采用AgCuTi活性钎料,在880℃/10min规范下成功实现了SiO2f/SiO2自身、SiO2f/SiO2与Cu和SiO2f/SiO2与1Cr18Ni9Ti三种接头的连接。实验结果表明,三种接头中靠近SiO2f/SiO2母材的界面处均形成了一层薄薄的扩散反应层组织,反应层中出现了Ti和O的富集,根据两者的原子比例推断生成了TiO2相;另外,三种接头中心区都形成了由灰色相和白色相共同组成的Ag-Cu共晶组织,其中灰色相为Cu基固溶体,白色相为Ag基固溶体。接头剪切强度结果显示,SiO2f/SiO2/Cu接头剪切强度为12.4MPa,SiO2f/SiO2/1Cr18Ni9Ti接头剪切强度为18.4MPa,接头中的残余应力是决定接头强度大小的重要因素之一。     

C_f/SiC复合材料与Ti合金的AgCuTi-W复合钎焊

本文利用AgCuTi-W复合钎料作中间层,在适当的工艺参数下真空钎焊Cf／SiC复合材料与Ti合金,利用SEM,EDS,XRD分析接头微观组织结构,利用剪切试验检测接头力学性能。研究结果表明：钎焊时,复合钎料中的Ti借助Cu-Ti液相与Cf／SiC复合材料反应,在Cf／SiC复合材料与连接层界面形成Ti3SiC2,Ti3Si和少量TiC化合物的混合反应层。复合钎料中的Cu与Ti合金中的Ti发生互扩散,在连接层与Ti合金界面形成不同成分的Cu—Ti化合物过渡层。钎焊后,形成W颗粒强化的致密复合连接层,W颗粒主要分布在Cu-Ti相中。W的加入缓解了接头的残余热应力,Cf／SiC／AgCuTi—W／TC4接头剪切强度明显高于CF／SiC／AgCuTi／TC4接头。     

采用Ti-Zr-Cu-Ni-Co钎料钎焊SiC纤维增强钛基复合材料的接头组织与性能

针对SiCf/β21S钛基复合材料,采用Ti-Zr-Cu-Ni-Co系新钎料,进行了钎焊实验和接头力学性能测试.实验结果表明:960℃/10min规范下的钎缝组织形貌单一,钎焊接头剪切强度平均值为157.8MPa;960℃/10min/5MPa规范下的钎缝主要由层片状组织组成,接头剪切强度平均值达到291.2MPa,较前者提高了85%左右,该接头经过900℃/2h热处理后组织变化不大.钎缝中的缺陷以及Ti和Zr与Cu,Ni和Co三种合金元素形成的脆性化合物相在接头中所占比例对接头性能影响很大.     

TiAl合金与42CrMo扩散钎焊的界面组织及形成机理

使用真空扩散钎焊方法对870℃下TiAl/B-Ag72Cu/42CrMo进行了连接,利用金相显微镜、扫描电镜、电子探针成分线分析及成分定量分析等方法研究了TiAl/B-Ag72Cu/42CrMo扩散钎焊接头组织及接头反应层的形成机理.界面分析显示,B-Ag72Cu/42CrMo的界面未形成金属间化合物,而TiAl/B-Ag72Cu的界面上有Ti(Cu,Al)2金属间化合物产生.分析了连接接头金属间化合物的形成和长大机制,钎焊接头金属间化合物的形成和长大机制,分为等温凝固和冷却凝固两个阶段.元素的扩散是控制接头形成的主要因素.连接界面金属间化合物的形成和长大主要有钎料的熔化、沿晶界优先扩散、等温凝固、柱状和蘑菇状长大及纵向长大几个过程.     

Al2O3陶瓷与GH3536真空钎焊接头界面组织与力学性能

采用Ag-5.0Cu-1.0Al-1.25Ti银基钎料通过真空钎焊的方法实现了Al₂O₃陶瓷与镍基高温合金GH3536的连接。为明确钎焊接头的界面形成机理,通过扫描电子显微镜和X射线衍射分析的测试方法研究了接头的界面组织结构与物相组成。同时探究了钎焊温度与保温时间对接头微观组织与力学性能的影响规律,从而实现工艺参数的优化。研究表明：在钎焊温度为970℃,保温时间为10 min的条件下,Al₂O₃/GH3536钎焊接头的典型界面组织为Al₂O₃/Ti₃（Cu, Al）₃O/Ag（s, s）+AlCu₂Ti/TiNi₃+TiFe₂/GH3536,其接头的抗剪强度最高可达到194±10 MPa。随着钎焊温度的升高和保温时间的延长,Ti₃（Cu, Al）₃O反应层的厚度增加,钎缝中的富Cu相减少,AlCu     

钎焊时间对CoFeNiCrCu高熵钎料钎焊SiC陶瓷接头组织与性能的影响

采用CoFeNiCrCu高熵合金为钎料对SiC陶瓷进行了钎焊连接,研究了钎焊时间对接头微观组织和力学性能的影响。结果表明,SiC/CoFeNiCrCu/SiC接头的典型界面组织为：SiC/Cr₂₃C₆+Cu（s, s）+Si（s, s）/HEAF+Cu（s, s）/Cr₂₃C₆+Cu（s, s）+Si（s, s）/SiC。随着钎焊时间的增加,组织中相的种类没有发生变化,接头在高熵效应的作用下仍主要由固溶体组成,接头中反应层厚度逐渐增大。当钎焊时间为90 min时,反应层厚度达到最大为25μm。但过厚的反应层使得接头在冷却过程中产生的应力在反应层中集中并导致反应层中产生裂纹等缺陷。当钎焊温度为1 180℃,保温60 min时,接头剪切强度最高达到61 MPa。此时,裂纹从远离接头的SiC陶瓷开始萌生并向接头方向扩展,最终断裂在陶瓷与反应层的界面处。     

钎焊温度对Ti60/AgCu/ZrO_2接头界面组织及性能的影响

采用AgCu钎料实现了Ti60合金和ZrO_2陶瓷的钎焊连接。使用扫描电子显微镜(Scanning Electron Microscope,SEM)、能谱仪(Energy Dispersive Spectrometer,EDS)和X射线衍射仪(X-Ray Diffractometer,XRD)等分析测试手段,对不同钎焊温度下获得的接头界面组织结构进行了分析。研究表明,Ti60/AgCu/ZrO_2接头典型界面组织为:Ti60合金/α-Ti+Ti_2Cu扩散层/TiCu+TiCu_2/Ag(s,s)+Cu(s,s)/Ti_3Cu_3O反应层/TiO反应层/ZrO_2陶瓷。随着钎焊温度的升高,α-Ti+Ti2Cu扩散层、TiCu+TiCu_2层、Ti3_Cu_3O层及TiO层厚度均逐渐增加,颗粒状Ti-Cu化合物不断长大,Ag(s,s)和Cu(s,s)含量逐渐减少。剪切试验表明,在钎焊温度为900℃、保温时间为10min条件下获得的接头室温抗剪强度最高为124.9 MPa,500℃和600℃抗剪强度分别为83.0 MPa和30.2 MPa。断口分析表明:接头沿ZrO_2陶瓷/钎料界面和靠近该界面的钎缝发生断裂。     

TiAl合金与ZrB2-SiC陶瓷非晶钎焊接头组织与力学性能

采用Cu_(41.83)Ti_(30.21)Zr_(19.76)Ni_(8.19)(at.%)非晶钎料对Ti48Al2Cr2Nb合金与Zr B_2-Si C陶瓷进行真空钎焊连接,通过扫描电镜、能谱分析、X射线衍射以及万能试验机对接头的微观组织和力学性能进行研究。结果表明:Ti Al合金与Zr B_2-Si C陶瓷钎焊接头的界面结构为Ti Al/Ti_2Al/Al Cu Ti/(Ti,Zr)_2(Cu,Ni)+Ti B+Ti Cu/Ti_5Si_3/ZS。当钎焊温度为910℃,随着保温时间的延长,靠近Zr B_2-Si C一侧反应层宽度逐渐增大,接头中弥散分部的Ti B和Ti Cu聚集长大。接头剪切强度随着保温时间的延长先上升后降低,当钎焊温度为910℃,保温20 min时,接头剪切强度最大,为187 MPa,通过对各工艺的接头断口分析,发现接头均断裂在陶瓷侧,断裂方式为脆性断裂。     

Al/Mg搅拌摩擦点焊–钎焊接头的微观组织与拉伸剪切性能研究

采用搅拌摩擦点焊–钎焊工艺进行2A14铝合金和AZ31镁合金的连接,使用扫描电子显微镜(Scanning electron microscope,SEM)、能量色散谱(Energy dispersive spectroscopy,EDS)和X射线衍射仪(X–ray diffraction,XRD)研究不同参数下接头的微观组织、化学成分及物相组成,采用电子万能试验机对接头进行拉伸剪切性能测试。研究结果表明,搅拌区主要由Al–Mg系金属间化合物和少量MgZn相、MgZn₂相组成;热力影响区主要由富Zn固溶体和Mg₇Zn₃相组成;热影响区靠近铝合金处的锌钎料没有与其他元素发生反应,靠近镁合金处的锌钎料与镁元素发生反应,生成了Mg–Zn系金属间化合物。当轴肩下压量为0.5 mm,搅拌头旋转速度为950 r/min时,接头的拉伸剪切载荷达到最大值7.6 kN。     

以Ti/V/Cu、V/Cu为中间层的TiAl合金

用真空扩散连接方法对TiAl/Ti/V/Cu/40Cr钢及TiAl/V/Cu/40Cr钢进行了研究。结果表明,以Ti/V/Cu作中间层的接头拉伸强度高于以V/Cu作中间层的接头强度。界面分析显示,Ti/V、V/Cu、Cu/40Cr钢的各个结合界面处未形成金属间化合物,而TiAl/Ti的结合界面上有Ti3Al产生;在TiAl/V的界面上有Ti3Al、Al3V两种金属间化合物产生;界面上脆性金属间化合物的产生是接头发生断裂的原因。     

有翼高超声速再入飞行器气动设计难点问题

有翼高超声速再入飞行器是近年来的研究热点,气动设计是飞行器设计的关键。为了更清楚地认识有翼高超声速再入飞行器气动设计的难点问题,对有翼高超声速再入飞行器的发展、优势及总体任务剖面进行了介绍,从5个方面详细介绍了该类飞行器气动设计的难点问题,包括多约束复杂面对称气动布局设计、高温真实气体效应对气动特性影响、天地差异与天地换算方法、反作用控制系统(RCS)喷流干扰对气动特性的影响以及气动数据不确定度等,简要阐明了这些难点问题对总体设计的重要性以及初步的解决思路,为有翼高超声速再入飞行器气动设计提供了一些参考。     

Simulation and Analysis of Crashworthiness of Fuel Tank for Helicopters

Crashworthiness requirement of fuel tanks is one of the important requirements in helicopter designs. The relations among the protection frame, textile layer and rubber layer of the fuel tank are introduced. Two appropriate FE models are established, one is for an uncovered helicopter fuel tank without protection frame, and the other is for fuel tank with protection frame. The dynamic responses of the two types of fuel tanks impinging on the ground with velocities of 17.3 m/s are numerically simulated for the purpose of analyzing energy-absorbing capabilities of the textile layer and protection frame. The feasibility of the current crashworthiness design of the fuel tank is examined though comparing the dynamic response behaviors of the two fuel tanks.     

The effect of inlet conditions on the flow and heat transfer in multiple rotating cavity with axial throughflow

This paper discusses experimental results from two different build configurations of a heated multiple rotating cavity test rig.Measurements of heat transfer from the discs and tangential velocities are presented.The test rig is a 70% full scale version of a high pressure compressor stack of an axial gas turbine engine.Of particular interest are the internal cylindrical cavities formed by adjacent discs and the interaction of these with a central axial throughflow of cooling air.Tests were carried out for a range of non-dimensional parameters representative of high pressure compressor internal air system flows(Re up to 5×106 and Rez up to 2×105).Two different builds have been tested.The most significant difference between these two build configurations is the size of the annular gap between the(non-rotating) drive shaft and the bores of the discs.The heat transfer data were obtained from thermocouple measurements of surface temperature and a conduction solution method.The velocity measurements were made using a two component,LDA system.The heat transfer results from the discs show differences between the two builds.This is attributed to the wider annular gap allowing more of the throughflow to penetrate into the cavity.There are also significant differences between the radial distributions of tangential velocity in the two builds of the test rig.For the narrow annular gap,there is an increase of non-dimensional tangential velocity V/Ωr with radial location to solid body rotation V/Ωr=1.For the wider annular gap,the non-dimensional velocities show a decrease with radial location to solid body rotation.      

ν-gap度量及其在飞行控制律评估中的应用

 传统控制律评估方法主要用于单输入单输出（SISO）系统，且对模型参数摄动考虑不够全面,针对这些不足，研究了ν-gap度量方法。在介绍系统广义稳定裕度相关概念的基础上，给出了ν-gap度量的定义、特点和性质以及近似摄动模型的计算，提出ν-gap度量评估控制律的步骤。实例结果表明，该方法不仅克服了上述传统评估方法的缺陷，而且还有根据所求的各摄动影响情况忽略影响小的元素，以减少计算量及可以找到最坏情况下的参数摄动组合等优点。     

突破技术趋同，波音再现竞争优势

 波音公司面临着来自空客公司的巨大挑战,企业战略性创新才是公司成功的关键。为此波音公司的全部战略性研究集中在扩大产品的差异性上,体现在3个方面：电子化（e-Enabled）运营环境、整体复合材料机身部件的制造技术和支持波音787客机的全球协同环境（GCE）。     

临近空间飞行器测控与信息传输系统频段选择

 临近空间飞行器是高性能信息化武器平台,测控（TT&;C）与信息传输系统是其信息保障的核心,而选择合理、可行的频段是展开系统设计的前提和基础。频段选择影响到整个技术方案的制定,是一个需综合考虑、影响深远并具有战略意义的关键问题,从国际电联（ITU）国际标准、高速数传、接收信噪比（SNR）、“三抗”、超视距中继、黑障、雨衰以及设备研制成熟度8个方面全面、细致论证了近空间平台测控系统的频段选择问题,最终得出在视距链路中以Ka频段为宜,在超视距链路中以Ku/Ka双频段为宜的结论。     

基于弯曲激波压缩系统的高超声速进气道反设计研究进展

总结了近十年来弯曲激波压缩研究的主要成果。提出了弯曲激波压缩系统的新概念,即利用特殊设计的楔形弯曲压缩面或空间弯曲压缩面,产生一系列与前缘弱激波相互交汇或叠加的压缩波系,从而使前缘激波弯曲,形成特殊的弯曲激波,它与波后的等熵压缩波来共同完成对气流的压缩。在此基础上,实现了由给定出口气动参数的超声速内流道反设计,实现了由给定压缩面压力分布和给定压缩面马赫数分布要求的型面反设计,实现了由给定激波波面的压缩型面反设计。研究证明,弯曲压缩面-弯曲激波压缩系统具有良好的综合气动性能,为高性能高超声速进气系统的气动设计提供了一种全新的设计方法。     

Integrated Entry Guidance for Reusable Launch Vehicle

A method for the implementation of integrated three-degree-of-freedom constrained entry guidance for reusable launch vehicle is presented. Given any feasible entry conditions, terminal area energy management interface conditions, and the reference trajectory generated onboard then, the method can generate a longitudinal guidance profile rapidly, featuring linear quadratic regular method and a proportional-integral-derivative tracking law with time-varying gains, which satisfies all the entry corridor constraints and meets the requirements with high precision. Afterwards, by utilizing special features of crossrange parameter, establishing bank-reversal corridor, and determining bank-reversals according to dynamically adjusted method, the algorithm enables the lateral entry guidance system to fly a wide range of missions and provides reliable and good performance in the presence of significant aerodynamic modeling uncertainty. Fast trajectory guidance profiles and simulations with a reusable launch vehicle model for various missions and aerodynamic uncertain-ties are presented to demonstrate the capacity and reliability of this method.     

Experimental Study on Effects of Fuel Injection on Scramjet Combustor Performance

In order to investigate the effects of fuel injection distribution on the scramjet combustor performance, there are conducted three sets of test on a hydrocarbon fueled direct-connect scramjet test facility. The results of Test A, whose fuel injection is carried out with injectors located on the top-wall and the bottom-wall, show that the fuel injection with an appropriate close-front and centralized distribution would be of much help to optimize combustor performances. The results of Test B, whose fuel injection is performed at the optimal injection locations found in Test A, with a given equivalence ratio and different injection proportions for each injector, show that this injection mode is of little benefit to improve combustor performances. The results of Test C with a circumferential fuel injection distribution displaies the possibility of ameliorating combustor performance. By analyzing the effects of injection location parameters on combustor performances on the base of the data of Test C, it is clear that the injector location has strong coupled influences on combus- tor performances. In addition, an inner-force synthesis specific impulse is used to reduce the errors caused by the disturbance of fuel supply and working state of air heater while assessing combustor performances.     

(高)超声速流动试验技术及研究进展

近年来,与高速飞行器相关的(高)超声速流动受到了极大的关注。这类流动所具有的非定常性、强梯度和可压缩性对试验方法和风洞设计技术提出了挑战。超声速纳米示踪平面激光散射(NPLS)技术是由作者所在团队研发的非接触光学测试技术。它能够以较高的空间分辨率来揭示超声速三维流场的一个瞬态剖面的时间解析的流动结构。介绍了NPLS技术以及基于NPLS开发的密度场测量、雷诺应力测量和气动光学波前测量等方法,并回顾了这些技术在超声速边界层、超声速混合层、超声速压缩拐角、激波/边界层相互作用和光学头罩绕流等流动中的应用,清晰地再现了边界层、混合层、激波等典型流场结构及其时空演化特性。另外,为了模拟和研究高空大气条件下边界层自然转捩和超声速混合层的转捩特性,介绍了高超声速静风洞、超-超混合层风洞的设计技术以及层流化喷管的设计方法。