| 小角度晶界对DD5镍基单晶高温合金力学性能的影响 |
| |
| 引用本文： | 秦健朝,崔仁杰,黄朝晖,赵金乾,张毅鹏,宗毳,陈升平.小角度晶界对DD5镍基单晶高温合金力学性能的影响[J].航空材料学报,2017,37(3). |
| |
| 作者姓名： | 秦健朝 崔仁杰 黄朝晖 赵金乾 张毅鹏 宗毳 陈升平 |
| |
| 作者单位： | 北京航空材料研究院 先进高温结构材料重点实验室,北京,100095 |
| |
| 摘 要： | 采用籽晶法制备了二代镍基单晶高温合金DD5小角度晶界试样,研究小角度晶界对DD5合金力学性能的影响。结果表明:在870℃中温拉伸中,晶界角度小于16.1°时,合金抗拉强度和屈服强度无明显变化;晶界角度小于11.4°时,伸长率维持在15%以上;晶界角度大于11.4°后,伸长率开始快速下降;在980℃/250 MPa持久条件下,当晶界角度小于5.1°时,持久寿命维持在140 h以上;当晶界角度大于5.1°时,持久寿命随晶界角度增大开始缓慢下降,至14.8°时,持久寿命仍保持为原来的85%;当晶界角度大于14.8°后持久寿命开始快速下降;在1093℃/158MPa持久条件下,当晶界角度小于5.1°时,持久寿命维持在30 h以上;当晶界角度大于5.1°时,持久寿命随晶界角度增大而下降。
|
| 关 键 词： | 高温合金 小角度晶界 持久寿命 拉伸性能 |
Effect of Low Angle Grain Boundaries on Mechanical Properties of DD5 Single Crystal Ni-base Superalloy |
| |
| QIN Jianchao,CUI Renjie,HUANG Zhaohui,ZHAO Jingqian,ZHANG Yipeng,ZONG Cui,CHEN Shengping.Effect of Low Angle Grain Boundaries on Mechanical Properties of DD5 Single Crystal Ni-base Superalloy[J].Journal of Aeronautical Materials,2017,37(3). |
| |
| Authors: | QIN Jianchao CUI Renjie HUANG Zhaohui ZHAO Jingqian ZHANG Yipeng ZONG Cui CHEN Shengping |
| |
| Abstract: | The effects of low angle grain boundaries on the mechanical properties of second generation single crystal superalloy DD5 were investigated and the test specimens were prepared by using seeds.The results show that at 870 ℃,the yield strength and breaking strength showed no difference when the angle is below 16.1°.The elongation is higher than 15% when the angle is below 11.4°,but the elongation decreases quickly when angle is above 11.4°.At 980 ℃/250 MPa,the rupture life is higher than 130 h when the angle is below 5.1°,and decreased slowly when the angle is above 5.1°.The rupture life still remaines 85% when the angle is 14.8°.But the rupture life decreases quickly when the angle is above 14.8°.At 1093 ℃/158 MPa,the rupture life is higher than 30 h when the angle is below 5.1°,and decreases when the angle is above 5.1°. |
| |
| Keywords: | superalloy low angle grain boundary rupture life tensile property |
| 本文献已被 CNKI 万方数据 等数据库收录！ |
|