共查询到19条相似文献,搜索用时 343 毫秒
1.
2.
3.
张宏波%姜召阳%孙陈诚%王俊山%胡子君 《宇航材料工艺》2007,37(1):19-22
比较了几种不同工艺制备的针刺毡C/C复合材料。对针刺碳毡织物首先进行预增密处理,得到初始密度和碳纤维含量较高的坯料,然后用树脂浸渍法进一步致密化。研究表明,用该方法制备的C/C复合材料比未经预处理的试样,拉伸强度提高39%,压缩强度提高14%,层间剪切强度提高36%。通过SEM观察和常温力学性能的测试,分析表明工艺的改进是强度提高的主要原因。 相似文献
4.
比较了两种不同工艺制备的针刺无纬布C/C复合材料。研究表明,在沥青浸渍/碳化之前对针刺预制体进行CVI预增密处理后,其C/C复合材料轴向拉伸强度提高了234%,层剪强度提高了126%;热扩散率明显升高,轴向线胀系数下降,表现出良好的综合性能。 相似文献
5.
6.
7.
以聚丙烯腈预氧化纤维针刺毡为预制体,经碳化后采用CVI和树脂浸渍(IR)工艺制备出不同密度的多孔C/C预制件,然后采用气体压力浸渗方法制备了C/C-Cu复合材料.采用氢氧(H2-O2)焰对C/C-Cu的烧蚀性能进行测试考核.结果表明:以密度为0.99 g/cm3的C/C预制件制备出的C/C-Cu复合材料的线烧蚀率和质量烧蚀率均小于密度为1.9 g/cm3的C/C复合材料,其烧蚀性能良好;在烧蚀过程中C/C-Cu的铜基体的熔化吸收了大量的热量,降低了材料的表面温度,提高了材料的抗烧蚀性能;烧蚀机制主要是热氧化烧蚀和机械冲刷的综合作用. 相似文献
8.
夏鸿雁%侯卫权%张晓虎%吴书峰 《宇航材料工艺》2008,38(3):37-39
以T300无纬布与PAN碳纤维网胎叠层针刺预制体,高温煤沥青为浸渍剂,采用和高压浸渍炭化相结合的液相浸溃方式制备C/C复合材料.通过对材料力学、热物理性能测试及扫描电镜下显微结构的观察分析.可以得出,引入z向网胎纤维,使材料的z向剪切及压缩、x-y向拉伸及弯曲强度较整体毡C/C材料提高.同时,材料的线胀系数表现为各向异性,而热导率各向异性程度低于整体毡C/C材料,材料的制备周期缩短. 相似文献
9.
10.
以天然气作为气源采用自行研发的C/C复合材料快速制备新技术制备C/C复合材料样件,测试分析了新工艺制备C/C复合材料的力学性能,并与以丙烯为炭源气采用传统等温等压CVI工艺制备C/C复合材料的力学性能进行了对比。研究结果表明:相比于传统工艺,采用新工艺制备C/C复合材料的拉伸强度和模量分别提高了12.0%和20.1%;垂直弯曲强度和模量分别提高了11.7%和12.4%。 相似文献
11.
12.
碳化硼对碳/碳复合材料的催化石墨化作用 总被引:3,自引:0,他引:3
本文研究了用B4C作催化剂,以降低C/C复合材料的石墨化温度,并比较分析了添加B4C后,对C/C复合材料力学、热物理性能的影响。结果表明,添加B4C后,在比通常石墨化温度低400℃的情况下,石墨化度反而增加了14%,达到了85%。C/C复合材料的抗热震性能也有提高。同时应用X射线衍射(XRD)、X射线光电子能谱(XPS)等分析手段,分析了B4C对C/C复合材料的催化石墨化机理。 相似文献
13.
C/C复合材料光谱发射率测量研究 总被引:1,自引:0,他引:1
使用石英灯辐射加热器对C/C复合材料进行加热试验,分别用NiCr-NiSi热电偶及红外测温仪测量材料的背面温度,通过加热过程中的背面温度曲线,得到了材料的ελ-T图.结果表明:在1 123~1 273K情况下,ελ(λ=1.6μm)在0.93~0.87,随温度升高,C/C复合材料的光谱发射率ελ呈下降趋势. 相似文献
14.
A seal device as an important component of aeroengines has decisive influence on per- formance, reliability, and working life of aeroengines. With the development of aeroengines, demands on the performance characteristics of seal devices are made strictly. Finger seal as a novel kind of sealing device, recently attracts more and more attentions in academic circles and engineer- ing fields at home and abroad. Research on finger seals has been extensively developed, especially on leakage and wear performances under dynamic conditions. However, it is a pity that the work on finger seals has been limited with a single approach that is improving the performance by structural optimization; in addition, the technology of dynamic analysis on finger seals is weak. Aiming at the problems mentioned above, a distributed mass equivalent dynamic model of finger seals considering the coupling effect of overlaid laminates is established in the present paper, the dynamic perfor- mance of 2.5 dimension C/C composite finger seal is analyzed with the model, and then the effects of fiber bundle density and fiber bundle preparation direction on finger seal's dynamic performance are discussed, as well as compared with those of Co-based alloy finger seal. The current work is about dynamic analysis of finger seals and application of C/C composite in this paper may have much academic significance and many engineering values for improving research level of finger seal dynamics and exploring feasibility of C/C composite being used for finger seals. 相似文献
15.
16.
17.
罗新%李贺军%李克智 《宇航材料工艺》2006,36(4):7-11
综述了C/C复合材料CVI工艺数值模拟的基本原理,软计算在工艺优化与控制的应用,以性能模拟的研究现状;分析了现今模拟存在的问题;提出了今后C/C复合材料计算机模拟的发展方向. 相似文献
18.
在"锥形体纤维单向缠绕技术"的基础上进行了碳纤维单向缠绕制备C/C扩张段成型工艺的探索,制备出了Φ180 mm C/C扩张段试验件,并对其进行了性能测试及整体探伤.测试结果为:超声探伤分贝差为15 dB的缺陷面积小于5%;沿母线方向层间剪切强度大于10 MPa,大端环向层间剪切强度偏小;内压爆破压强为0.6 MPa,破裂模式较好.试验结果表明,采用碳纤维单向缠绕技术制备C/C扩张段工艺可行. 相似文献
19.