RTM 用耐高温R802 树脂工艺及性能

研究了RTM用耐高温R802邻苯二甲腈树脂黏度随温度、时间的变化,不同升温速率下的DSC特性,常、高温复合材料弯曲、层间剪切强度、树脂与纤维的界面等。黏度随时间变化曲线表明,其140℃下RTM工艺窗口不少于180 min;DSC曲线表明,在180℃时开始凝胶,固化温度203℃,后处理温度256℃;力学性能测试结果表明,R802/MT300复合材料200℃下弯曲强度保持率为103.8%,500℃下弯曲强度保持率为41.1%,300℃下层间剪切强度较常温提高18%,500℃下层间剪切强度保持率为44%,其树脂与纤维结合良好。     

可溶性改性双马来酰亚胺树脂基体的研究

在双马来酰亚胺/二元胺/改性剂A预聚体系中加入环氧丙烯酸树脂,制备了一种可用作耐热复合材料基体的改性双马来酰亚胺树脂。用DSC研究了该树脂基体的反应特性,并制定出了合适的固化工艺参数:改性树脂基体经140℃/1 h 160℃/1 h 180℃/2 h初固化,于220℃/8 h后固化处理,其热变形温度(HDT)为245℃;该树脂与玻璃纤维制备的单向复合材料层压板的室温拉伸强度、弯曲强度和层间剪切强度分别为1 030 MPa、1 600 MPa和92．1 MPa;180℃下测得弯曲强度保持率为67．8%,层间剪切强度保持率为63．2%,用DMA法测得T_g为273℃。     

后处理温度对邻苯二甲腈基复合材料高温性能的影响

制备了MT300/邻苯二甲腈复合材料,分析了不同后处理温度对其在室温和400℃下力学性能的影响。结果表明,复合材料的后处理温度由315℃提高到330℃,会使其室温下的弯曲强度和模量明显提高;但继续提高后处理温度至375℃,室温下的弯曲强度则不断下降而弯曲模量未出现显著变化;在400℃的测试温度下,复合材料的弯曲强度、模量和压缩强度则均随后处理温度提升逐步提高。复合材料的室温压缩性能随后处理温度升高呈下降趋势,但在350℃处理后其室温压缩强度又出现明显上升。室温、400℃下层间剪切强度则均随后处理温度由315℃升高至375℃而呈先下降后上升趋势。     

TG800碳纤维/双马树脂基预浸料等温固化动力学

为复合材料成型工艺参数制定提供准确信息,采用动态力学分析法(DMTA)对国产TG800碳纤维/802双马树脂基预浸料等温固化动力学进行研究,根据损耗模量E″在恒温扫描过程中出现的拐点可准确确定固化凝胶点。以储能模量E′相对增长率为固化反应速率指标,考察不同恒温阶段反应程度增长模式,并建立了固化反应动力学模型。分别采用Hsich非平衡热力学涨落理论和Avrami方程对预浸料固化反应过程中活化能变化规律进行分析。结果表明:Hsich理论得出TG800/802预浸料反应活化能为49. 5 kJ/mol;Avrami方程得出恒温阶段前期活化能均小于后期,且温度越高对应活化能越低。TG800/802在200℃恒温时前期活化能为78. 8 kJ/mol,小于后期109 kJ/mol,温度升高至240℃后活化能降至32. 4 kJ/mol。通过计算不同恒温阶段固化度佐证了双马树脂固化制度150℃/1 h+180℃/2 h+200℃/4 h的可行性,为TG800/802预浸料的工程化应用提供了技术支撑。     

7501 氰酸酯树脂及其复合材料性能

研究了7501 氰酸酯树脂的工艺和耐热性能,以EW220 布为增强材料,采用RTM 成型工艺制备
了EW220/7501 复合材料层板,研究了其室温和高温力学性能。结果表明:7501 氰酸酯树脂的最低黏度为87
mPa·s,开放期大于10 h,300℃固化后,热分解温度为431℃,Tg 可达421℃;EW220/7501 复合材料室温下具有
良好的力学性能,其中拉伸强度为393 MPa,压缩强度为356 MPa,弯曲强度为602 MPa,层间剪切强度为43
MPa,在300℃下,各项力学性能保持率均≥80%。     

高硅氧/有机硅复合材料高温弯曲性能研究

研究了不同温度对高硅氧/有机硅复合材料弯曲性能的影响;采用红外光谱仪对甲基苯基硅树脂在室温～600℃的结构进行了表征;使用热重分析仪,对基体树脂的热稳定性进行了测量;通过动态热机械分析仪对复合材料的动态力学性能进行了测定;采用扫描电镜对复合材料弯曲断口的形貌进行了观察。,结果表明,室温～600℃范围内弯曲强度随温度的升高而降低,弯曲强度在200℃,300℃,600℃分别出现了明显的降低。复合材料的玻璃化转变、树脂分解和裂解是弯曲性能下降的主要原因。     

RTM 用R801 树脂工艺及性能

对一种新型RTM用双马来酰亚胺树脂R801的固化反应特性、成型工艺及其制备的复合材料性能进行了研究,DSC曲线表明该树脂体系的固化温度为170～220℃;黏度随温度变化曲线表明在70～120℃,树脂黏度增长缓慢,具有不少于7 h的适用期;在90℃左右时,其初始黏度<100 mPa.s,工艺操作窗口时间≥10 h;该树脂制备的MT300碳纤维复合材料在300℃时的压缩、弯曲、层剪性能保持率均≥63%。     

新型含硅芳炔树脂复合材料制备工艺

以含硅芳炔树脂为基体、高强玻璃布为增强材料制备了新型含硅芳炔树脂复合材料,探讨了树脂的固化工艺,研究了树脂含量、成型温度和成型压力对复合材料性能的影响,确定了含硅芳炔树脂复合材料成型的工艺参数:树脂质量分数31%、升温程序170℃/2h+210℃/2h+250℃/4h、成型压力1.0MPa。优化工艺条件下制备的复合材料弯曲强度达278MPa。     

温度条件对碳纤维上浆剂与双马树脂反应及其复合材料界面粘结的影响

为了研究工艺温度对复合材料界面的调控作用,设计采用三阶段固化工艺(即扩散、固化和后固化),考察了不同温度制度下3种碳纤维/双马树脂(BMI)复合材料界面粘结性能的变化规律。采用原子力显微镜(AFM)和傅里叶变换红外光谱(FTIR)深入分析了上浆剂对纤维表面粗糙度和化学特性的影响,研究了上浆剂的反应活性及其与双马树脂的反应性,采用微珠脱粘方法测试了碳纤维/树脂的界面剪切强度(IFSSs)。结果表明,200℃处理2h后3种碳纤维上浆剂均发生部分反应,并且170℃,2h后上浆剂均与双马树脂发生化学反应。对比不同温度条件可以发现后固化阶段对碳纤维/双马体系的界面剪切强度影响显著,未经后固化的复合材料界面性能最低;110℃和140℃恒温扩散阶段对碳纤维/双马体系的界面剪切强度的影响不明显。同种温度条件下,CF1和CF3上浆剂与双马树脂的反应程度高于CF2,相应的CF1和CF3与双马树脂的界面剪切强度较高,表明上浆剂与双马树脂间的化学反应程度是影响其界面粘结性能的主要因素。该研究结果对我国碳纤维上浆剂的研制具有参考价值。     

耐高温双马树脂体系

研究了803树脂的反应特性、流变特性,MT300/803复合材料的耐热性能和力学性能,并分析了复合材料的微观形貌.结果表明:803树脂具有很高的活性、良好的流动性及工艺性;MT300/803复合材料具有优异的耐高温性能,DMA储能模量转变点约为300℃,T<,d><'5>为396℃,其室温、高温力学性能优异;803树脂与MT300碳纤维界面强度高、匹配性好.综合分析,803树脂及其复合材料具有优异的耐高温性能,可推广应用于航天高性能耐高温结构复合材料领域.     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。