不同粉末粒度的Al-Li-Mg-Zr挤压合金的拉伸断口特征

本文用SEM研究了粒度分别为<40μm、40～100μm、100～154μm的挤压A1-3.3Li-1.01Mg-0.06Zr合金的拉伸断口。其共同特征是裂纹均起始于试样内部的夹渣,并以放射剪切特征扩展。颗粒度不同,剪切源的粗细及形式也不同。颗粒度<40μm的合金,剪切源细且呈劈-剪型(aI),表现为穿晶与个别沿晶断裂,沿粉末边界脱开的二次裂纹较多且粗。40～100μm的粉末合金,断口的放射剪切源粗,呈锯齿型(aII),出现穿晶加个别沿晶的层状断裂。沿粉粒界面劈开的二次裂纹较少,并存在一些塑性变形良好的小锥特征。100～154μm粉末合金的断口放射剪切源粗并呈aI型,明显可见沿粉界劈开的二次裂纹为穿晶沿晶混合断裂。     

非对称载荷下TC17合金超高周疲劳试验

通过试验研究了110Hz和20kHz两种频率正弦式非对称载荷作用下TC17合金材料的疲劳失效行为,结果表明:载荷频率对TC17合金的疲劳强度和疲劳失效机理影响不明显,两种频率载荷作用下TC17合金的疲劳失效均存在表面诱发疲劳失效和内部诱发疲劳失效。表面诱发的疲劳失效主要是由循环载荷作用下试样机械加工缺陷和表面滑移所导致的,内部诱发的疲劳失效主要是由于材料初生α相在非对称循环载荷作用下发生解理断裂而导致的,失效形式的不同使得材料的应力-疲劳寿命（S-N）曲线呈双线性。萌生于TC17合金试样内部的疲劳裂纹可分为3个阶段:初生α相的解理断裂阶段、短裂纹扩展阶段和长裂纹扩展阶段。由裂纹萌生区特征可以确定室温条件下,应力比为0.1时,TC17合金疲劳长裂纹扩展门槛值为3.3MPa·m1/2。      

应力比对Ti-6Al-2Zr-1Mo-1V合金疲劳裂纹扩展行为的影响

采用三点弯曲试样,对钛合金Ti-6Al-2Zr-1Mo-1V在R=0.1,0.3和0.5三个应力比条件下的疲劳裂纹扩展行为进行研究,得到相应实验条件下的疲劳裂纹扩展速率,并结合断口分析探讨应力比R对该合金疲劳裂纹扩展行为和断裂机理的影响。结果表明:随着应力比R增大,Ti-6Al-2Zr-1Mo-1V合金在同一ΔK时的疲劳裂纹扩展速率增大,裂纹扩展对应的应力强度因子ΔK范围和扩展门槛值ΔK_(th)减小;三个应力比R作用下试样的疲劳断口表面均可见一些疲劳台阶和二次裂纹;随着应力比R的增加,试样断口表面粗糙度增加,二次裂纹减小;在R=0.1,0.3和0.5三个应力比条件下的疲劳断裂均表现为穿晶断裂。     

添加微量Sc对Mg-3Li合金高应变率变形行为的影响

利用Hopkinson压杆对Mg-3Li和Mg-3Li-1Sc合金进行了高应变率冲击实验,分析了添加少量Sc对Mg-3Li合金冲击变形行为及其应变率效应的影响.结果表明,在1350s～3000s-1应变率范围内,两种合金的动态应力-应变行为均表现出显著的应变率强化效应.但随应变率继续升高,合金的动态变形行为转为应变率弱...     

考虑小裂纹特性的裂纹扩展数值分析方法及实验验证

为了对工程断裂关键件进行全面的损伤容限分析,需要发展一种能够考虑小裂纹阶段的疲劳裂纹扩展数值分析方法。在Paris公式的基础上基于镍基粉末高温合金小裂纹扩展行为特点,提出了一种小裂纹加长裂纹阶段的裂纹扩展物理力学过程描述,并以此建立了裂纹扩展速率模型。同时考虑到工程应用,将该模型通过FRANC3D软件的用户子程序,与有限元方法结合,构建了一种可分析实际工程结构例如航空发动机涡轮盘上疲劳裂纹扩展的数值分析方法。针对带初始缺陷的FGH96合金标准试棒进行了裂纹扩展数值分析,并与开展的裂纹扩展寿命实验进行了对比。数值计算结果与实验结果吻合较好,表明该方法能够充分考虑小裂纹阶段的裂纹扩展行为特点,适用于分析工程结构疲劳裂纹扩展的全过程。     

航空用高强高韧铝合金疲劳断口特征的研究

采用金相显微镜、扫描电镜及能谱分析对T7451状态7B04铝合金疲劳断口进行了研究,揭示了该合金疲劳裂纹萌生与扩展的微观特征。合金的疲劳断口可明显划分为疲劳裂纹源区、裂纹稳定扩展区及瞬断区三个区域:疲劳裂纹从材料夹杂(大小约为(7~10)μm×(11~14)μm的富铁脆性金属间化合物粒子)处萌生,在样品表面或近表面区域形成后呈放射状扩展;疲劳裂纹扩展区可以观察到疲劳破坏的一些典型特征;瞬断区的断口形貌跟静载断裂相似,形成不平坦的粗糙表面。     

基于扩展有限元的改性双基推进剂的开裂过程模拟研究

为研究和模拟改性双基推进剂(CMDB)在准静态条件下的断裂特性,利用扩展有限元XFEM技术,建立了中心直裂缝含加载平台的圆盘形三维模型。基于线粘弹性理论,通过单轴拉伸实验直接获取改性双基推进剂的最大拉应力8.21MPa,作为仿真模型中裂纹粘聚区的断裂强度,模拟了固体推进剂在静态加载条件下裂纹实时扩展过程。结果表明实验和仿真过程中裂纹均首先呈I型扩展,最后以复合断裂形式扩展失效。讨论了推进剂在压缩断裂过程中裂纹扩展区的应力变化对裂纹扩展的影响,发现实验预期结果与仿真结果符合性良好,说明扩展有限元法能够为改性双基推进剂断裂过程的数值模拟提供新的方法。     

GH33A疲劳/蠕变交互作用下裂纹扩展特性研究

本文采用交流电位法研究了镍基高温合金GH33A在700℃、疲劳/蠕变交互作用下的裂纹扩展特性。用光学显微镜和扫描电镜对断裂特征进行了分析。结果表明:疲劳/蠕变交互作用加速裂纹扩展,且dα/dN和⊿K在双对数坐标上呈折线规律变化,实验证明:弹塑性断裂力学参数C作为疲劳/蠕变交互作用下裂纹扩展判据是可行的,并建立了经验关系式。疲劳/蠕变交互作用促进裂纹沿晶扩展。主裂纹与W型微裂纹的连接和沿滑移面剪切型扩展是疲劳/蠕变交互作用的两种主要微观断裂机理。     

Al-5.3Cu-0.8Mg-0.6Ag合金的超塑性变形

研究了Al-5.3Cu-0.8Mg-0.6Ag合金板在400～520℃以及应变速率为1×10^-4 ～ 1×10^-1/s下的超塑性变形能力及其变形机制.结果显示,轧制态的Al-5.3Cu-0.8Mg-0.6Ag合金在500℃及应变速率5×10^-4/s时的最大伸长率为320%,应变速率敏感系数m达到0.58.高应变速率下超塑性变形过程中主要机制为晶界滑动,协调机制则是空洞的形核长大与断裂.     

镍基高温合金蠕变裂纹扩展的微观力学分析

光滑和预制裂纹的高温合金试件的应力持久寿命的实验结果说明,预先存在的小裂纹,严重地降低高温合金构件的应力持久强度和寿命。 扫描电镜和金相照片分析说明,裂纹沿晶界孔洞扩展。根据孔洞增长和与主裂纹顶端会合的微观力学分析,用蠕变J积分参量和裂纹张开位移速率推导出蠕变裂纹扩展公式。GH_(33A)高温合金的实验数据论证了上面的断裂力学分析。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。     

Research on Auto-detection for Remainder Particles of Aerospace Relay Based on Wavelet Analysis

Aerospace relay is one kind of electronic components which is used widely in national defense system and aerospace system. The existence of remainder particles induces the reliability declining, which has become a severe problem in the development of aerospace relay. Traditional particle impact noise detection (PIND) method for remainder detection is ineffective for small particles, due to its low precision and involvement of subjective factors. An auto-detection method for PIND output signals is proposed in this paper, which is based on direct wavelet de-noising (DWD), cross-correlation analysis (CCA) and homo-filtering (HF), the method enhances the affectiv-ity of PIND test about the small particles. In the end, some practical PIND output signals are analysed, and the validity of this new method is proved.