Study on the Anisotropy of Meniscus in the Growing Sapphire

This study is aimed at predicting the relationship between the meniscus and the quality of the sapphire crystals produced by the micro-pulling and shoulder at cooled center (SAPMIC) technique. As with different orientations, the shapes of the meniscus vary, so an investigation into the anisotropy of the meniscus shapes is very important for the final quality of the sapphire crystal. An effective model to describe meniscus shapes and their formation process has been presented. The model has been applied to a sapphire crystal of 200 mm diameter in order to check its reliability. The results show that the model proves to be useful for forecasting the final shapes of the sap-phire crystal made by the SAPMIC technique.     

GH4169合金自然萌生小裂纹扩展行为的试验研究

为了研究镍基GH4169高温合金自然萌生小裂纹的扩展行为,采用单边缺口拉伸(SENT)试样进行了室温下应力比R=0.1,0.5的小裂纹扩展试验。在长裂纹近门槛值区域,观察到明显的小裂纹效应,疲劳小裂纹扩展寿命占全寿命的大部分。利用扫描电子显微镜(SEM)和能谱分析仪(EDS)对试样断口表面进行微观分析,结果表明,疲劳小裂纹起始于合金中的夹杂(Ti(C,N)或Nb(C,N)),并且倾向于以半圆形向试样内部扩展。试样的断裂模式存在由晶体学小平面断裂向疲劳条带断裂的转变,该断裂模式转变处对应小裂纹扩展速率曲线上裂纹加速扩展前的急速降低点。     

TC11与TC17异质钛合金线性摩擦焊连接机理研究

为了探明TC11与TC17异质钛合金线性摩擦焊接头连接机理,采用扫描电镜来研究接头不同位置的微观形貌。结果表明,在振幅为3mm、频率为40Hz、摩擦压力为66.7MPa、摩擦时间为2s的条件下,在接头表面表现为"摩擦磨损"特征。在距接头表面2.5mm处,接头具有"粘着剪切"特征,且原始摩擦界面上有微孔存在,TC11钛合金发生了动态再结晶,而TC17未发生动态再结晶。在距接头表面5mm处,界面上有微孔存在,且在TC17焊缝与热机械影响区(TMAZ)交界处产生裂纹。在距接头表面7.5mm处,原始摩擦界面无微孔存在,在TC17焊缝与TMAZ交界处有裂纹存在。在距接头表面10mm处,接头内无缺陷存在。接头内不同位置的形貌在一定程度上反映了接头的形成过程。     

摩擦时间对异质钛合金线性摩擦焊接头微观组织的影响

采用光学显微镜和扫描电镜研究TC11与TC17异质钛合金线性摩擦焊接头微观组织的特点.结果表明,在振幅为3mm、频率为40Hz、摩擦压力为66.7MPa、顶锻压力为80MPa、顶锻时间为30s的条件下,随着摩擦时间的延长,初生β相动态再结晶晶粒尺寸和α相片层宽度增加.在同一接头内部,接头表面的β相动态再结晶晶粒尺寸比接...     

Thermal Stresses and Cracks During the Growth of Large-sized Sapphire with SAPMAC Method

本文利用有限元法对冷心放肩微量提拉法(SAPMAC)生长大尺寸蓝宝石单晶过程中的热应力进行了模拟计算,应用临界缺陷理论解释了裂纹的萌生与扩展机理。研究表明,晶体内的热应力主要与晶体生长速率,环境温度和结晶取向有关;较大热应力多出现在结晶界面,放肩、收尾以及直径急剧变化等位置;最大热应力总是出现在籽晶与新生晶体的界面附近。裂纹将在临界缺陷位置产生,并在应力作用下沿a或m面扩展。计算结果与实验结果基本吻合,通过晶体生长系统和生长工艺的改进,对晶体的开裂问题得到了有效的抑制。     

Anhydrous based shear-thickening polishing of KDP crystal

Based on the special physical–chemical characteristics of optical crystal in the field of aeronautics, a new anhydrous based shear-thickening polishing (ASTP) method has been proposed to restrain deliquescence and to improve physical properties for KDP machining. The ultra-precision polishing of KDP crystal is completed by ASTP. A kind of anhydrous based thickening polishing slurry (ATPS) was proposed in our work, and high-performance rheological properties were determined to achieve the ASTP of KDP crystal. A material removal model of ASTP in KDP machining is established, followed by the verification experiment of the prediction model. The maximum error of the predictive model is only 9.8%, which proves the validity of the material removal model for KDP polishing. The polishing experiments were carried out on the polishing platform developed by ourselves. The results show that the new polishing method can polish 20 mm × 20 mm × 5 mm KDP crystal and obtain a super-smooth surface with a surface roughness of 1.37 nm and high shape accuracy. The surface accuracy of polished KDP crystal reaches up to 0.68λ (RMS). The experimental results show that the ASTP is a potential ultra-precision machining method for KDP crystal.     

深过冷熔体中的晶体形核与快速长大

 以特制的无机盐玻璃作为净化剂去除液态Ni-0.39％B-6.58％Si合金中的异质晶核,获得363K(0.229T_L)过冷度,采用高速摄影及快速红外测温技术研究了深过冷熔体的快速凝固行为。     

NiCrAlYSi涂层/DD6单晶高温合金界面再结晶和互扩散行为

采用电子束物理气相沉积(EB-PVD)在单晶高温合金DD6基体上沉积NiCrAlYSi涂层.利用X射线衍射(XRD)、扫描电镜(SEM)、能谱仪(EDS)以及透射电镜(TEM)等研究了高温扩散过程中NiCrAlYSi/DD6的界面再结晶和互扩散行为.研究结果表明合金表面喷砂处理后的涂层试样经1 323 K真空热处理4 ...     

Si-Zr-B涂层结构稳定性及对DD3单晶高温合金深过冷的非催化形核惰性

以 Si O2 玻璃粉、分析纯 Zr O2 粉为粉料,分析纯 C2 H5OH,Zr OCl2 · 8H2 O,去离子 H2 O与分析纯Si(OC2 H5) 4按 4∶ 0.1 1∶ 3∶ 1的摩尔比配制的前驱液经 3 5℃,1 80 min水解 -聚合反应后形成的 Si O2 -Zr O2溶胶为粘结剂,H3 BO3 为软化剂,用熔模制壳技术在壳型内壁制备了 Si-Zr-B基底涂层。利用溶胶 -凝胶原理,以 Si O2 -Zr O2 溶胶中加入 H3 BO3 形成的 Si O2 -Zr O2 -B2 O3 溶胶为原料,经浸涂 -分级热处理和 80 0℃玻璃化热处理后,在基底涂层表面制备了适宜厚度的同成分玻璃薄膜涂层。将涂层在 1 5 0 0℃保温 3 0 min后,XRD结果表明,涂层的析晶量仅为 1 %～ 3 %,具有很高的高温结构稳定性。过冷实验表明,DD3单晶高温合金可在该 Si-Zr-B涂层壳型内获得最大 1 4 0 K过冷度,完全可以实现深过冷快速凝固,证明 Si-Zr-B涂层具有良好的非催化形核惰性。     

Synthesis of Iron-containing Carbon Microparticles from Deoiled Asphalt and Ferrocene

The deoiled asphalt as the carbon source and the ferrocene as the metal source and the catalyst precursor were chosen to synthe-size iron-containing carbon microparticles through co-carbonization at the temperature of about 450 ℃ for 3 h. The resulting products were treated at 2 000 ℃ for 2 h. All samples were examined by high resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD). The results show that the iron particles in the heat-treated material are completely coated by carbon. In addition to the fully filled carbon microparticles as well as hollow carbon ones, also form carbon fibers with hollow centers. The formation mechanism of the as-prepared products was discussed briefly.     

粉末冶金镍基高温合金FGH96高温疲劳寿命分散性特征

通过宽载荷水平大子样试验研究了缺陷对粉末冶金镍基高温合金FGH96的疲劳寿命分散性的影响,获得FGH96在宽载荷水平下的疲劳寿命分布特征.通过扫描电镜对疲劳失效断口进行统计分析,揭示缺陷在不同载荷条件下的作用.结果表明:①FGH96中导致疲劳失效的缺陷主要为非金属夹杂;②在高应力水平下（1200,1100MPa）下,导致表面萌生裂纹的夹杂是最差疲劳寿命的主导因素,使得疲劳寿命分散性较大;③在中间应力水平（1000MPa）下,在材料内部萌生裂纹的夹杂并不影响疲劳寿命的分散性;④在低应力水平（900MPa）下,疲劳破坏均萌生于内部,在材料内部夹杂处萌生的裂纹并不影响疲劳寿命的分散性.因此,在高应力水平下的寿命预测需要考虑缺陷信息.      

不同晶体取向单晶锗的力学性能

为了研究微纳米尺度下单晶锗的力学特性,采用纳米压痕仪对单晶锗(100)(110)和(111)晶面进行了纳米压痕实验,并通过原子力显微镜对材料表面进行了观测。根据单晶锗各晶面的位移-载荷曲线,对单晶锗各晶面的弹性回复率、硬度、弹性模量与压入深度之间的关系进行了分析。结果表明:单晶锗在加载过程中分别经历了弹性变形、塑性变形和脆性变形三个阶段。当压入深度超过500 nm时,加载曲线上有突进点产生;当压入深度超过100 nm时,卸载曲线上有突退点产生。单晶锗的残余压痕形貌表现为凸起状,表明单晶锗具有较低的加工硬化趋势。当压入深度达到100 nm时,单晶锗表现出明显的尺寸效应,且单晶锗(111)晶面具有最低硬度和弹性模量值。表明相对于其他两个晶面,单晶锗(111)晶面具有更好的塑性变形能力。     

激光焊接ZL114A/5A06 异种铝合金接头组织及性能

采用激光焊接ZL114A/5A06异种铝合金,通过参数优化以获得性能优良的焊接接头,利用光学显微镜(OM)、拉力试验机、高温疲劳试验机、SEM和EDS对接头的显微组织、力学性能和拉伸断口进行了研究。结果表明:焊缝中心区的金相组织为等轴晶;接头焊后不经热处理,抗拉强度可达到265 MPa,为母材强度的80%以上,并有很好的抗疲劳性能;断口分析显示断裂位置在ZL114A母材一侧的熔合线附近;在保证焊透的前提下,激光功率越小,晶粒越细小,接头强度越高。对框架蒙皮结构铝合金贮箱产品试验件进行了焊接,试验件达到了产品各项性能指标要求。     

熔铝氧化渗透合成SiC_p/Al_2O_3-Al复合材料的微观结构分析

以低成本的熔铝氧化渗透合成新方法制备了SiCp/Al2 O3 Al复合材料。借助X光电子谱 (XPS)、光学金相显微镜、透射电镜 (TEM)、X射线衍射 (XRD)等手段研究了该种复合材料的微观结构 ,并分析了影响微观结构的主要因素及其影响规律。结果表明 ,Al2 O3 和Al作为复合材料基体呈双连续分布 ,它们各自的含量可在较大范围内受SiC颗粒的粒度所控制。在熔铝氧化渗透合成的SiCp/Al2 O3 Al复合材料中 ,各组成相之间无界面反应 ,也无晶间相 ,Al2 O3 在SiC颗粒表面二次形核并直接生长的现象普遍存在 ,并由此形成了具有良好物理冶金结合的Al2 O3 SiC一体化陶瓷骨架     

La3＋掺杂 Ni0．35 Co0．15 Zn0．5 Fe2 O4铁氧体的制备及微波吸收性能

采用溶胶-凝胶自蔓延法制备 La3＋掺杂 Ni0．35 Co0．15 Zn0．5 Fe2 O4,并研究不同掺杂量对样品微观结构、电磁参数及微波吸收性能的影响。通过 X 射线衍射仪、扫描电镜研究了样品的相结构和微观形貌,使用振动样品磁强计与矢量网络分析仪分别对样品的静态磁性能及在1～12GHz 的电磁参数进行了研究,并计算了不同厚度（3 mm、5 mm、8 mm）下材料的反射损耗。研究表明,适量掺杂 La3＋能够提高 Ni0．35 Co0．15 Zn0．5 Fe2 O4铁氧体的吸波性能,并使吸收频带向高频移动。其中样品 Ni0．35 Co0．15 Zn0．5 La0．04 Fe2 O4与石蜡混合厚度为5mm 时,最小反射损耗为－28．4dB,小于－10dB 带宽为3．7GHz。     

化学镀SiC/Ni-P功能梯度材料工艺、组织及性能

通过对化学镀Ｎｉ－ Ｐ－ ＳｉＣ复合镀层的研究,找到了制备ＳｉＣ／Ｎｉ－ Ｐ 功能梯度材料（ＦＧＭ） 的工艺方法。并采用光学显微镜、电子探针分析仪及热震试验等方法和手段对功能梯度材料的组织、形貌、成分与镀层结合力进行了研究。结果表明,功能梯度材料中ＳｉＣ微粒以弥散状态沿镀层厚度方向呈梯度分布,无团聚结块现象,材料致密,组织细小。功能梯度材料较单层Ｎｉ－ Ｐ－ ＳｉＣ复合镀层以及Ｎｉ－ Ｐ／Ｎｉ－ Ｐ－ ＳｉＣ 双层镀层具有更好的结合强度。     

热障涂层的激光表面改性参数优化和结构设计

热障涂层是航空发动机涡轮叶片关键核心技术之一,但在服役条件下常受环境沉积物、熔盐等的腐蚀而过早失效。激光表面改性是一种提高涂层抗腐蚀性能的有效办法,但改性涂层的激光工艺优化和结构设计亟待研究。本文采用脉冲Nd：YAG激光系统对Y₂O₃部分稳定ZrO₂（YSZ）热障涂层进行表面改性,研究了激光功率、扫描速度以及光束长度对改性层厚度、微观结构的影响。结果表明,激光改性层呈致密的柱状晶结构,并有纵向裂纹贯穿其中。改性层的厚度与激光功率成正比,受扫描速度影响不大,与光束长度成反比。激光功率过高,则改性层裂纹增加明显;光束长度过大,则改性层与下方涂层的界面缺陷增多,不利于界面结合。优化的激光改性参数为：激光的功率为75~80 W,扫描速度8 mm/s,光束长度为160 mm。设计了双层激光改性层,每层中的纵向裂纹不连续,使得整个改性层中无贯穿的纵向裂纹,有助于抑制高温腐蚀熔体的内渗。     

基于标样比对测试的固体火箭发动机工业CT检测工艺

针对固体火箭发动机CT检测缺少行业标准的问题,使用正密度材料块模拟界面脱粘缺陷和使用合金块模拟药柱内部缺陷来制作标样发动机,对标样发动机和实际发动机进行CT检测对比试验,并解剖取样验证。结果表明发动机CT检测和射线照相、解剖试验结果吻合,标样发动机设计满足研究需要。同时确定了工业CT系统发现缺陷的最小能力:脱粘面积20 mm×20 mm,宽度0.4 mm,气孔和夹杂直径5 mm,裂纹宽度0.4 mm。建立检测标准规范了固体火箭发动机CT检测工艺。     

纯钛搅拌摩擦焊晶粒细化机制

通过搅拌摩擦焊实现了5 mm纯钛的可靠连接,并对焊接接头组织进行了细致研究。通过光学、扫描电子显微镜和透射电子显微镜对纯钛搅拌摩擦焊组织进行了精细表征,对焊接过程中的再结晶机制进行了研究。结果表明：采用搅拌摩擦焊可以得到成型良好,组织致密的焊缝;焊缝组织可以分为焊核区( NZ)、热机影响区( TMAZ)、热影响区( HAZ)和母材区( BM);根据各区组织形态和结构特点对纯钛搅拌摩擦焊动态再结晶过程进行了分析,揭示了纯钛搅拌摩擦焊焊缝细化机制;钛的层错能较大,搅拌摩擦产生的位错不能完全分解,遇到阻碍时,只能通过滑移和攀移继续运动,在多次搅拌摩擦作用下,位错缠结堆积,位错密度不断上升,产生新的晶界,从而形成细小晶粒,实现晶粒细化。     

大体积液态铝合金的净化和深过冷

采用无机盐类净化剂,在高频电磁悬浮熔炼装置上对大体积Al83Y10Ni7合金进行净化处理,获得了78.1℃的大过冷度;使用DSC技术和常规金相方法分析了深过冷熔体中的晶体形核和凝固组织。实验结果表明,在熔体的强制对流条件下,适当配比的无机盐净化剂有较强的微观净化效果,并使其微观组织明显细化。在自由凝固条件下,深过冷液态金属的细化效果仅受控于形核过冷度,与其体积的大小无关。