Preparation and Properties of an Out-of-Autoclave T800/607 C/E Composite |
| |
| ZHOU Yu,FAN Mengjin,SHANG Chengyuan,LING Hui and SUN Hongjie.Preparation and Properties of an Out-of-Autoclave T800/607 C/E Composite[J].Aerospace Materials & Technology,2017,47(3):57-60. |
| |
| Authors: | ZHOU Yu FAN Mengjin SHANG Chengyuan LING Hui and SUN Hongjie |
| |
| Institution: | Aerospace Research Institute of Material & Processing Technology, Beijing 100076,Aerospace Research Institute of Material & Processing Technology, Beijing 100076,Aerospace Research Institute of Material & Processing Technology, Beijing 100076,Aerospace Research Institute of Material & Processing Technology, Beijing 100076 and Aerospace Research Institute of Material & Processing Technology, Beijing 100076 |
| |
| Abstract: | The cure kinetics of the epoxy resin 607 for an out-of-autoclave(OoA) composite was investigated by differential scanning calorimetry(DSC),and the cure kinetic formula of the resin was established. The prepreg with dry fiber regions remaining and the OoA composites were prepared. The quality and properties of the T800/607 composite were studied. The results indicated that the T800/607 prepreg owed a tack life at room temperature over 30 days and the void content of the OoA composite is far below 1%. The short beam shear strength and flexural strength of the OoA composite are 96.7 and 1480 MPa,respectively, which can be compared with the autoclave cured ones. |
| |
| Keywords: | Composite Out of autoclave Cure dynamics Prepreg |