脆性断裂特征。热解碳界面层的存在，有利于纤维的拔出，但由于其结晶程度较低，仍然存在纤维束内部的脆性断裂。     

固体冲压发动机喷管用C/C-SiC复合材料

采用"化学气相渗透+先驱体浸渍裂解"(CVI+PIP)混合工艺制备固体冲压发动机用C/C-SiC复合材料喷管内层,综合考查复合材料的微观结构、弯曲性能和抗烧蚀性能以及固冲发动机C/C-SiC喷管内层水压和点火实验。结果表明:复合材料的弯曲强度达到197 MPa,且断裂破坏行为呈现典型的韧性模式;复合材料具有优异的抗氧化烧蚀性能,氧化烧蚀200 s后线烧蚀率仅为0.0063 mm·s-1;研制的C/C-SiC复合材料构件的水压爆破压强为6.5 MPa,表明构件具有良好的整体承载能力;C/C-SiC复合材料喷管内层高温综合性能通过了固体冲压发动机点火实验考核。     

ZrB2 改性C/ C-SiC 复合材料性能研究

采用碳纤维复合网胎针刺预制体,通过溶液浸渍工艺制备了碳纤维增强C/C-SiC和C/C-SiC-ZrB2陶瓷基复合材料,并对材料的力学、热物理和烧蚀性能进行了分析对比。结果表明:针刺C/C-SiC-ZrB2复合材料的面内弯曲强度、厚度方向的压缩强度、层间剪切强度分别为199、274和19.3 MPa,各性能均低于对应的针刺C/C-SiC复合材料。针刺C/C-SiC-ZrB2材料与针刺C/C-SiC材料相比,热导率得到大幅度提高,而线胀系数略微有所降低。2 500 K、600 s风洞试验后,针刺C/C-SiC-ZrB2复合材料表现出良好的抗氧化烧蚀性能,质量烧蚀率约0.4×10-4g/s。     

高硅氧纤维/酚醛泡沫复合材料的结构与性能

以高硅氧短切纤维毡为增强体,分别以酚醛树脂和酚醛泡沫为基体,制备了高硅氧/酚醛与高硅氧/酚醛泡沫两种复合材料,采用红外光谱分析、扫描电镜分析、热失重分析等方法对其结构和性能进行了表征。结果表明,两种材料具有相似的基体化学结构和相近的固化反应温度,均具有良好的耐热性能,性能测试结果表明,复合材料中基体由酚醛树脂变成酚醛泡沫后,力学性能明显降低,同时,密度由1.65 g/cm3降低至0.5 g/cm3,热导率由0.5 W/(m·K)降低至0.09 W/(m·K)。     

PIP工艺制备SiC晶须增强SiCf/SiC复合材料的性能

以不同界面层厚度的SiC纤维为增强相,采用先驱体浸渍裂解工艺(PIP)制备SiC_f(PyC)/SiC复合材料,并在复合材料基体中引入SiC晶须,对其性能进行研究。结果表明:热解碳(PyC)界面层厚度约为230 nm时,SiC纤维拔出明显,SiC_f/SiC复合材料拉伸强度、弯曲强度和断裂韧度分别达到192.3 MPa、446.9 MPa和11.4 MPa?m^1/2;在SiC_f/SiC复合材料基体中引入SiC晶须后,晶须的拔出、桥连及裂纹偏转等增韧机制增加了裂纹在基体中传递时的能量消耗,使复合材料的断裂韧度和弯曲强度分别提高了22.9%和9.1%。