航空Ti600合金与其梯度功能修复涂层的腐蚀特性对比分析

为修复损伤的 Ti600合金结构件,开发新型耐蚀涂层,应用 Nd:YAG 激光在 Ti600表面制备了钛基梯度功能涂层材料(Functional Gradient Materials,FGM),并测试其耐腐蚀性能.结果表明,Ti600基体和 FGM 耐蚀性均较好;在微观上均呈现局部腐蚀的特性,表面呈腐蚀微坑形貌;极化电位较低;自腐蚀电流小,在30~90 nA/cm2之间.FGM 耐蚀性能较 Ti600得到提高,腐蚀电流为 Ti600的72%     

常温腐蚀对Al-Si涂层氧化行为的影响

研究了未经 /经常温腐蚀的 DZ1 2 5镍基合金表面 Al-Si涂层的高温氧化行为。结果表明 ,经腐蚀的涂层等温氧化行为发生变化。在初始阶段 ,经腐蚀的试样增重大于未经腐蚀的试样 ,而且经腐蚀的试样的耐高温性能明显下降。氧化皮中主要是 Al2 O3及少量的 Ti O2 .     

多孔Si3 N4 表面Al-Y-Si-O-N 陶瓷涂层的制备和表征

采用溶胶-凝胶法,利用Al2O3-Y2O3-SiO2溶胶中氧化物与基体中的Si3N4颗粒反应制备一层致密A1-Y-Si-O-N陶瓷涂层.主要研究了烧结温度对陶瓷涂层的组织和性能的影响,利用XRD和EDS分析涂层的相组成和微区元素组成,通过SEM观察涂层的微观形貌.结果显示:在1 400℃烧结时,能够制备出较为致密的陶瓷涂层,涂层由β -siMon,Si2ON,SiO2和非晶相组成;与基体相比,试样的吸水率下降了32.8％～90％,强度提高了2.1％～25.9％.     

Si和Ti对Nb-6Hf-4Zr-2B合金组织和室温力学性能的影响

 为了寻求Nb合金的强度和塑性的平衡,设计了以Nb基固溶体Nbss为主导相的Nb-xSi-6Hf-4Zr-2B-yTi(x=4,8;y=10,30;原子分数)合金,研究了Si和Ti对合金组织和室温力学性能的影响。结果表明,合金由Nbss、Nb3Si和Nb5Si3等3相组成。4Si-(10,30)Ti合金铸态组织是Nb枝晶和分布在枝晶间的硅化物(Nb3Si和Nb5Si3),8Si-(10,30)Ti合金Nb枝晶间分布的是Nb/硅化物(Nb5Si3)的共晶和Nb3Si,随着Si和Ti含量的增加,硅化物体积分数增加。1 600 ℃退火50 h可使部分Nb3Si共析分解,改变合金的组织形貌和各相的体积分数。随着Si和Ti含量的增加,合金的硬度和强度增加,但塑性和韧性降低。Nb枝晶的失效方式为解理断裂,而硅化物为脆性断裂。     

Ti3Al基合金微弧氧化膜的制备和性质

利用微弧氧化方法在Ti3Al基合金上制备了厚度达120 μm的陶瓷膜.研究了陶瓷膜的生长曲线,发现膜层厚度随着氧化时间的增加而增加,在不同氧化阶段生长速度不同,膜层以向外生长为主;显微结构和硬度分析都发现,陶瓷膜分为两层结构,即内层和外层,陶瓷膜内外层的主要物相是(Ti0.6Al0.2Nb0.2)O2相,外层中还有一定数量的无定形SiO2相;陶瓷膜的最大显微硬度可以达到基体硬度的3倍左右.显微划痕实验表明:膜与基体间结合力大于40N,膜与基体结合良好.电化学极化曲线测试显示陶瓷膜在3.5%盐水溶液中的耐蚀性与Ti3Al基体相比有较大的提高.     

碳纤维表面CVD硅涂层对其性能的影响

 分析了碳纤维表面化学气相沉积Ｓｉ涂层的相结构,研究了Ｓｉ涂层对碳纤维抗氧化性能及强度的影响。结果表明：涂层中Ｓｉ元素呈非晶态分布；Ｓｉ涂层可提高碳纤维的抗氧化性能；氧化温度不同,Ｓｉ涂层碳纤维的氧化失重或增重规律也不相同。同时,Ｓｉ涂层降低了碳纤维拉伸强度,而适度空气氧化又可使Ｓｉ涂层碳纤维强度得到大幅度提高；Ｓｉ涂层碳纤维的强度随氧化温度、氧化时间的变化而改变。     

激光熔覆制备WCp/Ni-Si-Ti复合涂层

在Ni基高温合金表面预置3种不同WC含量的Ni78Si13Ti9(at%)粉末,采用激光熔覆制备了WC和原位自生TiC复相陶瓷增强Ni3(Si,Ti)基复合涂层.利用扫描电镜、能谱分析仪和X射线衍射仪对熔覆层组织进行分析,并测量了其显微硬度.结果表明,熔覆层与基体呈冶金结合,熔覆层组织主要由Ni(Si)固溶体、Ni3(Si,Ti)金属间化合物和WC-TiC复相陶瓷组成.随WC添加量增加,涂层中复相陶瓷含量增多;孔隙率增大;碳化物形态演变历程为不规则状、花瓣状以及不规则状和花瓣状共存.     

Liquid-Solid Phase Equilibria of Nb-Si-Ti Ternary Alloys

To determine the liquid-solid phase equilibria of the Nb-Si-Ti ternary system, Nb-Si-Ti alloys of different compositions are prepared. By means of scanning electron microscopy （SEM）, X-ray diffraction （XRD） and electron probe microanalysis （EPMA）, the phases in the alloys, such as Si-based solutions, Ti（Nb）Si, Ti（Nb）Si2, Nb（Ti）Si2, Ti（Nb）5Si4, Nb（Ti）5Si3, Ti（Nb）5Si3, Nb（Ti）3Si and Nb-based solutions are identified, and the phase evolution is analyzed. As a result, the microstmctural and microchemical evidence provides a clear definition of the Nb-Si-Ti liquidus surface projection and indicates that the ternary phase diagram has seven transition reactions.     

Ti6Al4V合金微弧氧化陶瓷膜的组织结构研究

采用微弧氧化技术在钛合金表面成功制备出膜厚约100μm的致密陶瓷膜以提高钛合金的耐磨性.SEM结果表明,陶瓷膜完整连续,与基体呈犬牙状牢固结合.XRD衍射结果表明:陶瓷膜主要由金红石型二氧化钛和Al2TiO4晶体相组成.显微硬度结果表明钛合金微弧氧化陶瓷膜的显微硬度为862HV而基体合金硬度仅为412HV,陶瓷膜的硬度远远高于基体合金的显微硬度.摩擦磨损试验表明,镀膜的钛合金磨损量远小于不镀膜钛合金的磨损量,陶瓷膜能提高基体的摩擦磨损性能.     

基于甲基三甲氧基硅烷/正硅酸乙酯的聚碳酸酯耐磨涂层

以甲基三甲氧基硅烷(MTMS)水解聚合产物作为主要成膜物质,引入正硅酸乙酯(TEOS)水解产物硅溶胶作为无机增强物,采用溶胶凝胶法在聚碳酸酯(PC)表面形成耐磨涂层。结果表明:PC表面形成了Si—O—Si的交联网络结构。通过测试耐磨实验前后光学性能的变化研究表面涂覆涂层的聚碳酸酯的耐磨性能与涂层组分之间的关系。当涂层原料MTMS和TEOS的摩尔比为2∶1时,聚碳酸酯的耐磨性能达到最优,500次摩擦后雾度为13.22%,为纯PC的56.21%。     

原位法制备C/C复合材料SiC/Si-Al2O3-mullite复合抗氧化涂层

 以Si和Al₂O₃为原料,采用原位生成法在带有SiC内涂层的炭/炭（C/C）复合材料表面制备出Si-Al₂O₃-mullite（莫来石）抗氧化涂层。采用X射线衍射、扫描电镜和氧化实验研究了Al₂O₃含量等工艺因素对Si-Al2O3-mullite涂层的物相组成、结构形貌、抗氧化性能影响。结果表明：Al₂O₃质量含量为30%~40%时,涂层主要由Si,mullite和Al₂O₃三相组成,涂层致密无裂纹,抗氧化性能最佳。在1 500 ℃等温氧化测试显示,SiC/Si-Al₂O₃-mullite复合涂层比单一的SiC涂层抗氧化性能有明显提高,1 500 ℃等温氧化75 h试样失重为4.6%。涂层试样失重的主要原因是涂层中产生了不可愈合的孔隙缺陷。     

碳／碳复合材料表面沉积SiC的形态和成分

在ＰＡＮ碳布和沥青基体碳的Ｃ／Ｃ复合材料表面涂复了ＳｉＣ。用ＣＨ４和Ｎ,为载气的ＳｉＣｌ４作原料,用Ｈ２为稀释气,在两种气体混合比和三种温度下化学气相沉积ＳｉＣ涂层。分析表明,涂层的主要元素有Ｃ,Ｓｉ、Ｃｌ和微量Ｃａ。电镜观察表明,涂层中Ｃ原子含量为６２％时呈菜花状或云团状,而当Ｃ／Ｓｉ比接近于１时,表面呈菠萝状。     

高速电弧喷涂FeNiCrAl涂层制备工艺对涂层性能影响

FeNiCrAl涂层是一种用作轴类零部件的表面耐磨防护材料,为深入研究高速电弧喷涂工艺对FeNiCrAl涂层性能的影响机理,对不同喷涂参数下制备的涂层的组织结构、结合强度、物相组成和显微硬度等性能进行分析表征,探究“喷涂电流-涂层组织结构-结合强度”之间的关系。结果表明：喷涂电流对涂层的组织致密性及结合强度影响较大;喷涂电流200 A、电压34 V、喷涂距离160 mm的工艺参数下制备的FeNiCrAl涂层组织致密,孔隙率约8.76%,结合强度52.3 MPa,涂层硬度约626 HV0.1,约为基体硬度的1.6倍;影响机理与Fe-Al金属间化合物和Cr0.19 Fe0.1 Ni0.11固溶体在涂层内部均匀弥散分布有关。     

Corrosion mechanism investigation of TiN/Ti coating and TC4 alloy for aircraft compressor application

It is imperative to develop multifunctional erosion and corrosion resistant coatings for compressor blades of aircraft engines in harsh environment. PVD (Physical Vapor Deposition) technology has the advances in processing erosion-resistant coatings; however, the performance of PVD coatings to combat corrosion depends on various coating defects. Determining and comparing the corrosion performances of PVD TiN/Ti coating and uncoated TC4 alloy was the main objective of present work. The 960 h salt spray corrosion and 116 h hot corrosion tests were conducted to simulate the grounding and working environments of the aircraft compressors. The corrosion mechanisms due to the coating defects such as pinhole, columnar boundary and large grain were analyzed based on the OM, Confocal microscope, electrochemical measurements, SEM, XRD and EDS results. Owing to the disordered state associated with the columnar boundary and the coating defect, nitrogen could be easily replaced by oxygen in the hot corrosion process, these structures were channels for fast diffusion of oxygen. Moreover, the Gibbs energy changes of Ti oxidation and TiN oxidation were thermodynamically calculated according to the working condition of aircraft compressors, and considerable research effort was focused on mapping out the phase diagram of Ti, TiN and high pressure gases. The findings of this research can provide insights into developing multifunctional coatings for future aircraft engines.     

连接压力在Ti/Ni/Ti复合层TLP扩散连接Si3N4陶瓷中的作用机制

研究了Ｔｉ／Ｎｉ／Ｔｉ复合层ＴＬＰ扩散连接Ｓｉ３Ｎ４陶瓷时压力对接头形成的作用机制。结果表明,ＴＬＰ来不及与陶瓷发生充分反应并形成高强度结合界面就已完全凝固,为形成高强度的结合界面,必须进一步发生固态扩散反应。只有当连接过程中施加足够的压力,才能保证ＴＬＰ在其存在期间充分铺展陶瓷,并在ＴＬＰ完全凝固后形成大量扩散通道,为固态扩散反应提供必要条件。     

磁性涂层碳纤维各向异性铺层板的反射率计算

对磁性涂层碳纤维各向异性铺层板反射率的计算是研究其结构吸波材料性能的基础.本文基于磁性涂层碳纤维单向板的电磁特性分析,研究了电磁波在磁性涂层碳纤维复合材料板中的传输特性.首先推导了单层各向异性复合材料板中的传播常数和波阻抗,在此基础上用传输矩阵法进一步推导了适用于带有磁性涂层碳纤维复合材料铺层板的反射特性.利用此计算方法求解了各向异性复合材料铺层板在不同极化入射电场、材料板不同铺层层数、方向、厚度下的反射特性.最终根据以上算法,开发出各向异性复合材料铺层板结构吸波材料反射率的优化设计软件.     

Cyclic Oxidation Behavior of an EB-PVD CoCrAlY Coating Influenced by Substrate/coating Interdiffusion

To reveal the influence of substrate/coating interdiffusion on the cyclic oxidation property of a metallic coating, cyclic oxidation behavior of an EB-PVD CoCrAlY coating on directionally solidified Ni-based superalloy DZ125 at 1 050 oC is investigated. The 40 μm thick CoCrAlY coating has a cyclic oxidation life of around 160 h, and the oxidation constant is 1.915× 10.7 mg4·cm.8·s.1. However, severe spallation of the oxides containing Co, Cr, Ni, Ta and Ti occurs with longer cyclic oxidation. The degradation in oxidation resistance for the coating is related to the depletion of Al due to the oxide spallation and interdiffusion. Severe interdiffusion between the coating and underlying substrate occurs at 1 050 oC. The composition of the substrate has an important effect on the thermal cycling lifetime of the coating. The influencing mechanism is discussed.     

金属间化合物Ho_2Co_(17-x)Si_x的磁性能机制研究

研究了非磁性原子Si替代Co对Ho2 Co17金属间化合物结构和磁性的影响。X射线衍射表明 ,所有Ho2 Co17 xSix(x =0 .5 ,1.0 ,1.5 ,2 .0 ,2 .5 ,3.0 )化合物都为Th2 Ni17型六角结构 ;化合物的晶格常数和单胞体积都随Si含量的增加而呈线性下降。磁性测量表明 ,Ho2 Co17 xSix 化合物的居里温度和饱和磁化强度均随Si含量的增加而呈线性下降。从热磁曲线测量观察到 ,当 0 .5≤x≤ 3.0时Ho2 Co17 xSix 化合物出现由易面到易轴的自旋重取向 ,自旋重取向温度Tsr随Si原子含量的增加先下降 ,而后又上升 ,在x =2 .5处出现最低点。     

含稀土TiCx增强钛基激光熔覆层组织与耐磨性

采用同轴送粉激光熔覆技术在Ti6Al4V合金表面成功制备了含稀土CeO₂的碳化钛增强钛基激光熔覆层。运用渗透探伤、光学显微镜、X射线衍射仪、扫描电镜、能谱分析仪、电子探针、显微硬度计、摩擦磨损试验机等分析和测试方法研究了碳化钛增强钛基激光熔覆层的成形质量、微观组织、元素分布、硬度和摩擦磨损性能。结果表明,涂层内无裂纹缺陷,仅在层间过渡区分布有少量气孔（孔隙率为1.65%）。涂层中物相主要包括富Ti、Cr元素的β固溶体（CrTi₄）、缺位型碳化钛（TiC_x）和稀土氧化物（CeO₂）。熔覆层各微区的碳化钛形貌存在显著差异,熔覆层顶部和中部区域呈发达树枝晶状和针状,而结合区由针状和小尺寸不发达枝晶组成。碳化钛枝晶中碳元素分布不均匀,一次枝晶含碳量高于二次枝晶。基体相中Ni和Cr元素呈现明显偏析,而Al和V元素分布相对均匀。此外,稀土氧化物CeO₂主要分布于TiC_x与CrTi₄相界以及CrTi₄晶粒边界处。与基材相比,尽管TiC_x增强钛基复合涂层具有较高的摩擦系数,但其耐磨性显著增加（提高近52%）。熔覆层和基材磨损机制均为黏着磨损和磨粒磨损的复合磨损模式,但熔覆层的磨损程度较轻。     

Ti（Y）N镀覆刀具及膜-基界面状态的研究

研究了离子镀ＴｉＮ和Ｔｉ（Ｙ）Ｎ镀层对刀具寿命及膜－基界面状态的影响。结果表明：刀具镀覆Ｔｉ（Ｙ）Ｎ后寿命显著提高,试验数据分散度减小,可信度大大提高,这主要是膜－基界面状态改善,结合力大大提高之故。并对微观机制进行了较为系统的讨论