综述了Laves相Cr_2Nb金属间化合物的结构和变形机制及其韧化研究进展,重点评价了细晶增韧、软第二相增韧和合金化增韧这三种方法,指出了存在的问题及今后的研究方向。     

超细晶Laves相NbCr2颗粒增强Nb基复合材料的制备及其组织性能研究

采用机械合金化 热压工艺制备了Laves相NbCr2增强的Nb基复合材料。研究了Nb-22.5Cr配比成分的Nb,Cr元素粉经MA30h后在1250℃分别热压10min,20min和30min所获得的Nb/NbCr2复合材料的组织和性能。结果表明:三种热压时间均可制备出组织均匀,致密度高的Nb/NbCr2复合材料,体积分数约为30%的近等轴状的Laves相NbCr2颗粒弥散分布于Nb固溶体基体中。热压20min的试样具有最佳的组织和性能,其Laves相NbCr2的晶粒尺寸达到亚微米级,致密度达到99.2%,维氏硬度为9.41GPa,屈服强度为2950 MPa,抗压强度为3345 MPa,塑性应变达到了7.01%,充分实现了Laves相NbCr2颗粒强化和细晶强韧化的效果。     

机械合金化＋热压制备Laves相NbCr2合金及其组织性能研究

采用机械合金化 热压工艺路线来制备化学配比成分的单相Laves相NbCr2合金.研究了Cr,Nb元素粉经20h球磨后在1200℃,1250℃和1300℃不同时间热压所获得的Laves相NbCr2合金的组织和性能.结果表明:1250℃×0.5h热压获得的Laves相NbCr2合金组织均匀,晶粒尺寸达到微/纳米级,致密度达到97.1%,室温断裂韧性高于5.07MPa·m1/2.与熔铸工艺制备的单相Laves相NbCr2合金的断裂韧性1.50MPa·m1/2相比,所制备的单相Laves相NbCr2合金的室温断裂韧性大大提高,充分实现了细晶韧化的效果.     

Ni-Cr-Al合金Ti+Nb微合金化前后相含量及其分布对高温性能的影响

研究了Ni-Cr-Al合金及其Ti+Nb微合金化+时效处理后,合金中相含量及其分布对900℃拉伸及900℃/29.5MPa持久拉神性能的影响.结果表明,微合金化后,合金中γ′及M23C6相总量增加; 其900℃抗拉强度和900℃/29.5MPa持久寿命相应增加;晶界上MN相含量的增加以及M23C6相含量的减少有利于合金高温抗拉强度和持久寿命的提高.     

用于阻抗变换层的Li2O-Al2O3-SiO2玻璃陶瓷制备及其微波介电特性

 采用热压和凝浇注无压烧结的方法制备了Li₂O-Al₂O3-SiO₂ 玻璃陶瓷阻抗变换层,研究表明烧结的工艺方法和参数对该玻璃陶瓷的致密度和复介电常数有很大的影响。在较高烧结温度和压力下,该玻璃陶瓷的复介电常数保持不变。降低烧结温度和压力时,能够得到一系列复介电常数在较小范围内变化的Li₂O-Al₂O₃-SiO₂ 玻璃陶瓷,但复介电常数不随频率发生变化。将该玻璃陶瓷作为吸波材料的阻抗变换层后,大幅度提高了材料的吸波性能,而且其制备工艺对吸波性能也有一定的影响,可以通过改变该玻璃陶瓷的烧结条件来满足不同吸波材料设计对阻抗匹配层的多种要求。     

镍掺杂对α-Al2O3烧结过程、微观结构及力学性能的影响

 首先采用非均相沉淀包裹法制备金属镍包裹α-Al₂O₃复合微球粉体,然后采用热压烧结制备了Al₂O₃/Ni金属陶瓷。通过X射线衍射仪（XRD）、扫描电子显微镜（SEM）、能谱仪（EDS）对复合粉体及热压烧结产物的成分和结构进行了表征,利用阿基米德法测量了复合陶瓷的密度,分别通过三点弯曲法和单边切口横梁法对陶瓷试条的抗弯强度和断裂韧性进行评估。研究发现：金属镍的引入活化了α-Al₂O₃的烧结,镍粒子均匀地分布在氧化铝的晶界上,增加了弱界面,提高了氧化铝的断裂韧性,最高可达7.62 MPa·m^1/2。     

固溶温度对定向凝固高温合金DZ22的组织和性能的影响

 随着固溶温度的提高,显微组织发生明显的变化,共晶Υ′相和初生的粗大Υ′相不断回溶,重新析出更多更细的Υ′相。与此同时,晶界状态也逐渐变成“细线”状。元素的枝晶偏析减小,中、高温的纵向持久寿命增加。但是,中温横向持久寿命显著降低。在试验中测定了DZ22合金的初熔温度为1230～1240°C,并进行了提高初熔温度的试验。文中讨论了确定定向凝固合金回溶温度的原则,根据试验结果,认为DZ22台金选用1200～1210°C为宜。     

循环冷处理对30CrMnSiNi2A钢力学性能的影响

30CrMnSiNi2A钢用作飞机的主要承力件。该钢通常经等温淬火和低温回火后使用。在这种热处理状态下,钢的组织中总有一定量的残余奥氏体。夏日飞机停在地面,温度可达50℃以上;飞上同温层后,温度可降至-60℃,甚至更低一些。故一次地-空-地循环即相当于材料经受一次50℃--60℃-50℃的冷处理。因此,本文用循环冷处理来模拟飞机的地-空-地循环,以研究高强度钢中介稳奥氏体在飞行过程中及其对力学性能的影响。     

某些因素对30CrMnSiNi2A钢门槛值影响的研究

 本文研究了30CrMnSiNi2A超高强钢的降载方式,应力比、试样厚度及裂纹长度对门槛值及低速疲劳裂纹扩展行为的影响。氧化物诱发的闭合效应与氢脆机制的相互作用导致了高强钢的门槛值与应力比的弱相关性。证实了试样厚度及裂纹长度在所观察的范围内对门槛值及低速扩展无明显的影响。     

离心叶轮内稀释固液两相流动的数值模拟

 对固液两相流动进行了数值模拟。液相和固相分别采用 k- ε湍流模型和代数颗粒流( AP)湍流模型并考虑了液固两相间的相互作用。用此模型结合 SIMPLE- C算法对离心叶轮内的稀释固液两相流动进行了计算并研究了颗粒对流场的影响。计算结果同试验结果基本一致     

Thermoelectric Properties of Mg_2Si_(1-x)Sn_x Synthesized by Bulk Mechanical Alloying

Bulk mechanical alloying (BMA) has been successfully applied to solid-state synthesis of p-type and n-type thermoelectric mate-rials Mg2Si1–xSnx (x = 0, 0.2, 0.4, 0.6, 0.8, 1) from element-powders at the room temperature in a relatively short time. The electrical conductivity, the Seebeck coefficient and the thermal conductivity of the Mg2Si1–xSnx are quite sensitive to the x-content. With the x-content rising, the electrical conductivity increases. When x = 0.6, it reaches the lowest and Mg2Si shows an n-type of semi-conducting. However, when x = 0.2 and T >525 K, the Seebeck coefficient of the samples will change the opposite way. While x≥0.4, the samples present a p-type of semi-conducting. The figure of merit, Z of Mg2Si1–xSnx will be obtained in the range from 300 K to 700 K. When x = 0.6, Z proves to be higher than that of other samples at 300 K≤T≤650 K.     

Thermoelectric Properties of Mg2Si1-xSnx Synthesized by Bulk Mechanical Alloying

Bulk mechanical alloying （BMA） has been successfully applied to solid-state synthesis of p-type and n-type thermoelectric materials Mg2Si1-xSnx （x = 0, 0.2, 0.4, 0.6, 0.8, 1） from element-powders at the room temperature in a relatively short time. The electrical conductivity, the Seebeck coefficient and the thermal conductivity of the Mg2Si1-xSnx are quite sensitive to the x-content. With the x-content rising, the electrical conductivity increases. When x = 0.6, it reaches the lowest and Mg2Si shows an n-type of semi-conducting However, when x = 0.2 and T 〉525 K, the Seebeck coefficient of the samples will change the opposite way. While x≥0.4, the samples present a p-type of semi-conducting. The figure of merit, Z of Mg2Si1-xSnx will be obtained in the range from 300 K to 700 K. When x = 0.6, Z proves to be higher than that of other samples at 300 K≤ T≤650 K.     

9Cr13Mo3Co3Nb2V马氏体不锈钢微观组织研究

对不同热处理状态下的微观组织结构进行了研究.采用物理化学相分析技术研究了9Cr13Mo3Co3Nb2V退火、淬火以及最终热处理制度下析出相的类型、含量及组成结构式.并用X射线小角散射(SAXS)(small angle x-ray scatter)分析了不同热处理制度下析出相在不同粒度间隔中的质量分布.结果表明:①9Cr13Mo3Co3Nb2V钢退火状态的组织为珠光体 碳化物(M23C6,MC和M6C),淬火状态组织为马氏体 碳化物(M23C6和MC),最终热处理状态的组织为回火马氏体 碳化物(M23 C6,MC和M3C);②小颗粒(≤300nm)碳化物析出相粒度分析表明,9Cr13Mo3Co3Nb2V钢退火、淬火状态析出相平均粒度相差不大,粗大颗粒较多,而最终热处理状态的析出相平均粒度明显减小,且细小颗粒比例较大.     

稀土元素La,Ce对机械合金化TiAl合金显微组织和性能的影响

采用机械合金化结合粉末冶金技术制备Ti-44.7Al-xLa-yCe(原子分数/%,下同)合金材料.利用扫描电镜和金相显微镜研究不同La,Ce添加量对机械合金化TiAl基合金的显微组织的影响,并对合金的力学性能进行测试.研究表明,通过机械合金化在TiAl基合金系统中添加微量稀土元素La,Ce对TiAl基合金的细化作用非常明显,TiAl的强度开始随着稀土元素La的增加而增加,当La元素含量为0.5%时,达到峰值,然后强度随稀土含量的增加而下降;而合金的强度却随添加Ce的含量的增加而直线下降,同时添加稀土La的TiAl合金的强度远高于加稀土Ce的TiAl合金的强度.     

热处理对9 Cr13 Mo3 Co3 Nb2 V组织与硬度的影响

采用金相分析、硬度测试等技术手段,研究热处理对马氏体不锈钢9Cr13Mo3Co3Nb2V组织和硬度的影响。结果表明：9Cr13Mo3Co3Nb2V经淬火、冰冷处理及多次回火后,残余奥氏体充分转变为回火马氏体,并产生较强的二次硬化效果,进而获得稳定的组织和高的硬度;在350℃以上回火时,由于组织中二次碳化物的析出,开始出现二次硬化倾向,至480~520℃时,回火硬度达到了最大值。     

固溶处理定向凝固高温合金DZ8的组织与力学性能

观察了1260℃与1240℃固溶温度热处理后DZ8合金的显微组织,比较了两者的拉伸与持久性能.结果表明:采用1260℃固溶温度热处理,DZ8合金存在少于1％的γ+γ'共晶相,但富Hf相发生初熔;采用1240℃固溶温度热处理,合金未发现初熔但仍存在12％左右的γ+γ'共晶相.DZ8合金分别采用1260℃与1240℃固溶温度热处理后,室温、700℃与980℃拉伸性能以及980℃/205 MPa持久性能相当,但采用1260℃固溶温度热处理的D28合金其760℃/725 MPa持久性能较采用1240℃固溶温度热处理的有所下降.     

SHS法反应合成Al3Ti/Al复合材料的研究

通过将5Al-Ti体系混合粉末预制块在一定温度下预热,原位制备出Al3Ti/Al复合材料,并探讨了其生成机理和影响因素.研究发现:Al粉和Ti粉混合预热生成Al3Ti是由Al粉的熔化诱导;在高于热爆起始温度下预热时,Al3Ti直接以热爆反应机制生成;在低于热爆起始温度下预热时,Al3Ti按扩散-热爆反应机制生成.预热温度、Ti粉粒度及冷却速度是影响材料组织性能的关键因素.通过适当工艺制备出具有性能优异的Al3Ti/Al复合材料,其硬度是铝基体的3.6倍,耐磨性高.