钛合金TC4盘铣开槽加工铣削力研究

由于盘铣刀具直径大,切削余量大,造成钛合金盘铣开槽过程中铣削力较大,进而引起刀具振动,缩短刀具寿命。为实现对钛合金盘铣开槽过程的优化与控制,本文设计单因素实验和正交实验,利用三向压电式测力仪测量铣削力数据,采用线性回归技术建立铣削力模型并以“F”检验法对模型进行显著性检验;利用极差分析法分析工艺参数对铣削力的影响规律,利用响应曲面法分析工艺参数对铣削力的交互影响规律。研究结果表明：对于切削深度变化敏感度依次为铣削力F_x＞进给速度＞主轴转速;对于进给速度变化敏感度依次为铣削力F_y＞切削深度＞主轴转速;对于铣削力F_z变化敏感度依次为主轴转速＞切削深度。铣削力随着主轴转速的增大而减小,随着切削深度和进给速度的增大而增大。另外铣削力F_x大于F_y和F_z,对加工性能和刀具磨损起主导作用。     

微小型车铣加工表面粗糙度分析及预测模型建立

随着尖端科学技术和国防工业的不断发展,微小型车铣加工技术作为一种先进的切削加工方法被广泛应用在军民制造领域。为获得微小型正交车铣加工参数引起的零件表面粗糙度的变化规律,以高效车铣复合加工机床正交车铣轴类零件的表面粗糙度为研究对象,采用三水平五因素正交实验分析法和多元线性回归预测法,重点研究了车铣加工参数与表面粗糙度之间的关系、车铣加工参数与表面粗糙度预测模型数值关系。结果表明,采用相同刀具下正交车铣加工轴类零件,其工件尺寸、车削主轴转速、工件进给量、铣削主轴转速和切削深度依次从大到小影响零件表面粗糙度质量,可指导高效车铣复合加工机床的加工工艺参数优化。     

GFRP铣槽加工铣削力及表面粗糙度研究

铣槽是复合材料较常用的机械加工形式之一。为研究玻璃纤维增强复合材料(Glass Fiber Reinforced Plastic,GFRP)铣槽加工中各加工参数对铣削力和表面粗糙度的影响,开展了以主轴转速、进给速度和轴向切深为因素的正交试验,研究铣削力和表面粗糙度的变化规律。并用Matlab软件对铣削力和表面粗糙度的试验数据进行回归分析,建立了铣削力和粗糙度的经验公式,最后通过试验验证铣削力和表面粗糙度经验公式的正确性。结果表明:轴向切深对铣削力影响最大,其次是主轴转速,进给速度对铣削力影响最小;主轴转速对粗糙度的影响最大,其次是进给速度,轴向切深对粗糙度的影响最小。试验结果与铣削力、表面粗糙度经验公式算得的数值对比,误差范围都在20%以内。     

TC4钛合金侧铣加工表面形貌分析及工艺参数优化

TC4钛合金是 1种典型的不易加工材料,其切削加工表面质量很难控制。为实现面向侧铣加工表面形貌的切削工艺参数优选,开展了 TC4钛合金侧铣加工实验研究。首先,探究了加工表面微观缺陷特征及其形成机制;然后,采用粗糙度参数 Ra和 Sa对铣削表面形貌进行定量表征,并分析了切削速度、进给量和切削深度对表面粗糙度参数的影响;最后,基于遗传算法(Genetic Algorithm,GA)对铣削工艺参数进行了优化。研究发现,加工表面微观缺陷主要有进给刀痕等固有缺陷和黏附颗粒等随机缺陷。铣削表面粗糙度随主轴转速的增大先减小后增大;随径向切深的增大先增大后减小;随进给量先增大后减小。在主轴转速 n = 1 093 r/min、径向切深 ae = 0.2 mm、每转进给量 f = 0.06 mm/r的条件下可以获得较小的表面粗糙度。     

单晶硅超精密切削工艺参数优化与实验研究

为提高单点金刚石车削单晶硅的表面质量,以表面粗糙度为优化目标,设计正交切削实验,过方差分析、响应曲面分析和极差分析研究主轴转速、进给速度和切削深度对表面粗糙度的影响。结果表明：主轴转速对表面粗糙度影响显著,其贡献率最大,主轴转速越大,表面粗糙度值越小;建立表面粗糙度回归模型,主轴转速和进给速度的交互作用对表面粗糙度的影响最大;获得最优切削参数组合,即主轴转速3 300 r/min,进给速度2 mm/min,切削深度5 µm。在此切削条件下,获得了表面粗糙度Ra 2.7 nm的高质量单晶硅元件,在扫描电镜下观察其表面相对光滑,切屑呈带状,材料在延性域内去除。     

铣削参数对GH4169高温合金表面完整性的影响

通过球头铣刀铣削工艺试验和表面状态测试,采用响应曲面法研究了铣削参数对GH4169高温合金表面完整性的影响,建立了表面粗糙度和表面残余应力预测模型,获得了铣削后GH4169高温合金表层微观力学和微观组织分布。结果表明：表面粗糙度与每齿进给量和铣削深度呈正相关,表面残余压应力与铣削深度呈正相关,与进给量呈负相关,随着铣削参数水平的增大,铣削表层趋向于残余拉应力状态;表层出现加工硬化现象,铣削参数水平的增大使得硬化层加深,最大硬化层深度约为65 m;近表层晶粒被切断破坏,发生了塑性流动,塑性变形层深度在10～25 m范围。     

碳/ 碳复合材料机械加工残余应力实验研究与规律分析

采用适宜于测试复合材料的残余应力测试方法——钻孔法,通过二次通用旋转组合设计实验,采用电镀金刚石刀具铣磨加工碳/碳复合材料,选取切削深度、切削宽度、切削速率、进给量四个因素进行实验.实验结果分析表明,回归得到基于二次多项式的数学模型,进一步分析了残余应力随各加工参数的变化规律,整体寻优得到了残余应力的极值.研究表明,铣磨加工碳/碳复合材料,残余应力皆为压应力.伴随着切削速率的增长,残余应力存在渐进值.本次实验中,残余应力趋于-16 MPa稳定.伴随着切削宽度、切削深度、进给量的增大,机械加工残余应力表现为先增大后减小(压应力即残余应力的绝对值先减小后增大).本次实验中,各加工参数的变化分界点分别为:切削宽度aw=6mm;切削深度ap=0.5 mm;进给量f=200 mm/min .     

γ-TiAl合金铣削加工表面残余应力研究

为了探索高温理想结构材料γ-Ti Al合金铣削表面残余应力特性,结合正交试验数据处理方法中的极差分析法,建立各工艺因素情况下不同水平对表面残余应力的关系曲线,并对其工艺过程中的热力影响机理进行分析;同时建立面向残余应力的各因素灵敏度数学模型,进而确定以获取较大残余压应力为目标的工艺参数优选区间。研究表明:在试验参数限定范围内,步进方向以及进给方向均呈现为残余压应力,主要原因是冷塑性变形占主导作用。通过对灵敏度数学模型进行分析,发现残余应力对设计变量中的铣削速度变化最敏感,对每齿进给量、铣削深度和铣削宽度的敏感程度近似相同,为Ti Al金属间化合物铣削表面残余应力控制研究提供了理论依据。     

钛合金TB6铣削参数对表面完整性的影响研究

通过TB6钛合金的侧铣加工试验,研究了工艺参数对钛合金加工表面完整性的影响规律.试验结果表明:每齿进给量的变化对加工表面形貌和粗糙度的影响最大;增大每齿进给量和铣削宽度,表面残余压应力有所增大,残余应力影响层变深,材料的硬化深度和硬化程度也有所增大;每齿进给量和铣削宽度的变化对塑性变形层的深度影响较小.     

激光辅助车削工艺参数对单晶硅表面质量的影响

为了提高单晶硅激光辅助车削加工表面质量,通过开展激光辅助和常规车削加工试验,结合表面粗糙度、表面形貌及拉曼光谱检测,研究激光辅助车削技术对加工质量的影响。基于正交试验方法,研究单晶硅激光辅助车削工艺参数对表面粗糙度的影响;通过方差分析和极差分析评估各因素对表面粗糙度的影响。研究结果表明：与常规车削相比,激光辅助车削可有效提高加工表面质量,降低材料表面的残余应力。主轴转速、进给速度、切削深度和脉冲占空比对表面粗糙度的贡献率分别为17.51%、44.48%、6.69%和14.70%。确定最佳加工参数组合如下：主轴速度为4 000 r/min,进给速度为2 mm/min,切削深度为5μm,脉冲占空比为30%,最终获得表面粗糙度Rq为2.4 nm的高质量表面。     

高速端面铣削加工引入残余压应力场的试验研究

为研究高速铣削加工表面残余应力分布,在统计试验设计指导下,使用X射线衍射/电解抛光方法对试样表层、次表层残余应力分布进行测量,得出残余应力分布曲线经验预报公式,探讨切削参数对残余压应力场特征指标的影响规律。研究结果表明,合理的高速切削工艺将在加工表面内引入类似喷丸强化效果的残余压应力场;(3,1)有理式模型与三阶多项式模型是描述高速铣削引入残余应力分布曲线的有效拟合公式;高速切削工艺参数对加工表面残余应力场的产生有直接影响,每齿进给量是决定残余压应力分布的关键因素,每齿进给量的变化将引起残余应力场形成机理的改变。     

TC17钛合金铣削刀具磨损对残余应力影响研究

为了获得高性能航空发动机用TC17钛合金材料铣削过程中刀具磨损对残余应力的影响规律,通过对不同刀具后刀面磨损量下铣削工件表层残余应力的测试,建立了刀具磨损对残余应力的影响关系,并对影响机理进行了分析。结果表明,硬质合金刀具低速铣削钛合金时,刀具对已加工表面的挤光效应引起的残余压应力占主导地位;不同刀具后刀面磨损量下,残余压应力沿深度方向先增大达到一个最大压应力值后,然后减小趋向于零应力;表面残余应力、最大残余压应力以及残余应力的影响深度都随刀具后刀面磨损量的增大呈增大趋势。     

Investigation on surface roughness,residual stress and fatigue property of milling in-situ TiB2/7050Al metal matrix composites

For higher efficiency and precision manufacturing, more and more attentions are focused on the surface roughness and residual stress of machined parts to obtain a good fatigue life. At present, the in-situ TiB₂/7050Al metal matrix composites are widely researched due to its attractive properties such as low density, good wear resistance and improved strength. It is of great significance to investigate the machined surface roughness, residual stress and fatigue life for higher efficiency and precision manufacturing of this new kind material. In this study, the surface roughness including two-dimensional and three-dimensional roughness, residual stress and fatigue life of milling in-situ TiB₂/7050Al metal matrix composites were analyzed. It was found from comparative investigation that the three-dimensional surface roughness would be more appropriate to represent the machined surface profile of milling particle reinforced metal matrix composites. The cutting temperature played a great role on the residual stress. However, the effect of increasing cutting force could slow down the transformation from compressive stress to tensile stress under 270 °C. An exponential relationship between three-dimensional roughness and fatigue life was established and the main fracture mechanism was brittle fracture with observation of obvious shellfish veins, river pattern veins and wave shaped veins in fracture surface.     

Effects of in-situ TiB2 particles on machinability and surface integrity in milling of TiB2/2024 and TiB2/7075 Al composites

In-situ ceramics particle reinforced aluminum matrix composites are favored in the aerospace industry due to excellent properties. However, the hard ceramic particles as the reinforcement phase bring challenges to machining. To study the effect of in-situ TiB₂ particles on machinability and surface integrity of TiB₂/2024 composite and TiB₂/7075 composite, milling experiments were performed, and compared with conventional 2024 and 7075 aluminum alloys. In-situ TiB₂ particles clustered at the grain boundaries and dispersed inside the matrix alloy grains hinder the dislocation movement of the matrix alloy. Therefore, the milling force and temperature of the composites are higher than those of the aluminum alloys due to the increase of the strength and the decrease of the plasticity. In the milling of composites, abrasive wear is the main wear form of carbide tools, due to the scratching of hard nano-TiB₂ particles. The composites containing in-situ TiB₂ particles have machining defects such as smearing, micro-scratches, micro-pits and tail on the machined surface. However, in-situ TiB₂ particles impede the plastic deformation of the composites, which greatly reduces cutting edge marks on the machined surface. Therefore, under the same milling parameters, the surface roughness of TiB₂/2024 composite and TiB₂/7075 composite is much less than that of 2024 and 7075 aluminum alloy respectively. Under the milling conditions of this experiment, the machined subsurface has no metamorphic layer, and the microhardness of the machined surface is almost the same as that of the material. Besides, compared with 2024 and 7075 aluminum alloy, machined surfaces of TiB₂/2024 composite and TiB₂/7075 composite both show tensile residual stress or low magnitude of compressive residual stress.     

超高强度钢立铣工件温度分析及对加工表面质量的影响

以航空难加工材料300M钢为研究对象,基于立铣加工中的工件温度判断在铣削加工中是否出现了金相组织转变,进而分析不同工况下影响加工表面质量的因素。首先,将移动热源法应用于铣削加工中,计算考虑后刀面磨损的立铣加工工件温度,实验表明,计算值与实验值相比误差在10%以内。然后,分析了工件温度在时间上与空间上的分布,以及不同刀具磨损和加工参数条件下工件表面的温升规律,据此预测加工表面是否出现了组织转变,并结合金相组织观察进一步确认。最后,依据加工表面质量物理层面残余应力和显微硬度的检测数据,初步探讨了各因素对表面质量的影响。结果表明,在研究的加工参数范围内,并未达到金相组织转变温度,表面质量主要受铣削热力作用下的剪切面塑性凸出效应、后刀面挤光效应和热效应的影响。     

基于响应曲面法的高速内冷铣削AISI304不锈钢铣削力

针对硬质合金刀具高速内冷铣削AISI304不锈钢时,切削力大、切削温度高及加工表面质量低的问题。基于响应曲面中心复合设计方法进行高速内冷铣削实验,建立了铣削力分量二阶回归预测模型,并进行了实验验证。对比了干式与内冷铣削后的加工表面质量,分析了铣削参数对铣削力分量的影响规律,以铣削力分量最小为目标优化了铣削参数。结果表明:进给力和径向力的预测值与实验值的误差分别为4. 77%和6. 16%;内冷铣削的Ra为0. 193～0. 327μm;对铣削力分量的影响是铣削深度转速进给量,随着铣削深度和转速的增加,进给力先升高后降低,径向力逐步增加,铣削深度与转速的交互作用对进给力和径向力的影响显著;转速11 643. 63 r/min、铣削深度1 mm、进给量0. 08 mm/r为最优铣削参数组合。     

TB6钛合金抛光表面完整性试验

针对目前TB6钛合金类零件主要依靠手工抛光的技术问题,提出了羊毛毡轮数控抛光工艺,研究了抛光参数对表面粗糙度、表面硬度、表面残余应力的影响,进行了羊毛毡轮抛光参数优化,优选出了一组抛光参数:线速度v_s=19.63m/s,进给速度v_f=300mm/min,预压量a_p=0.5mm,加工行宽w=0.5mm。在此抛光参数下,羊毛毡轮抛光能够有效去除铣削刀纹,抛光后表面粗糙度R_a=0.15μm,并且抛光后表面残余应力为压应力。试验结果表明,该抛光方法能够有效地改善零件的表面完整性。     

磨粒磨损对砂带磨削TC17表面完整性的影响研究

砂带磨粒磨损直接影响磨削表面质量进而影响构件综合服役性能.以表面完整性为评估指标,对砂带磨损前后钛合金的表面加工质量进行了试验研究,揭示了砂带磨粒磨损对磨削TC17表面粗糙度、残余应力和表面硬度的影响规律及机制.结果表明,磨粒磨损后由于高度均匀化、单位面积切削磨粒数增加、磨削深度减小,使得表面粗糙度减小、纹理均匀细腻,...