DD6单晶高温合金扭转小角度晶界的拉伸性能

在760℃,850℃和980℃温度条件下,研究了DD6单晶高温合金扭转小角度晶界的横向拉伸性能和断裂特征.结果表明,相同晶界角度的试样,随着温度的升高,DD6单晶高温合金拉伸强度降低.在760℃,850℃和980℃三个温度下,晶界角度分别为10.8°,6.4°,3.8°时,试样出现沿晶断裂,小角度晶界试样的拉伸强度降低.小角度晶界试样沿晶断裂明显降低试样的拉伸塑性.     

EB-PVD制备NiCoCrAlY/NiCr微层板的拉伸性能研究

采用电子束物理气相沉积(EB—PVD)方法制得NiCoCrAlY／NiCr微层板。研究了NiCoCrAlY／NiCr微层板的室温和高温拉伸性能，并采用SEM观察和分析了样件的拉伸断口。结果表明：由于微层界面的存在，微层板表现出良好的高温延迟断裂特性，材料的断裂强度在600％：时达到最佳；随着温度的升高，断裂方式由沿晶脆性断裂为主逐步过渡到沿晶脆性断裂和部分的韧窝韧性断裂的混合断裂方式。     

等离子体微弧氧化表面处理LYl2铝合金的高温拉伸性能

采用等离子体微弧氧化技术对LY12铝合金表面进行氧化处理，对处理前后材料的高温拉伸性能进行了研究，用SEM观察试样拉伸断口及陶瓷涂层形貌。结果表明：在高温条件下，LY12铝合金表面陶瓷化后拉伸强度有一定提高，且随温度的升高，拉伸强度提高的比率增大，说明在高温条件下陶瓷涂层对铝基体起到了一定的隔热作用；表面陶瓷化对LY12铝合金的延伸率影响不大。试样为典型的韧性断裂，且断裂后陶瓷膜层没有出现大面积脱落，表明陶瓷涂层与铝基体结合良好。     

块体纳米晶铝的力学性能及变形机理

采用雾化粉体+挤压(Ato+Ext)、雾化粉体+热等静压+挤压(Ato+HIP+Ext)、低温球磨+挤压(Cryo+Ext)、低温球磨+热等静压+挤压(Cryo+HIP+Ext)四组不同的工艺制备块体纳米晶/细晶铝,并测定了室温拉伸性能,分析了这些块体材料的拉伸应力-应变曲线,利用透射电镜和扫描电镜观察了试样断口附近的位错活动及试样的断口形貌,讨论了其变形机理和断裂机理。研究结果表明:球磨粉体制备的块体纳米晶铝的强度远高于雾化粉体制备的块体超细晶铝,四组块体材料在拉伸过程中均不存在加工硬化现象;块体超细晶铝在拉伸过程中发生了明显的位错运动,对于块体纳米晶铝,尺寸≤100nm的晶粒在拉伸过程中内部基本不发生位错运动;块体超细晶铝大部分区域发生穿晶断裂,而块体纳米晶铝基本发生沿晶断裂。     

高温处理对中密度针刺C/C复合材料性能的影响

针对C/C复合材料脆性问题,对密度为1.60 g/cm3的碳布叠层针刺C/C复合材料进行了1800、2 000、2 200和2 500℃的高温处理,研究了不同热处理温度对C/C复合材料微晶结构、力学和抗热震等性能的影响.结果表明,高温处理使针刺C/C复合材料的层间剪切和面内拉伸强度出现不同程度的降低,但材料的断裂伸长率和抗热震性能得到大幅度提高.其中,1 800℃高温处理后的C/C复合材料具有优异的力学和抗热震性能.     

钨渗铜材料在真空高压开关上的应用

为适应高压真空开关抗熔焊、耐电蚀、高电导、低含气量等要求，对传统的生产工艺作了一系列改进，采用纯钨粉经模压成型、高温烧结，然后一次完成渗铜和覆铜。结果表明，钨骨架强度高，钢呈网状分布，基体组织细小均匀，气体含量低，覆铜层与钨铜基体结合紧密，从而满足了使用要求，降低了成本，获得了较好的经济效益。     

HIP-Re 组织及力学性能

采用粉末冶金热等静压技术制备了HIP-Re纯铼材料,分析了不同热处理状态对材料微观结构及室温和高温性能的影响。结果表明,热处理温度对材料拉伸性能影响较大,经1 800℃/1.5 h真空处理HIP-Re抗拉强度达到1 196 MPa,伸长率为19.1%;2 000℃抗拉强度达到69 MPa,伸长率达17%以上。粉末冶金铼的晶粒组织多为2～8μm细小等轴晶,HIP-Re断裂方式为沿晶断裂与穿晶断裂共同作用,高温断裂方式为晶间断裂与滑移断裂,在拉伸形变过程中,Re材料内部产生了大量协变的裂纹及微孔,裂纹扩展连接导致断裂。     

热处理对激光选区熔化GH3536合金高温拉伸性能的影响

利用激光选区熔化（selective laser melting,SLM）技术可近净成形GH3536合金复杂零件,其高温力学性能是能否安全服役的重要考量指标,本工作研究热处理对SLM成形GH3536合金的微观组织与高温拉伸性能的影响。在1225℃下进行1 h热处理以探究组织性能调控机制,测试GH3536增材试样沉积态与热处理态高温下的拉伸性能,采用扫描电镜研究热处理前后增材GH3536试样的微观组织演变。结果表明：热处理可有效消除晶粒内部的胞状亚晶结构,使位错滑移能力显著增强,其在室温、650、815℃环境下断裂伸长率分别提高75%、92%、683%;另外,柱状晶纵横比的减小使热处理试样的各向异性显著降低;断口分析表明随着拉伸环境温度的增加,热处理试样的断裂模式由沿晶断裂转变为混合断裂。     

选区激光熔化IN718合金室温及高温拉伸性能研究

采用选区激光熔化技术制备了IN718合金,对其凝固组织形成机制和热处理固态相变行为进行了研究,分析了IN718合金经热处理后的室温和高温拉伸断裂机理。研究结果表明,选区激光熔化IN718合金沉积态显微组织为沿沉积增高方向定向生长的树枝晶,枝晶间分布着纳米级Laves相。经标准热处理后晶粒形态没有明显变化,大量γ′和γ′′相以及针状δ相弥散析出,Laves相含量减少,合金硬度较沉积态高约40%。经热处理后,合金垂直于沉积增高方向试样抗拉强度高于锻件,平行于沉积增高方向的试样塑性优于锻件,高温拉伸强度与锻件相当,室温及高温拉伸断裂机制均为微孔聚集型的穿晶韧性断裂。     

2D-C/SiC缺口试样的拉伸行为

研究了具有双边对称圆弧缺口（试样厚3 mm宽4 mm,缺口半径2 mm,缺口深0.6 mm）的二维正交编织C/SiC试样在室温空气中与高温真空下拉伸行;测量了拉伸过程中的应力、应变、初始模量和电阻;并用SEM观察断口.结果表明,2D-C/SiC材料除室温下缺口试样的拉伸强度低于光滑试样外,高温下两者基本相当,两者都随温度的升高变化也基本一致.高温下缺口试样拉伸强度与光滑试样相当说明,该材料对应力集中不敏感;室温时对应力集中敏感.缺口试样的断裂应变要远小于光滑试样的断裂应变.2D-C/SiC材料缺口试样基体裂纹开裂应力随着试验温度的上升逐渐增加.缺口试样的相当模量高于同一温度下光滑试样的弹性模量,两者都随着试验温度上升而增加,在1 100℃达最大值,然后开始下降.电阻表征的损伤大体上随载荷增加而增加,1 300℃和1 500℃条件下,较小载荷范围内有下降现象.从室温到1 500℃,所有断口中与载荷方向垂直的纤维束断裂面平整,平行于载荷方向的纤维束断面参差不齐.2D-C/SiC复合材料总体上仍属于脆性断裂,局部上有纤维或纤维束内小的纤维集团拔出,吸收了较多的能量,存在增韧机制.     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。     

Research on Auto-detection for Remainder Particles of Aerospace Relay Based on Wavelet Analysis

Aerospace relay is one kind of electronic components which is used widely in national defense system and aerospace system. The existence of remainder particles induces the reliability declining, which has become a severe problem in the development of aerospace relay. Traditional particle impact noise detection (PIND) method for remainder detection is ineffective for small particles, due to its low precision and involvement of subjective factors. An auto-detection method for PIND output signals is proposed in this paper, which is based on direct wavelet de-noising (DWD), cross-correlation analysis (CCA) and homo-filtering (HF), the method enhances the affectiv-ity of PIND test about the small particles. In the end, some practical PIND output signals are analysed, and the validity of this new method is proved.