Effect of sodium tartrate concentrations on morphology and characteristics of anodic oxide film on titanium alloy Ti–10V–2Fe–3Al

The effect of sodium tartrate concentrations on morphology and characteristics of ano-dic oxide film on titanium alloy was investigated. The alloy substrates were anodized in different concentration solutions of sodium tartrate with the addition of PTFE emulsion and their morphol-ogy and characteristics were analyzed. The anodic oxide film presented a uniform petaloid drums and micro-cracks morphology. Additionally, micro-cracks dramatically swelled with the increase of the tartrate concentrations. The thickness of the anodic oxide film increased with the concentra-tions until the concentration reached 15 g/L. The results of Raman analysis illustrate that all sam-ples have similarity in the crystal structure, consisting of mainly amorphous TiO2, some anatase TiO2 and a small amount of rutile TiO2. And the ratios of anatase TiO2 and rutile TiO2 increase with the concentrations until it reaches 15 g/L. Furthermore, the intensity of the peaks increases with enhanced concentrations until the concentration reaches 15 g/L. The corrosion resistance of the anodic oxide film is increased by the sodium tartrate with higher concentrations before 15 g/L. The coefficient of friction of the anodic oxide film reduces with the concentrations until the concentration reaches 15 g/L, then the coefficient of friction of the anodic oxide film increases with the concentrations.

Effect of sodium tartrate concentrations on morphology and characteristics of anodic oxide film on titanium alloy Ti–10V–2Fe–3Al

The effect of sodium tartrate concentrations on morphology and characteristics of ano-dic oxide film on titanium alloy was investigated. The alloy substrates were anodized in different concentration solutions of sodium tartrate with the addition of PTFE emulsion and their morphol-ogy and characteristics were analyzed. The anodic oxide film presented a uniform petaloid drums and micro-cracks morphology. Additionally, micro-cracks dramatically swelled with the increase of the tartrate concentrations. The thickness of the anodic oxide film increased with the concentra-tions until the concentration reached 15 g/L. The results of Raman analysis illustrate that all sam-ples have similarity in the crystal structure, consisting of mainly amorphous TiO2, some anatase TiO2 and a small amount of rutile TiO2. And the ratios of anatase TiO2 and rutile TiO2 increase with the concentrations until it reaches 15 g/L. Furthermore, the intensity of the peaks increases with enhanced concentrations until the concentration reaches 15 g/L. The corrosion resistance of the anodic oxide film is increased by the sodium tartrate with higher concentrations before 15 g/L. The coefficient of friction of the anodic oxide film reduces with the concentrations until the concentration reaches 15 g/L, then the coefficient of friction of the anodic oxide film increases with the concentrations.