纤维铺层方式对CFRP?铝合金单搭接胶接接头拉伸性能影响

为了分析异质材料胶接接头内部典型应力分布规律与刚度退化特点,探究不同铺层方式对异质材料单搭接胶接接头内部应力分布状态影响规律,开展试验和仿真相关研究。首先,制备不同铺层方式的CFRP（carbon fiber reinforce plastic）?铝合金单搭接胶接接头试验件,使用拉伸试验机进行拉伸试验,获得基本试验数据。其次,利用连续损伤模型、3D Hashin失效判据和Cohesive Zone Model研究异质材料胶接接头不同部位典型破坏特点。结果表明,随着复合材料板中0°铺层比例增加,胶接接头极限载荷呈现增加趋势,与之相反接头拉伸位移逐渐缩短。接头铺层方式与载荷方向共同影响胶接接头力学性能,当复合材料板内部各个方向纤维铺层较为均匀时,可以有效降低接头应力集中,载荷方向与铺层纤维方向一致时,可有效提高接头连接强度。复合材料板中0°铺层占比对接头的极限载荷和刚度退化（scalar stiffness degradation,SDEG）影响较大,0°占比越小接头承载能力越弱,接头刚度退化越复杂。      

复合材料双搭接接头拉伸强度研究

对不同胶层厚度的复合材料双搭接接头拉伸强度进行了试验研究,结果表明接头的破坏模式是胶层剪切破坏,并且接头的极限强度随胶层厚度的增加而增大。在此基础上建立解析模型对复合材料双搭接接头胶层剪切破坏进行研究,模型中考虑了复合材料层板单层的各向异性及胶层的理想弹塑性材料属性,通过与有限元模型计算结果进行对比,验证了解析模型在计算胶层剪切应变/应力分布时的有效性。解析模型使用最大剪切应变准则计算接头的极限拉伸强度,计算得到的接头极限强度与试验结果吻合良好。     

复合材料胶接搭接接头应力分析方法研究

胶接是复合材料结构主要连接方法之一,对胶接接头进行应力分析是保证复合材料安全性、耐久性的关键。在初步设计阶段,一般采用解析方法对胶接接头进行应力分析及参数研究。针对复合材料双搭接和单搭接胶接接头,在Tsai等人的理论分析方法（TOM方法）基础上,提出了一种改进的搭接接头剪应力分析方法,该方法考虑了被胶接件的剪切变形,认为被胶接件只有在靠近胶层的半个厚度上产生剪切变形,剪应力沿该半厚度呈线性分布。算例分析结果表明：本文方法比现有的分析方法更接近于有限元模拟结果,可用于估算复合材料胶接接头剪应力分布。     

复合材料沉头双钉单搭接连接静强度分析

对复合材料沉头双钉单搭接机械连接接头进行了静态拉伸试验,并建立了三维有限元模型,编写了材料失效准则和刚度退化准则的累积损伤程序,计算了连接孔的挤压应力和接头损伤,预测了连接的失效载荷。数值计算表明:单搭接产生的附加弯矩使孔边应力沿板厚呈三角形分布;孔边挤压损伤和螺帽的侧向压缩损伤以及极限载荷与试验结果吻合;位于搭接板自由端的钉孔弯曲变形较小,应设计为沉头孔。     

胶接修复对碳纤维复合材料层合板挠度的影响

为了研究胶接修复对碳纤维复合材料层合板弯曲挠度的影响，试验设置了阶梯搭接和斜面搭接两种搭接方式，通过三点弯曲实验和数字图像相关技术（DIC）来研究胶接接头的弯曲变形情况。结果表明，在相同搭接长度下，阶梯搭接试件的失效载荷和弯曲强度均低于斜面搭接试件；试件的弯曲挠度与强度和搭接长度有关，搭接长度越长，弯曲强度越高，而弯曲挠度越小。由此表明，搭接长度越长，胶接层合板的强度越高，但不利于层合板的柔性变形。     

胶粘剂弹性模量对铝合金单搭接接头应力应变分布的影响

利用弹塑性有限元法研究胶粘剂的弹性模量对单搭接接头应力应变分布的影响.结果表明,随着弹性模量的增加,接头的应力峰值逐渐增大,并由胶层向胶瘤转移,其刚度越大,应变越小.低弹性模量胶粘剂的接头,载荷主要由胶层承担,胶层受力很均匀,而胶瘤的作用很小,胶瘤并没有很大地降低胶层中的应力峰值.高弹性模量胶粘剂的接头,胶瘤的作用很大,承担了很大一部分载荷,而胶层中部受力很不均匀.     

间隙连接对胶接接头应力分布和强度的影响

运用弹塑性有限元法结合实验研究了连续和间隙连接的单搭接接头应力分布规律，并考虑了胶瘤的影响。结果表明，在相当大间隙长度范围内和适当的间隙位置条件下，间隙连接接头并没有大幅度地减小其承载能力，相反其有效搭接区域剪切强度呈明显升高趋势；胶层应力峰值仍然发生在搭接末端；胶瘤承担了相当大的载荷作用；过大的间隙长度以及不当的间隙位置会导致胶层靠近间隙端应力集中明显加剧，成为新的高应力区，可能导致接头破坏模式的改变。实验结果与数值分析结果很好地吻合。     

复合材料层合板单搭接机械连接横向力研究

在复合材料单搭接连接结构中,由于载荷的偏心作用,在搭接处产生沿板厚度方向的横向力,使得接头产生横向位移并使螺栓偏转。采用试验及有限元方法对复合材料双钉单搭接机械连接中螺栓、螺母在静载荷作用下的应力进行研究,并进行结果分析。结果表明:单搭接中偏心矩在螺栓上的螺纹位置产生较大的应力,使螺栓发生断裂破坏;在螺母中产生较大的弯曲应力,使螺母发生破坏;在连接区两端对层合板施加横向约束能够有效降低螺栓、螺母中的应力幅值;计算结果与试验破坏模式吻合。     

TC4 钛合金扩散焊接头剪切疲劳性能研究

为了研究钛合金扩散焊接头在航空航天领域焊接性能的稳定性，制备了双搭接形式的接头试样，在温度为 910 ℃、压力为 3.4 MPa 条件下对 TC4 钛合金板材进行扩散连接，并对双搭接接头试样开展静强度试验，获得试样在焊缝界面处的平均剪切强度约为 199.4 MPa，试样断裂前后接头没有发生明显的塑性变形。此外，对双搭接接头试样还开展了不同载荷水平下的疲劳性能试验。结果表明：疲劳试样存在3种不同破坏模式。在高载荷水平下，试样会在切应力主导下发生基板与搭接板的完全脱焊；在低载荷水平下，试样会在正应力主导下发生基板沿厚度方向的断裂；在中等载荷水平下，试样先发生局部脱焊随后沿基板厚度方向断裂。 在上述失效模式分析的基础上，结合疲劳寿命试验数据分别得到接头的正应力 - 寿命和切应力 - 寿命曲线。     

复合材料单搭胶接接头静力与疲劳裂纹扩展研究

胶层裂纹是复合材料胶接接头的常见损伤形式之一,严重影响复合材料结构的完整性。以胶接结构中常见的复合材料单搭胶接接头为研究对象,建立其三维数值模型,采用双线性内聚力本构关系表征静态裂纹扩展,并将静态模型扩展至疲劳裂纹扩展模型;结合静力与疲劳试验,对单搭胶接接头的应力应变分布规律、裂纹扩展与破坏机理展开研究。结果表明：单搭胶接接头在静力和疲劳载荷下,由于偏心拉伸应变呈非线性变化,搭接区域两端由于应力集中首先出现裂纹,由两端向中央区域扩展并迅速贯穿整个搭接区域,静力失效模式为内聚破坏,疲劳断面为界面脱胶。     

Mechanical behaviour of adhesively single lap joint under buckling conditions

Adhesive Single Lap Joints have been subjected to tensile and bending investigations by many researchers. However, the joint is also likely to experience buckling loading in some aerospace applications. The aim of this work is to investigate the joint behaviour under quasi-static buckling conditions. For this purpose, the joints with three different adherend thicknesses and 25 mm overlap length were tested using two different types of adherends and an adhesive film. They were modelled using a non-linear Finite Element Method via the ABAQUS Explicit package programme. Load to failure and stress distributions in the joints were predicted and compared with the experimental results, which were found in a good agreement. The adhesive layer in the joint was assumed to experience shear stresses under the buckling mode, similar to that in tensile loading, yet, the stress concentrations at the ends of the overlap, the main cause of the failure, resulted in different effects on the joint performance; for the buckling mode the critical stresses were in compression but for the tensile case in peeling. Unlike the latter, the former was found to prevent failure of the layer depending on the adherend thickness, causing different failure mechanisms. There were two different failure modes of the joints; a complete failure in the adhesive layer and large plastic deformation of adherends which could be a good source for crashworthiness situations. Mechanical properties of the adherends were found to play important roles on the joint performance.     

Tensile properties analysis of CFRP-titanium plate multi-bolt hybrid joints

Hybrid joints have better tensile properties than pure bonded and bolted bolts, and are increasingly used in the aerospace field. Tensile tests are carried out for the Hybrid Bonded/Bolted(HBB) joints of Carbon Fiber Reinforced Polymer(CFRP) laminate and titanium alloy plate under different bolt numbers, and the corresponding load–displacement curves are obtained. At the same time, based on Continuum Damage Mechanics(CDM) theory, which is derived from 3D Hashin failure criteria, and a Cohesive Z...     

Z-pin增强树脂基复合材料单搭接连接性能

为提高复合材料单搭接头的连接性能,制备了不同参数的Z-pin增强单搭接头,通过拉伸试验,研究了Z-pin体积分数、直径以及植入角度对单搭接头连接性能的影响规律,分析了Z-pin对单搭接头性能的增强机理。结果表明Z-pin能明显提高复合材料单搭接头的连接性能：植入角度为90°、Z-pin直径为0.5 mm时,在0%~3.0%体积分数范围内,单搭接头强度随着Z-pin体积分数的增加呈线性增加,含3.0% Z-pin的接头剪切强度为16.76 MPa,比无Z-pin的接头强度提高了33.2%;Z-pin体积分数为1.5%、植入角度为90°时,Z-pin直径变化对单搭接头强度影响不大;含Z-pin体积分数为1.5%、直径为0.5 mm时,随着Z-pin植入角度（背离搭接末端）的增加,单搭接头强度先增加后下降,失效模式从Z-pin拔出失效转变为Z-pin剪断失效;在植入角度为40°时,剪切强度最大（21.04 MPa）,比无Z-pin的接头剪切强度提高了67.1%。Z-pin植入角度（倾向于搭接末端）对单搭接头强度无影响。     

纤维增强树脂基复合材料连接结构强度与失效分析

采用拉伸试验和有限元分析方法研究纤维增强树脂基复合材料螺栓连接与胶–螺混合连接结构的失效机理。通过拉伸–剪切试验分析其载荷–位移曲线,结合有限元仿真结果及断面微观结构变化分析其结构强度和失效机理。结果表明,螺栓连接结构孔周碳纤维丝束受到螺栓挤压力变形后传递给树脂基体。因此,呈现纤维屈曲变形,树脂基体由均匀分布状被断裂的纤维短束挤压变成团簇状,形成结构不均匀而出现薄弱区域。胶–螺混合连接结构呈现拉伸断裂式破坏,断口处碳纤维丝束在拉伸–剪切作用下从环氧树脂基体中拔出并损伤断裂,丝束方向杂乱排布。附着在碳纤维丝束周围的树脂基体从均匀分布状变为团聚状,连接结构在达到极限载荷之后出现拉伸断裂,呈现净截面破坏,并且在重新分配载荷之后板材之间的胶粘剂对纤维的破坏会起延滞作用。材料强度、螺栓强度、胶层强度及螺栓宽径比等因素均会成为影响连接结构失效破坏的因素。     

胶粘剂力学性能参数对劈裂载荷作用下胶接接头中应力分布的影响

运用三维有限元法分析了胶粘剂力学性能参数对劈裂载荷作用下胶接接头(简称劈裂接头)应力分布规律的影响.结果表明:胶粘剂弹性模量和泊松比的变化对劈裂接头应力分布有着直接影响;随着弹性模量或泊松比升高,胶层内应力分布重心向左端移动,左端应力集中加强,峰值应力上升,但是泊松比对胶层最大主应力峰值的影响不如弹性模量的影响明显.     

胶粘剂弹性模量对间隙接头应力和强度的影响

 运用弹塑性有限元法,研究了胶粘剂弹性模量对含间隙的铝合金单搭接接头的影响。通过分析胶层和被粘物的应力分布,结果表明：间隙连接对接头端部的应力分布无明显影响,但对间隙附近的应力峰值影响较大;随着胶粘剂弹性模量的增大,间隙附近的应力峰值反而减小;对于高弹性模量胶粘剂接头,间隙对接头的应力峰值无明显影响,在不降低接头名义强度的基础上极大地提高了接头的实际强度;而对于低弹性模量胶粘剂接头,间隙使得接头的应力峰值明显上升,显著地降低了接头的名义强度和实际强度。数值模拟结果与已发表的试验数据大致吻合。