镍掺杂对α-Al2O3烧结过程、微观结构及力学性能的影响

 首先采用非均相沉淀包裹法制备金属镍包裹α-Al₂O₃复合微球粉体，然后采用热压烧结制备了Al₂O₃/Ni金属陶瓷。通过X射线衍射仪（XRD）、扫描电子显微镜（SEM）、能谱仪（EDS）对复合粉体及热压烧结产物的成分和结构进行了表征，利用阿基米德法测量了复合陶瓷的密度，分别通过三点弯曲法和单边切口横梁法对陶瓷试条的抗弯强度和断裂韧性进行评估。研究发现：金属镍的引入活化了α-Al₂O₃的烧结，镍粒子均匀地分布在氧化铝的晶界上，增加了弱界面，提高了氧化铝的断裂韧性，最高可达7.62 MPa·m^1/2。

Effects of Ni-doping on the Sintering Process, Microstructure and Mechanical Properties of α-Al2O3

Ni coated α-Al₂O₃ composite microspheres are first synthesized by heterogeneous precipitation coating method, and then Al₂O₃/Ni cermets are prepared by hot press sintering of the as prepared Ni-coated α-Al₂O₃ powders. The microstructural features of the resultant Al₂O₃ Ni cermets and the crystalline phases of precipitated precursors, reduced powders and sintered cermets are characterized by scanning electron microscope(SEM), energy dispersive spectroscopy(EDS), and X-ray diffractometer (XRD). The relative densities of cermets are measured by Archimedes’ method, and the flexural strength and fracture toughness are estimated by the three point bending and single-edge notched beam methods. The results exhibit that the Ni-doping activated the sintering of α-Al₂O₃, and Ni particles are uniformly distributed at the interface of alumina grains, which increase the weak interfaces, and enhance the fracture toughness of alumina, achieving a maximum value of 7.62 MPa·m^1/2.