工艺制度对粉末TA15钛合金组织性能的影响

文摘研究不同保温时间和制粉方法对热等静压TA15钛合金的微观组织、拉伸性能和拉伸断口形貌的影响。结果表明:粉末TA15钛合金组织由等轴α-Ti、层状α-Ti和少量β-Ti组成。热等静压保温时间为20min时粉末TA15钛合金已达到致密,随着保温时间延长到120 min组织逐渐均匀长大。采用等离子旋转电极法的粉末TA15钛合金的拉伸性能优于惰性气体雾化粉末TA15钛合金。拉伸断裂模式为韧性断裂,断口微观形貌为韧窝。     

低温复杂结构件特种成形工艺

研究了等离子旋转电极制备低温钛合金球形粉末的特性,采用热等静压成形工艺,制备低温钛合金粉末冶金材料,并对比分析了组织与性能.以低碳钢为材质,加工装配专用芯模,开展粉末冶金TA7 ELI钛合金构件净成形技术研究,实现了大尺寸、薄壁、半封闭式火箭发动机低温转子高性能、高可靠性的整体净成形.结果表明:等离子旋转电极制备的低温钛合金球形粉末,具有非常高的球形度和振实密度,粒径分布可依据需求控制在一定范围内,非金属夹杂含量每千克不超过20个;粉末冶金低温钛合金材料性能全面达到同批次锻件性能水平,微观组织呈等轴状;粉末冶金低温钛合金氢泵叶轮已通过了发动机型号低温全程试车考核.     

硫酸环境电解对热等静压钛合金性能的影响北大核心CSCD

酸环境电解去除包套是热等静压成形复杂钛合金构件的关键工序之一。针对目前酸环境电解对热等静压钛合金性能影响研究较少的现状,研究在40℃的硫酸溶液中,不同电解时间对热等静压TA15钛合金表面钝化膜、氢含量和力学性能的影响。结果表明:电解时间分别为15、30、45、60 d时,热等静压TA15钛合金表面钝化膜厚度逐渐增加,到60 d时钝化膜厚度达到了175.3μm;氢含量在15 d时增幅非常小,平均值低于2×10^(-5),30 d后则显著增加,到60 d时平均氢含量达到5.4×10^(-4);热等静压TA15材料屈服和抗拉强度随着电解时间的延长逐渐降低,塑性变化不大。硫酸环境电解直接影响热等静压钛合金材料的表面质量和力学性能,后续需强化工艺控制。     

电子束熔丝成形TC17钛合金显微组织与拉伸性能研究

针对电子束熔丝(EBWD)成形TC17钛合金开展了显微组织调控与力学性能研究。成形态EBWD TC17钛合金的成分均匀性较好,具有沿z方向外延生长并贯穿多个沉积层的粗大β柱状晶组织,柱状晶内部为细密的网篮状组织。经过热等静压后,β柱状晶内部呈现粗短棒状α网篮组织。经过固溶时效处理后,β基体中同时存在粗短棒状α相和细小的次生α相。成形态EBWD TC17材料的抗拉强度为935MPa,延伸率为9.0%;热等静压态材料的抗拉强度为904MPa,延伸率为18.0%;二重固溶+时效后,由于析出的细小次生α相起到了沉淀强化的作用,材料的抗拉强度较热等静压态提高了18%(至1066MPa),但塑性显著下降(至7.5%),其拉伸断口的韧窝数量也大幅减少。     

粉末热等静压成形TA7 ELI高承压泵壳体的性能和尺寸控制

基于粉末热等静压近净成形技术,在930℃/120 MPa/3 h的条件下开展了TA7 ELI（超低间隙）高承压泵壳体的成形研究,通过两批次粒度存在差异的粉末（粉末表面为胞晶形貌,D50为67μm、74μm）分析了制粉时的粒度波动对成形材料力学性能的影响,并结合有限元仿真手段开展了高承压泵壳体的粉末收缩规律研究。此外,根据高承压泵在液体火箭发动机中的实际服役情况,对近净成形的高承压泵毛坯进行解剖,分析了特征截面位置的显微组织及硬度分布情况。结果表明,粉末热等静压近净成形技术制备的TA7 ELI合金力学性能达到锻件水平,粉末粒度波动对合金力学性能无显著影响,高承压泵壳体的显微组织均匀,特征截面的硬度值波动小,壳体内部流道关键尺寸实测结果与模拟预测结果的最大偏差为5.37%。     

粉末耐热钛合金组织性能及成形技术

采用热等静压技术及旋转电极粉,采用预合金粉粉末冶金工艺开展了粉末耐热钛合金TC11(Ti-6.5AJ-3.5Mo-1.5Zr-0.3Si)制备技术研究,研制出了全致密粉末TC11合金,通过热处理工艺研究优化粉末TC11材料的组织和性能.利用光学显微镜,对其组织进行了分析,用SEM观察了旋转电极粉末形貌,对室温及高温(550℃)拉伸性能及弹性模量等进行了测试分析.粉末TC11合金的组织和性能与同批次TC11锻棒材料进行了对比研究.利用特殊模具成形,开展了粉末TC11构件近净成形技术的研究,实现了整体大尺寸、带网格加强筋的薄壁粉末TC11合金航天飞行器舱体件近净成形,且未检测出内部缺陷.研究结果表明,粉末TC11合金具有与锻造材料相当的拉伸性能,而弹性模量更优,其金相组织均匀细致,形成了网篮组织,并有围绕其分布的等轴α.粉末TC11合金及合适的近净成形技术可在高性价比、高可靠性的轻质耐热航天飞行器构件制备中得到应用.     

置氢TC4钛合金粉末热等静压制件组织与性能研究

采用置氢钛合金粉末热等静压成形与钛合金热氢处理技术相结合的新工艺路线制备合金,研究了置氢量及热等静压工艺参数对置氢TC4合金粉末热等静压制件组织性能的影响规律。结果表明:随着置氢量的增加,置氢TC4合金粉末热等静压后制件的密度呈逐渐增高的趋势;热等静压制件的片层状组织尺寸变薄、针状的组织变细,等轴颗粒组织愈来愈多;退火后制件的显微组织中等轴状的颗粒增多,压缩屈服强度和抗压强度均逐渐增大;热等静压制件与粉末原料的氢含量及相组成基本相近,真空退火除氢后氢含量则达到了安全使用水平,置氢量0.42%TC4合金粉末热等静压制件致密效果好、综合力学性能高。     

Ti-6Al-2Zr-1Mo-1V合金粉末冶金工艺

研究了Ti-6Al-2Zr-1Mo-1V合金预合金粉末经热等静压烧结后的力学性能和显微组织。结果表明，等离子旋转电极粉末氧增量低，粒度分布较集中，颗粒内部组织细小均匀；粉末钛合金材料室温拉伸强度不低于970MPa，伸长率为16％-21％，组织为均匀的条状α相和细小的β转变组织。     

激光熔化沉积快速成形TC4钛合金的焊接性能

为了探索激光熔化沉积快速成形技术制备TC4钛合金的焊接性能,分别采用电子束焊、激光焊两种方法制备接头试样,并借助金相、硬度试验等方法获得接头力学性能、显微组织及硬度。结果表明:两种焊接方法得到的接头抗拉强度最高达953 MPa,焊接系数均0.9;激光和电子束焊接焊缝为网篮状α'相马氏体组织,热影响区为α相和针状马氏体组织组成。激光熔化沉积快速成形TC4钛合金和传统工艺制造的TC4钛合金在焊接特性方面表现相当。     

TA15钛合金环件径轴向辗轧成形全过程组织演变模拟

钛合金环件径轴向辗轧成形制造全过程通常包含加热环坯转移、辗轧成形及轧制环件冷却3个阶段,而每个阶段都将对最终环件的微观组织产生重要影响。因此,研究阐明钛合金材料在该成形制造全过程的微观组织演变特征与规律,对控制环件最终的组织和性能至关重要。以TA15钛合金环件径轴向辗轧为研究对象,首先阐明了TA15钛合金在上述各阶段的微观组织演变机制与演变模型,进而基于ABAQUS软件平台,建立了TA15钛合金环件径轴向辗轧成形制造全过程的宏微观耦合有限元(FE)模型。通过大量模拟研究表明:加热环坯转移阶段促使初生α相的体积分数增加,晶粒尺寸略微增大;辗轧成形阶段一定程度上细化了初生α相晶粒尺寸,而对初生α相体积分数影响不明显;轧制环件冷却阶段会使初生α相体积分数明显增加,晶粒尺寸增大。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。