适应高压燃烧的HTPB/AP/Al推进剂用钙盐降速剂研究

研究了碳酸钙(CaCO_3)和一种自制钙盐(CaOr)对HTPB/AP/Al推进剂燃烧性能和常温力学性能的影响,采用DSC-TG和SEM方法对比研究了CaOr、CaCO_3对AP热分解的影响,及含两种化合物的推进剂熄火表面形貌。结果表明,在3~17 MPa压强范围内,CaCO_3和CaOr均能有效降低HTPB/AP/Al推进剂的燃速和压强指数,CaOr比CaCO_3具有更好的燃速抑制效果,在高压段内的压强指数可降为0.17,达到平台推进剂水平。CaOr的加入使AP两个阶段的分解放热峰均向高温方向移动,CaCO_3对AP的低温分解峰没有影响,使AP的高温分解峰推迟。CaOr的降速效果优于CaCO_3的主要原因是其推迟了AP的低温分解峰,同时改变了AP的热分解历程,且在凝聚相中的分散性更好。     

复合固体推进剂燃面上复盖分数的确定

本文基于PU/AP和HTPB/AP复合固体推进剂在不同压力下中止燃烧的燃面采用X射线光电子能谱的测试结果,对燃面上氧化剂AP颗粒表面受熔化粘合剂复盖的面积分数进行了半定量计算。结果表明,在燃烧压力大于1.96MPa时,两种推进剂燃面上的粘合剂复盖分数,随压力上升而增加。这一结果将有助于复合固体推进剂稳态燃烧模型的深化和改进。     

降速剂对低燃速NEPE推进剂高压燃烧性能的影响

添加降速剂和调节RDX/AP含量是调节NEPE推进剂燃速的两种常用途径。采用水下声发射燃速测试仪、密闭燃烧器、BSF φ75 mm发动机等测试方法,研究了低燃速NEPE推进剂静态高压燃烧性能规律和发动机动态高压燃烧稳定性。研究发现,NEPE推进剂的中低压区燃速随着降速剂含量增大而显著降低,高压区燃速降低幅度相对较小,燃速-压强(r-p)曲线在15 MPa和45 MPa出现两个拐点,而且降低RDX含量对降低高压段燃速作用显著。BSF φ75 mm发动机试车结果表明,低RDX含量的C1配方(28%)最大工作压强不超过20 MPa,而高RDX含量(38%)的C4配方最大工作压强达到30 MPa。发动机稳定燃烧的最大压强随NEPE推进剂的燃速降低而下降,主要原因是低燃速推进剂铝粉燃烧效率降低使凝聚相燃烧产物含量和粒度增大。     

HMX/RDX粒度对硝胺推进剂高低压燃烧特性的影响

采用水下声发射法测试推进剂药条不同压强下的燃速,按维也里公式r=bpn计算某压强段的压强指数n,研究了含不同粒度HMX、RDX的硝胺推进剂高低压燃烧性能。结果表明,在低压段(3~9 MPa),无论粒度大小,相对无硝胺推进剂配方,n值均降低;在高压段(15~20 MPa),推进剂n值与硝胺粒度呈指数关系,粒度越小,n值越低;含硝胺的推进剂存在一个压强点,其与硝胺粒度有关,低于该压强点时推进剂燃速是细粒度硝胺高于粗粒度硝胺的,高于该压强点则反之;对20 MPa下,推进剂燃速与硝胺粒度呈非线性二项式关系,粒度越大,燃速越大。     

高压强指数NEPE推进剂研究

分析了AP含量、增塑荆含量、催化剂种类、含能粘合剂体系等对NEPE推进剂燃烧性能的影响,找出了提高其燃速压强指数的有效方法.同时,采用DSC、单幅摄影、燃烧波测试等方法,研究了ZH-2催化NEPE推进荆的机理.实验结果表明,NEPE推进剂燃速压强指数提高至0.67,同时在宽压强(1.5～30 MPa)范围内消除了压强指数拐点.     

复合燃速调节剂对NEPE推进剂高压燃烧性能的影响

利用DSC-TG联用和燃速测试等方法,从降低CMDB推进剂和AP类复合推进剂压强指数的燃速调节剂中,筛选出了纳米PbO、QC、C及SEA、Fe2O3、Co3O4等燃速调节剂,并考察了这些燃速调节剂对NEPE推进剂燃烧性能的影响。通过分析两类燃速调节剂发挥作用的主要压强区间及其对推进剂燃速的影响趋势,对两类燃速调节剂进行了复配研究。试验结果表明,复合调节剂ZH-2(由纳米过渡金属氧化物、铅/铜盐等复配而成)使NEPE推进剂高压(10~25 MPa)燃速压强指数由0.78降低至0.62,而且在宽压强范围内消除了压强指数的拐点。     

GAP/CL-20高能固体推进剂燃烧性能影响因素

采用水下声发射法测试了推进剂静态燃速,用线性回归法计算了推进剂燃速压强指数;研究了GAP/CL-20高能固体推进剂中增塑比及固体组分AP、CL-20、Al粉粒度等配方组成因素对燃烧性能的影响。研究结果表明,增塑比一定范围内的变化不会对推进剂燃烧性能产生显著影响,其燃速和燃速压强指数基本不变;CL-20粒度减小或AP粒度增加均会导致燃速不同程度的降低,Al粒度减小也会使燃速减小,但在达到一定程度后,燃速又增加;推进剂燃速压强指数随CL-20、Al粉粒度减小和AP粒度增加而减小,并对其燃烧性能的影响机制进行了简单分析。     

镁铝富燃料推进剂燃烧性能研究

为了研究镁铝富燃料推进剂燃烧性能,采用捏合机混合物料、真空浇注、恒温固化的方法制备推进剂试样,用靶线法测试推进剂燃速(0.5~2.0 MPa),用Vieille经验公式r=apn计算压强指数。研究表明,细粒度AP含量增加,燃速逐渐增加,而压强指数先升高后降低。采用复合催化剂GFP/Fe2O3可同时提高燃速和压强指数。当催化剂质量含量为5%时,改变GFP/Fe2O3比对推进剂的燃速及压强指数的影响与氧化剂AP级配有关。对于细粒度AP含量高的配方,GFP/Fe2O3对燃速和压强指数影响较大。金属含量对燃速影响较大,对压强指数影响很小。而Mg/Al比对燃速和压强指数影响都很小。随着氧化剂中KP含量增大,燃速呈下降趋势,压强指数先升高后下降。     

含SrCO3低燃速HTPB推进剂燃烧压强温度敏感特性研究

针对含SrCO3低燃速HTPB推进剂的燃烧特性，进行了不同压强或初温条件下的燃速测量、近距单幅摄影及CCD图像采集、SEM-能谱分析、TG—DTG分析等实验研究。结果表明：SrCO3的使用可显著降低推进剂的燃速压强指数和温度敏感系数；压强因素比初温条件对燃烧火焰形貌的影响大；高、常温熄火表面元素皆发生聚集，但在不同温度下熄火，元素的含量及各元素重叠的相对位置发生改变；添加SrCO3会让AP的分解峰向高温方向移动，抑制AP的分解并降低燃速，导致AP的两分解峰之间失重速率与热释放量增加，使凝相燃烧表面温度升高，燃速温度系数降低。     

GAP微烟推进剂的燃烧性能影响因素研究

通过配方组分对GAP推进剂燃烧性能影响的分析,确定了影响GAP微烟推进剂燃烧性能的主要因素,并在此基础上研究了推进剂燃烧性能的变化规律,通过选择合适的增塑剂、调整AP和HMX的相对含量及AP粒度级配,可使推进剂基础配方静态燃速在6 MPa下达到10.5～12.0 mm/s,3～10 MPa下静态压强指数可降至0.40以下。     

Mechanism of steady-state burning of composite solid propellants including those with negative pressure-exponents

The mechanism of steady-state burning of AP-based composite solid propellants has been studied by means of single-frame microphotography with self-illumination or laser-shadow for the observation of the burning samples and scanning electron microscope for the examination of extinguished combustion strands. It has been found that covering of the molten binder over the oxidizer surface is not a particular phenomenon of PU propellants in the mesa-burning region, but a general phenomenon taking place under quite extensive circumstances. The experimental results also indicated that the local covering may not result in local extinction and features of the propellant combustion in the mesa-region are quite analogous to those of pure AP crystal deflagrating in the Regime III. A new theoretical model has been further developed, in which the existence of the covering of molten binder over oxidizer surface has been taken into consideration. And in analysing the part of AP surface covered with molten binder, the condensed-phase reaction and opposed gasification of covered AP are considered. The model developed for AP-based composite solid propellants can be used to explain plateau, mesa and normal burning features and to analyse the effects of initial temperature and AP particle size on burning behaviors.     

氧化剂和团聚硼粒度对富燃料推进剂燃速特性的影响

考察了细AP和团聚硼含量对含硼富燃料推进剂燃速特性的影响.结果表明,随细AP含量和团聚硼含量的增大,推进剂燃速增加,燃速压强指数也呈增加趋势.同时,以BDP模型为基础,将硼粒度对推进剂燃速特性的影响引入燃速表达式,表达式表明细AP和团聚硼有利于提高氧化剂的燃烧表面积在燃面上的比例,从而有利于提高推进剂的燃速.     

纳米NdCoO3对小球粘接高燃速推进剂燃烧性能的影响

采用盐助溶液燃烧法制备了平均粒径为10 nm、分散性良好的钙钛矿型纳米NdCoO3。用DSC考察了不同质量分数的纳米NdCoO3对AP和双基粘接剂热分解的影响,研究了纳米NdCoO3对小球粘接高燃速推进剂燃烧的催化作用。结果表明,随纳米NdCoO3催化剂质量分数的增加,催化效率先增大后减小,在质量分数为3%时催化效率最佳,此时AP高温分解峰温大幅降低,双基粘接剂的分解峰温也得到降低,二者的表观分解热增大。同时,对应的小球粘接高燃速推进剂燃速较高,压强指数较低。     

AP-CMDB推进剂燃速压强指数的变化分析与辨识

采用燃烧模型分析了AP-CMDB推进剂的燃速压强指数与推进剂配方组成和火箭发动机燃烧室压强之间的耦合关系．指出了该推进剂的燃速压强指数随AP颗粒和双基母体的燃速差而变化,对于确定配方组成的AP-CMDB推进剂,则该指数将主要随压强而变化,且近似呈对数关系。采用C-K法对特定配方进行了压强指数辨识,辨识结果能够较准确地预示脉冲推力器的内弹道性能。     

含硼富燃料推进剂低压燃烧模型

针对含硼富燃料推进剂低压燃烧的凝相反应和气相燃烧具有气相反应在燃面上的惰性“沉积层”中进行、气相放热主要由AP与HTPB分解产物的扩散燃烧产生的特点,以BDP模型为基础,建立了含硼富燃料推进剂低压燃烧模型,分析了“沉积层”对气相燃烧的影响。结果分析认为,“沉积层”的存在是含硼富燃料推进剂能在较低压强下维持稳定燃烧,并具有较高燃速和压强指数的主要原因。燃烧模型实质是对BDP模型的拓展,利用该模型定性解释了含硼富燃料推进剂低压下特有的燃烧现象。     

NEPE推进剂主要组分催化分解的研究

应用原位红外光谱仪研究了NEPE推进剂主要组分HMX、AP、NG及聚醚胶在升温至爆燃过程中,凝聚相红外光谱的变化。并研究了对NEPE推进剂提高燃速明显的YB2-450和降低压强指数效果较好的B2Pb两种催化剂对上述分解过程红外谱图的影响。发现B2Pb主要催化了HMX的分解,YB2-450主要催化了NG的分解,YB2-450还可在高温下加速AP的分解。这些结果为解释NEPE推进剂的燃烧特性提供了一定的试验依据。     

团聚硼对富燃料推进剂燃烧性能的影响

考察了不同粒度、不同包覆剂的团聚硼对含硼富燃料推进剂燃烧性能的影响。结果表明,随团聚硼颗粒粒度的增大,推进剂的燃速增加,低压可燃极限降低,但燃速压强指数呈下降的趋势;包覆材料AP、L iF有利于提高推进剂的燃速,降低低压可燃极限,但不利于提高燃速压强指数。