以21 mm厚度2195铝锂合金板材为对象,研究了T8态时效时预变形量对其微观组织及力学性能的影响以及不同因素对屈服强度的贡献.结果表明:随着预变形量增大,时效时析出的T1相尺寸减小,数密度增大;而θ'相尺寸和数密度都减小.148℃/38h时效时,预变形量从3％增加到15％,屈服强度由596 MPa增大到638 MPa...     

固溶前退火处理对2050铝锂合金冷轧薄板力学性能与组织的影响

采用拉伸性能测试、电子背散射衍射分析(EBSD)、扫描电子显微镜(SEM)和透射电子显微镜(TEM),研究了固溶前退火处理(300℃/4 h,400℃/2 h)对2050铝锂合金冷轧薄板T8时效后力学性能、晶粒组织和析出相的影响。研究结果表明:固溶前退火处理导致2050铝锂合金冷轧薄板固溶态不完全再结晶数量增多,晶粒长厚比增大,小角度晶界比例增加,同时使合金Goss织构密度增大。T8时效后主要强化相为T_1相和θ′相。固溶前退火处理可导致后续T8时效时T_1相在不同{111}_(Al)面上析出差异,其中部分{111}_(Al)面上T_1相析出减少,而预拉伸变形时承受高分切应力{111}_(Al)面上T_1相析出增加,从而影响合金的力学性能。固溶前300℃/4 h退火处理可使T8时效后合金屈服强度和抗拉强度提高,伸长率基本保持不变。     

Cu、Li 含量对Mg、Ag、Zn 复合微合金化铝锂合金力学性能及微观组织的影响

通过18个不同Cu(3.24%~4.16%)、Li(0.94%~1.44%)含量的0.4Mg+0.4Ag+0.4Zn复合微合金化Al-Cu-Li合金,研究总结了T8时效处理时Cu含量及Li含量对铝锂合金强度和微观组织的影响,并采用合金中非固溶Cu、Li原子总分数及Cu/Li原子分数比例阐明了强度及微观组织的影响规律及机理。结果表明:合金中时效强化相包括T1相(Al2Cu Li)、θ'相(Al2Cu)和δ'相(Al3Li)。Cu、Li原子总分数及其比例增加,合金中时效强化相总量及T1相比例大,合金强度较高。而Cu/Li原子分数比例较低,δ'相比例增加,T1相比例下降,合金强度降低。     

二次时效对微合金化的Al-Cu-Li 微观组织及力学性能的影响

通过常规力学性能、扫描电镜、透射电镜等测试分析方法研究了T8I6二次时效制度对Mg、Ag和Zn复合微合金化的Al-3.48Cu-1.44Li合金微观组织和力学性能的影响.结果表明,与单级时效相比,二次时效合金强度提高,而塑性略降;合金强度随第三级时效时间的延长进一步提高.最优的合金其抗拉强度(UTS)、屈服强度(YS)和延伸率分别为613.7、564.9 MPa和6.8％.合金的强化相主要为T1相,另有少量的θ'相和S'相.二次时效促进强化相,特别是T1相的二次沉淀,提高合金的强度,同时几乎不损失塑性.     

基于同步辐射技术的WE54镁合金原位时效研究

利用原位同步辐射技术对WE54镁合金时效过程进行研究。通过对比固溶态(T4)和固溶后冷轧预变形(T4-D)两组合金,揭示WE系列合金在300℃时效温度下析出相演变过程以及预变形对时效析出动力学的影响。原位时效研究表明:T4-D合金的强化相β1(Mg3(Nd, Y))在时效开始3 min后快速形核;时效9 min后β1开始向β(Mg14Nd2Y)转变,时效36 min后此转变结束,此后β占主导地位;对于T4合金的时效析出过程,β1在时效开始6 min后形核;时效18 min后β1开始向β转变;时效78 min后此转变结束。同步辐射衍射结合透射电子显微镜(TEM)结果分析发现:通过轧制预变形可以加速合金的时效进程并促进形成网状分布的时效析出相,这种分布有利于合金获得良好的时效强化效果。     

高强Al-Cu-Li-X铝锂合金2A97三级时效工艺及性能研究

以新型高强Al-Gu-Li-X铝锂合金2A97为研究对象,通过拉伸试验研究两种三级时效工艺及其改型工艺对合金性能的影响.结果表明,含有δ′相二次析出过程的三级时效和含有δ′相回溶过程的三级时效处理合金的强度和塑性达到T6峰值时效水平,三级时效改型工艺由于增加变形使前者合金的强度升高,塑性降低,使后者的强度显著提高.三级时效和单级时效合金的主要显微组织有δ′相、θ″/θ′相和T1相.三级时效改型工艺由于增加变形促进δ′相析出和δ′相回溶,同时变形促进T1相析出,从而改变了主要强化相δ′相和T1相的数量.     

预拉伸处理对2 A97薄板组织和性能的影响

通过室温拉伸、腐蚀试验、TEM等手段,研究人工时效前预拉伸处理对2A97铝锂合金组织和性能的影响。结果表明：在相同时效工艺下,经3%的预拉伸变形后,2A97合金的强度和耐蚀性能都有较大提高,其中抗拉强度提高了32 MPa,晶间腐蚀等级变为点蚀等级;预拉伸处理促进了时效过程中T1相在晶内的均匀弥散析出,降低了δ′相的含量,抑制了晶界平衡相的析出,从而改善了合金的强度和耐蚀性能。     

低Cu含量Al-Mg-Si-Cu合金的T78双级时效

采用拉伸和加速腐蚀试验,分别测试了预时效（180℃）+再时效（190、200、210℃）对一种低Cu含量Al-Mg-Si-Cu合金拉伸性能和晶间腐蚀的影响,结果表明,延长预时效和再时效时间或提高再时效温度,合金强度逐渐降低,同时,腐蚀类型按晶间腐蚀→均匀腐蚀→坑蚀顺序演化。其中,经预时效（180℃/2~8 h）+再时效（200℃/6 h或210℃/2 h）处理,合金抗拉强度、屈服强度和延伸率分别为380~395 MPa、360~380 MPa和12%~15%,腐蚀类型为均匀腐蚀,实现强度与耐蚀性的良好配合。透射电镜观察表明,随着双级时效程度的增加,合金强度的降低源于基体β"相的减少及β'相和Q'相的增加;晶间腐蚀倾向的降低与晶界Q相大间距、断续分布有关;坑蚀的形成则与结晶Q相吸收周围析出相、形成基体无析出区有关。     

预变形对Al-Cu-Mn-Mg-Ag合金的组织与力学性能的影响

采用显微硬度测试、拉伸力学性能测试、扫描电镜及透射电镜观察等分析手段,研究了预变形对Al-Cu-Mn-Mg-Ag合金的组织与力学性能的影响.结果表明:时效前的冷轧变形加速了Al-Cu-Mn-Mg-Ag合金的时效进程,提高了时效的峰值硬度,促进Ω相的析出,增加Ω相的数量.随着变形量的增加,合金时效过程中双阶段时效硬化的现象减弱,预变形小于10%时,时效过程中出现明显的双阶段时效硬化特征,预变形大于10%时,时效过程仅出现明显的单阶段时效硬化特征;随着预变形量的增加,合金的抗拉强度和屈服强度逐渐增加,延伸率逐渐降低.综合考虑合金的强度和塑性,Al-Cu-Mn-Mg-Ag合金的预变形量应为10%～20%.     

应力时效对Al-Cu-Mg-Ag耐热铝合金组织与性能的影响

采用硬度测试、光学显微镜、透射电镜等研究了时效过程中外加应力对A l-Cu-Mg-Ag合金组织与性能的影响。结果表明,在应力时效和无应力时效的条件下,合金组织中均发生了完全再结晶,时效过程中施加外应力没有改变合金再结晶晶粒的形貌,但对析出相有较大影响。在应力时效条件下,合金中θ′相和Ω相均沿某一方向呈择优取向析出,即有应力位向效应产生。应力时效能够促进θ′相的析出,而抑制Ω相的析出,合金的峰值硬度也有所降低。这可能是由于在应力时效初期引入了大量的位错,为θ′相的异相形核提供了有利的位置,从而使与θ′相具有相同化学成分的Ω相的析出受到抑制。这一点从时效前预拉伸(变形量为6%)能够使θ′相数量增多而Ω相数量减少,且硬度略有降低得到验证。在应力时效过程中,位错的存在不利于溶质原子的扩散,阻碍了原子团簇的形成,从而延缓了合金中强化相的析出。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。