Ti/Al/Ti_(46)Zr_(26)Cu_(17)Ni_(11)非晶层状复合材料界面相组成

利用DSC对真空甩带法制得的Ti_(46)Zr_(26)Cu_(17)Ni_(11)非晶薄带进行热分析,据此选择在693 K(T_g),753 K(T_g~T_(x1)),813 K(T_(x1))下对非晶合金进行不同时间真空热处理,分析非晶晶化行为,并以Ti_(46)Zr_(26)Cu_(17)Ni_(11)非晶合金、TA2和纯Al为原材料,利用Gleeble-3500热模拟试验机在873 K/10 MPa/8 h下制备层状复合材料,采用SEM、TEM、显微硬度计并结合热力学和元素扩散理论对界面层相组成、析出次序和性能进行研究。结果表明:Ti_(46)Zr_(26)Cu_(17)Ni_(11)非晶玻璃转变温度T_g=720 K,初始晶化温度T_(x1)=788 K;非晶晶化首先生成亚稳相I相,随后进一步析出三元或四元Laves相和Ti Ni相;热压后,纯Al和非晶晶化层间界面由薄层Al_3Ni和晶粒细小结构均匀的Al3(Ti0.6Zr0.4)层组成,界面平直无缺陷,总厚度与纯Ti、纯Al间界面层厚度比约为6.5∶1;Al_3(Ti_(0.6)Zr_(0.4))和Al_3Ti硬度相近,分别为(564.20±10.46)HV和(579.83±15.26)HV,但Al_3(Ti_(0.6)Zr_(0.4))层塑性更好。     

Fabrication of Ti/Al/Mg laminated composites by hot roll bonding and their microstructures and mechanical properties

Ti/Al/Mg laminated composites were successfully fabricated by hot roll bonding. The effects of the rolling reduction on the microstructural evolution and mechanical properties of the composites were explored. The results show that Ti/Al/Mg laminated sheets exhibit good interfacial bonding. The rolling reduction has a significant effect on the deformation inhomogeneity through the thickness of the Al layer. The initial grains of the Al layer near the Ti/Al interface are fragmented into fine equiaxed grains, and the grains at the center and near the Al/Mg interface are elongated. The R-cube shear texture of the Al layer forms near the Ti/Al interface and permeates into the center layer in the samples with greater rolling reductions. The β-fiber rolling texture of the Al layer is observed near the Al/Mg interface and increases with the increase of rolling reduction. The stress–strain curves indicate that the fracture appears first in the Mg layer. With the increasing rolling reduction, the ultimate tensile and yield strength values increase, and the elongation up to the Mg layer fracture decreases.     

不同编织结构Cf/Al复合材料高温压缩性能与失效机理

对基于真空气压浸渗法制备的三维五向、三维正交、叠层穿刺和2.5D浅交直联4种不同编织结构C_f/Al复合材料,分别在350℃和400℃下进行压缩试验,分析其高温压缩性能以及温度对复合材料压缩性能的影响,并进一步利用SEM观察叠层穿刺结构的断口形貌,探讨其压缩失效机理。结果表明,不同编织结构的复合材料在高温环境下压缩性能差异较大,三维正交结构的压缩强度最高,在350℃和400℃下分别为351.4 MPa和288.6 MPa;2.5D浅交直联结构的压缩强度最低,分别为87.3 MPa和52.2 MPa。同时不同编织结构的C_f/Al复合材料高温稳定性也存在较大差异,当温度由350℃升高到400℃时,2.5D浅交直联结构的压缩强度下降幅度较大,约为40.2%,其高温压缩稳定性较差;叠层穿刺结构的压缩强度下降幅度较小,约为4.0%,其高温压缩稳定性较好。叠层穿刺结构复合材料的高温压缩失效过程根据切线模量特征可分为两个阶段：第一阶段基体合金承受主要载荷,第二阶段基体与增强纤维共同承受载荷。     

碳纤维复合材料超声扫描分层检测及评价方法

由于碳纤维增强复合材料（CFRP）具有各向异性的特点,在其钻削加工中极易形成分层、撕裂以及毛刺等加工缺陷,而分层对碳纤维层合板构件的性能影响最大,因而建立一套准确的针对分层缺陷的检测、描述以及评价方法对层合结构碳纤维复合材料的有效应用具有重大意义。从分层缺陷的形成机理出发,通过对现有分层缺陷的检测以及评价体系的分析,提出了基于高频超声扫描显微镜（SAM）来进行分层缺陷检测评价的三维体积分层因子评价方法,并针对T800/X850碳纤维单向层合板对该方法进行了定征试验,最后通过对实际加工孔的分层缺陷的评价,综合对比了三维体积分层因子评价方法与传统评价方法的应用效果。结果表明：分层缺陷是由力热耦合引起的层间粘结失效,出口处更为严重;用超声扫描显微镜检测分层,可检测不少于8层的碳纤维复合材料,至少可以清晰表达5层的内部分层特征;分层会发生隔层传播,并且两个相邻铺层为同向的层间结合强度最好,不易产生隔层传播;三维体积分层因子可以更准确清晰地评价复合材料层合结构的内部缺陷。     

脉冲电流辅助粉末夹层TLP连接SiC_p/Al接头微观组织和力学性能

研究脉冲电流辅助瞬间液相(Transient Liquid Phase,TLP)扩散连接技术,采用粉末中间层,利用低压高强脉冲电流通过铝基复合材料搭接面与中间层,从而实现对SiC_p/2024Al复合材料板材的TLP扩散连接。分析不同工艺参数下连接试样的微观组织和力学性能,探索脉冲电流对铝基复合材料连接的影响机理。结果表明:采用真空压强为1×10~(-3)Pa,平均电流密度115 A/mm~2,连接预紧压力为0.5 MPa,连接时间60 min条件下,连接接头形成了良好的冶金连接界面,无缺陷产生;通过对连接接头微观组织观察发现,在脉冲电流作用下,接头原位生成弥散的高强度高硬度金属间化合物增强相,有效地提高了接头的力学性能。     

Ho_2O_3掺杂对原位合成HoAl-Al_2O_3/TiAl复合材料显微组织及性能的影响

采用固态置换反应原位合成工艺,利用Al—Ti—TiO2-Ho2O3体系的放热反应合成了HoAl-Al2O3／TiAl复合材料。利用XRD和SEM分析了Ho2O3掺：枭对原位合成HoAl,Al2O3颗粒强化钛铝基复合材料显微组织的影响,探讨了稀土氧化物（Ho2O3）的细化机制。测试了力学性能。结果表明：Al—Ti—TiO2-Ho2O3系原位合成的HoAl-Al2O3／TiAl复合材料由TiAl,Ti3Al,Al2O3以及HoAl相组成;HoAl金属间化合物弥散分布于基体晶粒和Al2O3颗粒交界处,限制颗粒长大,细化基体晶粒与Al2O3,颗粒,同时提高了HoAl,Al2O3颗粒在基体中的分散度;Ho2O3的引入改善了复合材料的力学性能。     

原位钛基复合材料中TiB的生成热力学及动力学

采用自蔓延高温合成（SHS）、感应熔炼和熔模精铸相结合的方法，利用Ti—B—Al体系制备出了原位自生TiB增强的钛基复合材料。借助XRD、SEM和TEM分析了复合材料的物相和增强体的形态。结果表明：在复合材料中只存在TiB增强体和Ti，无TiAl3杂质相形成，TiB增强体呈柱状短纤维，这与其B27晶体结构有关，且增强体／基体界面清洁无杂质污染，并从热力学和动力学两方面论述了在Ti—B—Al体系中制备TiB增强体的生成机制：在Ti-B—Al体系中，Al首先受热熔化使得Ti和B相继溶解于Al液中；Ti与Al之间先行发生化学反应形成Ti—Al金属间化合物，放出的热量进一步引发了溶解于液相中的B和Ti产生高温自蔓延形成Ti—B化合物。以热力学理论分析，应最终形成TiB2，但实际上由于动力学影响，最终形成了TiB。     

Effect of adding Nb foil on joint properties of laser fusion welding for TC4 titanium and 7075 aluminum alloy

It is difficult to gain effective Ti-Al fusion welding joints due to their differences in thermal properties and the appearance of brittle Ti-Al Intermetallic Compounds (IMCs). The experiments of laser fusion welding for TC4 titanium and 7075 aluminum alloy were carried out, temperature field and ductility/brittleness, as well as chemical potential of elements, were calculated, and the effect of adding Nb foil on mechanical properties of the weld was also investigated. The results suggested that Nb atoms tend to diffuse toward Al side, which is conducive to the participation of Nb in the metallurgical reaction and contributes to forming the Ti-Nb-Al IMC layer at the interface. As the thickness of Nb foil increases, the tensile-shear force of joint climbs first but then declines, and reaches the highest value of 1663 N with 0.10 mm-thickness Nb foil, representing 58.38% enhancement compared with the non-added one. Adding Nb foil slows down the heat transfer as a blocker, and thus both the melting amount of Al and the mixing area of Ti and Al decrease. In addition, Nb alloying reduces the brittleness of the Ti-Al compound. Hence, the joint properties of titanium/aluminum are improved with the addition of Nb foil.     

Ti合金与SiC_p/Al复合材料在无压浸渗同步复合过程中的相容性

采用熔铝无压浸渗复合工艺在高体份SiCp／Al复合材料制备过程中同步复合Ti合金零部件（圆柱体）,研究了这种跨宏-微观尺度、超混杂铝基复合材料的微观组织及性能,特别是SiCp／Al复合材料与Ti合金零部件之间的相容性。结果表明,复合材料性能优异、组织致密,SiC颗粒分布均匀、无偏聚现象。SiCp／Al复合材料与Ti合金之间的界面结合非常紧密,Ti元素向铝合金基体一侧有一定距离的扩散,并且出现了可增强界面结合的连续、无缺陷的界面反应物薄层,SEM和XRD分析表明界面反应产物为Al2Ti,界面剪切强度超过200MPa,完全可以满足在复合材料中的Ti合金零部件处加工装配孔的要求。     

GH220/Ti──N/CoCrAlTaY/Al三层复合涂层的界面稳定性及其自分层行为研究

 GH220/Ti-N/CoCrAlTaY/Al三层复合防护涂层经扩散退火后，各层间结合较好，Ti-N组织稳定，Al全部扩散进入CoCrAlTaY内部，形成β-CoAl相。1000℃时效试验发现，Al内扩散导致CoCrAlTaY分层，形成7个亚层（不包括氧化膜及Ti-N膜）,其中包括3个富Ta层、2个高Al及2个正常CoCrAlTaY层。各亚层间界面随时效时间延长而趋于平直、连续、完整。在一些亚层内侧观察到Kirkendal空穴，其形成与元素的外扩散有关。分析了GH220/Ti-N界面扩散区的形成原因，建立了富Ta层形成模型。     

纤维C涂层对SiC_f/Ti6Al4V界面及拉伸性能的影响

通过对SiC纤维增强Ti6Al4V复合材料的拉伸试件断口与界面观察,研究了SiC纤维C涂层对基体与纤维元素扩散、界面反应层厚度与成分、拉伸断口的影响。结果表明,与纤维无C涂层的SiCf/Ti6Al4V相比较,有纤维C涂层的SiCf/Ti6Al4V界面结合强度较弱、反应层厚度较厚,涂层能有效防止纤维性能在复合过程中下降,提高了复合材料拉伸强度。     

高体积分数SiCp/Al复合材料高温压缩界面研究

采用无压浸渗制备出高体积分数SiCp/Al多功能复合材料。对该复合材料进行了高温(高于基体熔点)压缩实验。利用XRD和TEM观察了SiCp/Al复合材料的界面结构,分析了高温压缩对复合材料界面的影响,研究了复合材料的复合机理。结果表明:高温压缩后的SiCp/Al复合材料的界面过渡层连续且厚度均匀,过渡层宽度减小了一个数量级;复合材料SiCp/Al界面结合机制包括扩散、位向和反应结合机制,复合材料SiCp/Al界面的这些结合机制,导致了增强相与基体之间很强的界面结合;复合材料的断裂方式为颗粒断裂,SiC增强颗粒与Al基体结合良好。     

原位反应合成Nb掺杂Al2O3/TiAl复合材料的显微结构分析

利用Al-Ti-TiO2体系原位反应合成了Nb掺杂Al2O3／TiAl复合材料。借助XRD和SEM研究了Nb掺杂Al2O3／TiAl的显微结构以及Nb引入量对复合材料显微结构的影响。结果表明，复合材料由TiAl、Ti3Al、Al2O3、Nb和NbAl3相构成，细小Al2O3颗粒分布于基体晶粒交界处，存在一定的团聚；Nb元素引入量的高低，可调节产物中TiAl和Ti3Al的相对含量，随Nb含量的增大，TiAl含量逐渐减少，Ti3Al则逐渐增大；同时，基体晶粒和Al2O3颗粒均有所细化，且分布逐渐均匀，材料的均匀性得到改善。     

Z-pin 点阵分布对层合板面内压缩性能的影响简

 Z-pin三维增强技术能显著提高层合板层间性能,但会一定程度上引起层合板面内性能劣化。本文着重研究Z-pin植入点阵分布对层合板的面内性能的影响,设计加工了在层合板中植入一定体积分数不同点阵分布的Z-pin增强层合板试样,并进行了面内压缩性能测试,获得了Z-pin的点阵分布对层合板面内压缩强度的影响规律,并利用有限元软件分析了Z-pin点阵分布对面内压缩强度的影响机制。研究表明,Z-pin的植入降低面内压缩强度的原因是其破坏了层合板中的部分承载纤维,层合板的压缩强度与垂直于加载方向截面上的Z-pin分布数量成反比;在层间增强要求允许条件下,Z-pin应尽量平行于面内载荷的承载方向植入。     

Z-pin点阵分布对层合板面内压缩性能的影响

Z-pin三维增强技术能显著提高层合板层间性能,但会一定程度上引起层合板面内性能劣化。本文着重研究Z-pin植入点阵分布对层合板的面内性能的影响,设计加工了在层合板中植入一定体积分数不同点阵分布的Z-pin增强层合板试样,并进行了面内压缩性能测试,获得了Z-pin的点阵分布对层合板面内压缩强度的影响规律,并利用有限元软件分析了Z-pin点阵分布对面内压缩强度的影响机制。研究表明,Z-pin的植入降低面内压缩强度的原因是其破坏了层合板中的部分承载纤维,层合板的压缩强度与垂直于加载方向截面上的Z-pin分布数量成反比;在层间增强要求允许条件下,Z-pin应尽量平行于面内载荷的承载方向植入。     

C_f/SiC复合材料与Ti合金的AgCuTi-W复合钎焊

本文利用AgCuTi-W复合钎料作中间层,在适当的工艺参数下真空钎焊Cf／SiC复合材料与Ti合金,利用SEM,EDS,XRD分析接头微观组织结构,利用剪切试验检测接头力学性能。研究结果表明：钎焊时,复合钎料中的Ti借助Cu-Ti液相与Cf／SiC复合材料反应,在Cf／SiC复合材料与连接层界面形成Ti3SiC2,Ti3Si和少量TiC化合物的混合反应层。复合钎料中的Cu与Ti合金中的Ti发生互扩散,在连接层与Ti合金界面形成不同成分的Cu—Ti化合物过渡层。钎焊后,形成W颗粒强化的致密复合连接层,W颗粒主要分布在Cu-Ti相中。W的加入缓解了接头的残余热应力,Cf／SiC／AgCuTi—W／TC4接头剪切强度明显高于CF／SiC／AgCuTi／TC4接头。     

PAXD法制备TiB/TiAl基复合材料及其力学性能研究

利用Al-Ti-B体系的放热反应,通过压力辅助放热弥散法(PAXD),原位合成了TiB/TiAl基复合材料.借助XRD,SEM分析了TiB/TiAl复合材料微观组织及并测试了其力学性能,探讨了TiB增强增韧TiAl金属间化合物的机制.研究结果表明:其增强相为TiB,基体相为TiAl和Ti3Al.TiB增强体主要以颗粒状、板状及细棒状均匀分布在基体中,其尺寸范围为亚微米级.复合材料的弯曲强度及断裂韧度较二元的TiAl金属间化合物有很大的提高.原位合成TiB/TiAl复合材料主要强化机制有:弥散强化、热膨胀合理失配强化机制、晶须(晶棒)强化.     

Al_2O_3/TiAl 复合材料的原位合成、结构与性能研究(英文)

以 Ti, Al, TiO2和 Nb2O5混合粉为原料,采用热压反应合成技术制备了 Al2O3/TiAl 复合材料。对复合材料的微观组织与力学性能进行了研究。结果表明:产物由γ-TiAl, α2-Ti3Al, Al2O3和 NbAl3相组成。原位反应形成的细小 Al2O3粒子主要分布在基体晶界处。随着 Nb2O5含量的增加,晶粒明显细化,Al2O3粒子呈弥散分布在基体中。最终形成了由γ和γ α2构成的特殊组织。随着 Nb2O5含量的增大,复合材料的硬度逐渐增大,抗弯强度和断裂韧性在 Nb2O5含量为 6 wt%时达到最大,分别为 398.5 MPa 和 6.99 MPa·m1/2。     

一种准确预测层合梁结构层间剪应力的新锯齿理论

层合梁是航空航天领域典型的承力构件,而过大的层间剪应力（层间处的横向剪应力）是导致其分层失效的主要原因。针对常见的层数较多的复合材料层合梁以及材料属性差异较大的三明治夹层梁,现有的理论模型仍然无法准确预测其横向剪应力。通过构造一个新的线性分段锯齿函数,提出了一种能够准确预测层合梁结构横向剪应力的新锯齿理论模型。几个典型的数值算例表明,本文提出的新锯齿理论模型在计算层数较多和材料属性差异较大的层合梁时,具有较高的计算精度,能够准确预测层合梁的分层。另外,该模型预先满足横向剪应力层间连续条件,无需三维平衡方程后处理就能够准确预测层合梁的横向剪应力。位移场中未知量个数少,不含横向位移的一阶导,便于C⁰梁单元的构造。     

热暴露对B/Al复合材料性能的影响

对经300℃、500℃高温热暴露的B／Al（LF6）复合材料的力学性能进行了研究，实验结果表明材料在300℃下热暴露时，性能下降速度较慢，100h后强度保留率约为76％，延伸率保留率为74％。而在500℃下热暴露时，5h以上强度就有明显降低。高温长时间热暴露后复合材料的断裂也从积累型转变为典型的非累积型断裂。通过透射电镜（TEM）及扫描电镜（SEM）对固态热压制造态和主温热暴露的界面状况进行了分析，认为界面反应是造成B／Al复合材料力学性能下降的主要原因。