RTM用炔基改性苯并噁嗪树脂工艺及力学性能

文摘为改善苯并噁嗪树脂对树脂传递模塑(RTM)成型工艺的适应性,并进一步提升苯丙噁嗪基复合材料的耐高温性能。提出利用炔基改性苯并噁嗪树脂,以提高树脂的交联密度,并改善树脂流变特性。结果表明:改性后的炔基苯并噁嗪树脂在81. 5℃时黏度低至805 mPa·s可满足RTM工艺灌注要求,在110℃其工艺窗口高达310 min。同时,炔基苯并噁嗪树脂的起始固化温度低至130℃,固化温度为167℃,后处理温度为208℃,满足低温固化要求。通过DMA与TGA分析,RTM成型低温固化苯并噁嗪/碳纤维复合材料的Tg为411℃,在N_2环境下800℃残留率高达88. 6%,表明其复合材料具有良好的耐高温性能。SEM观察发现该树脂与纤维界面粘结强度较高,碳纤维复合材料350℃拉伸性能保留率达99%以上,弯曲、层剪性能保留率达70%以上,压缩性能保留率也达60. 9%。     

增韧双马来酰亚胺与烯丙基苯并噁嗪共混物的性能

以间甲苯胺、烯丙基双酚A和多聚甲醛为原料合成了一种烯丙基型苯并噁嗪(BA-mt).将其与二苯甲烷型双马来酰亚胺、烯丙基双酚A (DABPA)以不同比例进行熔融共混,得到了增韧双马来酰亚胺与烯丙基苯并噁嗪的共混物BDB.用DSC对共混物的固化反应进行研究,用DMA和TGA研究了固化树脂热性能,结果表明,在BMI/DABPA中加入BA-mt后,固化树脂的热性能下降,但氮气氛中T10d仍高于400℃,800℃残炭率提高到33％以上.加入10份BA-mt改性BMI/DABPA的固化树脂的Tg为319℃;其弯曲性能提高,弯曲强度为44 MPa,弯曲模量为3.76 GPa.BMI/DABPA/BA-mt固化树脂的吸水率随BA-mt的加入而下降.     

适用于RTM成型的新型耐烧蚀苯并噁嗪树脂的研究

在低黏度的双环苯并噁嗪中间体（B-BOZ）中加入一种新型的多官能基单环苯并噁嗪（AS-BOZ）或一种交联剂（TPA）,复配制得了一种适用于BTM成型的新型耐烧蚀苯并噁嗪树脂,对树脂体系的黏度及固化物的热稳定性、力学性能、残碳率及碳的形貌进行了研究。结果表明，无论是AS-BOZ还是TPA的引入都使得双环苯并噁嗪体系黏度降低,同时提高体系的交联密度,使固化物的Tg和残碳率都大幅度提高.其中BA2-1固化物的Tg为250℃,800℃下氮气中残碳率为68%,质量烧蚀率为23.3 mg/s;BT2-1固化物的Tg为240℃,800℃下氮气中残碳率为70%，质量烧蚀率为20.1 mg/s,两体系高温下均能得到致密的碳层结构。     

苯并噁嗪杂化树脂及其复合材料的制备与性能

为提高苯并噁嗪(BZ)的热稳定性,通过BZ 与聚硅氮烷制备了一种苯并噁嗪杂化树脂(BZ-H),
并采用模压工艺制备了玻璃布/ BZ-H 复合材料。制备的BZ-H 树脂在70 ~170℃有较低的黏度和聚合温度、
较少的放热量及良好的固化工艺性。其固化物的Tg 为354. 7℃。在N2 气氛下,T5
d 为460℃,900℃ 的残重
(W900℃ )为75. 68%。在空气气氛下, T5
d 为466℃,W900℃ 为16. 39%。玻璃布/ BZ-H 复合材料在室温下的弯曲
强度、模量和层间剪切强度分别为433 MPa、22 GPa 和24 MPa,在350℃下的保留率分别为40%、68%和54%。
SEM 微观形貌观察表明,BZ-H 树脂与纤维间具有良好的粘接作用,该特征赋予了复合材料优良的力学性能。     

纳米碳粉改性苯并噁嗪树脂性能研究

文摘为了适应苯并噁嗪树脂在高性能领域的应用,采用纳米碳粉对其进行了改性研究。结果表明,纳米碳粉对苯并噁嗪树脂的固化有催化作用,降低了苯并噁嗪树脂的固化特征温度,在一定程度上克服了苯并噁嗪树脂高温固化的不足;同时,纳米碳粉的加入,提高了苯并噁嗪树脂的弯曲性能与压缩性能,起到了增强增韧树脂的效果。     

苯乙炔苯酐封端聚酰亚胺低聚物的合成与性能

将4-苯乙炔苯酐(4-PEPA)和3,3',4,4'-二苯醚四酸二酐(ODPA),与3,4'-二氨基二苯醚(3,4'-ODA)和1,4-双(4'-氨基-2'-三氟甲基苯氧基)苯(BTPB)或1,3-双(4-氨基苯氧基)苯(1,3,4-APB)混合物通过高温缩合聚合反应合成了两种苯乙炔苯酐封端的聚酰亚胺低聚物PI-1和PI-2,对其熔体黏度、热行为及固化物的热性能等进行了研究.实验表明,PI-1和PI-2低聚物在280℃时具有低的熔体黏度(＜1 Pa·s)和良好的熔体黏度稳定性;经371℃固化后形成的纯树脂固化物具有优异的耐热性能,5%热失重温度超过520℃,Tg超过330℃,有望成为适用于RTM工艺的复合材料基体树脂.     

改性含硅芳炔树脂及复合材料的制备和性能表征

通过胺解反应合成了二(3-乙炔基苯胺)-甲基乙烯基硅烷(SZMV),并对其物理结构进行了表征。将SZMV与含硅芳炔(PSA)树脂通过熔融共混的方法制备了改性PSA树脂(PSA/SZMV)。考察了改性PSA树脂的黏度、固化特性、耐热性能、介电性能以及复合材料的力学性能。研究结果表明SZMV的加入有效降低了树脂的黏度,使其加工工艺性能得到改善,氮气条件下树脂固化物的T5d高达571℃,仍保持良好的耐热性能,改性树脂的介电常数为2.9,复合材料的弯曲和层剪强度分别提高了45%和33.6%。     

含炔基酚醛树脂的合成与表征

研究了普通Novolac线性酚醛、氨催化resol型酚醛的炔丙基化树脂的简便合成;采用FTIR、 HNMR、GPC等表征了其分子结构;研究影响热固化过程的因素(分子量、炔基含量、羟甲基含量)和典型树 脂的固化动力学。黏度测定、DMA、TGA等分析结果表明该类树脂具有良好的工艺性,100℃的黏度不超过 400mPa·s;树脂可以在200～250℃进行热固化;热固化物耐热性比传统酚醛树脂有明显改进,DMA表明树 脂固化物具有高达370℃的玻璃化温度,TGA则表明其初始热分解温度在400℃以上;XRD结果表明树脂固 化物的碳化物是典型的玻璃碳。     

改性双马来酰亚胺树脂在RFI工艺中的应用

通过在改性双马来酰亚胺5405树脂中加入耐高温热塑性塑料聚芳醚砜(PES),获得了满足RFI工艺要求、具有良好成膜性的5405A树脂膜.该树脂膜在室温不粘手,能够任意弯曲.在熔渗温度(130℃)下,低黏度(≤500mPa·s)的保持时间长达70min.在宦温存放3个月后,不溶物含量由1.25%变化为2.02%,DSC曲线表明反应的峰始温度和峰顶温度与放置前无明显差异,130℃凝胶时间由137min变化为135min.参照5405树脂的固化工艺,制备了5405A树脂浇铸体和单向碳纤维帘子布(G0827)增强5405A复合材料,并对性能进行了评价.对比5405和5405A树脂树脂浇铸体的性能表明,5405A力学性能稍有降低,但韧性得到了明显提高.     

二烯丙基双酚 A 共聚双马来酰亚胺改性氰酸酯树脂的性能

采用二烯丙基双酚A和二苯甲烷型双马来酰亚胺与双酚A型氰酸酯共聚,以改善氰酸酯树脂的工艺和耐热性能;利用DSC,TGA,DMA表征了树脂的固化行为和耐热性能;此外,还研究了树脂的力学性能及高频下的介电性能。结果表明,改性后的氰酸酯树脂固化反应温度降低了约60℃,改性树脂固化物在氮气气氛下Td5约400℃,Tg约270℃,显示了良好的耐热性能。在7~15 GHz宽频范围下,改性树脂的介电常数3,介电损耗0.008~0.01,显示了良好的介电性能。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。