溶胶-凝胶法制备纳米TiO2 及粒径控制工艺

采用溶胶-凝胶法,以钛酸丁酯为前驱体,乙二醇作为螯合剂制备纳米TiO2 粒子。考察钛的乙二

醇盐的浓度、pH 值、温度等因素对TiO2 粒径的影响,并用红外光谱和SEM 对纳米TiO2 粒子进行结构和形貌表

征。结果表明,采用溶胶凝胶法可以制备出呈椭圆形且粒径分布均匀的TiO2 纳米粒子。使用硝酸铵可以有效

阻止TiO2 纳米粒子团聚。当pH 值为2 ~3、温度为20 ~40℃,钛的乙二醇盐在丙酮中的浓度为0. 03、0. 05 及

0. 07 M 时,粒径分别为150、240 及600 nm。

     

纳米多壁碳管结构变化对其复合材料微波性能影响

采用不同温度热处理纳米多壁碳管,研究纳米多壁碳管结构变化对相应复合材料的微波特性的影响.采用拉曼光谱分析表征纳米多壁碳管热处理前后的结构变化;测试纳米多壁碳管/石蜡复合材料在0.5 ～ 6GH介电谱.结果显示,热处理温度≤1000℃,纳米多壁碳管的ID/IG值基本不变,相应复合材料的复介电常数大致相等且吸波性能基本相同;热处理温度＞ 1000℃,ID/IG值明显减小,内部结构发生重排,纳米多壁碳管平均晶粒尺寸增大,相应的纳米多壁碳管复合材料的复介电常数无论实部还是虚部均明显下降,微波吸收峰向高频移动.通过热处理控制纳米多壁碳管的ID/IG值和平均晶粒尺寸,可以调整纳米多壁碳管复合材料的微波介电谱,达到调整纳米多壁碳管复合材料的微波吸收特性的目的.     

EOC-g-MAH 共混增韧PLA/ HGB 复合材料的结构及性能

采用熔融共混和模压成型工艺制备了马来酸酐接枝聚烯烃弹性体(EOC-g-MAH)共混增韧聚乳

酸/ 中空玻璃微珠(PLA/ HGB)复合材料,考察了EOC-g-MAH 的质量分数对复合材料的微观结构、力学性能

和热稳定性的影响。结果表明,EOC-g-MAH 的引入促进了基体对HGB 的表面润湿,显著增强了两者的界面

结合。随EOC-g-MAH 的含量增加,PLA/ HGB 复合材料的拉伸强度先上升后降低,并在含量为3% 时达到最

大值,较未改性体系提高了14. 23%,而弹性模量持续下降。在0 ~9%内,PLA/ HGB 复合材料的冲击韧性先急

剧上升而后趋缓,当EOC-g-MAH 的添加量为7%时,即可使增韧体系的冲击韧性提高近40%,表明EOC-g-

MAH 更有利于提高PLA/ HGB 复合材料的抗冲击性能。EOC-g-MAH 的引入使复合体系的热分解过程由一阶

失重转变为两阶失重,但对热分解温度几乎没有影响。

     

碳纤维增强树脂基复合材料壳体相贯线孔加工工艺

介绍一种用于碳纤维复合材料大直径不垂直相贯线孔加工方法。综合考虑了加工温度,加工质

量,排屑及加工效率等问题。结果表明,采用一种简易的加工工装保证了孔的尺寸及位置精度,使相贯线孔能

够一次性加工完成。通过对传统磨头的工艺改进解决了排屑及散热问题,并提高了复合材料的表面加工质量。

     

刚性短切碳纤维预制体和酚醛浸渍碳烧蚀体的制备及性能杨

以短切碳纤维、热固性酚醛树脂为原料,经真空成型得到短切碳纤维预制体(Fiberform),再以Fi鄄

berform 为骨架、酚醛树脂溶液为浸渍液,经反应干燥得到酚醛浸渍碳烧蚀体( PICA)。结果表明:Fiberform 具

有明显的各向异性,当Fiberform 的密度由0. 13 g/ cm3增大到0. 18 g/ m3 时,其纵向压缩强度由0. 10 MPa 增大

到0. 39 MPa,横向压缩强度由0. 33 MPa 增大到0. 79 MPa。PICA 具有酚醛气凝胶/ 碳纤维复合型结构,其密度

可以通过控制酚醛树脂溶液浓度来调节。当PICA 的密度由0. 27 g/ cm3增大到0. 43 g/ cm3,其纵向压缩强度由

0. 45 MPa 增大到2. 42 MPa,横向压缩强度由1. 36 MPa 增大到3. 12 MPa。PICA 的隔热性能与Fiberform 相近,

其纵向和横向热导率分别为0. 08 和0. 11 W/ (m·K)。

     

大尺寸多格栅复合材料框架共固化成型工艺

从铺层工艺优化设计、产品成型压力的保证等方面阐述大尺寸多格栅复合材料框架热压罐整体

成型的工艺方法。工程实践证明,将整体结构分解成多个工艺单元,先完成单元铺层,合模后完成剩余铺层的

方法可以完成该框架的坯件预成型;软硬模交替使用,软模传压、硬模保证框架几何尺寸的工艺方法能够实现

该框架的整体固化成型。制成的产品不仅上、下面平面度等形、位公差满足设计要求,产品的薄厚偏差、胶的含

量和产品质量偏差均能控制在允许的范围内。

     

高能机械加工表面纳米化40Cr钢组织结构与力学性能

利用超声高能机械加工处理工艺在40Cr钢表面制备了纳米晶表面层。采用SEM,TEM和纳米压痕技术等分析了表面纳米晶层的组织结构与力学性能。实验结果表明,表面是由分布均匀的纳米级铁素体和纳米级渗碳体晶粒构成的复合纳米结构,过渡区由纳米级的渗碳体晶粒和粗晶铁素体晶粒构成。表面平均晶粒尺寸为3nm。随着深度的增加,晶粒尺寸逐渐增大。表面硬度高达8GPa,为基体硬度的3倍,随着深度的增加,硬度迅速降低。表面层弹性模量为252GPa,与基体十分接近。     

纤维增强ＳｉＢＮ 陶瓷基复合材料的制备及性能

为了满足不同马赫数飞行器对透波材料提出的集透波、承载、防热、耐蚀、抗冲击于一体的性能

要求ꎬ本文开展了不同耐热区间纤维增强陶瓷基复合材料的研究ꎮ 采用ＰＩＰ 工艺分别制备了氧化铝、莫来石、

石英、氮化硅纤维增强ＳｉＢＮ 陶瓷基复合材料ꎬ并对其介电和力学性能进行了测试与评价ꎮ 结果发现莫来石纤

维增强ＳｉＢＮ 陶瓷基复合材料的介电常数和介电损耗分别为４.１~４.２ 和１.０×１０－２ ~９.７×１０－３ꎬ抗弯、拉伸、压缩

强度分别为９５.１２、３４.９５ 和８０.９２ ＭＰａꎬ具有最佳的综合性能ꎮ

     

定向破坏复合材料层合壳体结构铺层的分析与设计

以复合材料层合板为基本材料设计了一种结构新颖的定向破坏复合材料层合壳体结构,在导弹与

该壳体结构的初始接触区域预制缺陷区,导弹发射时以四瓣形式开裂,大幅度提高了导弹的发射效率。利用ANSYS

有限元模拟分析软件,通过强度分析确定了最佳铺层设计方案,单层板厚度为0.2 mm,采用基体本身加强预

置缺陷区的[0°/90°/ ±45°]2S 铺层方式。该种铺层方式的爆破载荷为0.21 MPa,最小顶破载荷为1 kN,完全能够

满足其在工作环境下既能承受一定的压力不漏气又能在较小的顶破载荷下自行破裂的设计要求。

     

激光重熔对喷射电沉积纳米结构镍涂层性能影响研究

采用喷射电沉积方法在45钢基体表面制备了纳米结构镍涂层,研究了激光重熔工艺对涂层性能的影响。用扫描电镜和X射线衍射仪对涂层表面形貌和晶粒尺寸进行分析,并对涂层做表面显微硬度测试和耐腐蚀性试验。结果表明:在优化的工艺参数下,喷射电沉积制备的镍涂层表面比较平整、结合较致密,由平均尺寸为13.7 nm的纳米晶颗粒组成,但涂层中仍存在一些孔隙及其它缺陷;经过激光重熔后,熔融区内的晶粒尺寸明显减小,涂层致密化程度有所提高并使涂层与基体由机械结合变为冶金结合,因此涂层的表面显微硬度和耐腐蚀性能得到明显的提高。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。     

Research on Auto-detection for Remainder Particles of Aerospace Relay Based on Wavelet Analysis

Aerospace relay is one kind of electronic components which is used widely in national defense system and aerospace system. The existence of remainder particles induces the reliability declining, which has become a severe problem in the development of aerospace relay. Traditional particle impact noise detection (PIND) method for remainder detection is ineffective for small particles, due to its low precision and involvement of subjective factors. An auto-detection method for PIND output signals is proposed in this paper, which is based on direct wavelet de-noising (DWD), cross-correlation analysis (CCA) and homo-filtering (HF), the method enhances the affectiv-ity of PIND test about the small particles. In the end, some practical PIND output signals are analysed, and the validity of this new method is proved.